CN103252824B - A kind of architectural concrete light wall plate preparation method - Google Patents
A kind of architectural concrete light wall plate preparation method Download PDFInfo
- Publication number
- CN103252824B CN103252824B CN201310202757.4A CN201310202757A CN103252824B CN 103252824 B CN103252824 B CN 103252824B CN 201310202757 A CN201310202757 A CN 201310202757A CN 103252824 B CN103252824 B CN 103252824B
- Authority
- CN
- China
- Prior art keywords
- cement
- layer
- decorative layer
- wall plate
- light wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to architectural concrete light wall plate prepared by a kind of architectural concrete light wall plate preparation method and the method, comprise the structure sheaf that cement rock ballast slurry or Cement-Screening slurry solidify decorative layer that rear surface is polished to and the first Cement fibre layer set gradually, nonwoven layer, the second Cement fibre layer are formed; Described first Cement fibre layer and described decorative layer compact siro spinning technology.Increase in structure sheaf and have nonwoven layer, and non-woven fabrics has softness, tension, the characteristic such as smooth, when picking raggle in structure sheaf, there is corresponding bending resistance, thickness, the volume that therefore, can reduce structure sheaf are little, namely maintain high compressive strength add tensile strength and impact strength because Cement fibre layer and nonwoven layer cooperatively interact, cement rock ballast slurry or Cement-Screening slurry solidify the texture that the decorative layer made on polishing surface, rear surface has stone material, do not need again at surface spraying material, durable, aesthetic property is good.
Description
Technical field
The present invention relates to a kind of wallboard and wallboard preparation method, there is the architectural concrete light wall plate relating to a kind of architectural concrete light wall plate preparation method and the method and prepare, belong to decorating outer wall of building field.
Background technology
Exposed wall decorative hangig panel of the prior art has clear-water concrete wallboard, calcium silicate board with microporous and JRC wallboard.
At present, clear-water concrete wallboard no decoration layer, belong to one-time cast-forming, entirety all embodies structurally, plant design plate, and standard is solid durable, any outer decoration that it goes without doing; But owing to being provided with steel skeleton, thickness is all at 8 centimeters to 10 centimeters, and the very large load requiring to build is large, and beam and column cross section increases, and the wallboard weight taking resource such as 1 meter × 3 meters in a large number can reach 1 ton; And have steel construction or reinforcing bar bar-mat reinforcement, take resource in a large number, cause the wasting of resources.
Calcium silicate board with microporous forms primarily of calcium silicates, by siliceous material (diatomite, bentonite, silica flour etc.), calcareous material, fortifying fibre etc. as primary raw material, through slurrying, becomes the operations such as base, steam-cured, sanding surface and the light weight board made.Although overcome the defect that clear-water concrete structure is thick and heavy, it is just for decorating structures such as indoor suspended ceilings.
JRC wallboard is glass fiber reinforced cement (Glass fiber Reinforced Cement, is abbreviated as GRC) is take glass fibre as reinforcing material, a kind of composite formed for matrix with cement paste or cement mortar.It has that compression strength is high, tensile strength and impact strength low, namely there is good rigidity and lack flexible feature, therefore, when being processed with the wallboard of groove, virtually need to increase wallboard thickness and shaping after be decorative colors by surface spraying material treatment surface and pattern, all there is no the texture of stone material, under exterior wall is chronically exposed to sunlight rainwater, cause wall skin to come off, affect result of use, and easily cause environmental pollution.
The processing of above-mentioned wallboard all needs the mould fixed, building to be specification manufactures around manufacturer production.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of architectural concrete light wall plate and preparation method thereof, overcome clear-water concrete decorative wall panels volume of the prior art large, need to increase building load, glass fiber reinforced cement wallboard needs external spray material and all do not have the defect of stone texture.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: the preparation method that the invention provides a kind of architectural concrete light wall plate, comprise type design, make mould, organize frock, the making of decorative layer and structure sheaf and the demoulding and maintenance, it is characterized in that, the production process of wherein said decorative layer comprises the following steps:
Step (1), puts into frock by described mould, and adopts gluing or jig method and described frock to fix;
Step (2), makes the first mixed material by cement, rock ballast, water wood fibre according to the percent mass ratio mixing and stirring of 1:1 ~ 3:0.38 ~ 0.05:0.03 ~ 0.05; Preferred cement, rock ballast, water wood fibre make the first mixed material according to the percent mass ratio mixing and stirring of 1:2:0.38:0.05.
