CN107513719A - A kind of metal cleaner for adding functional modification graphene and preparation method thereof - Google Patents
A kind of metal cleaner for adding functional modification graphene and preparation method thereof Download PDFInfo
- Publication number
- CN107513719A CN107513719A CN201710661241.4A CN201710661241A CN107513719A CN 107513719 A CN107513719 A CN 107513719A CN 201710661241 A CN201710661241 A CN 201710661241A CN 107513719 A CN107513719 A CN 107513719A
- Authority
- CN
- China
- Prior art keywords
- graphene
- metal
- triethanolamine
- functional modification
- metal cleaner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to metal detergent, discloses a kind of metal cleaner for adding functional modification graphene and preparation method thereof.The metal cleaner is made up of the water of 4~15wt% triethanolamines functionalization graphene, 13~25wt% surfactants, 1~2wt% metal inhibitors, 0.1~0.8wt% preservatives and surplus.The invention is added in metal cleaner using triethanolamine functionalization graphene, and triethanolamine and the graphene of triethanolamine functionalization graphene are Covalent bonding together, and substantial amounts of tertiary amine nitrogen and hydroxyl activity functional group is contained on its surface.Amino ion liquid functionalization graphene realizes graphene by the noncovalent interaction between imidazole ring and graphite annulus and is modified, graphene has the specific surface area of super large, by with after triethanolamine functionalization, there is very strong complexing, therefore possesses very strong adsorption capacity, not only remain the hydrophily and edible vegetable oil of triethanolamine, moreover it is possible to possess very strong adsorption capacity, it is not necessary to coordinate extra complexing agent to use.
Description
Technical field
The present invention relates to metal detergent, is cleaned more particularly, to a kind of metal for adding functional modification graphene
Agent and preparation method thereof.
Background technology
Metal cleaner is usually used in surface degreasing before and after intermetallic composite coating, scale removal in the industrial production using quite varied
And the cleaning before finished product assembling or packaging.In the electronics industry, must also be washed after printed circuit plate weld using cleaning agent
Remove the Harmful Residue.In addition, also usually use metal cleaner during plant equipment maintaining.
At present, conventional metal cleaner divides solvent-borne type, half solvent-borne type and aqua type.In solvent-borne type metal cleaner, stone
Oil solvent is inflammable, explosive and waste of resource.CFC is the most frequently used solvent-borne type metal cleaner, but because it is smelly to air
The destruction of oxygen layer and it is disabled.Thus, solvent-borne type metal cleaner is just progressively by half solvent-borne type and aqua type metal cleaner institute
Substitute.
For water base metal cleaning agent using surfactant as main component, water is solvent, and metal crust is cleaning object
Detergent.Water-base metal cleaning is formed by surfactant and a variety of additive compounds.Wherein surface-active contents be 10%~
40%, commonly use the compound of nonionic surfactant and anion surfactant.Conventional auxiliary agent builder (tripolyphosphate
Sodium, sodium metasilicate, sodium carbonate, sodium ethylene diamine tetracetate, the sodium acetate of secondary amino three etc.), corrosion inhibiter, stabilizer, solubilizer and foam
Stabilizer.Conventional is phosphate 6503 of alkylolamides class product such as coconut acid diethanolamide, alkylolamides etc..
In addition to energy stable foam, it can also increase viscosity and improve detergency.In addition, also containing defoamer (such as silicone oil, ethanol), filling
Agent, essence, colorant etc..
Water base metal cleaning agent is often based on paraffin removal oil removing in the prior art, to metal ion (such as copper of metal surface
Ion, iron ion) and follow-up anti-corrosion treatment DeGrain, and dispersiveness is unstable, causes cleaning not thorough, in order to
Solve the above problems, complexing agent and bleeding agent are often added in cleaning agent to have the function that adsorbing metal ions, still
One side DeGrain, is on the other hand formulated complexity, and cost is higher.
The content of the invention
The technical problems to be solved of the present invention are in view of the shortcomings of the prior art, creatively introduce addition functionalization
A kind of modified graphene, there is provided metal cleaner for adding functional modification graphene.
The present invention also provides the preparation method of the metal cleaner of the addition functional modification graphene.
The purpose of the present invention is achieved by the following technical programs:
A kind of metal cleaner for adding functional modification graphene is provided, by 4~15wt% triethanolamine function fossils
Black alkene, 13~25wt% surfactants, 1~2wt% metal inhibitors, the water group of 0.1~0.8wt% preservatives and surplus
Into.
