CN107538843A - Environment-friendly waterproof grid cloth and preparation method thereof - Google Patents
Environment-friendly waterproof grid cloth and preparation method thereof Download PDFInfo
- Publication number
- CN107538843A CN107538843A CN201710783880.8A CN201710783880A CN107538843A CN 107538843 A CN107538843 A CN 107538843A CN 201710783880 A CN201710783880 A CN 201710783880A CN 107538843 A CN107538843 A CN 107538843A
- Authority
- CN
- China
- Prior art keywords
- grid cloth
- weight
- preparation
- environment
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building material field, and more particularly to environment-friendly waterproof grid cloth and preparation method thereof；Including infiltrating knitmesh raw material with pretreating agent, bake, obtain pre-processing raw material；Standby grid cloth is woven with pretreatment raw material；At least two layers standby grid cloth superposition is bonded, obtains place where troops were originally stationed water grid cloth, waterproof coating is smeared in the outside of water grid cloth in place where troops were originally stationed；Wherein, pretreating agent includes the first stabilizer, the first powdered graphite, the first perlite powder, resin, plasticizer；The preparation method can quickly, easily prepare the grid cloth with stronger waterproof action, and the preparation method cost-effective can be put into；The waterproof grid cloth has stronger waterproof effect, and the waterproof grid cloth is applied into the fields such as decorations, can effectively lift the waterproof effect after building decoration and fitment.
Description
Technical field
The present invention relates to building material field, and more particularly to environment-friendly waterproof grid cloth and preparation method thereof.
Background technology
Grid cloth is a kind of special material, and cloth more common than in general is more solid more robust, has intensity height, alkali resistance good
Feature.Grid cloth is mainly widely used in：Wall reinforcing material (such as：Glass wall mesh, GRC wallboards, inside and outside EPS
Wall heat-insulating board, plasterboard etc.)；Enhancing cement products (such as：FRP Columns, flue etc.)；It is the special mesh sheet of granite, mosaic, big
Reason stone back of the body patch net；Waterproof roll cloth, asphalt roofing waterproof；The framework material of reinforced plastics, rubber；Fire-proof plate；Emery wheel base
Step；Highway pavement GSZ；Filleting band for building etc..
The logical production of existing grid cloth does not possess the effect of waterproof, it is difficult to meets the needs of market is changeable.In high temperature and rainy
Under weather, if decorating and renovating material is non-watertight, tends to go mouldy because being produced by moist, do not only result in fitting-up
Aesthetic measure reduces, and can also be unfavorable for the health of the living environment of people, threatens the health of people.
The content of the invention
It is an object of the invention to provide a kind of preparation method of environment-friendly waterproof grid cloth, the preparation method can quickly,
The grid cloth with stronger waterproof action is easily prepared, and the preparation method cost-effective can be put into.
Another object of the present invention is to provide a kind of environment-friendly waterproof grid cloth, the waterproof grid cloth has stronger waterproof
Effect, the waterproof grid cloth is applied to the fields such as decorations, can effectively lift the effect of the waterproof after building decoration and fitment
Fruit, aesthetic property is kept, also lift the sanitation degree of living environment, be advantageous to the health of people；The waterproof grid cloth also has excellent
Different mechanical strength, toughness etc..
The present invention is realized using following technical scheme.
The present invention proposes a kind of preparation method of environment-friendly waterproof grid cloth, and it includes infiltrating knitmesh former material with pretreating agent
Material, bake, obtain pre-processing raw material；Standby grid cloth is woven with pretreatment raw material；At least two layers standby grid cloth is folded
Add bonding, obtain place where troops were originally stationed water grid cloth, waterproof coating is smeared in the outside of water grid cloth in place where troops were originally stationed；Wherein, pretreating agent includes the
One stabilizer, the first powdered graphite, the first perlite powder, resin, plasticizer.
The present invention proposes a kind of environment-friendly waterproof grid cloth, and it is the preparation method making by above-mentioned environment-friendly waterproof grid cloth
's.
