CN107502789A - A kind of aluminum alloy materials - Google Patents
A kind of aluminum alloy materials Download PDFInfo
- Publication number
- CN107502789A CN107502789A CN201710710998.8A CN201710710998A CN107502789A CN 107502789 A CN107502789 A CN 107502789A CN 201710710998 A CN201710710998 A CN 201710710998A CN 107502789 A CN107502789 A CN 107502789A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- alloy
- aluminium
- aluminum alloy
- magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aluminum alloy materials, using aluminium as raw material, in addition to silicon, iron, cobalt, carbon, gold, magnesium, calcium, niobium and tin.The beneficial effects of the invention are as follows:The magnesium and silicon contained in alloy, the intensity of aluminium alloy is enhanced, improve the corrosion resistance, inoxidizability and solderability of aluminium alloy, the copper and iron contained in aluminium alloy, the intensity of aluminium alloy is enhanced, improves the machinability of aluminium alloy, improves the stability of aluminium alloy.
Description
Technical field
The present invention relates to a kind of metal material, more particularly to a kind of aluminum alloy materials.
Background technology
Aluminium alloy is most widely used a kind of non-ferrous metal structural material in industry, in Aeronautics and Astronautics, automobile, machinery
Widely applied in manufacture, ship and chemical industry.With the rapid development of science and technology and industrial economy, to aluminium alloy
Demand is increasing, and the research enabled aluminum alloy to is also goed deep into therewith.So far, when aluminium alloy is used for into automobile, for starting
Cylinder head, cylinder block or case of transmission of machine etc..The various aluminium alloys of component are crossed as this aluminium alloy motion, with
Actively the advantages of and light weight good using the processability of aluminium, and improve the engineering properties such as hardness, intensity or improve heat resistance etc. and change
Learn property.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of aluminum alloy materials.
The technical solution adopted by the present invention is:
A kind of aluminum alloy materials, using aluminium as raw material, in addition to silicon, iron, cobalt, carbon, gold, magnesium, calcium, niobium and tin.
Further, its parts by weight is respectively:
Further, the parts by weight of the silicon are 3-5 parts.
Further, the parts by weight of the cobalt are 0.4 part.
Further, the parts by weight of the magnesium are 2-4 parts.
The beneficial effects of the invention are as follows:The magnesium and silicon contained in alloy, enhances the intensity of aluminium alloy, improves aluminium alloy
Corrosion resistance, inoxidizability and solderability, the copper and iron contained in aluminium alloy, enhance the intensity of aluminium alloy, improve aluminium
The machinability of alloy, improve the stability of aluminium alloy.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A kind of aluminum alloy materials, using aluminium as raw material, in addition to silicon, iron, cobalt, carbon, gold, magnesium, calcium, niobium and tin, its parts by weight
Number is respectively:
The beneficial effects of the invention are as follows:The magnesium and silicon contained in alloy, enhances the intensity of aluminium alloy, improves aluminium alloy
Corrosion resistance, inoxidizability and solderability, the copper and iron contained in aluminium alloy, enhance the intensity of aluminium alloy, improve aluminium
The machinability of alloy, improve the stability of aluminium alloy.
Embodiment 2
A kind of aluminum alloy materials, using aluminium as raw material, in addition to silicon, iron, cobalt, carbon, gold, magnesium, calcium, niobium and tin, its parts by weight
Number is respectively:
The beneficial effects of the invention are as follows:The magnesium and silicon contained in alloy, enhances the intensity of aluminium alloy, improves aluminium alloy
Corrosion resistance, inoxidizability and solderability, the copper and iron contained in aluminium alloy, enhance the intensity of aluminium alloy, improve aluminium
The machinability of alloy, improve the stability of aluminium alloy.
Embodiment 3
A kind of aluminum alloy materials, using aluminium as raw material, in addition to silicon, iron, cobalt, carbon, gold, magnesium, calcium, niobium and tin, its parts by weight
Number is respectively:
The beneficial effects of the invention are as follows:The magnesium and silicon contained in alloy, enhances the intensity of aluminium alloy, improves aluminium alloy
Corrosion resistance, inoxidizability and solderability, the copper and iron contained in aluminium alloy, enhance the intensity of aluminium alloy, improve aluminium
The machinability of alloy, improve the stability of aluminium alloy.
The above described is only a preferred embodiment of the present invention, it is not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within present invention model claimed
Enclose.
Claims (5)
- A kind of 1. aluminum alloy materials, it is characterised in that:Using aluminium as raw material, in addition to silicon, iron, cobalt, carbon, gold, magnesium, calcium, niobium and tin.
- A kind of 2. aluminum alloy materials according to claim 1, it is characterised in that:Its parts by weight is respectively:
- A kind of 3. aluminum alloy materials according to claim 1, it is characterised in that:The parts by weight of the silicon are 3-5 parts.
- A kind of 4. aluminum alloy materials according to claim 1, it is characterised in that:The parts by weight of the cobalt are 0.4 part.
- A kind of 5. aluminum alloy materials according to claim 1, it is characterised in that:The parts by weight of the magnesium are 2-4 parts.