CN104693829A - 一种秸秆玻纤防火板型材及其制备方法 - Google Patents

一种秸秆玻纤防火板型材及其制备方法 Download PDF

Info

Publication number
CN104693829A
CN104693829A CN201510074363.4A CN201510074363A CN104693829A CN 104693829 A CN104693829 A CN 104693829A CN 201510074363 A CN201510074363 A CN 201510074363A CN 104693829 A CN104693829 A CN 104693829A
Authority
CN
China
Prior art keywords
parts
minute
zinc borate
prepared
straw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510074363.4A
Other languages
English (en)
Inventor
胡平
胡泽伦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Human Relations High Ferro Equipment Science And Technology Ltd Is Made Tranquil In Anhui
Original Assignee
Human Relations High Ferro Equipment Science And Technology Ltd Is Made Tranquil In Anhui
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Human Relations High Ferro Equipment Science And Technology Ltd Is Made Tranquil In Anhui filed Critical Human Relations High Ferro Equipment Science And Technology Ltd Is Made Tranquil In Anhui
Priority to CN201510074363.4A priority Critical patent/CN104693829A/zh
Publication of CN104693829A publication Critical patent/CN104693829A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种秸秆玻纤防火板型材，其特征在于，由下列重量份的原料制备制成：农作物秸秆70-80、玻璃纤维3-5、酚醛树脂7-9、聚氨酯4-5、硼酸锌2-3、聚磷酸铵1-2、松香1-1.5、吡啶硫酮钠0.4-0.6、增效填料10-12；本发明首先以农作物秸秆作为板材基料，添加玻璃纤维、硼酸锌等，耐热阻燃；添加松香与吡啶硫酮钠，防虫防腐；通过酚醛树脂与聚氨酯的双重作用，弥补了玻璃纤维耐磨性差的缺点；添加由特殊工艺制成的改性剂，进一步提高了阻燃性、韧性、耐磨性；本发明制得的板材强度超实木，防火防蛀防腐防潮，生产过程中无三废，节约木材用量，减少了秸秆焚烧造成的空气污染，为农民增加了收益。