The beneficial effect of the environment-friendly waterproof grid cloth of the embodiment of the present invention and preparation method thereof is：The preparation method can be fast
Speed, the grid cloth with stronger waterproof action is easily prepared, and the preparation method cost-effective can be put into.By this
Waterproof grid cloth prepared by preparation method has stronger waterproof effect, and the waterproof grid cloth is applied into the neck such as decorations
Domain, the waterproof effect after building decoration and fitment can be effectively lifted, keep aesthetic property, also lift the hygienic journey of living environment
Degree, be advantageous to the health of people；The waterproof grid cloth also has excellent mechanical strength, toughness etc..
Embodiment
, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical scheme be clearly and completely described.Unreceipted actual conditions person, builds according to normal condition or manufacturer in embodiment
The condition of view is carried out.Agents useful for same or the unreceipted production firm person of instrument, it is the conventional production that can be obtained by commercially available purchase
Product.
Environment-friendly waterproof grid cloth of the embodiment of the present invention and preparation method thereof is specifically described below.
The preparation method of the environment-friendly waterproof grid cloth of the present invention mainly includes：Knitmesh raw material are infiltrated with pretreating agent, are dried
System, obtain pre-processing raw material；Standby grid cloth is woven with pretreatment raw material；At least two layers standby grid cloth superposition is glued
Connect, obtain place where troops were originally stationed water grid cloth, waterproof coating is smeared in the outside of water grid cloth in place where troops were originally stationed.
Above-mentioned knitmesh raw material can include at least one of basalt fibre and glass fibre；Basalt fibre has
Good toughness, rub resistance, corrosion resistance etc., good insulating, the heat resistance of glass fibre are strong, corrosion resistance is good, mechanical strong
Degree is high, and clathrum is worked out jointly with basalt fibre and glass fibre, and the machinery that can effectively lift obtained clathrum is strong
Degree, toughness, corrosion resistance etc..
The mesh of standby grid cloth in the present invention can be various polygons, such as：Triangle, quadrangle, six sides
Shape etc., it is possible to further be various regular polygons.
Above-mentioned pretreating agent includes stabilizer (the first stabilizer), powdered graphite (the first powdered graphite), crushed crude pearlite
Last (the first perlite powder), resin and plasticizer.In detail, pretreating agent includes 10-20 parts by weight in parts by weight
Stabilizer, the powdered graphite of 30-50 parts by weight, the perlite powder of 20-30 parts by weight, the resin of 120-150 parts by weight, 5-10
Plasticizer.
Perlite powder is a kind of new material of lightweight, and has extremely low wettability power.Added in pretreating agent
Perlite powder, the water resistance of knitmesh raw material can be improved, avoids grid cloth from making moist.Preferably, perlite powder
Particle diameter can be 1000-1200 purposes, and thinner perlite powder can disperse more uniform in resin.
Graphite, there is stronger lubricant effect；Stone mill powder is added in pretreating agent to be promoted in pretreating agent
Various components are quick, uniformly scatter, and can also make pretreating agent when using pretreating agent pretreatment knitmesh raw material
Rapidly permeated in knitmesh raw material, it is ensured that knitmesh raw material obtain the performances such as corresponding waterproof.
Stabilizer can make the stable performance of pretreating agent, prevent the active principle in pretreating agent from decomposing, aoxidizing.Increase
Modeling agent is a kind of high polymer material auxiliary agent, and plasticizer can be with the toughness of reinforcing material, and plasticizer is added in pretreating agent can be with
Toughness and mechanical strength of grid cloth etc. are improved, thus the service life of grid cloth can be extended etc..
The mechanical strength and toughness that knitmesh raw material can be lifted using one side of resin, on the other hand can be by graphite
Powder, perlite powder are uniform, are securely attached on knitmesh raw material, it is ensured that the grid cloth of preparation can be prevented with excellent
Water effect.
Further, with pretreating agent knitmesh raw material are carried out with infiltration to carry out in such a way：Knitmesh is former
Material is positioned in pretreating agent, vibrates 50-70min under 120-150Hz frequency.Knitmesh former material is being infiltrated with pretreating agent
During material, coordinate vibration to carry out, the perlite powder in pretreating agent can be promoted to go deep into the inside of knitmesh raw material, and then effectively
The waterproof effect of grid cloth made from raising.
