CN107476528A - A kind of super clean bright on-slip brick and its manufacture method - Google Patents
A kind of super clean bright on-slip brick and its manufacture method Download PDFInfo
- Publication number
- CN107476528A CN107476528A CN201710432431.9A CN201710432431A CN107476528A CN 107476528 A CN107476528 A CN 107476528A CN 201710432431 A CN201710432431 A CN 201710432431A CN 107476528 A CN107476528 A CN 107476528A
- Authority
- CN
- China
- Prior art keywords
- slip
- super clean
- clean bright
- layer
- bright
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to architectural pottery technical field, more particularly to a kind of super clean bright on-slip brick and its manufacture method.Include basic unit, super clean bright layers, nanoscale anti-slip layer and stain-proofing layer successively from top to bottom.The manufacture method of super clean bright on-slip brick provided by the invention is applicable for super clean bright Anti-skidding polished tile and super clean bright on-slip glazed tile, more than 85 degree are can reach using super clean bright on-slip brick glossiness produced by the present invention, confficient of static friction under dry, wet condition can reach more than 0.6, effect is more excellent during hygrometric state, have super clean bright and skid-proof function concurrently, antifouling grade is suitable with common super clean bright brick, it can be widely applied to various public places, greatly reduce the safety coefficient fallen down accident, improve people's daily life triggered under dampness；High gloss, bright appearance characteristics attractive in appearance simultaneously, are advantageous to promote and are used in more high-grade public place.
Description
Technical field
The invention belongs to architectural pottery technical field, more particularly to a kind of super clean bright on-slip brick and its manufacture method.
Background technology
Super clean bright ceramic tile has the advantages that glossiness is high, antifouling property is good, and favor has been enjoyed since emerging, is described as building pottery
The revolutionary breakthrough of industry anti-soil technology, while the glossiness on surface is also substantially increased, many enterprises are successive in ceramic industry
Super clean bright brick is researched and developed.But super clean bright brick has that a critical defect-anti-slip effect is poor, excessively light is particularly met after water
It is sliding, personal safety is threatened, this seriously constrains super clean bright ceramic tile in public affairs such as house ornamentation, market, hospital, office building, apartments
Promote the use of in common place.
Traditional on-slip brick production method is that base substrate or glaze paint are corroded by chemicals, pothole is formed, using true
Empty absorption principle realizes anti-slip effect.But which causes surface gloss seriously to reduce because surface is corroded, antifouling difference
The defects of, the esthetic requirement that modern increasingly improves far can not be met.
Therefore, the antiskid property of super clean bright brick how is improved, realizing that on-slip is merged with the height of highlighted, antifouling etc. has become
Problem urgently to be resolved hurrily in industry.
The content of the invention
In order to solve the above problems, the invention provides a kind of super clean bright on-slip brick and its manufacture method, realize that ceramic tile exists
While with anti-slip effect, higher glossiness and soil resistance are still kept.
To achieve the above object, the technical solution adopted by the present invention is as follows：
A kind of super clean bright on-slip brick, includes basic unit, super clean bright layers, nanoscale anti-slip layer and stain-proofing layer successively from top to bottom.
The nanoscale anti-slip layer is formed on super clean bright layers surface, including anti-slip layer and repair layer.
The anti-slip layer is formed after carrying out some erosion to super clean bright layers by on-slip agent, and gather micropore on its surface, described
The depth of micropore is no more than 10 μm.
The granularity of renovation agent used in the repair layer is 40 ~ 100nm, partial repair anti-slip layer.
A kind of manufacture method of super clean bright on-slip brick, including following technological process：
A. kiln discharge semi-finished product are polished with known super clean bright technique, form super clean bright layers；
B. super clean bright layers are carried out with some erosion with on-slip agent, forms anti-slip layer；
C. part reparation is carried out to anti-slip layer with renovation agent, forms repair layer；
D. upper anti-fouling agent, is sorted, and is packed.
The kiln discharge semi-finished product can be polished bricks kiln discharge product or glazed tile kiln discharge product；
The on-slip agent main component is organic or inorganic acid, and the organic or inorganic acid is sulfuric acid, hydrochloric acid, phosphoric acid, boric acid, grass
One or more in acid, acetic acid, tartaric acid.
The main component of the renovation agent is silicone oil, and the silicone oil is methyl-silicone oil, ethyl silicon oil, amido silicon oil, line
Property silicone oil, methylhydroxy silicone oil, modified silicon oil, hydrogenation silicone oil in one or more.
