CN107475813B - 一种聚甲醛材料增强专用玄武岩纤维及其制备方法 - Google Patents
一种聚甲醛材料增强专用玄武岩纤维及其制备方法 Download PDFInfo
- Publication number
- CN107475813B CN107475813B CN201611084175.0A CN201611084175A CN107475813B CN 107475813 B CN107475813 B CN 107475813B CN 201611084175 A CN201611084175 A CN 201611084175A CN 107475813 B CN107475813 B CN 107475813B
- Authority
- CN
- China
- Prior art keywords
- basalt fibre
- parts
- preparation
- hypophosphites
- polyformaldehyde material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种聚甲醛材料增强专用玄武岩纤维及其制备方法，本发明玄武岩纤维是经过特殊浸润剂在生产过程中的处理而得到的，所述浸润剂包括以下重量份组分：40‑60份的成膜剂、5‑15份的偶联剂、1‑5份润滑剂、10‑20份的改性剂、30‑50份的溶剂；改性剂包括质量比为5‑8︰1‑3的次磷酸盐和酸；该玄武岩纤维由于表面粗糙度大并接枝有大量活性基团，玄武岩纤维与聚甲醛材料之间的化学键合和机械铆合能力强，该玄武岩纤维与聚甲醛材料的相容性好，能在聚甲醛材料中大量添加和应用。
Description
技术领域
本发明涉及玄武岩纤维领域，具体涉及一种聚甲醛材料增强专用玄武岩纤维及其制备方法。
背景技术
玄武岩纤维是一种新出现的新型无机环保绿色高性能纤维材料，是未来我国重点发展的四大高性能纤维之一，它是由二氧化硅、氧化铝、氧化钙、氧化铁和二氧化钛等氧化物组成的玄武岩石料在高温熔融后，通过纺丝工艺制备而成的。玄武岩连续纤维不仅稳定性好，而且还具有电绝缘性、抗腐蚀、抗燃烧、耐高温等多种优异性能，而且，玄武岩纤维的生产工艺产生的废弃物少，对环境污染小，产品废弃后可直接转入生态环境中，无任何危害，因而是一种名副其实的绿色、环保材料。玄武岩连续纤维已在纤维增强复合材料、摩擦材料、造船材料、隔热材料、汽车行业、高温过滤织物以及防护领域等多个方面得到了广泛的应用。
聚甲醛又名缩醛树脂、聚氧亚甲基。全名聚甲醛树脂，简称聚甲醛，英文缩写为POM，热塑性结晶聚合物，是五大通用工程塑料之一，综合性能优良，具有高的力学性能，如强度、模量、耐磨性、韧性、耐疲劳性和抗蠕变性，还具有优良的电绝缘性、耐溶剂性和可加工性；但由于聚甲醛中结晶度高（结晶度＞70%），导致聚甲醛材料存在韧性差（断裂伸长率＜15%）、成型收缩率（2.0-3.5%）大的缺陷，因此，在使用时多不使用纯的聚甲醛材料，聚甲醛材料需要进行力学性能、阻燃、耐腐蚀等增强复合改性处理后才能进行应用。现今对聚甲醛材料的纤维增强改性主要采用玻璃纤维材料进行改性处理，改性效果显著，但玻璃纤维生产成本高、环境污染大，严重限制了复合聚甲醛材料的应用，开发一种成本低廉、绿色环保、性能优异的新型纤维材料替代玻璃纤维对聚甲醛材料进行改性处理的问题急需得到解决。因而，可以预见，将无毒、无污染、来源广泛、性能优异、稳定好的玄武岩纤维用于聚甲醛材料的增强必将是今后提高聚甲醛材料性能的新趋势。但由于现有玄武岩纤维自身结构和性能稳定，纤维表面光滑、表面活性位点少，造成玄武岩纤维在改性过程中难以与聚甲醛材料化学键合和机械铆合形成统一的、稳定的整体，即玄武岩纤维在聚甲醛材料中是独立存在，对聚甲醛材料的改性增强作用相对较弱，增强效果不甚理想，玄武岩纤维添加量少。
发明内容
本发明的目的在于克服现有玄武岩纤维与聚甲醛材料相容性差的缺陷，提供一种聚甲醛材料增强专用玄武岩纤维及其制备方法；本发明玄武岩纤维是经过特殊浸润剂在生产过程中的处理而得到的，该玄武岩纤维由于表面粗糙度大并接枝有大量活性基团，玄武岩纤维与聚甲醛材料之间的化学键合和机械铆合能力强，该玄武岩纤维与聚甲醛材料的相容性好，能在聚甲醛材料中大量添加和应用。