After the completion of the infiltration of knitmesh raw material, baked, pretreating agent is solidified on knitmesh raw material, obtain pre- place
Raw material are managed, the temperature of above-mentioned baking can be 70-80 DEG C.
Standby grid cloth is woven into pretreatment raw material, and at least two layers standby grid cloth superposition is bonded, you can
To place where troops were originally stationed water grid cloth.
Waterproof coating is smeared in the outside of above-mentioned place where troops were originally stationed water grid cloth, you can the environment-friendly waterproof grid cloth of the present invention is made.
Above-mentioned waterproof coating can be water-proof acrylic acid paint, can also be asphalt paint etc..
In detail, the superposition bonding of standby grid cloth can be carried out in such a way：It is being overlapped mutually two of bonding
Viscous glutinous agent is smeared between standby grid cloth, and is dried, such as：The viscous glutinous agent of the surface smear of a standby grid cloth wherein, then
Another standby grid cloth is attached to the surface for having smeared viscous glutinous agent, then dried.
It is fine that above-mentioned viscous glutinous agent can include plastic cement, stabilizer (the second stabilizer), powdered graphite (the second powdered graphite), bamboo
Tie up powder and perlite powder (the second perlite powder).By weight, plastic cement, the 10- of 120-150 parts by weight can be included
The stabilizer of 30 parts by weight, the powdered graphite of 5-10 parts by weight, the treasure of the bamboo fibre powder of 10-20 parts by weight and 5-10 parts by weight
Pearl rock dust end.
On the one hand plastic cement can be successfully bonded between grid cloth, on the other hand can make powdered graphite, bamboo fibre powder,
Perlite powder is more uniformly dispersed in plastic cement, and can be uniformly attached to grid cloth, on the one hand also having can enter
Mechanical strength and toughness of one step enhancing grid cloth etc..Bamboo fibre powder has stronger antibacterial, antibacterial, except mite, deodorization, ventilative
The performances such as property, bamboo fibre powder are made an addition in bonding agent the anti-mold effect that can lift environmentally friendly waterproof net lattice cloth, and utilize
The gas permeability that bamboo fibre protrudes, the moisture that grid cloth is subject to excludes, and then keeps the degree of drying of grid cloth.Powdered graphite institute
It is more uniform that the lubricant effect having can aid in bamboo fibre powder and perlite powder to disperse in viscous glutinous agent, on the one hand makes
Anti-mold effect, the air permeable effect of grid cloth uniformly improve, and on the other hand ensure that the cementability of plastic cement is not destroyed, make standby net
The bonding that can stablize between lattice cloth.
Addition perlite powder can further reduce the ability of grid cloth water suction in viscous glutinous agent, and then improve grid
The waterproof ability of cloth.Particle diameter as preferred perlite powder can be 1000-1200 mesh.
Preferably, the particle diameter of powdered graphite can be 1000-1200 mesh, the particle diameter of bamboo fibre can be 1000-1200
Mesh.The tiny powdered graphite of particle diameter and bamboo fibre powder can more rapidly, uniformly scatter in plastic cement, also may be used after smearing
To be more uniformly distributed in grid cloth, and then make the performance of grid cloth, quality more stable, uniform.
Above-mentioned drying can be carried out under the conditions of 100-120 DEG C.In detail, can be in drying, with hot pressing one
And carry out, on the one hand can be rapidly completed the work of hot pressing, on the other hand can make between grid cloth it is viscous it is glutinous more firmly, enter
And improve the service life of the environment-friendly waterproof grid cloth, mechanical strength etc..
Environment-friendly waterproof grid cloth of the present invention and preparation method thereof is described in further detail with reference to embodiments.
Embodiment 1
Pretreating agent is prepared, by the stabilizer of 10 parts by weight, the powdered graphite (mesh of particle diameter 1000) of 30 parts by weight, 20 weight
The perlite powder (mesh of particle diameter 1000), the resin of 120 parts by weight of part, the mixing of 5 plasticizer.
