CN107487125A - It is modelled after an antique to make old tinware and preparation method thereof - Google Patents
It is modelled after an antique to make old tinware and preparation method thereof Download PDFInfo
- Publication number
- CN107487125A CN107487125A CN201710934611.7A CN201710934611A CN107487125A CN 107487125 A CN107487125 A CN 107487125A CN 201710934611 A CN201710934611 A CN 201710934611A CN 107487125 A CN107487125 A CN 107487125A
- Authority
- CN
- China
- Prior art keywords
- tinware
- antique
- modelled
- processing
- old
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Modelled after an antique make old tinware and preparation method thereof the present invention relates to a kind of.Preparation method:By tinware is heated, infrared ray, ultraviolet, drench with rain, wind, spraying, icing, illumination, oxygenation, the processing of the step such as humidification and ultrasonic wave.Specifically, S101:Tinware is heated, drenched with rain successively afterwards, the processing such as wind and spraying;S102:Product after S101 is handled carries out cooling processing, carries out illumination, oxygenation and humidification processing successively afterwards;Circulate S101 and S102 processing, obtain it is modelled after an antique make it is old after tinware.It is provided by the invention it is modelled after an antique make old tinware preparation method, simulation nature bag slurry process, tinware premature oxidation can be promoted, significantly shorten tinware oxidation and time that bag slurry is formed;The purpose of exploitation museum's spin-off is advocated, and the tinware color and luster being prepared is simple and unsophisticated, property is stable, can be effectively moistureproof, really realizes the water sweetness that is filled with water, and contains wine aroma alcohol, storage tea flavour is constant, and it is permanent to spend.
Description
Technical field
The present invention relates to tinwork manufacturing technology field, and in particular to one kind is modelled after an antique to make old tinware and preparation method thereof.
Background technology
It is well known that tin as the rare metal after ranking gold and silver, have cool in nature, rapid heat dissipation, it is nontoxic, without any metal
The advantages that peculiar smell, through the ages, enjoy the good reputation of " green metal ".By the chemical characteristic and metal-like of tin, tinware property
It will not be aoxidized under stable, normal temperature;And after the growing up to be a useful person of tin, make old through modelled after an antique, can not only show its simple and unadorned feature, match in excellence or beauty ancient tinware
Color and luster and simple and unsophisticated style;, can be as the collection having use value and it is had concurrently with Tibetan.
Metallic tin is used as the with a long history of memory carrier, and many food is all using tinfoil as main packing timber
Material, and the sealing property of tinwork and the characteristics of have superior radio resistance property, not only can effectively protection against the tide, can more keep tealeaves lasting
Delicious fragrance.Therefore, before more than 1,000 years, ancients are just understood with tinware come storing tea, are the good thing of tea storage.Modern tinware
Even more appeared in the form of tea can etc. in the visual field of people;Tinware is accomplished to store up tea flavour with its good sealing and performance of guaranteeing the quality
It is constant, contain wine aroma alcohol and well-known.
Tinware is modelled after an antique to make old most importantly bag slurry, but bag slurry is formed, it is necessary to the time integral in calendar month all the year round naturally.Base
In this, there is provided a kind of new quickly to realize tinware modelled after an antique to make old method particularly important.
The content of the invention
For in the prior art the defects of, modelled after an antique make old tinware and preparation method thereof the present invention is intended to provide a kind of.This hair
The modelled after an antique of bright offer makees old tinware preparation method, simulation nature bag slurry process, can promote tinware premature oxidation, significantly shorten tin
Device is modelled after an antique to make the old time;And the tinware color and luster that is prepared is simple and unsophisticated, property is stable, can be effectively moistureproof, really realizes and stores up tea
Taste is constant, contains wine aroma alcohol, and surface will not pollute with the time, on the contrary can be more and more brighter.In addition, preparation side provided by the invention
Method is easy to operate, and cost is relatively low, has good commercial promise.
Therefore, the present invention provides following technical scheme:
In a first aspect, the present invention provides, a kind of tinware is modelled after an antique to make old method, by tinware it is heated, drench with rain, infrared ray, purple
The processing of one or more steps in outside line, wind, spraying, icing, illumination, oxygenation, humidification and ultrasonic wave.
In the further embodiment of the present invention, comprise the following steps:S101:Tinware is heated, afterwards
Drenched with rain successively, wind and spray treatment;S102:Product after S101 is handled carries out cooling processing, carries out successively afterwards
Illumination, oxygenation and humidification processing.
In the further embodiment of the present invention, also include after S102:Product circulation S101 after S102 is handled
With S102 processing, finally give it is modelled after an antique make it is old after tinware.
