CN101747833A - Super high-temperature resistant coating and preparation method thereof - Google Patents
Super high-temperature resistant coating and preparation method thereof Download PDFInfo
- Publication number
- CN101747833A CN101747833A CN200810204516A CN200810204516A CN101747833A CN 101747833 A CN101747833 A CN 101747833A CN 200810204516 A CN200810204516 A CN 200810204516A CN 200810204516 A CN200810204516 A CN 200810204516A CN 101747833 A CN101747833 A CN 101747833A
- Authority
- CN
- China
- Prior art keywords
- coating
- super high
- temperature resistant
- resistant coating
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a super high-temperature resistant coating and a preparation method thereof. The coating comprises the following components in part by weight: 40 to 60 parts of organosilicon modified resin, 20 to 45 parts of coated metal powder, 10 to 15 parts of additive and 10 to 25 parts of solvent. Compared with the prior art, the super high-temperature resistant coating can protect a metal surface from being corroded in the operating state and high and low temperature alternating state of ultrahigh-temperature equipment, and has the advantages that: (1) the coating has excellent temperature-resistant performance and can be used at the temperature of higher than 800 DEG C for a long time; (2) the coating has the extremely good corrosion resistance on the premise of having excellent temperature tolerance; (3) the phenomena such as cracking, rusting and the like cannot be generated when an ambient temperature suddenly drops; and (4) priming paint is the same as the coating with easy construction.
Description
Technical field
The present invention relates to coating, relate in particular to a kind of super high-temperature resistant coating and preparation method thereof.
Background technology
At present, along with the continuous adjustment of production technique such as all kinds of chemical plant, refinery, power plant is upgraded, its all kinds of devices as: high-temperature boiler, gas barrier, chimney etc. are more and more higher to the requirement of every function of heat-resistant coating, originally traditional heat-resistant coating temperature resistant range is up to 700 ℃ usually, and temperature-change resistance is poor, return under the normal temperature state and work as high temperature service, the defective of its heat-resistant coating preservative property difference also can come out; So be badly in need of the heatproof protective system that a kind of heatproof can reach about 800 ℃, temperature-change resistance is good and antiseptic property is good on the market.
Summary of the invention
Purpose of the present invention is exactly to provide a kind of simple, corrosion-resistant fabulous super high-temperature resistant coating and preparation method thereof of constructing for the defective that overcomes above-mentioned prior art existence.
Purpose of the present invention can be achieved through the following technical solutions:
A kind of super high-temperature resistant coating is characterized in that, this coating comprises following component and content (weight part):
Organic-silicon-modified resin 40-60;
Coating metal powder 20-45;
Additive 10-15;
Solvent 10-25.
Described coating metal powder comprises coating iron powder or coating copper powder.
Described additive comprises hydrogenated castor oil, organosilane or vinylformic acid fire resistant resin.
Described solvent comprises dimethylbenzene and/or butanols.
A kind of preparation method of super high-temperature resistant coating is characterized in that, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content (weight part):
Organic-silicon-modified resin 40-60
Coating metal powder 20-45
Additive 10-15
Solvent 10-25;
(2) organic-silicon-modified resin, 3/1/2nd~four solvents are added in the reactor, 500-700 ℃ of pyroreaction hydrolysis, work in-process are made in polymerization 24 hours;
(3) work in-process are added in the equipment, add coating metal powder, additive, residual solvent again, 600-750 rev/min was stirred 35 minutes down;
(3) leave standstill 12-24 hour, make super high-temperature resistant coating.
Described coating metal powder comprises coating iron powder or coating copper powder.
Described additive comprises hydrogenated castor oil, organosilane or vinylformic acid fire resistant resin.
Described solvent comprises dimethylbenzene and/or butanols.