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 2 to 4 millimeters, and slight vibrations occur to there being minute bubbles.
The production process of wherein said structure sheaf comprises the following steps:
Step (1), stirs cement, aggregate chips, alkaline-resisting chopped strand and water according to the percent mass ratio of 1:1 ~ 3:0.03 ~ 0.05:0.38 ~ 0.05 and makes the second mixed material; Preferred cement, aggregate chips, alkaline-resisting chopped strand and water stir according to the percent mass ratio of 1:1:0.03:0.38 and make the second mixed material;
Step (2), when described decorative layer initial set and the non-film forming in surface time, add 3 to 5 millimeters of described second mixed materials;
Step (3), described second mixed material is equipped with layer of non-woven fabric, then after adding 3 to 5 millimeters of described second mixed materials, roll-in.
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 8 to 18 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material.
The invention has the beneficial effects as follows: because decorative layer adopts the mixed slurry of cement and rock ballast, product is preferably shaping solidifies the texture that the decorative layer made on polishing surface, rear surface has stone material, and do not need again at surface spraying material, durable, aesthetic property is good; And when described decorative layer initial set and the non-film forming in surface time, add the cement of 3 to 5 millimeters, mixed slurry that fiber is made, can ensure not only decorative layer and structure sheaf have good caking property but also can not merge; Layer of non-woven fabric is equipped with again on the mixed slurry of cement, fiber support, then after adding 3 to 15 millimeters of described second mixed materials, roll-in.Owing to being equipped with non-woven fabrics in the middle of the mixed slurry made at cement, fiber, this process ensure that structure sheaf has high compressive strength and tension and impact strength and bending resistance (folding) intensity, the thickness of wallboard can be effectively reduced like this, reduce the volume and weight of body of wall.
The texture of stone material can be there is in the present invention's cement slurry that after preferably adopting cement, rock ballast, water wood fibre to solidify according to the slurry that the percent mass ratio mixing and stirring of 1:2:0.38:0.05 is made, polishing removal is surperficial gently.Certainly according to its ratio of the design modifying of building designers or the requirement that some color materials meet design style can be added.
On the basis of technique scheme, the present invention can also do following improvement.
Further, the amount of alkaline-resisting chopped strand described in described second mixed material is 2% to the 5%(mass percent of described cement amount).
The beneficial effect of above-mentioned further scheme is adopted to be: the structure sheaf that the mixed slurry that this technical characteristic can ensure cement owing to adopting, fiber is made is made has compression strength of good performance.
Further, the particle diameter of described rock ballast is 0.5 to 2 millimeter.
The beneficial effect of above-mentioned further scheme is adopted to be: rock ballast adopts the particle diameter of 0.5 to 2 millimeter can ensure that decorative layer is 2 to 4 millimeters time, slight polishing can not make rock ballast fully expose, and can have again the texture of stone material when the design of guarantee decorative layer is thinner.
Further, stitching portion, the outside tick slot of described decorative layer goes out spline-simulating structure.
The beneficial effect of above-mentioned further scheme is adopted to be: can realize the seamless spliced of multiple sheet material, overall aesthetics and the amalgamation of composition are better.
Further, described second mixed material is equipped with layer of non-woven fabric, then re-lays layer of non-woven fabric after adding 3 to 5 millimeters of described second mixed materials, then add 3 to 10 millimeters of described second mixed materials, roll-in.