Prepare viscous glutinous agent, by the plastic cement of 120 parts by weight, the stabilizer of 10 parts by weight, 5 parts by weight powdered graphite (particle diameter
1000 mesh), the bamboo fibre powder (mesh of particle diameter 1000) of 10 parts by weight, 5 parts by weight perlite powder (mesh of particle diameter 1000) mixing.
With pretreating agent sized glass fibres, with the vibration of 120Hz frequencies during infiltration, 70min is infiltrated, in 70 DEG C of conditions
Lower drying, obtain pre-processing raw material.
Standby grid cloth is woven with pretreatment, the mesh of standby grid cloth is triangle.In the mutually viscous of standby grid cloth
The viscous glutinous agent of surface smear connect, two layers of standby grid cloth is superimposed, is dried under the conditions of 100 DEG C, obtains place where troops were originally stationed water grid cloth；
Smear water-proof acrylic acid paint in two outsides of place where troops were originally stationed water grid cloth, you can environment-friendly waterproof grid cloth is made.
Embodiment 2
Pretreating agent is prepared, by the stabilizer of 20 parts by weight, the powdered graphite (mesh of particle diameter 1200) of 50 parts by weight, 30 weight
The perlite powder (mesh of particle diameter 1200), the resin of 150 parts by weight of part, the mixing of 10 plasticizer.
Prepare viscous glutinous agent, by the plastic cement of 150 parts by weight, the stabilizer of 30 parts by weight, 10 parts by weight powdered graphite (particle diameter
1200 mesh), the bamboo fibre powder (mesh of particle diameter 1200) of 20 parts by weight, the perlite powder (mesh of particle diameter 1200) of 10 parts by weight it is mixed
Close.
Basalt fibre is infiltrated with pretreating agent, with the vibration of 150Hz frequencies during infiltration, 50min is infiltrated, in 80 DEG C of bars
Dried under part, obtain pre-processing raw material.
Standby grid cloth is woven with pretreatment, the mesh of standby grid cloth is quadrangle.In the mutually viscous of standby grid cloth
The viscous glutinous agent of surface smear connect, two layers of standby grid cloth is superimposed, is dried under the conditions of 120 DEG C and with hot pressing, obtains place where troops were originally stationed
Water grid cloth；In place where troops were originally stationed, water-proof acrylic acid paint is smeared in two outsides of water grid cloth, you can environment-friendly waterproof grid cloth is made.
Embodiment 3
Pretreating agent is prepared, by the stabilizer of 15 parts by weight, the powdered graphite (mesh of particle diameter 1100) of 40 parts by weight, 25 weight
The perlite powder (mesh of particle diameter 1100), the resin of 150 parts by weight of part, the mixing of 7 plasticizer.
Prepare viscous glutinous agent, by the plastic cement of 130 parts by weight, the stabilizer of 20 parts by weight, 7 parts by weight powdered graphite (particle diameter
1100 mesh), the bamboo fibre powder (mesh of particle diameter 1100) of 15 parts by weight, 7 parts by weight perlite powder (mesh of particle diameter 1100) mixing.
With pretreating agent sized glass fibres and basalt fibre, with the vibration of 130Hz frequencies, infiltration during infiltration
55min, dried under the conditions of 75 DEG C, obtain pre-processing raw material.
Standby grid cloth is woven with pretreatment, the mesh of standby grid cloth is triangle, basalt fibre and glass fibre
Amount ratio be 1:2.In the viscous glutinous agent of the surface smear being mutually bonded of standby grid cloth, two layers of standby grid cloth is superimposed,
Dried under the conditions of 110 DEG C, obtain place where troops were originally stationed water grid cloth；In place where troops were originally stationed, water-proof acrylic acid paint is smeared in two outsides of water grid cloth, i.e.,
Environment-friendly waterproof grid cloth can be made.
Embodiment 4
Pretreating agent is prepared, by the stabilizer of 12 parts by weight, the powdered graphite (mesh of particle diameter 1150) of 45 parts by weight, 28 weight
The perlite powder (mesh of particle diameter 1150), the resin of 130 parts by weight of part, the mixing of 8 plasticizer.