In the further embodiment of the present invention, in S101:Tinware is heated to 60 DEG C~160 DEG C, heat, drench with rain and
The time of wind is 1h.
In the further embodiment of the present invention, in S102:The temperature of cooling processing is cooling, light not less than -18 DEG C
It is 1h according to the time of, oxygenation and humidification processing and is carried out under the conditions of sound wave.
In the further embodiment of the present invention, illumination includes ultraviolet illumination and/or infrared ray shines.
In the further embodiment of the present invention, spraying makees old liquid progress, and the raw material modelled after an antique for making old liquid using modelled after an antique
Component includes black fiery soil, graphite, metal dust, black soya bean, black fungus, black mushroom, snakeheaded fish, fruit peel, shell, rice washing water, leftovers
One or more in dish, bark, leaf, grass roots, plant stalk, animal shell, liquid soap, five cereals and daily necessaries;For
The dosage of each raw material components preferably mixes raw material components equal proportion without specifically limited.
In the further embodiment of the present invention, the preparation method modelled after an antique for making old liquid includes:By the original modelled after an antique for making old liquid
Carry out fermentation process after material component is well mixed, until liquid is changed into black, filters afterwards and collect filtrate, obtain it is modelled after an antique make it is old
Liquid.
Second aspect, modelled after an antique make old tinware using what method provided by the invention was prepared.
The above-mentioned technical proposal of the present invention has advantages below compared with prior art:
(1) applicant has found by numerous studies:Strong anti-oxidation ability based on tinware, one layer is slowly generated in an atmosphere
Very thin oxide layer just can prevent it is further aoxidize, therefore, realize tinware it is modelled after an antique make old most important natural bag slurry process, it is necessary to
Time integral year in year out.It is provided by the invention it is modelled after an antique make old tinware preparation method, simulation nature bag slurry process, can promote
Tinware premature oxidation, significantly shortens that tinware is modelled after an antique makees the old time;And the tinware color and luster that is prepared is simple and unsophisticated, property is stable, can
With effectively moistureproof, really realize that storage tea flavour is constant, contain wine aroma alcohol.
(2) tinware provided by the invention is modelled after an antique makees old method, can be carried out in the seal case of baking oven formula.Seal box
Top has heating heater, bottom to have device for cooling and also automatic lifting, rotation, folding function inside body;Sealing
In casing be provided with wind, drench with rain, illumination, oxygenation, humidification, vibration, sound wave, spraying totally ten patterns, and temperature can be adjusted arbitrarily
Section.So as to simulate the weather of nature, six hours undergo spring, summer, autumn and winter, and along with ultraviolet illumination, infrared ray shines, just had
Make a clear distinction between the four seasons, the effect of day and night, so as to promoting tinware premature oxidation;Period is aided with spraying process, forms nature bag
Slurry.
(3) preparation method provided by the invention is easy to operate, and cost is relatively low, has good commercial promise.
The additional aspect and advantage of the present invention will be set forth in part in the description, and will partly become from the following description
Obtain substantially, or recognized by the practice of the present invention.
Brief description of the drawings
Fig. 1 be the embodiment of the present invention in tinware it is modelled after an antique make it is old used in the process of equipment schematic diagram.
Embodiment
The embodiment of technical solution of the present invention will be described in detail below.Following examples are only used for clearer
Explanation technical scheme, therefore be only used as example, and can not be limited the scope of the invention with this.
Experimental method in following embodiments, it is conventional method unless otherwise specified.
Test material used, is to be commercially available from conventional reagent shop unless otherwise specified in following embodiments.
Quantitative test in following examples, it is respectively provided with and repeats to test three times, data is to repeat the average value of experiment three times
Or mean+SD.
The present invention provides that a kind of tinware is modelled after an antique to make old method, by tinware it is heated, drench with rain, wind, spraying, icing, light
According to the processing of one or more steps in, oxygenation, humidification and sound wave.Specifically include following steps:
S101:Tinware is heated, drenched with rain successively afterwards, wind and spray treatment.Wherein, by tinware plus
For heat to 60 DEG C~160 DEG C, it is 1h to heat, drench with rain with the time of wind.
S102:Product after S101 is handled carries out cooling processing, carries out illumination, oxygenation and humidification processing successively afterwards.
Wherein, the temperature of processing of cooling is not less than -18 DEG C, and the time that cooling, illumination, oxygenation and humidification are handled is 1h and in sound
Carried out under the conditions of ripple.