The beneficial effect of above-mentioned further scheme is adopted to be: according to the thickness of Demand Design wallboard of building designers and the flexural strength of wallboard, multi-layer nonwoven fabrics can be added in Cement fibre slurry, flexibility and the bending resistance of wallboard can be improved.
The present invention also provides a kind of architectural concrete light wall plate, comprises the structure sheaf that cement rock ballast slurry or Cement-Screening slurry solidify decorative layer that rear surface is polished to and the first Cement fibre layer set gradually, nonwoven layer, the second Cement fibre layer are formed; Described first Cement fibre layer and described decorative layer compact siro spinning technology.
The invention has the beneficial effects as follows: increasing in structure sheaf has nonwoven layer, and non-woven fabrics has softness, tension, the characteristic such as smooth, when picking raggle in structure sheaf, there is corresponding bending resistance, therefore, the thickness of structure sheaf can be reduced, volume is little, namely maintain high compressive strength add tensile strength and impact strength because Cement fibre layer and nonwoven layer cooperatively interact, cement rock ballast slurry or Cement-Screening slurry solidify the texture that the decorative layer made on polishing surface, rear surface has stone material, do not need again at surface spraying material, durable, aesthetic property is good.
Further, described decorative layer is 2 millimeters.
The beneficial effect of above-mentioned further scheme is adopted to be: the weight and volume reducing wallboard, economize energy.
Further, described wallboard is 10 millimeters to 20 millimeters.The thickness of preferred wallboard is 10 to 15 millimeters.
Adopt the beneficial effect of above-mentioned further scheme to be: the weight and volume reducing wallboard, really accomplish energy-conserving and environment-protective.
Accompanying drawing explanation
Fig. 1 is a kind of architectural concrete light wall plate of the present invention preparation method schematic flow sheet;
Fig. 2 is the structural representation of a kind of architectural concrete light wall plate of the present invention
In accompanying drawing, the list of parts representated by each label is as follows:
1, decorative layer, 2, structure sheaf, 2-1, the first Cement fibre layer, 2-2, nonwoven layer, 2-3, the second Cement fibre layer.
Detailed description of the invention
Be described principle of the present invention and feature below in conjunction with accompanying drawing, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1
As shown in Figure 1, the preparation method of a kind of architectural concrete light wall plate of the present invention, comprise type design, make styrofoam making former, the making organizing frock, decorative layer and structure sheaf and the demoulding and maintenance, the production process of wherein said decorative layer comprises the following steps:
Step (1), puts into frock by described mould, adopts the method for jig to fix on mould and described frock, and lay one deck bottom ash in described mould; This step can ensure that decorative layer is dismantled easily and ensures the easy polishing of decor surface.
Step (2), cement, rock ballast, water wood fibre are made the first mixed material according to the percent mass ratio mixing and stirring of 1:2:0.38:0.05, and the particle diameter of described rock ballast is 0.5 ~ 0.8 millimeter;
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 2 millimeters, and slight vibrations occur to having minute bubbles; Little rock ballast is evenly distributed in slurry.
The production process of wherein said structure sheaf comprises the following steps:
Step (1), by cement, aggregate chips, alkaline-resisting chopped strand and water according to 1:1:0.03:0.38(percent mass ratio) ratio mixing and stirring makes the second mixed material;
Step (2), when described decorative layer initial set and the non-film forming in surface time, (namely in the pasty state, or at 25 DEG C, solidify the state of 15 minutes); Add 3 millimeters of described second mixed materials;
Step (3) is equipped with layer of non-woven fabric on described second mixed material, then after adding 3 millimeters of described second mixed materials, roll-in;
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 8 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material, make finished product architectural concrete light wall plate, warehouse-in after packaging.
The stitching portion, outside being finally also included in described decorative layer is picked and has been dug out spline-simulating structure.