Description

一种秸秆玻纤防火板型材及其制备方法
技术领域
本发明涉及建筑材料领域，特别是一种秸秆玻纤防火板型材及其制备方法。
背景技术
我国是农业大国，秸秆资源相当丰富，大部分的秸秆被焚烧，污染环境的同时还存在着安全隐患。近年来，在政府鼓励下，对农作物秸秆回收利用有了进一步发展，除了传统的粉碎还田、加工饲料以外，还用于造纸及建筑装饰材料等。
近年来有将秸秆进行综合利用的例子，如将秸秆板应用于装饰板等的，但是大多数的装饰板采用的都是有机材料和秸秆粉的混合，其防火性能差，或者就是工艺过于繁琐，不利用工业生产。本发明首先以农作物秸秆作为板材基料，添加玻璃纤维、硼酸锌等，耐热阻燃；添加松香与吡啶硫酮钠，防虫防腐；通过酚醛树脂与聚氨酯的双重作用，弥补了玻璃纤维耐磨性差的缺点；添加由特殊工艺制成的改性剂，进一步提高了阻燃性、韧性、耐磨性；制成秸秆玻纤防火板型材，工艺简单，便于操作，强度超过实木板材，防火防虫蛀，稳定性好，产品安全环保，无三废，减少了树木的砍伐量，保护资源的同时为农民朋友创造了经济价值，值得像全社会推广。
发明内容
本发明的目的是提供一种秸秆玻纤防火板型材及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种秸秆玻纤防火板型材，由下列重量份的原料制备制成：农作物秸秆70-80、玻璃纤维3-5、酚醛树脂7-9、聚氨酯4-5、硼酸锌2-3、聚磷酸铵1-2、松香1-1.5、吡啶硫酮钠0.4-0.6、增效填料10-12；
所述增效填料由以下重量份的原料制备而成：轻烧氧化镁9-11、二氧化硅3-4、碳纤维2-3、沉淀法白炭黑2-3、木棉纤维3-4、聚乳酸2-3、橡胶粉1.5-2、乙酰柠檬酸三乙酯1-2、环氧树脂2-3、三乙烯四胺0.1-0.2、促进剂DTDM 0.3-0.5、膨胀石墨1-2；制备方法如下：首先将轻烧氧化镁、二氧化硅、沉淀法白炭黑、膨胀石墨混合后研磨成600-800目粉末，然后与聚乳酸、橡胶粉一同放入双螺杆挤出机中搅拌，温度控制在150℃-220℃，搅拌8-10分钟，再降温至100℃-150℃，加入其余剩余成分继续搅拌10-15分钟，挤出自然冷却，干燥固化后粉碎即得。
本发明所述一种秸秆玻纤防火板型材，由以下具体步骤制成：首先将农作物秸秆烘干，使其含水量小于20%，去杂质后粉碎成粉末，与玻璃纤维、硼酸锌、增效填料混合均匀，再加入其余剩余成分搅拌均匀后放入双螺杆挤出机中混炼15-20分钟，控制温度在150℃-200℃，然后挤入模具中，控制挤压力在70-90MPa，加热至150℃，保温10-15分钟，待固化成型后脱模即可。
本发明的有益效果是：本发明首先以农作物秸秆作为板材基料，添加玻璃纤维、硼酸锌等，耐热阻燃；添加松香与吡啶硫酮钠，防虫防腐；通过酚醛树脂与聚氨酯的双重作用，弥补了玻璃纤维耐磨性差的缺点；添加由特殊工艺制成的改性剂，进一步提高了阻燃性、韧性、耐磨性；本发明制得的板材强度超实木，防火防蛀防腐防潮，生产过程中无三废，节约木材用量，保护了森林资源，减少了秸秆焚烧造成的空气污染，为农民增加了收益。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种秸秆玻纤防火板型材，由下列重量份（公斤）的原料制备制成：农作物秸秆70、玻璃纤维3、酚醛树脂7、聚氨酯4、硼酸锌2、聚磷酸铵1、松香1、吡啶硫酮钠0.4、增效填料10；
所述增效填料由以下重量份（公斤）的原料制备而成：轻烧氧化镁9、二氧化硅3、碳纤维2、沉淀法白炭黑2、木棉纤维3、聚乳酸2、橡胶粉1.5、乙酰柠檬酸三乙酯1、环氧树脂2、三乙烯四胺0.1、促进剂DTDM 0.3、膨胀石墨1；制备方法如下：首先将轻烧氧化镁、二氧化硅、沉淀法白炭黑、膨胀石墨混合后研磨成600-800目粉末，然后与聚乳酸、橡胶粉一同放入双螺杆挤出机中搅拌，温度控制在150℃-220℃，混练8-10分钟，再降温至100℃-150℃，加入其余剩余成分继续混炼10-15分钟，挤出自然冷却，干燥固化后粉碎即得。
本发明所述一种秸秆玻纤防火板型材，由以下具体步骤制成：首先将农作物秸秆烘干，使其含水量小于20%，去杂质后粉碎成粉末，与玻璃纤维、硼酸锌、增效填料混合均匀，再加入其余剩余成分搅拌均匀后放入双螺杆挤出机中混炼15-20分钟，控制温度在150℃-200℃，然后挤入模具中，控制挤压力在70-90MPa，加热至150℃，保温10-15分钟，待固化成型后脱模即可。
本发明实施例制成的秸秆玻纤防火板型材，容量为1.12g/cm3，静曲强度为172.4Mpa，防火效果显著，可在800℃-1000℃高温下20分钟无鼓泡开裂，无燃烧。

Claims (2)

1.一种秸秆玻纤防火板型材，其特征在于，由下列重量份的原料制备制成：农作物秸秆70-80、玻璃纤维3-5、酚醛树脂7-9、聚氨酯4-5、硼酸锌2-3、聚磷酸铵1-2、松香1-1.5、吡啶硫酮钠0.4-0.6、增效填料10-12；
所述增效填料由以下重量份的原料制备而成：轻烧氧化镁9-11、二氧化硅3-4、碳纤维2-3、沉淀法白炭黑2-3、木棉纤维3-4、聚乳酸2-3、橡胶粉1.5-2、乙酰柠檬酸三乙酯1-2、环氧树脂2-3、三乙烯四胺0.1-0.2、促进剂DTDM 0.3-0.5、膨胀石墨1-2；制备方法如下：首先将轻烧氧化镁、二氧化硅、沉淀法白炭黑、膨胀石墨混合后研磨成600-800目粉末，然后与聚乳酸、橡胶粉一同放入双螺杆挤出机中搅拌，温度控制在150℃-220℃，混练8-10分钟，再降温至100℃-150℃，加入其余剩余成分继续混炼10-15分钟，挤出自然冷却，干燥固化后粉碎即得。
2.根据权利要求1所述一种秸秆玻纤防火板型材，其特征在于，由以下具体步骤制成：首先将农作物秸秆烘干，使其含水量小于20%，去杂质后粉碎成粉末，与玻璃纤维、硼酸锌、增效填料混合均匀，再加入其余剩余成分搅拌均匀后放入双螺杆挤出机中混炼15-20分钟，控制温度在150℃-200℃，然后挤入模具中，控制挤压力在70-90MPa，加热至150℃，保温10-15分钟，待固化成型后脱模即可。
CN201510074363.4A 2015-02-12 2015-02-12 一种秸秆玻纤防火板型材及其制备方法 Pending CN104693829A (zh)