Wherein, the triethanolamine of triethanolamine functionalization graphene and graphene are Covalent bonding together, and its surface is contained greatly
The tertiary amine nitrogen of amount and hydroxyl activity functional group.Amino ion liquid functionalization graphene passes through non-between imidazole ring and graphite annulus
Covalent effect realizes graphene modification, because triethanolamine functionalization graphene has the specific surface area of super large, by with three
After ethanolamine-functionalized, there is very strong complexing, therefore possess very strong adsorption capacity, not only remain triethanolamine
Hydrophily and edible vegetable oil, moreover it is possible to possess very strong adsorption capacity
Preferably, the surfactant be cocoanut fatty acid diethanolamide, sodium sulfate of polyethenoxy ether of fatty alcohol,
Lauryl sodium sulfate one or two or three kinds.
Preferably, the metal cleaner of the addition functional modification graphene is composed of the following components:
Preferably, the metal inhibitor is BTA.
Preferably, the preservative is sodium hydroxy methyl glycinate.
A kind of preparation method for the metal cleaner for adding functional modification graphene, comprises the following steps:
S1. prepared by triethanolamine functionalization graphene:
S11. graphene oxide is used to be dissolved in for raw material in deionized water, concentration is 2~3mg/L, and pH is 1~2, ultrasound
Uniform dispersion is dispersed to, by uniform dispersion and triethanolamine by volume 20~25:1 mixing, obtains mixed liquor;
S12. by heating in water bath for reaction 2~5h of the mixed liquor in step S11 at 70~90 DEG C, will reaction rear suspension liquid from
The heart separates, and is washed till neutrality with absolute ethyl alcohol and deionized water, is dried at 60~70 DEG C, obtains triethanolamine function graphite
Alkene;
S2. 4~15wt% triethanolamine functionalization graphene, 13~25wt% surface is added in a kettle successively
Activating agent, 1~2wt% metal inhibitor, the water of 0.1~0.8wt% preservative and surplus, are stirred to black even liquid
Body, finally give the metal cleaner of addition functional modification graphene;
Wherein, the surfactant is cocoanut fatty acid diethanolamide, sodium sulfate of polyethenoxy ether of fatty alcohol, ten
Sodium dialkyl sulfate one or two or three kinds;
The metal inhibitor is BTA;
The preservative is sodium hydroxy methyl glycinate.
Preferably, the ultrasonic disperse time is 30min in step S11.
Preferably, mixing time is 1~2h in step S2, and mixing speed is 80~100r/min.
A kind of application of the metal cleaner of the addition functional modification graphene is provided, applied to cleaning metal work
Tool, cleaning method are as follows:Water is added to match somebody with somebody for 3%~5% by concentration the metal cleaner of the addition functional modification graphene
Into working solution, it is cleaned by ultrasonic metal works at 25 DEG C~40 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows:
The invention is added in metal cleaner using triethanolamine functionalization graphene, triethanolamine function
The triethanolamine of graphite alkene and graphene are Covalent bonding together, and substantial amounts of tertiary amine nitrogen and hydroxyl activity function is contained on its surface
Group.Amino ion liquid functionalization graphene realizes graphene by the noncovalent interaction between imidazole ring and graphite annulus and changed
Property, because triethanolamine functionalization graphene has the specific surface area of super large, by with after triethanolamine functionalization, have it is very strong
Complexing, therefore possess very strong adsorption capacity, not only remain the hydrophily and edible vegetable oil of triethanolamine, moreover it is possible to possess
Very strong adsorption capacity, it is not necessary to coordinate extra complexing agent to use.
The surfactant of the present invention is using fatty acid oil diglycollic amide, sodium sulfate of polyethenoxy ether of fatty alcohol and 12
Sodium alkyl sulfate, synergy is produced by nonionic surfactant and anion surfactant, can effectively reduce table
Face tension force, reach preferable paraffin removal effect.
The present invention is used as organic inhibitor using BTA, in molecule while has polar group and nonpolar base
, many electron atomses be present in polar group, these atoms contain lone pair electrons, and electronegativity is big.Organic inhibitor
Polar group provides lone pair electrons, coordinate bond is formed with the metal ion of metal, so as to be adsorbed in gold in a manner of chemisorbed
On metal surface, while non-polar group is stretched in solution.Contact of the metal with corrosive medium has so on the one hand been effectively isolated,
The diffusion of corrosion reaction product is hindered, while also changes double electrical layerses, improves the activation energy of corrosion reaction, final suppression
The progress of corrosion reaction is made.