Embodiment 2
As shown in Figure 1, the preparation method of a kind of architectural concrete light wall plate of the present invention, comprises type design, makes mould, organizes frock, the making of decorative layer and structure sheaf and the demoulding and maintenance, and the production process of wherein said decorative layer comprises the following steps:
Step (1), puts into frock by described mould, adopts the method for jig to fix on mould and described frock, and lay one deck bottom ash in described mould; This step can ensure that decorative layer is dismantled easily and ensures the easy polishing of decor surface.
Step (2), cement, rock ballast, water wood fibre are made the first mixed material according to the percent mass ratio mixing and stirring of 1:1:0.38:0.05, and the particle diameter of described rock ballast is 0.5 ~ 1 millimeter.
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 3 millimeters, and slight vibrations occur to having minute bubbles; Little rock ballast is evenly distributed in slurry.
The production process of wherein said structure sheaf comprises the following steps:
Step (1), by cement, aggregate chips, alkaline-resisting chopped strand and water according to 1:2:0.05:0.5(quality than proportion by subtraction) ratio mixing and stirring makes the second mixed material;
Step (2), when described decorative layer initial set and the non-film forming in surface time, add 3 millimeters of described second mixed materials;
Step (3) is equipped with layer of non-woven fabric on described second mixed material, then after adding 3 millimeters of described second mixed materials, roll-in;
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 8 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material.
The stitching portion, outside being finally also included in described decorative layer is picked and has been dug out spline-simulating structure.
Embodiment 3
As shown in Figure 1, the preparation method of a kind of architectural concrete light wall plate of the present invention, comprises type design, makes mould, organizes frock, the making of decorative layer and structure sheaf and the demoulding and maintenance, and the production process of wherein said decorative layer comprises the following steps:
Step (1), puts into frock by described mould, adopts the method for jig to fix on mould and described frock, and lay one deck bottom ash in described mould; This step can ensure that decorative layer is dismantled easily and ensures the easy polishing of decor surface.
Step (2), makes the first mixed material by cement, rock ballast, water wood fibre according to the percent mass ratio mixing and stirring of 1:3:0.05:0.5, the particle diameter of described rock ballast is 0.6 ~ 1.2 millimeter.
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 4 millimeters, and slight vibrations occur to having minute bubbles; Little rock ballast is evenly distributed in slurry.
The production process of wherein said structure sheaf comprises the following steps:
Step (1), by cement, aggregate chips, alkaline-resisting chopped strand and water according to 1:2:0.04:0.45(mass percent) ratio mixes and makes the second mixed material.
Step (2), when described decorative layer initial set and the non-film forming in surface time, add 4 millimeters of described second mixed materials;
Step (3) is equipped with layer of non-woven fabric on described second mixed material, then after adding 5 millimeters of described second mixed materials, roll-in; Manufactured Board after roll-in, makes concrete rib in the behind of plate, forms rib structure and plate integrally combine and become flexible structure at the periphery of plate.
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 8 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material, make finished product architectural concrete light wall plate, warehouse-in after packaging.
The stitching portion, outside being finally also included in described decorative layer is picked and has been dug out spline-simulating structure.
Embodiment 4
As shown in Figure 1, the preparation method of a kind of architectural concrete light wall plate of the present invention, comprise type design, make mould, organize frock, the making of decorative layer and structure sheaf and the demoulding and maintenance, the production process of wherein said decorative layer comprises the following steps: wherein said mould is that styrofoam is made; Different mould size and shapes can be designed as required, meet design style and the requirement of different designs teacher and meet the needs installed.
Step (1), puts into frock by described mould, mould and described fixture glue cementation is determined, and lay one deck bottom ash in described mould; This step can ensure that decorative layer is dismantled easily and ensures the easy polishing of decor surface.
Step (2), cement, rock ballast, water wood fibre are made the first mixed material according to the percent mass ratio mixing and stirring of 1:2.5:0.38:0.05, and the particle diameter of described rock ballast is 0.8 to 1.5 millimeter.
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 4 millimeters, and slight vibrations occur to having minute bubbles; Little rock ballast is evenly distributed in slurry.