The step b and c can be carried out step by step, and it is complete that on-slip agent and renovation agent also can be mixed into latter step by a certain percentage
Into.
Ratio is volume ratio 1 both when the on-slip agent and renovation agent are used in mixed way：（1~4）.
Beneficial effect is the present invention compared with prior art：The manufacture method pair of super clean bright on-slip brick provided by the invention
It is applicable in super clean bright Anti-skidding polished tile and super clean bright on-slip glazed tile；Utilize super clean bright on-slip brick gloss produced by the present invention
Degree can reach more than 85 degree, and the confficient of static friction under dry, wet condition can reach more than 0.6, and effect is more excellent during hygrometric state, has concurrently super
Clean bright and skid-proof function, antifouling grade is suitable with common super clean bright brick, can be widely applied to various public places, greatly drops
That triggers under low tide wet condition falls down accident, improves the safety coefficient of people's daily life；High gloss, light are attractive in appearance simultaneously
Appearance characteristics, be advantageous to promote and be used in more high-grade public place.
Brief description of the drawings
The present invention is further described with reference to the accompanying drawings and examples.
Fig. 1 is the structural representation of super clean bright on-slip glazed tile.
Fig. 2 is the structural representation of super clean bright Anti-skidding polished tile.
Wherein：101st, green body layer；102nd, ground glaze layer；103rd, ink-jet decorative layer；104th, transparent glaze layer；2nd, super clean bright layers；3、
Nanoscale anti-slip layer；301st, anti-slip layer；302nd, repair layer；4th, stain-proofing layer；5th, micropore.
Embodiment
The invention will now be described in further detail with reference to the accompanying drawings.
Embodiment 1：Super clean bright on-slip glazed tile
A kind of super clean bright on-slip glazed tile as shown in Figure 1, include basic unit, super clean bright layers 2, nanoscale on-slip respectively from down to up
Layer 3 and stain-proofing layer 4, the basic unit is from top to bottom by green body layer 101, ground glaze layer 102, ink-jet decorative layer 103 and transparent glaze layer 104
Form；The nanoscale anti-slip layer 3 is formed on the super clean surface of bright layers 2, including anti-slip layer 301 and repair layer 302；The anti-slip layer
301 be to be formed after carrying out some erosion to super clean bright layers 2 by on-slip agent, and gather micropore 5 on its surface, the depth of the micropore 5
No more than 10 μm；The granularity of renovation agent used in the repair layer 302 is 40 ~ 100nm, partial repair anti-slip layer 301, ensures product
Glossiness and resistance to soiling.
A kind of manufacture method of super clean bright on-slip glazed tile, comprises the following steps：
A. glazed tile kiln discharge product are polished with known super clean bright technique, form super clean bright layers；
B. super clean bright layers are carried out with some erosion with on-slip agent, forms anti-slip layer；
C. part reparation is carried out to anti-slip layer with renovation agent, forms repair layer；
D. upper anti-fouling agent, is sorted, and is packed；
The on-slip agent main component is organic or inorganic acid, and the organic or inorganic acid is sulfuric acid, hydrochloric acid, phosphoric acid, boric acid, grass
One or more in acid, acetic acid, tartaric acid；
The main component of the renovation agent is silicone oil, and the silicone oil is selected from methyl-silicone oil, ethyl silicon oil, amido silicon oil, linear
One or more in silicone oil, methylhydroxy silicone oil, modified silicon oil, hydrogenation silicone oil；
The step b and c can be carried out step by step, and on-slip agent and renovation agent also can in proportion be mixed to latter step and completed；
Ratio is volume ratio 1 when the on-slip agent and renovation agent are used in mixed way：（1~4）；
The mechanism of the step b and c carries out pressurization polishing to pass sequentially through 3 ~ 10 groups of mills after dropping liquid.
Embodiment 2：Super clean bright Anti-skidding polished tile
A kind of super clean bright Anti-skidding polished tile as shown in Figure 2, includes basic unit respectively from down to up（Green body layer 101）, super clean bright layers 2,
Nanoscale anti-slip layer 3, stain-proofing layer 4；The nanometer anti-slip layer 3 is formed on the super clean surface of bright layers 2, including anti-slip layer 301 and reparation
Layer 302；The anti-slip layer 301 is to be formed after carrying out some erosion to super clean bright layers 2 by on-slip agent, and gather micropore 5 on its surface,
The depth of the micropore 5 is no more than 10 μm；The granularity of renovation agent is 40 ~ 100nm used in the repair layer 302, and partial repair stops
Slip layer 301, ensure the glossiness and resistance to soiling of product.
