CN107540334A - 一种氯氧镁水泥基秸秆轻质复合材料及其制备方法 - Google Patents
一种氯氧镁水泥基秸秆轻质复合材料及其制备方法 Download PDFInfo
- Publication number
- CN107540334A CN107540334A CN201710871762.2A CN201710871762A CN107540334A CN 107540334 A CN107540334 A CN 107540334A CN 201710871762 A CN201710871762 A CN 201710871762A CN 107540334 A CN107540334 A CN 107540334A
- Authority
- CN
- China
- Prior art keywords
- stalk
- parts
- light
- mass ratio
- oxychloride cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于建筑保温材料技术领域,具体涉及一种氯氧镁水泥基秸秆轻质复合材料及其制备方法。本发明的技术方案如下:一种氯氧镁水泥基秸秆轻质复合材料,包括以下质量比的原料成分:轻烧镁粉43‑51份,氯化镁10‑15份,水40‑44份,磷酸0.40‑0.53份,双氧水0.5‑1.85份和秸秆纤维,秸秆纤维堆积体积:水泥净浆体积=0.75‑1.25;轻烧镁粉的氧化镁含量为95%,活性68%。本发明提供的氯氧镁水泥基秸秆轻质复合材料,具有绿色环保、保温隔热的优点。
Description
技术领域
本发明属于建筑保温材料技术领域,具体涉及一种氯氧镁水泥基秸秆轻质复合材料及其制备方法。
背景技术
以三聚氰胺、酚醛树脂或脲醛树脂等作为粘合剂制备复合材料,进而制成板材,易释放出有害物质,危害身体健康,且该类粘合剂属易燃物质,带来消防隐患。有人利用普通硅酸盐水泥和秸秆制备复合材料,但复合材料表面光滑的蜡状层不利于秸秆和水泥的界面结合,秸秆中析出的糖类物质对该类水泥具有明显的缓凝作用,会影响复合材料的强度。另外,段状秸秆在拌合过程中出现上浮,很难搅拌均匀。将玉米秸秆掺入普通硅酸盐水泥会降低复合材料的强度,为了确保复合材料的强度,玉米秸秆的掺量有限,复合材料的容重也较大。
玉米秸秆作为农业废弃物,年产量巨大,却未得到合理利用,被抛弃田野甚至被就地焚烧,严重污染大气。采用破碎处理后得到的秸秆纤维可以解决拌合不均的问题,而纤维形态也有利于高质量的界面结合。相比于段状秸秆,纤维状秸秆使得糖类物质在体系中均匀分散,避免了集中缓凝作用带来的内部缺陷。
发明内容
本发明提供一种氯氧镁水泥基秸秆轻质复合材料及其制备方法,具有绿色环保、保温隔热的优点。
本发明的技术方案如下:
一种氯氧镁水泥基秸秆轻质复合材料,包括以下质量比的原料成分:轻烧镁粉43-51份,氯化镁10-15份,水40-44份,磷酸0.40-0.53份,双氧水0.5-1.85份和秸秆纤维,秸秆纤维堆积体积:水泥净浆体积=0.75-1.25;轻烧镁粉的氧化镁含量为95%,活性68%。
一种上述的氯氧镁水泥基秸秆轻质复合材料的制备方法,包括以下步骤:
(1)将晒干后的玉米秸秆经破碎机破碎,得到秸秆纤维;
(2)称取所述质量比的氯化镁和水,配制卤液,并掺入所述质量比的磷酸,并在室温下静置24h;
(3)称取所述质量比的轻烧镁粉,将掺入磷酸的卤液倒入轻烧镁粉中,搅拌均匀,再掺入秸秆纤维,继续搅拌均匀,制成拌合物;
