CN107497860A - 一种能提高不锈钢性能的加工方法 - Google Patents
一种能提高不锈钢性能的加工方法 Download PDFInfo
- Publication number
- CN107497860A CN107497860A CN201710720903.0A CN201710720903A CN107497860A CN 107497860 A CN107497860 A CN 107497860A CN 201710720903 A CN201710720903 A CN 201710720903A CN 107497860 A CN107497860 A CN 107497860A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- oil
- roll
- processing method
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种能提高不锈钢性能的加工方法，包括步骤：不锈钢进行热轧工艺，所述热轧工艺中用到的轧辊上涂覆有润滑剂，润滑剂是水油混合物，在涂覆过程中，以水包油的润滑剂在轧辊的辊面上展开，将所述不锈钢放入到所述轧辊上，进入变形区进行加热并施加压力，一部分油进行燃烧，另一部分油以油膜的形式存在于轧辊和不锈钢之间，进行热轧。通过上述方式，本发明的能提高不锈钢性能的加工方法,通过加入润滑油的方式，防止轧辊上的黑面弄到不锈钢表面上，能够提高轧辊的作业效率，减少轧辊次数，提高不锈钢的各种性能。
Description
技术领域
本发明涉及不锈钢加工领域，特别是涉及一种能提高不锈钢性能的加工方法。
背景技术
不锈钢是不锈耐酸钢的简称，耐空气、蒸汽、水等弱腐蚀介质或具有不锈性的钢种称为不锈钢；而将耐化学腐蚀介质（酸、碱、盐等化学浸蚀）腐蚀的钢种称为耐酸钢。由于两者在化学成分上的差异而使他们的耐蚀性不同，普通不锈钢一般不耐化学介质腐蚀，而耐酸钢则一般均具有不锈性。“不锈钢”一词不仅仅是单纯指一种不锈钢，而是表示一百多种工业不锈钢，所开发的每种不锈钢都在其特定的应用领域具有良好的性能。现有的不锈钢加工过程中，会用到轧辊，现有的轧辊上的黑面会弄到不锈钢表面，影响不锈钢使用。
发明内容
本发明主要解决的技术问题是提供一种能提高不锈钢性能的加工方法，加工效果好。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种能提高不锈钢性能的加工方法，包括步骤：不锈钢进行热轧工艺，所述热轧工艺中用到的轧辊上涂覆有润滑剂，润滑剂是水油混合物，在涂覆过程中，以水包油的润滑剂在轧辊的辊面上展开，将所述不锈钢放入到所述轧辊上，进入变形区进行加热并施加压力，一部分油进行燃烧，另一部分油以油膜的形式存在于轧辊和不锈钢之间，进行热轧。
在本发明一个较佳实施例中，所述润滑油为基础油或油性剂。
在本发明一个较佳实施例中，所述基础油为矿物油、聚烯烃或酯类油。
在本发明一个较佳实施例中，所述油性剂为植物油、脂肪酸、动物油、合成脂或固体润滑剂。
在本发明一个较佳实施例中，所述变形区加热的温度为150-200摄氏度。
在本发明一个较佳实施例中，所述变形区施加的压力为100-150MPa。
本发明的有益效果是：本发明的能提高不锈钢性能的加工方法,通过加入润滑油的方式，防止轧辊上的黑面弄到不锈钢表面上，能够提高轧辊的作业效率，减少轧辊次数，提高不锈钢的各种性能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
提供一种能提高不锈钢性能的加工方法，包括步骤：不锈钢进行热轧工艺，所述热轧工艺中用到的轧辊上涂覆有润滑剂，润滑剂是水油混合物，在涂覆过程中，以水包油的润滑剂在轧辊的辊面上展开，将所述不锈钢放入到所述轧辊上，进入变形区进行加热并施加压力，一部分油进行燃烧，另一部分油以油膜的形式存在于轧辊和不锈钢之间，进行热轧。
优选地，所述润滑油为基础油或油性剂。
优选地，所述基础油为矿物油、聚烯烃或酯类油。
优选地，所述油性剂为植物油、脂肪酸、动物油、合成脂或固体润滑剂。
优选地，所述变形区加热的温度为150-200摄氏度。
优选地，所述变形区施加的压力为100-150MPa。
本发明的有益效果是：
一、所述能提高不锈钢性能的加工方法通过加入润滑油的方式，防止轧辊上的黑面弄到不锈钢表面上；
二、所述能提高不锈钢性能的加工方法能够提高轧辊的作业效率，减少轧辊次数，提高不锈钢的各种性能。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种能提高不锈钢性能的加工方法，其特征在于，包括步骤：不锈钢进行热轧工艺，所述热轧工艺中用到的轧辊上涂覆有润滑剂，润滑剂是水油混合物，在涂覆过程中，以水包油的润滑剂在轧辊的辊面上展开，将所述不锈钢放入到所述轧辊上，进入变形区进行加热并施加压力，一部分油进行燃烧，另一部分油以油膜的形式存在于轧辊和不锈钢之间，进行热轧。
2.根据权利要求1所述的能提高不锈钢性能的加工方法，其特征在于，所述润滑油为基础油或油性剂。
3.根据权利要求2所述的能提高不锈钢性能的加工方法，其特征在于，所述基础油为矿物油、聚烯烃或酯类油。
4.根据权利要求2所述的能提高不锈钢性能的加工方法，其特征在于，所述油性剂为植物油、脂肪酸、动物油、合成脂或固体润滑剂。
5.根据权利要求1所述的能提高不锈钢性能的加工方法，其特征在于，所述变形区加热的温度为150-200摄氏度。
6.根据权利要求1所述的能提高不锈钢性能的加工方法，其特征在于，所述变形区施加的压力为100-150MPa。