CN107541142A - A kind of high temperature organosilicon paint and its production method - Google Patents
A kind of high temperature organosilicon paint and its production method Download PDFInfo
- Publication number
- CN107541142A CN107541142A CN201710965099.2A CN201710965099A CN107541142A CN 107541142 A CN107541142 A CN 107541142A CN 201710965099 A CN201710965099 A CN 201710965099A CN 107541142 A CN107541142 A CN 107541142A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- paint
- production method
- organic siliconresin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature organosilicon paint, is made up of following raw material according to parts by weight：Organic siliconresin：30 40 parts；Heat resistant paint：5 10 parts；Solvent：20 30 parts；Auxiliary agent：25 parts；A kind of production method of high temperature organosilicon paint, the production method of the high temperature organosilicon paint comprise the following steps：S1；Stirred under normal pressure；S2：Grinding；S3 is packed.Organosilicon heat-resistant lacquer is formulated by organic siliconresin, heat resistant paint, auxiliary agent, solvent etc..Product has surface drying dry rapid, and adhesive force is good, pliability is good, (list) bi-component package, easy for construction.The characteristics of non-viscous paints such as high temperature resistant.
Description
Technical field
The present invention relates to high temperature organosilicon paint technical field, specially a kind of high temperature organosilicon paint and its production
Method.
Background technology
High temperature organosilicon paint is a kind of high performance high-temperature resistant coating, and film has good closure after film forming
Energy.Product energy resistance to 250-800 DEG C of high temperature (depending on color and luster).Suitable for all resistant to elevated temperatures environment, high temperature corrosion Jie is protected it from
The erosion of matter.Such as engine housing, chimney, blast pipe, heat exchanger.Product has surface drying dry rapid, and adhesive force is good, flexible
Property is good, (list) bi-component package, easy for construction.The characteristics of non-viscous paints such as high temperature resistant.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of organosilicon fire-resistant proposed applies
Material and its production method.
To achieve the above object, the present invention provides following technical scheme：
A kind of high temperature organosilicon paint, it is made up of following raw material according to parts by weight：
Organic siliconresin：30 parts；
Heat resistant paint：5 parts；
Solvent：20 parts；
Auxiliary agent：2 parts；
Preferably, the organic siliconresin.
Preferably, the heat resistant paint particle diameter is 400 mesh.
Preferably, a kind of production method of high temperature organosilicon paint, it is characterised in that：The high temperature organosilicon paint
Production method comprises the following steps：
S1：Stirred under normal pressure：Organic siliconresin：30 parts；Heat resistant paint：5 parts；Solvent：20 parts；Auxiliary agent：2 parts；Stirring three
Ten minutes to 50 minutes,
S2：Enter grinder and be ground to fineness 30um
S3：Packaging：S2 product is packed according to specification requirement.
A kind of high temperature organosilicon paint provided by the invention, the high temperature organosilicon paint not only have preferable anti-corrosion
Performance, and be that a kind of cost is cheap, excellent performance, full-featured high temperature organosilicon paint.
Embodiment
Based on the embodiment in the present invention, those of ordinary skill in the art are obtained under the premise of creative work is not made
The every other embodiment obtained, belongs to the scope of protection of the invention.
Embodiment 1
A kind of high temperature organosilicon paint, it is made up of following raw material according to parts by weight：
Organic siliconresin：32 parts；
Heat resistant paint：6 parts；
Solvent：21 parts；
Auxiliary agent：2 parts；
Preferably, the organic siliconresin.
Preferably, the heat resistant paint particle diameter is 400 mesh.
A kind of production method of high temperature organosilicon paint, the production method of the high temperature organosilicon paint include following step
Suddenly：
S1：Organic siliconresin is stirred under normal pressure：32 parts；Heat resistant paint：6 parts；Solvent：21 parts；Auxiliary agent：2 parts；Stir 30
Minute was by 50 minutes；
S2：Enter grinder and be ground to fineness 30um；
S3：Packaging：S2 product is packed according to specification requirement.
Embodiment 2
A kind of high temperature organosilicon paint, it is made up of following raw material according to parts by weight：
Organic siliconresin：33 parts；
Heat resistant paint：7 parts；
Solvent：25 parts；
Auxiliary agent：3 parts；
Preferably, the organic siliconresin.
Preferably, the heat resistant paint particle diameter is 400 mesh.
A kind of production method of high temperature organosilicon paint, the production method of the high temperature organosilicon paint include following step
Suddenly：
S1：Stirred under normal pressure：Organic siliconresin：33 parts；Heat resistant paint：7 parts；Solvent：25 parts；Auxiliary agent：3 parts；Stirring three
Ten minutes to 50 minutes；
S2：Enter grinder and be ground to fineness 30um；
S3：Packaging：S2 product is packed according to specification requirement.
Embodiment 3
A kind of high temperature organosilicon paint, the formula of the high temperature organosilicon paint is by including the component systems of following parts by weight
Into：
Organic siliconresin：40 parts；
Heat resistant paint：10 parts；
Solvent：30 parts；
Auxiliary agent：5 parts；
Preferably, the organic siliconresin.
Preferably, the heat resistant paint particle diameter is 400 mesh.
A kind of production method of high temperature organosilicon paint, the production method of the high temperature organosilicon paint include following step
Suddenly：
S1：Stirred under normal pressure：Organic siliconresin：40 parts；Heat resistant paint：10 parts；Solvent：30 parts；Auxiliary agent：5 parts；Stirring three
Ten minutes to 50 minutes；
S2：Enter grinder and be ground to fineness 30um；
S3：Packaging：S2 product is packed according to specification requirement.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
- A kind of 1. high temperature organosilicon paint, it is characterised in that：It is made up of following raw material according to parts by weight：Organic siliconresin：30-40 parts；Heat resistant paint：5-10 parts；Solvent：20-30 parts；Auxiliary agent：2-5 parts.
- A kind of 2. high temperature organosilicon paint according to claim 1, it is characterised in that：By following raw material according to parts by weight Composition：Organic siliconresin：30 parts；Heat resistant paint：5 parts；Solvent：20 parts；Auxiliary agent：2 parts.
- A kind of 3. high temperature organosilicon paint according to claim 1, it is characterised in that：The organic siliconresin.
- A kind of 4. high temperature organosilicon paint according to claim 1, it is characterised in that：The heat resistant paint particle diameter is 400 mesh.
- A kind of 5. high temperature organosilicon paint according to claim 1, it is characterised in that：The auxiliary agent is defoamer, stream Flat agent.
- A kind of 6. production method of high temperature organosilicon paint as claimed in claim 1, it is characterised in that：The organosilicon fire-resistant The production method of coating comprises the following steps：S1：Stirred under normal pressure：Organic siliconresin：30 parts；Heat resistant paint：5 parts；Solvent：20 parts；Auxiliary agent：2 parts；Stir 30 points Clock was by 50 minutes；S2：Enter grinder and be ground to fineness 30um；S3：Packaging：S2 product is packed according to specification requirement.