Prepare viscous glutinous agent, by the plastic cement of 130 parts by weight, the stabilizer of 18 parts by weight, 7 parts by weight powdered graphite (particle diameter
1050 mesh), the bamboo fibre powder (mesh of particle diameter 1100) of 12 parts by weight, 6 parts by weight perlite powder (mesh of particle diameter 1100) mixing.
With pretreating agent sized glass fibres, with the vibration of 130Hz frequencies during infiltration, 65min is infiltrated, in 70 DEG C of conditions
Lower drying, obtain pre-processing raw material.
Standby grid cloth is woven with pretreatment, the mesh of standby grid cloth is six corner shapes.In the mutual of standby grid cloth
The viscous glutinous agent of the surface smear of bonding, three layers of standby grid cloth are superimposed, is dried under the conditions of 110 DEG C, obtains place where troops were originally stationed water grid cloth；
In place where troops were originally stationed, asphalt paint is smeared in two outsides of water grid cloth, you can environment-friendly waterproof grid cloth is made.
Embodiment 5
Pretreating agent is prepared, by the stabilizer of 18 parts by weight, the powdered graphite (mesh of particle diameter 1100) of 32 parts by weight, 25 weight
The perlite powder (mesh of particle diameter 1100), the resin of 135 parts by weight of part, the mixing of 8 plasticizer.
Prepare viscous glutinous agent, by the plastic cement of 145 parts by weight, the stabilizer of 27 parts by weight, 8 parts by weight powdered graphite (particle diameter
1200 mesh), the bamboo fibre powder (mesh of particle diameter 1000) of 16 parts by weight, 9 parts by weight perlite powder (mesh of particle diameter 1100) mixing.
With pretreating agent sized glass fibres, with the vibration of 140Hz frequencies during infiltration, 60min is infiltrated, in 78 DEG C of conditions
Lower drying, obtain pre-processing raw material.
Standby grid cloth is woven with pretreatment, the mesh of standby grid cloth is triangle.In the mutually viscous of standby grid cloth
The viscous glutinous agent of surface smear connect, four layers of standby grid cloth are superimposed, is dried under the conditions of 110 DEG C and with hot pressing, obtains place where troops were originally stationed
Water grid cloth；In place where troops were originally stationed, water-proof acrylic acid paint is smeared in two outsides of water grid cloth, you can environment-friendly waterproof grid cloth is made.
Embodiment 6
Pretreating agent is prepared, by the stabilizer of 14 parts by weight, the powdered graphite (mesh of particle diameter 1200) of 42 parts by weight, 22 weight
The perlite powder (mesh of particle diameter 1200), the resin of 125 parts by weight of part, the mixing of 9 plasticizer.
Prepare viscous glutinous agent, by the plastic cement of 125 parts by weight, the stabilizer of 16 parts by weight, 5 parts by weight powdered graphite (particle diameter
1100 mesh), the bamboo fibre powder (mesh of particle diameter 1100) of 13 parts by weight, 7 parts by weight perlite powder (mesh of particle diameter 1000) mixing.
With pretreating agent sized glass fibres, with the vibration of 135Hz frequencies during infiltration, 55min is infiltrated, in 74 DEG C of conditions
Lower drying, obtain pre-processing raw material.
Standby grid cloth is woven with pretreatment, the mesh of standby grid cloth is quadrangle.In the mutually viscous of standby grid cloth
The viscous glutinous agent of surface smear connect, three layers of standby grid cloth are superimposed, is dried under the conditions of 115 DEG C and with hot pressing, obtains place where troops were originally stationed
Water grid cloth；In place where troops were originally stationed, water-proof acrylic acid paint is smeared in two outsides of water grid cloth, you can environment-friendly waterproof grid cloth is made.
Comparative example
From commercially available grid cloth as a comparison case.
