CN107501950A - 基于led灯的新型材料 - Google Patents

基于led灯的新型材料 Download PDF

Info

Publication number
CN107501950A
CN107501950A CN201710864334.7A CN201710864334A CN107501950A CN 107501950 A CN107501950 A CN 107501950A CN 201710864334 A CN201710864334 A CN 201710864334A CN 107501950 A CN107501950 A CN 107501950A
Authority
CN
China
Prior art keywords
parts
lampshade
silica gel
led
transparent silica
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710864334.7A
Other languages
English (en)
Inventor
王俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Master Technology Co Ltd
Original Assignee
Chongqing Master Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Master Technology Co Ltd filed Critical Chongqing Master Technology Co Ltd
Priority to CN201710864334.7A priority Critical patent/CN107501950A/zh
Publication of CN107501950A publication Critical patent/CN107501950A/zh
Pending legal-status Critical Current

Abstract

本发明公开了基于LED灯的新型材料，包括LED灯的灯罩，所述灯罩组成材料，按重量份数比包括以下组分，透明硅胶20‑30份，黄色荧光粉30‑45份，高锰酸钾酸性溶液0.5‑1份，石蜡10‑25份，二氧化锰18‑37份；所述黄色荧光粉的粒径为5‑10μm，所述透明硅胶的粘度为5000‑8000cps，还包括灯罩的制造步骤，步骤1：将上述高锰酸钾酸性溶，石蜡，二氧化锰，搅拌20分钟后得到混合液，将混合液高温加热；步骤2：步骤1中的混合液冷却后，加入透明硅胶搅拌；得到半成品；步骤3：将步骤2中的半成品加入黄色荧光粉，加热搅拌1小时；倒入灯罩模具中，步骤4：待步骤3中模具内灯罩成型后取出，再灯罩外层涂布聚脂薄膜层，晾干保存，所述透明硅胶由以下重量份数比组分组成。