The production process of wherein said structure sheaf comprises the following steps:
Step (1), by cement, aggregate chips, alkaline-resisting chopped strand and water according to 1:1.5:0.045:0.4(mass percent) ratio mixing and stirring makes the second mixed material.
Step (2), when described decorative layer initial set and the non-film forming in surface time, add 5 millimeters of described second mixed materials;
Step (3) is equipped with layer of non-woven fabric on described second mixed material, then after adding 5 millimeters of described second mixed materials, roll-in; Manufactured Board after roll-in, install galvanizing steelframe in the behind of plate, zinc-plated steel frame passes through
6 reinforcing bars and plate integrally combine and become flexible structure.
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 12 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material, make finished product architectural concrete light wall plate, warehouse-in after packaging.
The stitching portion, outside being finally also included in described decorative layer is picked and has been dug out spline-simulating structure.
Embodiment 5
The preparation method of a kind of architectural concrete light wall plate of the present invention, comprises type design, makes mould, organizes frock, the making of decorative layer and structure sheaf and the demoulding and maintenance, and the production process of wherein said decorative layer comprises the following steps:
Step (1), puts into frock by described mould, and lays one deck bottom ash in described mould; This step can ensure that decorative layer is dismantled easily and ensures the easy polishing of decor surface.
Step (2), cement, rock ballast, water wood fibre are made the first mixed material according to the percent mass ratio mixing and stirring of 1:2:0.0.45:0.05, and the particle diameter of described rock ballast is 0.7 to 1.8 millimeter.
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 3.5 millimeters, and slight vibrations occur to having minute bubbles; Little rock ballast is evenly distributed in slurry.
The production process of wherein said structure sheaf comprises the following steps:
Step (1), by cement, aggregate chips, alkaline-resisting chopped strand and water according to 1:3:0.04:0.5(mass percent) ratio mixing and stirring makes the second mixed material.
Step (2), when described decorative layer initial set and the non-film forming in surface time, add 3.5 millimeters of described second mixed materials;
Step (3), described second mixed material is equipped with layer of non-woven fabric, then is laying layer of non-woven fabric after adding 5 millimeters of described second mixed materials, then adds 7 millimeters of described second mixed materials, roll-in.
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 15 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material, make finished product architectural concrete light wall plate, warehouse-in after packaging.
The polishing degree cement slurry that just removing is surperficial, the texture of namely indistinct appearance stone material; Compared with terrazzo, the operating space that terrazzo needs is large, and machine vibration is large, needs constantly to water in bruting process.And the wallboard skin in the present invention is decorative layer, and thickness is very thin, only need polish gently, and without the need to watering, without the need to rock ballast is exposed completely, the texture of stone material can be there is, without the need to spray paint again, save operation and resource, and outer durable, the defect such as can not cause that existing wallboard needs spray paint to cause that cortex comes off.
The stitching portion, outside being finally also included in described decorative layer is picked and has been dug out spline-simulating structure.
Embodiment 6
As shown in Figure 2, a kind of architectural concrete light wall plate of the present invention, comprises the structure sheaf that cement rock ballast slurry or Cement-Screening slurry solidify decorative layer that rear surface is polished to and the first Cement fibre layer set gradually, nonwoven layer, the second Cement fibre layer are formed; Described first Cement fibre layer and described decorative layer compact siro spinning technology.Described decorative layer is 2 millimeters; Described wallboard is 10 millimeters.First and second described Cement fibre layer is also fiber felt.
Embodiment 7
A kind of architectural concrete light wall plate of the present invention, comprises the structure sheaf that cement rock ballast slurry or Cement-Screening slurry solidify decorative layer that rear surface is polished to and the first Cement fibre layer set gradually, nonwoven layer, the second Cement fibre layer are formed; Described first Cement fibre layer and described decorative layer compact siro spinning technology.Described decorative layer is 3 millimeters; Described wallboard is 12 millimeters.