Compared with prior art, the present invention can effectively protect the metal table not corrode at ultrahigh-temperature equipment working state and high and low temperature alternative state, has the following advantages:
(1) the heat resistance excellence can be for a long time used being higher than under 800 ℃ the temperature;
(2) having under the excellent durothermic prerequisite, has fabulous erosion resistance;
(3), can not produce phenomenons such as cracking, corrosion thus when the envrionment temperature rapid drawdown;
(4) the bottom surface lacquer is constructed simply for a kind of coating.
Embodiment
The invention will be further described below in conjunction with specific embodiment.
Embodiment 1
A kind of preparation method of super high-temperature resistant coating, this method comprises following processing step:
(1) will have silicon modified resin 40kg, solvent xylene 15kg to add 500 ℃ of pyroreaction hydrolysis in the still, work in-process were made in polymerization in 24 hours;
(2) will make in the work in-process adding equipment, and add again behind coating metal powder 20kg and additive hydrogenated castor oil 10kg, the solvent xylene 5kg and stirred (600 rev/mins) 35 minutes;
(3) leave standstill 12 hours, make super high-temperature resistant coating, test index;
(4) send quality test portion qualified after, packing warehouse-in.
Embodiment 2
A kind of preparation method of super high-temperature resistant coating, this method comprises following processing step:
(1) will have silicon modified resin 50kg, solvent butanols 15kg to add 700 ℃ of pyroreaction hydrolysis in the still, work in-process were made in polymerization in 24 hours;
(2) will make in the work in-process adding equipment, and add again behind coating metal powder 30kg and additive organosilane 10kg, the solvent butanols 5kg and stirred (600-750 rev/min) 35 minutes;
(3) leave standstill 12 hours, make super high-temperature resistant coating, test index;
(4) send quality test portion qualified after, packing warehouse-in.
Embodiment 3
A kind of preparation method of super high-temperature resistant coating, this method comprises following processing step:
(1) will have silicon modified resin 60kg, solvent 15kg to add pyroreaction hydrolysis in the still, work in-process were made in polymerization in 24 hours;
(2) will make to add again in the work in-process adding equipment behind coating metal powder 45kg and additive 15kg, the solvent 5kg and stir (600 rev/mins) 35 minutes;
(3) leave standstill 24 hours, make super high-temperature resistant coating, test index;
(4) send quality test portion qualified after, packing warehouse-in.
Claims (8)
1. a super high-temperature resistant coating is characterized in that, this coating comprises following component and content (weight part):
Organic-silicon-modified resin 40-60;
Coating metal powder 20-45;
Additive 10-15;
Solvent 10-25.
2. super high-temperature resistant coating according to claim 1 is characterized in that, described coating metal powder comprises coating iron powder or coating copper powder.
3. super high-temperature resistant coating according to claim 1 is characterized in that, described additive comprises hydrogenated castor oil, organosilane or vinylformic acid fire resistant resin.
4. super high-temperature resistant coating according to claim 1 is characterized in that described solvent comprises dimethylbenzene and/or butanols.
5. the preparation method of a super high-temperature resistant coating as claimed in claim 1 is characterized in that, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content (weight part):
Organic-silicon-modified resin 40-60
Coating metal powder 20-45
Additive 10-15
Solvent 10-25;
(2) organic-silicon-modified resin, 3/1/2nd~four solvents are added in the reactor, 500-700 ℃ of pyroreaction hydrolysis, work in-process are made in polymerization 24 hours;
(3) work in-process are added in the equipment, add coating metal powder, additive, residual solvent again, 600-750 rev/min was stirred 35 minutes down;
(3) leave standstill 12-24 hour, make super high-temperature resistant coating.
6. the preparation method of super high-temperature resistant coating according to claim 5 is characterized in that, described coating metal powder comprises coating iron powder or coating copper powder.
7. the preparation method of super high-temperature resistant coating according to claim 5 is characterized in that, described additive comprises hydrogenated castor oil, organosilane or vinylformic acid fire resistant resin.
8. the preparation method of super high-temperature resistant coating according to claim 5 is characterized in that, described solvent comprises dimethylbenzene and/or butanols.