(4)在拌合物中掺入所述质量比的双氧水,搅拌均匀,待其充分发泡后浇筑于模具中;
(5)4h后脱模,置于室内环境养护,形成成品。
所述的制备方法,其中所述秸秆纤维长度为10mm-20mm,其形状为针杆状。
本发明的有益效果为:第一,选用的氯氧镁水泥具有较高的抗折强度,同时密度小,适用于制备轻质复合材料,尤其是轻质板材,而秸秆纤维的掺入降低了氯氧镁水泥的脆性,提高了韧性;第二,选取氯氧镁水泥作为胶凝材料,其黏结性好、快凝等特点有利于与秸秆纤维的界面结合,从而形成复合材料中增强相与基体相的协同效应;第三,氯氧镁水泥快凝的特点也有利于H2O2发泡,发泡后的材料容重低,具有良好的保温隔热性能,而秸秆纤维同样起到增韧作用。
具体实施方式
实施例1:
本实施例给出一种氯氧镁水泥基秸秆轻质复合材料,其制备工艺为:
(1)通过破碎机对玉米秸秆进行破碎处理,形成长度为10mm的秸秆纤维;
(2)通过目数为80目的网筛,将上述秸秆纤维中的秸秆粉末筛除;
(3)按质量比对原料进行混合,轻烧镁粉为44.2份,氯化镁为11.4份,水为42.8份,磷酸为0.4份,秸秆纤维掺量体积比(即秸秆纤维堆积体积:水泥净浆体积)=1;制成拌合物;
(4)在上述拌合物中掺入占质量比为1.1的双氧水,充分搅拌,使其均匀发泡;
(5)待拌合物充分发泡后,将其浇筑入模,4h后脱模养护于正常室温。
实施例2:
本实施例给出一种氯氧镁水泥基秸秆轻质复合材料,其制备工艺为:
(1)通过破碎机对玉米秸秆进行破碎处理,形成长度约为15mm的秸秆纤维;
(2)通过目数为80目的网筛,将上述秸秆纤维中的秸秆粉末筛除;
(3)按质量比对原料进行混合,轻烧镁粉为46.8份,氯化镁为10.3份,水为40.8份,磷酸为0.5份;秸秆掺量体积比为1.25;制成拌合物;
(4)在上述拌合物中掺入占质量比为1.6份的双氧水,充分搅拌,使其均匀发泡;
(5)待拌合物充分发泡后,将其浇筑入模,4h后脱模养护于正常室温。
实施例3:
本实施例给出一种氯氧镁水泥基秸秆轻质复合材料,其制备工艺为:
(1)通过破碎机对玉米秸秆进行破碎处理,形成长度约为20mm的秸秆纤维;
(2)通过目数为80目的网筛,将上述秸秆纤维中的秸秆粉末筛除;
(3)按质量比对原料进行混合,轻烧镁粉为49.5份,氯化镁为13.3份,水为42.4份,磷酸为0.5份;秸秆掺量体积比为1.10;制成拌合物;
(4)在上述拌合物中掺入占拌合物质量比为1.8份的双氧水,充分搅拌,使其均匀发泡;
(5)待拌合物充分发泡后,将其浇筑入模,4h后脱模养护于正常室温。
Claims (3)
1.一种氯氧镁水泥基秸秆轻质复合材料,其特征在于,包括以下质量比的原料成分:轻烧镁粉43-51份,氯化镁10-15份,水40-44份,磷酸0.40-0.53份,双氧水0.5-1.85份和秸秆纤维,秸秆纤维堆积体积:水泥净浆体积=0.75-1.25;轻烧镁粉的氧化镁含量为95%,活性68%。
2.一种如权利要求1所述的氯氧镁水泥基秸秆轻质复合材料的制备方法,其特征在于,包括以下步骤:
(1)将晒干后的玉米秸秆经破碎机破碎,得到秸秆纤维;
(2)称取所述质量比的氯化镁和水,配制卤液,并掺入所述质量比的磷酸,并在室温下静置24h;
(3)称取所述质量比的轻烧镁粉,将掺入磷酸的卤液倒入轻烧镁粉中,搅拌均匀,再掺入秸秆纤维,继续搅拌均匀,制成拌合物;
(4)在拌合物中掺入所述质量比的双氧水,搅拌均匀,待其充分发泡后浇筑于模具中;
(5)4h后脱模,置于室内环境养护,形成成品。
3.根据权利要求2所述的制备方法,其特征在于,所述秸秆纤维长度为10mm-20mm,其形状为针杆状。