Embodiment 8
A kind of architectural concrete light wall plate of the present invention, comprises the structure sheaf that cement rock ballast slurry or Cement-Screening slurry solidify decorative layer that rear surface is polished to and the first Cement fibre layer set gradually, nonwoven layer, the second Cement fibre layer are formed; Described first Cement fibre layer and described decorative layer compact siro spinning technology.Described decorative layer is 2 millimeters; Described wallboard is 15 millimeters.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (9)
1. a preparation method for architectural concrete light wall plate, comprises type design, makes mould, organizes frock, the making of decorative layer and structure sheaf and the demoulding and maintenance, and it is characterized in that, the production process of wherein said decorative layer comprises the following steps:
Step (1), puts into frock by described mould, and adopts gluing or jig method and described frock to fix;
Cement, rock ballast, water and wood fibre are made the first mixed material according to the percent mass ratio mixing and stirring of 1:1 ~ 3:0.38 ~ 0.5:0.03 ~ 0.05 by step (2), and the particle diameter of described rock ballast is 0.5 to 2 millimeter;
Step (3), adds in described mould by the first mixed material be stirred, and the thickness of described first mixed material is 2 to 4 millimeters, and slight vibrations occur to there being minute bubbles;
The production process of wherein said structure sheaf comprises the following steps:
Step (1), makes the second mixed material by cement, aggregate chips, alkaline-resisting chopped strand and water according to the percent mass ratio mixing and stirring of 1:1 ~ 3:0.03 ~ 0.05:0.38 ~ 0.5;
Step (2), when described decorative layer initial set and the non-film forming in surface time, add described second mixed material of 3 to 5 millimeters thick;
Step (3), described second mixed material is equipped with layer of non-woven fabric, then after described second mixed material adding 3 to 5 millimeters thick, roll-in;
The production process of the wherein said demoulding comprises the following steps:
Step (1), wallboard final set, after 8 to 18 hours, removes described frock;
Step (2), after frock is removed, after being overturn by wallboard, takes out described mould, described rock ballast is exposed slightly the polishing of the outer surface of described decorative layer, occur the texture of stone material.
2. the preparation method of a kind of architectural concrete light wall plate according to claim 1, is characterized in that, production process step (1) mould of described decorative layer lays one deck decorative layer bottom ash after installing in described mould.
3. a kind of preparation method of architectural concrete light wall plate according to claim 1 or 2, it is characterized in that, the stitching portion, outside of described decorative layer is picked and is dug out spline-simulating structure.
4. a kind of preparation method of architectural concrete light wall plate according to claim 1 or 2, it is characterized in that, described second mixed material is equipped with layer of non-woven fabric, layer of non-woven fabric is re-layed after adding 3 to 5 millimeters of described second mixed materials again, then described second mixed material of 3 to 10 millimeters thick is added, roll-in.
5. the preparation method of a kind of architectural concrete light wall plate according to claim 4, is characterized in that, manufactured Board after roll-in, makes concrete rib or install galvanizing steelframe in the behind of plate, forms concrete rib structure or galvanizing steelframe passes through at edges of boards
reinforcing bar and the integrator structure that hardens.
6. a kind of preparation method of architectural concrete light wall plate according to claim 1 or 2, it is characterized in that, described mould is that styrofoam is made.
7. the architectural concrete light wall plate adopting the preparation method of a kind of architectural concrete light wall plate described in any one of claim 1 to 6 to prepare, it is characterized in that, comprise the structure sheaf that cement rock ballast slurry or Cement-Screening slurry solidify decorative layer that rear surface is polished to and the first Cement fibre layer set gradually, nonwoven layer, the second Cement fibre layer are formed; Described first Cement fibre layer and described decorative layer compact siro spinning technology.
8. the preparation method of a kind of architectural concrete light wall plate according to claim 7, it is characterized in that, the thickness of described decorative layer is 3 millimeters.
9. a kind of preparation method of architectural concrete light wall plate according to claim 7 or 8, it is characterized in that, described architectural concrete light wall plate integral thickness is 10 millimeters to 20 millimeters.