CN108034864A - Aluminum alloy materials - Google Patents
Aluminum alloy materials Download PDFInfo
- Publication number
- CN108034864A CN108034864A CN201711385457.9A CN201711385457A CN108034864A CN 108034864 A CN108034864 A CN 108034864A CN 201711385457 A CN201711385457 A CN 201711385457A CN 108034864 A CN108034864 A CN 108034864A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy materials
- count
- weight percentage
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of aluminum alloy materials.The aluminum alloy materials, count by weight percentage, including:Aluminium 94 96%, silicon 1 2.5%, manganese 1 1.5%, zirconium 0.5 1.5%;Also alternative addition zinc and magnesium, the content of zinc is usually 0.25 0.5%, and the content of magnesium is usually 0.5 1.5%.Aluminum alloy materials of the present invention have good tensile property and die casting, convenient processing after shaping, while also have certain corrosion resistance.
Description
Technical field
The present invention relates to a kind of aluminum alloy materials.
Background technology
Aluminium alloy density is low but intensity is higher, and near or above high-quality steel, plasticity is good, can be processed into various section bars,
With excellent electric conductivity, thermal conductivity and corrosion stability, therefore aluminium alloy is in Aeronautics and Astronautics, automobile, machine-building, ship and change
Learning in industry has extensive application, is most widely used non-ferrous metal structural material in industry.It is at full speed with industrial economy
Development, it is increasing to the demand of aluminium alloy extrusions, to the requirement such as corrosion resistance, die casting performance, solderability of aluminium alloy
Also it is higher and higher.But the properties of aluminum alloy materials tend not to take into account, can only be brought up again for application scenario demand
Rise some performances and reach requirement, the present invention is intended to provide a kind of die casting performance and the excellent aluminium alloy material of corrosion resistance
Material.
The content of the invention
To achieve the above object, the present invention provides a kind of aluminum alloy materials.
Technical scheme is as follows:Aluminum alloy materials, count by weight percentage, including:Aluminium 94-96%, silicone content
For 1-2.5%, manganese 1-1.5%, zirconium 0.5-1.5%.
Preferably, the aluminum alloy materials, also contain zinc 0.25-0.5% count by weight percentage.
Preferably, the aluminum alloy materials, also contain magnesium 0.5-1.5% count by weight percentage.
Most preferably, the aluminum alloy materials, count by weight percentage, including aluminium 95.8%, silicone content 1%, manganese
1.2%, zirconium 0.5%, zinc 0.5%, magnesium 0.5%.
Compared with prior art, the beneficial effects of the present invention are:The aluminum alloy materials have good tensile property
With die casting, convenient processing after shaping, while also there is certain corrosion resistance.
Embodiment
With reference to embodiment, the present invention is described in further detail, embodiment be only used for illustrate rather than
Limit protection scope of the present invention.
Embodiment 1:
The aluminum alloy materials, count by weight percentage, including:Aluminium 95%, silicone content 2.5%, manganese 1%, zirconium 1.5%.
Embodiment 2:
Aluminum alloy materials, count by weight percentage, including:Aluminium 96%, silicone content 1%, manganese 1.5%, zirconium 1.5%.
Embodiment 3:
Aluminum alloy materials, count by weight percentage, including:Aluminium 94.5%, silicone content 2.2%, manganese 1.2%, zirconium 0.8%, zinc
0.5%, magnesium 0.8%.
Embodiment 4:
Aluminum alloy materials, count by weight percentage, including:Aluminium 94%, silicone content 1.5%, manganese 1.25%, zirconium 1.5%, zinc
0.25%, magnesium 1.5%.
Embodiment 5:
The aluminum alloy materials, count by weight percentage, including aluminium 95.8%, silicone content 1%, manganese 1.2%, zirconium 0.5%, zinc
0.5%, magnesium 0.5%.
Above example performance comparison situation such as following table:
Do not introduce the manufacture method of the magnesium-aluminium alloy material in the present invention specifically, because its manufacture method can use it is existing conventional
Manufacture method, this will not be repeated here.
Although description of this invention combination embodiments above carries out, those skilled in the art
Member can carry out many replacements, modifications and variations according to above-mentioned content, be obvious.Therefore, it is all it is such substitute,
Improve and change is included in the spirit and scope of appended claims.
Claims (4)
1. aluminum alloy materials, count by weight percentage, including:Aluminium 94-96%, silicone content 1-2.5%, manganese 1-1.5%, zirconium
0.5-1.5%。
2. aluminum alloy materials according to claim 1, it is characterised in that also contain zinc 0.25- count by weight percentage
0.5%。
3. aluminum alloy materials according to claim 2, it is characterised in that also contain magnesium 0.5- count by weight percentage
1.5%。
4. aluminum alloy materials according to claim 3, it is characterised in that count by weight percentage, including aluminium 95.8%,
Silicone content is 1%, manganese 1.2%, zirconium 0.5%, zinc 0.5%, magnesium 0.5%.