A kind of manufacture method of super clean bright Anti-skidding polished tile, comprises the following steps：
A. polished bricks kiln discharge product are polished with known super clean bright technique, form super clean bright layers；
B. super clean bright layers are carried out with some erosion with on-slip agent, forms anti-slip layer；
C. part reparation is carried out to anti-slip layer with renovation agent, forms repair layer；
D. upper anti-fouling agent, is sorted, and is packed；
The on-slip agent main component is organic or inorganic acid, and the organic or inorganic acid is sulfuric acid, hydrochloric acid, phosphoric acid, boric acid, grass
One or more in acid, acetic acid, tartaric acid；
The main component of the renovation agent is silicone oil, and the silicone oil is selected from methyl-silicone oil, ethyl silicon oil, amido silicon oil, linear
One or more in silicone oil, methylhydroxy silicone oil, modified silicon oil, hydrogenation silicone oil；
The step b and c can be carried out step by step, and on-slip agent and renovation agent also can in proportion be mixed to latter step and completed；It is described to stop
Ratio is volume ratio 1 when lubrication prescription and renovation agent are used in mixed way：（1~4）；
The mechanism of the step b and c carries out pressurization polishing to pass sequentially through 3 ~ 10 groups of mills after dropping liquid.
Embodiment 3
Main performance is tested：
Upper table main performance contrast table of super clean bright ceramic tile for the super clean bright on-slip brick of the present invention and commonly.
Above-described is only the preferred embodiment of the present invention, and the description is merely to explain the principles of the invention,
And limiting the scope of the invention can not be construed in any way, do not departing from this hair for those skilled in the art
It is bright create design on the premise of, the modification and improvement made belong to protection scope of the present invention.
Claims (10)
- A kind of 1. super clean bright on-slip brick, it is characterised in that：Include basic unit, super clean bright layers successively from top to bottom（2）, nanoscale on-slip Layer（3）And stain-proofing layer（4）.
- 2. super clean bright on-slip brick according to claim 1, it is characterised in that：The nanoscale anti-slip layer（3）Super clean bright Layer（2）Surface is formed, including anti-slip layer（301）And repair layer（302）.
- 3. super clean bright on-slip brick according to claim 2, it is characterised in that：The anti-slip layer（301）Pass through on-slip agent pair Super clean bright layers（2）Formed after carrying out some erosion, gather micropore on its surface（5）, the micropore（5）Depth be no more than 10 μm.
- 4. super clean bright on-slip brick according to claim 2, it is characterised in that：The repair layer（302）Renovation agent used Granularity is 40 ~ 100nm, partial repair anti-slip layer（301）.
- A kind of 5. manufacture method of super clean bright on-slip brick, it is characterised in that：Including following technological process：A. kiln discharge semi-finished product are polished with known super clean bright technique, form super clean bright layers；B. super clean bright layers are carried out with some erosion with on-slip agent, forms anti-slip layer；C. part reparation is carried out to anti-slip layer with renovation agent, forms repair layer；D. upper anti-fouling agent, is sorted, and is packed.
- 6. the manufacture method of super clean bright on-slip brick according to claim 5, it is characterised in that：The kiln discharge semi-finished product can be with For polished bricks kiln discharge product or glazed tile kiln discharge product.
- 7. the manufacture method of super clean bright on-slip brick according to claim 5, it is characterised in that：The on-slip agent main component For organic or inorganic acid, the organic or inorganic acid be sulfuric acid, hydrochloric acid, phosphoric acid, boric acid, oxalic acid, acetic acid, one kind in tartaric acid or It is a variety of.
- 8. the manufacture method of super clean bright on-slip brick according to claim 5, it is characterised in that：The renovation agent it is main into It is divided into silicone oil, the silicone oil is methyl-silicone oil, ethyl silicon oil, amido silicon oil, linear silicone oils, methylhydroxy silicone oil, modified silicon One or more in oil, hydrogenation silicone oil.
- 9. the manufacture method of super clean bright on-slip brick according to claim 5, it is characterised in that：The step b and c can divide Step is carried out, and on-slip agent and renovation agent also can by a certain percentage be mixed to latter step and completed.
- 10. the manufacture method of super clean bright on-slip brick according to claim 9, it is characterised in that：The on-slip agent and reparation Ratio is volume ratio 1 both when agent is used in mixed way：（1~4）.