The present invention surrounds triethanolamine functionalization graphene, is selected by Surfactant, metal inhibitor and preservative
Select, and optimize the proportioning of each component, maximization adjusts each component while reaching effect, reaches cost-effective purpose.
The metal cleaner concentration of present invention addition functional modification graphene is low, it is only necessary to which 3%~5% adds water to match somebody with somebody
Into working solution, reaction at normal temperatures can reach the effect of cleaning metal.
Embodiment
The present invention is further illustrated with reference to specific embodiment.Following examples are only illustrative examples, not structure
Into inappropriate limitation of the present invention, the multitude of different ways that the present invention can be limited and covered by the content of the invention is implemented.It is unless special
Do not mentionlet alone bright, the present invention reagent, compound and the equipment that use is the art conventional reagent, compound and equipment.
Embodiment 1
The present embodiment provides a kind of preparation method of triethanolamine functionalization graphene, comprises the following steps:
S1. prepared by triethanolamine functionalization graphene:
S11. graphene oxide is used to be dissolved in for raw material in deionized water, concentration 2mg/L, pH 1, ultrasonic disperse
30min, uniform dispersion is obtained, by uniform dispersion and triethanolamine by volume 20:1 mixing, obtains mixed liquor;
S12. by heating in water bath for reaction 2h of the mixed liquor in step S11 at 70 DEG C, reaction rear suspension liquid is centrifuged,
And neutrality is washed till with absolute ethyl alcohol and deionized water, dried at 60 DEG C, obtain triethanolamine functionalization graphene.
Embodiment 2
The present embodiment provides a kind of preparation method of triethanolamine functionalization graphene, comprises the following steps:
S1. prepared by triethanolamine functionalization graphene:
S11. graphene oxide is used to be dissolved in for raw material in deionized water, concentration 3mg/L, pH 2, ultrasonic disperse
30min, uniform dispersion is obtained, by uniform dispersion and triethanolamine by volume 25:1 mixing, obtains mixed liquor;
S12. by heating in water bath for reaction 5h of the mixed liquor in step S11 at 90 DEG C, reaction rear suspension liquid is centrifuged,
And neutrality is washed till with absolute ethyl alcohol and deionized water, dried at 70 DEG C, obtain triethanolamine functionalization graphene.
Embodiment 3
The present embodiment provides a kind of preparation method for the metal cleaner for adding functional modification graphene, including following step
Suddenly:
S1. the triethanolamine functionalization graphene being prepared using embodiment 1 is as raw material;
S2. 4wt% triethanolamine functionalization graphene, 10t% coco-nut oil fatty acid is added in a kettle successively
Diglycollic amide, 2wt% sodium sulfate of polyethenoxy ether of fatty alcohol, 1wt% ten sodium dialkyl sulfate, 1wt% benzo three
The water of nitrogen azoles, 0.1wt% sodium hydroxy methyl glycinate and surplus, 1~2h, 80~100r/min of mixing speed are stirred, to black
Uniform liquid, finally give the metal cleaner of addition functional modification graphene.
4~embodiment of embodiment 13
In 4~embodiment of embodiment 13 and 1~comparative example of comparative example 2 mass percent of each component and each component with
Embodiment 3 is different, and specific reaction method is same as Example 1, does not repeat one by one.Table 1 gives embodiment 3~13 and contrast
The metal cleaner each component of addition functional modification graphene and the mass percent of each component of 1~comparative example of example 2.
Table 1
Comparative example 3
This comparative example is substantially the same manner as Example 3, and difference is, triethanolamine functionalization graphene is substituted for into three
Monoethanolamine.
Performance detection is with characterizing
It is concentration (PH that embodiment 3~13 and comparative example 1,2,3 are taken into 3%:10 ± 5) in 25 DEG C~40 DEG C of temperature
Cleaning performance, detergency ability, anti-corrosive properties and antifoam performance is carried out to compare:Test basis:JB/T4322.2-1999《Water-base metal
Cleaning agent test method》And JB/T4322.1-1999《Water base metal cleaning agent》, it is specific as shown in table 2:
Table 2
Analysis of conclusion:
With the addition of triethanolamine functionalization graphene, properties substantially increase, but work as triethanolamine functionalization
After graphene reaches 9wt%, properties increase unobvious, from comparative example 1 as can be seen that triethanolamine function ought not be added
Effect is worst when graphite alkene, and reason is that triethanolamine functionalization graphene has very high adsorptivity as adsorbent
Ability, it is mainly attributed to the specific surface area of the dilute super large of graphite and the triethanolamine heavy metal chelating structure being modified.It is huge to compare table
Graphite dilute surface modification of area tertiary amine alcohol, considerably increases the strong avtive spot of adhesion, easily with heavy metal copper ion
Very strong complexing occurs, so as to have a higher adsorption capacity, and triethanolamine functionalization graphene be also equipped with it is very stable
Dispersiveness, from comparative example 2 as can be seen that using triethanolamine substitute triethanolamine functionalization graphene effect it is poor, reason
It is, triethanolamine has the non-pole of hydrophilic polar group and oleophylic as bleeding agent in the molecular structure of bleeding agent
Property group, the lubricant component parent of its lipophilic group and wax dirt the inside, but be a lack of complexing agent and can not remove the gold of metal surface
Belong to ion, in addition, also illustrating that triethanolamine functionalization graphene also retains the hydrophily and edible vegetable oil of triethanolamine.