Tinware provided by the invention is modelled after an antique, which to make old process, to be carried out in the seal case of baking oven formula, as shown in Figure 1.It is close
Joint sealing body the inside top is provided with heating heater (high-temperature region), bottom is provided with device for cooling (low-temperature space) and also has certainly
Dynamic lifting, rotation, folding function;In seal case be provided with wind, drench with rain, illumination, oxygenation, humidification, vibration, sound wave, spraying altogether
Ten patterns, and temperature can be adjusted arbitrarily.So as to simulate the weather of nature, six hours undergo spring, summer, autumn and winter, added
Ultraviolet illumination, infrared ray shine, just have make a clear distinction between the four seasons, the effect of day and night, so as to promote tinware premature oxidation;Period
It is aided with spraying process, forms nature bag slurry.
Preferably, also include after S102:The processing of product circulation S101 and S102 after S102 is handled, finally give
It is modelled after an antique make it is old after tinware.
Preferably, spraying is made old liquid and carried out using modelled after an antique, and the raw material components modelled after an antique for making old liquid include black fiery soil, graphite,
Metal dust, black soya bean, black fungus, black mushroom, snakeheaded fish, fruit peel, shell, rice washing water, leftover, bark, leaf, grass roots, plant
One or more in thing stalk, animal shell, liquid soap, five cereals and daily necessaries.The preparation method modelled after an antique for making old liquid includes:
Fermentation process is carried out after the raw material components modelled after an antique for making old liquid are well mixed, until liquid is changed into black, filters and collects afterwards
Filtrate, obtain modelled after an antique making old liquid.
Illustrated with reference to embodiment:
Embodiment one
A kind of tinware of present invention offer is modelled after an antique to make old method, comprises the following steps:
S101:Tinware is heated to 60 DEG C, drenched with rain successively afterwards, wind and spray treatment.Wherein, heat, drench with rain
Time with wind is 1h;Spraying is made old liquid and carried out using modelled after an antique, and the raw material components modelled after an antique for making old liquid such as include at the parts by weight
Graphite, metal dust, black soya bean, black fungus and black mushroom;The preparation method modelled after an antique for making old liquid includes:Make each of old liquid by modelled after an antique
Fermentation process is carried out after raw material components are well mixed, until liquid is changed into black, filters afterwards and collects filtrate, obtain work modelled after an antique
Old liquid.
S102:Product after S101 is handled carries out being cooled to -18 DEG C, carries out successively at illumination, oxygenation and humidification afterwards
Reason.Wherein, the time of cooling, illumination, oxygenation and humidification processing is 1h, and S102 is carried out under the conditions of sound wave.
The processing of product circulation S101 and S102 after S102 is handled 50 times, finally give it is modelled after an antique make it is old after tinware.
Embodiment two
A kind of tinware of present invention offer is modelled after an antique to make old method, comprises the following steps:
S101:Tinware is heated to 120 DEG C, drenched with rain successively afterwards, wind and spray treatment.Wherein, heat, drench with rain
Time with wind is 1h;Spraying is made old liquid and carried out using modelled after an antique, and the raw material components modelled after an antique for making old liquid such as include at the parts by weight
Graphite, leaf, grass roots, liquid soap, black soya bean, black fungus and black mushroom;The preparation method modelled after an antique for making old liquid includes:By work modelled after an antique
Fermentation process is carried out after each raw material components of old liquid are well mixed, until liquid is changed into black, filters afterwards and collects filtrate, obtain
Make old liquid to modelled after an antique.
S102:Product after S101 is handled carries out being cooled to -10 DEG C, carries out successively at illumination, oxygenation and humidification afterwards
Reason.Wherein, the time of cooling, illumination, oxygenation and humidification processing is 1h, and S102 is carried out under the conditions of sound wave.
The processing of product circulation S101 and S102 after S102 is handled 100 times, finally give it is modelled after an antique make it is old after tinware.
Embodiment three
A kind of tinware of present invention offer is modelled after an antique to make old method, comprises the following steps:
S101:Tinware is heated to 160 DEG C, drenched with rain successively afterwards, wind and spray treatment.Wherein, heat, drench with rain
Time with wind is 1h;Spraying is made old liquid and carried out using modelled after an antique, and the raw material components modelled after an antique for making old liquid such as include at the parts by weight
Graphite, shell, rice washing water, bark, leaf, grass roots, black soya bean, black fungus and black mushroom;The preparation method bag modelled after an antique for making old liquid
Include:Fermentation process is carried out after each raw material components modelled after an antique for making old liquid are well mixed, until liquid is changed into black, is filtered afterwards simultaneously
Filtrate is collected, obtains modelled after an antique making old liquid.
S102:Product after S101 is handled carries out being cooled to -5 DEG C, carries out successively at illumination, oxygenation and humidification afterwards
Reason.Wherein, the time of cooling, illumination, oxygenation and humidification processing is 1h, and S102 is carried out under the conditions of sound wave.