Water proofing property detection is carried out to embodiment 1-6 and the grid cloth of comparative example, each grid cloth of identical weight is taken, first 60
DEG C baking oven in grid cloth baked into weight, weigh (weight 1), then grid cloth is soaked in 1h in water, weigh (weight 2), count
The ratio (weight 1 of weight 2/) (being repeated 3 times) of grid cloth weight twice is calculated, the results are shown in Table 1.
The water proofing property testing result of each group grid cloth of table 1
As seen from the results in Table 1, it is smaller with the ratio after drying after grid cloth of the invention soaks in water, and then can be with
Illustrate that the water proofing property of the environment-friendly waterproof grid cloth of the present invention is stronger.
In summary, the beneficial effect of environment-friendly waterproof grid cloth of the embodiment of the present invention and preparation method thereof is：The preparation
Method can quickly, easily prepare the grid cloth with stronger waterproof action, and the preparation method can save cost
Input.The waterproof grid cloth prepared by the preparation method has stronger waterproof effect, and the waterproof grid cloth is applied into dress
The fields such as decorations finishing, can effectively lift the waterproof effect after building decoration and fitment, keep aesthetic property, also lift living environment
Sanitation degree, be advantageous to the health of people；The waterproof grid cloth also has excellent mechanical strength, toughness etc..
Embodiments described above is part of the embodiment of the present invention, rather than whole embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the scope of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiment in the present invention, what those of ordinary skill in the art were obtained under the premise of creative work is not made
Every other embodiment, belongs to the scope of protection of the invention.
Claims (10)
1. a kind of preparation method of environment-friendly waterproof grid cloth, it is characterised in that including infiltrating knitmesh raw material with pretreating agent, dry
System, obtain pre-processing raw material；Standby grid cloth is woven with the pretreatment raw material；By at least two layers standby grid cloth
Superposition bonding, obtains place where troops were originally stationed water grid cloth, and waterproof coating is smeared in the outside of the place where troops were originally stationed water grid cloth；Wherein, the pre- place
Managing agent includes the first stabilizer, the first powdered graphite, the first perlite powder, resin, plasticizer.
2. the preparation method of environment-friendly waterproof grid cloth according to claim 1, it is characterised in that the waterproof coating is third
Olefin(e) acid water-repellent paint.
3. the preparation method of environment-friendly waterproof grid cloth according to claim 1, it is characterised in that the pretreating agent is by weight
Measure part meter, including first powdered graphite of first stabilizer of 10-20 parts by weight, 30-50 parts by weight, 20-30 weight
Measure first perlite powder, the resin of 120-150 parts by weight of part.
4. the preparation method of environment-friendly waterproof grid cloth according to claim 1, it is characterised in that the infiltration is according to following
Mode is carried out：The knitmesh raw material are positioned in the pretreating agent, vibrate 50-70min under 120-150Hz frequencies.
5. the preparation method of environment-friendly waterproof grid cloth according to claim 1, it is characterised in that it is described superposition bonding according to
In the following manner is carried out：Viscous glutinous agent is smeared between two standby grid cloths for being overlapped mutually bonding, and is dried.
6. the preparation method of environment-friendly waterproof grid cloth according to claim 5, it is characterised in that the viscous glutinous agent includes modeling
Glue, the second stabilizer, the second powdered graphite, bamboo fibre powder and the second perlite powder.
7. the preparation method of environment-friendly waterproof grid cloth according to claim 6, it is characterised in that the viscous glutinous agent is by weight
Part meter, including described in second stabilizer of the plastic cement of 120-150 parts by weight, 10-30 parts by weight, 5-10 parts by weight
Second powdered graphite, the bamboo fibre powder of 10-20 parts by weight and the second perlite powder of 5-10 parts by weight.
8. the preparation method of environment-friendly waterproof grid cloth according to claim 6, it is characterised in that the bamboo fibre powder
Particle diameter is 1000-1200 mesh.
9. the preparation method of environment-friendly waterproof grid cloth according to claim 6, it is characterised in that second powdered graphite
Particle diameter be 1000-1200 mesh.
10. a kind of environment-friendly waterproof grid cloth, it is characterised in that it is as the environment-friendly waterproof net described in claim any one of 1-9
What the preparation method of lattice cloth made.