CN107553624A - 一种阻燃竹地板的加工方法 - Google Patents

一种阻燃竹地板的加工方法 Download PDF

Info

Publication number
CN107553624A
CN107553624A CN201710809069.2A CN201710809069A CN107553624A CN 107553624 A CN107553624 A CN 107553624A CN 201710809069 A CN201710809069 A CN 201710809069A CN 107553624 A CN107553624 A CN 107553624A
Authority
CN
China
Prior art keywords
bamboo
processing method
flame
retardant agent
blank plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710809069.2A
Other languages
English (en)
Inventor
王莉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710809069.2A priority Critical patent/CN107553624A/zh
Publication of CN107553624A publication Critical patent/CN107553624A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃竹地板的加工方法，所述的加工方法，包括以下步骤：(1)阻燃树脂胶的制备：所述阻燃树脂胶由70～98wt％的热塑性聚合物和2～30wt％的所述复合阻燃剂为原料制得的，所述复合阻燃剂由0.1～50wt％的介孔分子筛和50～99.9wt％的纳米改性有机硅为原料制得，以质量百分含量计；(2)将表面涂胶竹条弦面侧拼热压成侧压板；(3)制成竹坯板：将步骤(2)制成的竹坯板，将竹坯板上、下面打胶，然后进行固化，按纵向、横向交叉叠放，并对齐进行组坯热压，再经修边、开榫槽、砂光、涂饰、干燥工序制成阻燃竹地板。

Description

一种阻燃竹地板的加工方法
技术领域
本发明涉及一种竹地板的加工方法，具体地说，涉及一种阻燃竹 地板的加工方法。
背景技术
竹地板是一类小规格的竹材人造板，它具有表面硬度高、光洁度 好、耐磨损、色泽淡雅的优点，格调清新高雅，能产生古朴自然的 装饰效果；由于热传导率低，所以还有冬暖夏凉的特性，无论在什 么季节，都可以舒适地赤脚在上面行走，特别适合铺装在老人、小孩的起居室，因而深受人们欢迎；但是我们在选用时，也要考虑其安 全性能，如遇明火时，因温度过高，就会燃烧，造成更为严重的损 失。
发明内容
为了克服现有技术的不足，本发明提供一种阻燃竹地板的加工方 法。
本发明采用了如下技术方案：一种阻燃竹地板的加工方法，所 述的加工方法，包括以下步骤：
(1)阻燃树脂胶的制备：所述阻燃树脂胶由70～98wt％的热 塑性聚合物和2～30wt％的所述复合阻燃剂为原料制得的，所述 复合阻燃剂由0.1～50wt％的介孔分子筛和50～99.9wt％的 纳米改性有机硅为原料制得，以质量百分含量计；
(2)将表面涂胶竹条弦面侧拼热压成侧压板，平压压力为 1-2MPa，侧压压力为1.5-2.5MPa，热压温度为140-160℃，热压时 间为8-12min，
(3)制成竹坯板：将步骤(2)制成的竹坯板，将竹坯板上、下 面打胶，打胶厚度0.8-1mm，然后进行固化10-20min，按纵向、横 向交叉叠放，并对齐进行组坯热压，压力为3-3.5MPa，热压温度为 140-160℃，热压时间为8-12min，再经修边、开榫槽、砂光、涂饰、 干燥工序制成阻燃竹地板。
进一步地，所述热塑性聚合物的用量优选为80～98wt％、所述复 合阻燃剂的用量优选为2～20wt％；
进一步地，所述热塑性聚合物的用量进一步优选为85～ 94wt％、所述复合阻燃剂的用量进一步优选为6～15wt％。
有益效果：本发明复合阻燃剂的制备原料无机介孔分子筛，具有 巨大的比表面积，其与有机硅阻燃剂结合使得无机介孔分子筛发挥协 同效应，从而大幅度提高了有机硅阻燃剂的阻燃效力。
具体实施方式
下面结合实施例对本发明做进一步说明：
实施例1：
一种阻燃竹地板的加工方法，所述的加工方法，包括以下步骤：
(1)阻燃树脂胶的制备：所述阻燃树脂胶由70～98wt％的热 塑性聚合物和2～30wt％的所述复合阻燃剂为原料制得的，所述 复合阻燃剂由0.1～50wt％的介孔分子筛和50～99.9wt％的 纳米改性有机硅为原料制得，以质量百分含量计；所述热塑性聚合物 的用量进一步优选为85～94wt％、所述复合阻燃剂的用量进一步优 选为6～15wt％。
(2)将表面涂胶竹条弦面侧拼热压成侧压板，平压压力为 1-2MPa，侧压压力为1.5-2.5MPa，热压温度为140-160℃，热压时 间为8-12min，
(3)制成竹坯板：将步骤(2)制成的竹坯板，将竹坯板上、下 面打胶，打胶厚度0.8-1mm，然后进行固化10-20min，按纵向、横 向交叉叠放，并对齐进行组坯热压，压力为3-3.5MPa，热压温度为 140-160℃，热压时间为8-12min，再经修边、开榫槽、砂光、涂饰、 干燥工序制成阻燃竹地板。

Claims (3)

1.一种阻燃竹地板的加工方法，其特征在于，所述的加工方法，包括以下步骤：
(1)阻燃树脂胶的制备：所述阻燃树脂胶由70～98wt％的热塑性聚合物和2～30wt％的所述复合阻燃剂为原料制得的，所述复合阻燃剂由0.1～50wt％的介孔分子筛和50～99.9wt％的纳米改性有机硅为原料制得，以质量百分含量计；
(2)将表面涂胶竹条弦面侧拼热压成侧压板，平压压力为1-2MPa，侧压压力为1.5-2.5MPa，热压温度为140-160℃，热压时间为8-12min，
(3)制成竹坯板：将步骤(2)制成的竹坯板，将竹坯板上、下面打胶，打胶厚度0.8-1mm，然后进行固化10-20min，按纵向、横向交叉叠放，并对齐进行组坯热压，压力为3-3.5MPa，热压温度为140-160℃，热压时间为8-12min，再经修边、开榫槽、砂光、涂饰、干燥工序制成阻燃竹地板。
2.根据权利要求1所述的阻燃竹地板的加工方法，其特征在于，所述热塑性聚合物的用量优选为80～98wt％、所述复合阻燃剂的用量优选为2～20wt％。
3.根据权利要求2所述的阻燃竹地板的加工方法，其特征在于，所述热塑性聚合物的用量进一步优选为85～94wt％、所述复合阻燃剂的用量进一步优选为6～15wt％。
CN201710809069.2A 2017-09-09 2017-09-09 一种阻燃竹地板的加工方法 Pending CN107553624A (zh)