The processing of product circulation S101 and S102 after S102 is handled 80 times, finally give it is modelled after an antique make it is old after tinware.
In addition, in order to preferably evaluate each embodiment it is modelled after an antique make it is old after tinware effect, carry out following test:
Specifically, the tinwork of various embodiments of the present invention has excellent glossiness, and its brightness reaches 300~
320Lux.Based on this, the tinwork of each embodiment is subjected to long-time storage, its metallic luster is observed and carries out brightness survey
Examination, concrete outcome are as shown in table 1.
Brightness performance test/Lux of each embodiment tinwork of table 1
10 minutes | Half a year | 1 year | |
Embodiment one | 312 | 305 | 300 |
Embodiment two | 315 | 306 | 298 |
Embodiment three | 309 | 303 | 299 |
Certainly, except the situation that embodiment one is enumerated to embodiment three, the species and percentage by weight of other raw material components,
Condition and parameter in preparation process etc. are also possible.
It is provided by the invention it is modelled after an antique make old tinware preparation method, simulation nature bag slurry process, tinware can be promoted to shift to an earlier date oxygen
Change, significantly shorten that tinware is modelled after an antique makees the old time;And the tinware color and luster that is prepared is simple and unsophisticated, property is stable, can effectively protection against the tide,
Really realize that storage tea flavour is constant, contain wine aroma alcohol.In addition, preparation method provided by the invention is easy to operate, cost is relatively low, has
Good commercial promise.
In the description of this specification, it is to be understood that reference term " one embodiment ", " some embodiments ", " show
The description of example ", " specific example " or " some examples " etc. mean to combine the specific features of the embodiment or example description, structure,
Material or feature are contained at least one embodiment or example of the present invention.In this manual, above-mentioned term is shown
The statement of meaning property is necessarily directed to identical embodiment or example.Moreover, specific features, structure, material or the spy of description
Point can combine in an appropriate manner in any one or more embodiments or example.In addition, in the case of not conflicting,
Different embodiments or example and its feature described in this specification can be combined and combined by those skilled in the art.
Although embodiments of the invention have been shown and described above, it is to be understood that above-described embodiment is example
Property, it is impossible to limitation of the present invention is interpreted as, one of ordinary skill in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changed, replacing and modification.
Claims (9)
1. a kind of tinware is modelled after an antique to make old method, it is characterised in that:
By the tinware it is heated, drench with rain, wind, spraying, icing, illumination, oxygenation, humidification and sound wave, infrared ray and ultraviolet
The processing of middle one or more steps.
2. tinware according to claim 1 is modelled after an antique to make aging method, it is characterised in that comprises the following steps:
S101:The tinware is heated, drenched with rain successively afterwards, wind and spray treatment;
S102:Product after S101 processing is subjected to cooling processing, carries out illumination, oxygenation and humidification processing successively afterwards.
3. tinware according to claim 2 is modelled after an antique to make aging method, it is characterised in that:
Also include after the S102:
By the S102 processing after product circulation S101 and S102 processing, finally give it is modelled after an antique make it is old after tinware.
4. tinware according to claim 2 is modelled after an antique to make aging method, it is characterised in that:
In the S101:
The tinware is heated to 60 DEG C~160 DEG C, the heating, to drench with rain with the time of wind be 1h.
5. tinware according to claim 2 is modelled after an antique to make aging method, it is characterised in that:
In the S102:
The temperature of the cooling processing is not less than -18 DEG C, and the time of the cooling, illumination, oxygenation and humidification processing is 1h
And carried out under the conditions of sound wave.
6. tinware according to any one of Claims 1 to 5 is modelled after an antique to make aging method, it is characterised in that:
The illumination includes ultraviolet illumination and/or infrared ray shines.
7. tinware according to any one of Claims 1 to 5 is modelled after an antique to make aging method, it is characterised in that:
The spraying makees old liquid progress using modelled after an antique, and the raw material components modelled after an antique for making old liquid include black fiery soil, graphite, metal
Powder, black soya bean, black fungus, black mushroom, snakeheaded fish, fruit peel, shell, rice washing water, leftover, bark, leaf, grass roots, plant stalk,
One or more in animal shell, liquid soap, five cereals and daily necessaries.
8. tinware according to claim 7 is modelled after an antique to make aging method, it is characterised in that:
The preparation method modelled after an antique for making old liquid includes:
By the raw material components modelled after an antique for making old liquid it is well mixed after carry out fermentation process, until liquid is changed into black, mistake afterwards
Filter and collect filtrate, obtain described modelled after an antique making old liquid.
9. modelled after an antique make old tinware according to what any one of claim 1~8 methods described was prepared.