From 9~embodiment of embodiment 13 and comparative example 2 as can be seen that when surfactant uses coco-nut oil fatty acid two
Best results when glycollic amide, sodium sulfate of polyethenoxy ether of fatty alcohol and lauryl sodium sulfate, reason are nonionic
Surfactant produces synergy with anion surfactant, can effectively reduce surface tension, reach preferable paraffin removal
Effect.
Claims (10)
1. a kind of metal cleaner for adding functional modification graphene, it is characterised in that by 4~15wt% triethanolamine functions
Graphite alkene, 13~25wt% surfactants, 1~2wt% metal inhibitors, the water group of 0.1~0.8wt% preservatives and surplus
Into.
2. the metal cleaner of functional modification graphene is added according to claim 1, it is characterised in that live on the surface
Property agent be cocoanut fatty acid diethanolamide, sodium sulfate of polyethenoxy ether of fatty alcohol, one kind of lauryl sodium sulfate or two
Kind or three kinds.
3. the metal cleaner of functional modification graphene is added according to claim 2, it is characterised in that by following components
Composition:
4~15wt% of triethanolamine functionalization graphene
10~15wt% of cocoanut fatty acid diethanolamide
2~8wt% of sodium sulfate of polyethenoxy ether of fatty alcohol
1~2wt% of lauryl sodium sulfate
1~2wt% of metal inhibitor
0.1~0.8wt% of preservative
Water surplus.
4. the metal cleaner of functional modification graphene is added according to claim 3, it is characterised in that the metal delays
Erosion agent is BTA.
5. the metal cleaner of functional modification graphene is added according to claim 3, it is characterised in that the preservative
For sodium hydroxy methyl glycinate.
6. a kind of preparation method for the metal cleaner for adding functional modification graphene, it is characterised in that comprise the following steps:
S1. prepared by triethanolamine functionalization graphene:
S11. graphene oxide is used to be dissolved in for raw material in deionized water, concentration is 2~3mg/L, and pH is 1~2, ultrasonic disperse
To uniform dispersion, by uniform dispersion and triethanolamine by volume 20~25:1 mixing, obtains mixed liquor;
S12. by heating in water bath for reaction 2~5h of the mixed liquor in step S11 at 70~90 DEG C, reaction rear suspension liquid centrifugation is divided
From, and neutrality is washed till with absolute ethyl alcohol and deionized water, dried at 60~70 DEG C, obtain triethanolamine functionalization graphene;
S2. 4~15wt% triethanolamine functionalization graphene, 13~25wt% surface-active is added in a kettle successively
Agent, 1~2wt% metal inhibitor, the water of 0.1~0.8wt% preservative and surplus, stir to black even liquid, finally
Obtain adding the metal cleaner of functional modification graphene;
Wherein, the surfactant is cocoanut fatty acid diethanolamide, sodium sulfate of polyethenoxy ether of fatty alcohol, dodecane
Base sodium sulphate one or two or three kinds;
The metal inhibitor is BTA;
The preservative is sodium hydroxy methyl glycinate.
7. the preparation method of the metal cleaner of functional modification graphene is added according to claim 6, it is characterised in that
The ultrasonic disperse time is 30min in step S11.
8. the preparation method of the metal cleaner of functional modification graphene is added according to claim 6, it is characterised in that
Mixing time is 1~2h in step S2, and mixing speed is 80~100r/min.
9. adding the application of the metal cleaner of functional modification graphene according to Claims 1 to 5 any one, it is special
Sign is, applied to cleaning metal works.
10. the method applied according to claim 9, it is characterised in that by the gold of the addition functional modification graphene
Category cleaning agent is that 3%~5% plus water are made into working solution by concentration, is cleaned by ultrasonic metal works at 25 DEG C~40 DEG C.