Description

基于LED灯的新型材料
技术领域
本发明涉及一种灯罩，具体涉及基于LED灯的新型材料。
背景技术
近年来，全球化石能源正随着工业化进程的发展而造成减少，节能减排，低碳生活已受到关注。随着发光二极管的发明，从照明角度考虑节能减排已具有现实的可能。
LED是一种固态的半导体器件，它可以直接把电转化为光。LED的心脏是一个半导体的晶片，该晶片附着在一个支架上，一端是负极，另一端连接电源的正极。半导体晶片由两部分组成，一部分是P型半导体，在它里面空穴占主导地位，另一端是N型半导体，电子占主导地位。但这两种半导体连接起来的时候，它们之间就形成一个“P-N结”。当电流通过导线作用于这个晶片的时候，电子就会被推向P区，在P区里电子跟空穴复合，然后就会以光子的形式发出能量，这就是LED发光的原理。
LED灯管是在透光的灯管内部设置一排LED发光单元，现有技术存在的技术问题如下：存在透光度差，透射光衰减大、雾面均匀度差的问题与不足；LED灯管存在破裂的可能，从而存在安全隐患。
发明内容
本发明所要解决的技术问题是适应现实的需要，如何设计一种透光度好、透射光衰小、雾面均匀、防爆的LED照明灯罩，目的在于提供基于LED灯的新型材料，解决适应现实的需要，如何设计一种透光度好、透射光衰小、雾面均匀、防爆的LED照明灯罩的问题。
本发明通过下述技术方案实现：
基于LED灯的新型材料，包括LED灯的灯罩，所述灯罩组成材料，按重量份数比包括以下组分，透明硅胶20-30份，黄色荧光粉30-45份，高锰酸钾酸性溶液0.5-1份，石蜡10-25份，二氧化锰18-37份；所述黄色荧光粉的粒径为5-10μm，所述透明硅胶的粘度为5000-8000cps，还包括灯罩的制造步骤，步骤1：将上述高锰酸钾酸性溶，石蜡，二氧化锰，搅拌20分钟后得到混合液，将混合液高温加热；步骤2：步骤1中的混合液冷却后，加入透明硅胶搅拌；得到半成品；步骤3：将步骤2中的半成品加入黄色荧光粉，加热搅拌1小时；倒入灯罩模具中，步骤4：待步骤3中模具内灯罩成型后取出，再灯罩外层涂布聚脂薄膜层，晾干保存。LED灯管是在透光的灯管内部设置一排LED发光单元，现有技术存在的技术问题如下：存在透光度差，透射光衰减大、雾面均匀度差的问题与不足；LED灯管存在破裂的可能，从而存在安全隐患，本发明为了解决这一问题，采用了制造新型灯罩，所述采用的胶粘剂为透明的，且其粘度达到5000-8000cps，因此可以将黄色荧光粉更好的融合后固定在树脂薄膜的表面。涂布速度快，聚酯薄膜的涂布宽幅较宽，成品的宽度可以在0.2m～2.0m之间，相同时间内生产的产品数量多，提高生产效率。解决了传统问题的不足。
所述透明硅胶由以下重量份数比组分组成，硅胶70-95份，催化剂0.7-1.3份，水溶剂10-15份，硅氧烷0.5-0.7份。进一步，作为本发明的优选方案。
所述聚酯薄膜层中基材的热收缩率小于或等于1％。进一步，作为本发明的优选方案。
所述聚脂薄膜层中基材的透光率大于或等于90％，进一步，作为本发明的优选方案。
本发明与现有技术相比，具有如下的优点和有益效果：
1、本发明基于LED灯的新型材料，粘度达到5000-8000cps，因此可以将黄色荧光粉更好的融合后固定在树脂薄膜的表面；
2、本发明基于LED灯的新型材料涂布速度快，聚酯薄膜的涂布宽幅较宽，成品的宽度可以在0.2m～2.0m之间，相同时间内生产的产品数量多，提高生产效率，；
3、本发明基于LED灯的新型材料，聚脂薄膜层中基材的透光率大于或等于90％，不会因为增加灯罩导致透光不好。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白，下面结合实施例，对本发明作进一步的详细说明，本发明的示意性实施方式及其说明仅用于解释本发明，并不作为对本发明的限定。
实施例1
本发明基于LED灯的新型材料，包括LED灯的灯罩，所述灯罩组成材料，按重量份数比包括以下组分，透明硅胶20-30份，黄色荧光粉30-45份，高锰酸钾酸性溶液0.5-1份，石蜡10-25份，二氧化锰18-37份；所述黄色荧光粉的粒径为5-10μm，所述透明硅胶的粘度为5000-8000cps，还包括灯罩的制造步骤，步骤1：将上述高锰酸钾酸性溶，石蜡，二氧化锰，搅拌20分钟后得到混合液，将混合液高温加热；步骤2：步骤1中的混合液冷却后，加入透明硅胶搅拌；得到半成品；步骤3：将步骤2中的半成品加入黄色荧光粉，加热搅拌1小时；倒入灯罩模具中，步骤4：待步骤3中模具内灯罩成型后取出，再灯罩外层涂布聚脂薄膜层，晾干保存。粘度达到5000-8000cps，因此可以将黄色荧光粉更好的融合后固定在树脂薄膜的表面。涂布速度快，聚酯薄膜的涂布宽幅较宽，成品的宽度可以在0.2m～2.0m之间，相同时间内生产的产品数量多，提高生产效率。
实施例2
本发明基于LED灯的新型材料，包括LED灯的灯罩，所述灯罩组成材料，按重量份数比包括以下组分，透明硅胶20-30份，黄色荧光粉30-45份，高锰酸钾酸性溶液0.5-1份，石蜡10-25份，二氧化锰18-37份；所述黄色荧光粉的粒径为5-10μm，所述透明硅胶的粘度为5000-8000cps，还包括灯罩的制造步骤，步骤1：将上述高锰酸钾酸性溶，石蜡，二氧化锰，搅拌20分钟后得到混合液，将混合液高温加热；步骤2：步骤1中的混合液冷却后，加入透明硅胶搅拌；得到半成品；步骤3：将步骤2中的半成品加入黄色荧光粉，加热搅拌1小时；倒入灯罩模具中，步骤4：待步骤3中模具内灯罩成型后取出，再灯罩外层涂布聚脂薄膜层，晾干保存。所述透明硅胶由以下重量份数比组分组成，硅胶70-95份，催化剂0.7-1.3份，水溶剂10-15份，硅氧烷0.5-0.7份。所述聚酯薄膜层中基材的热收缩率小于或等于1％。所述聚脂薄膜层中基材的透光率大于或等于90％，不会因为增加灯罩导致透光不好。粘度达到5000-8000cps，因此可以将黄色荧光粉更好的融合后固定在树脂薄膜的表面。涂布速度快，聚酯薄膜的涂布宽幅较宽，成品的宽度可以在0.2m～2.0m之间，相同时间内生产的产品数量多，提高生产效率。
以上所述的具体实施方式，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施方式而已，并不用于限定本发明的保护范围，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.基于LED灯的新型材料，包括LED灯的灯罩，其特征在于：所述灯罩组成材料，按重量份数比包括以下组分，透明硅胶20-30份，黄色荧光粉30-45份，高锰酸钾酸性溶液0.5-1份，石蜡10-25份，二氧化锰18-37份；所述黄色荧光粉的粒径为5-10μm，所述透明硅胶的粘度为5000-8000cps，还包括灯罩的制造步骤，
步骤1：将上述高锰酸钾酸性溶，石蜡，二氧化锰，搅拌20分钟后得到混合液，将混合液高温加热；
步骤2：步骤1中的混合液冷却后，加入透明硅胶搅拌；得到半成品；
步骤3：将步骤2中的半成品加入黄色荧光粉，加热搅拌1小时；倒入灯罩模具中，
步骤4：待步骤3中模具内灯罩成型后取出，再灯罩外层涂布聚脂薄膜层，晾干保存。
2.根据权利要求1所述的基于LED灯的新型材料，其特征在于：所述透明硅胶由以下重量份数比组分组成，硅胶70-95份，催化剂0.7-1.3份，水溶剂10-15份，硅氧烷0.5-0.7份。
3.根据权利要求1所述的基于LED灯的新型材料，其特征在于：所述聚酯薄膜层中基材的热收缩率小于或等于1％。
4.根据权利要求1所述的基于LED灯的新型材料，其特征在于：所述聚脂薄膜层中基材的透光率大于或等于90％。
CN201710864334.7A 2017-09-22 2017-09-22 基于led灯的新型材料 Pending CN107501950A (zh)