为了实现上述发明目的，本发明提供了一种聚甲醛材料增强专用玄武岩纤维的制备方法，包括以下步骤：
（1）将玄武岩矿石进行粉碎处理，得到玄武岩矿石粉体；
（2）将步骤1得到粉体加热，熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液进行拉丝，得到玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝用浸润剂进行浸润改性处理；
（5）将步骤4得到的经过浸润改性处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
上述一种聚甲醛材料增强专用玄武岩纤维的制备方法，步骤4中所述浸润剂包括以下重量份组分：40-60份的成膜剂、5-15份的偶联剂、1-5份润滑剂、10-20份的改性剂、30-50份的溶剂；所述浸润剂能快速对玄武岩纤维表面进行腐蚀、活化，形成粗糙表面，并接枝大量活性基团，从而提高玄武岩纤维与聚甲醛材料之间的化学键合和机械铆合能力，提高玄武岩纤维与聚甲醛材料的相容性；所述的机械铆合是指基体材料通过收缩应力包紧粗糙表面的纤维而产生的摩擦结合。
上述浸润剂，其中所述的改性剂包括次磷酸盐︰酸按质量比5-8︰1-3混合而成的混合物；优选的，所述的改性剂包括次磷酸盐︰酸按质量比6︰2混合而成的混合物。
上述浸润剂，其中所述的次磷酸盐为二甲基次磷酸盐、乙基甲基次磷酸盐、甲基正丙基次磷酸盐、甲烷二甲基次磷酸盐、苯-1，4-二甲基次磷酸盐、甲基苯基次磷酸盐或二苯基次磷酸盐的一种或多种；其中所述的酸为亚硫酸、草酸、甲酸、乙酸、乙二酸中的一种或多种；其中所述的成膜剂为丁二烯树脂成膜剂；其中所述的偶联剂为含有醛基、醚基中一种或多种基团的改性硅烷偶联剂；其中所述的润滑剂为硬脂酸甲酯和硬脂酸锌中的一种。
上述浸润剂，其中所述的溶剂为乙醇的水溶液；所述溶剂中乙醇与水的体积比为1-3︰1；优选的，乙醇的水溶液中乙醇与水的体积比为2︰1。
一种聚甲醛材料增强专用玄武岩纤维材料的制备方法，本发明方法将生产过程中得到的中间产物玄武岩纤维原丝用特殊组份的浸润剂进行处理，使纤维表面粗糙度增加并接枝大量活性基团，有助于聚甲醛材料在玄武岩纤维表面进行化学键合和机械铆合，从而直接得到与聚甲醛材料相容性很好的玄武岩纤维；该玄武岩纤维能在聚甲醛材料中大量添加和应用。
上述一种聚甲醛材料增强专用玄武岩纤维的制备方法，其中步骤1中所述的玄武岩矿石粉体粒径为0.1-2mm，粒径越小，加热熔融时速度越快，耗能越低，但粉碎成本增加优选的，所述玄武岩矿石粉体粒径为0.5-1mm。
上述一种聚甲醛材料增强专用玄武岩纤维的制备方法，其中步骤2中所述的熔融温度为1100-1500℃，温度过低，熔融速度慢，耗时长，耗能高，温度过高，对设备要求高，设备成本增加；优选的，所述熔融温度为1250-1350℃。
上述一种聚甲醛材料增强专用玄武岩纤维的制备方法，其中步骤3中所述的拉丝的速度为1500-3000m/min，拉丝速度过快，拉伸张力过大，会造成纤维断裂；拉丝速度过慢，得到的玄武岩纤维直径较大，不利于玄武岩纤维的应用。
上述一种聚甲醛材料增强专用玄武岩纤维的制备方法，其中步骤3中所述的玄武岩纤维原丝直径控制在2-50μm，原丝直径过大，冷却慢，造成纤维内外应力分布不仅，纤维缺陷大，不利于实际应用，原丝直径过小，拉丝工艺操作困难，容易断裂；优选的，所述的玄武岩纤维原丝直径控制在4-15μm。
上述一种聚甲醛材料增强专用玄武岩纤维的制备方法，其中步骤4中所述的浸润剂温度控制在50-80℃，温度越高，反应速度越快，处理效果越好，但温度过高，表面处理程度控制困难，产品质量不稳定；优选的，所述的浸润剂温度控制在60-70℃。
为了实现上述发明目的，进一步的，本发明提供了一种聚甲醛材料增强专用玄武岩纤维，所述聚甲醛材料增强专用玄武岩纤维是通过上述制备方法制备得到的；通过上述制备方法制备的得到的聚甲醛材料增强专用玄武岩纤维，表面粗糙度大并接枝有大量活性基团，玄武岩纤维与聚甲醛材料之间的化学键合和机械铆合能力强，与聚甲醛材料的相容性好，能在聚甲醛材料中大量添加和应用。
与现有技术相比，本发明的有益效果：
1、本发明聚甲醛材料增强专用玄武岩纤维的制备方法，利用浸润剂对玄武岩纤维原丝进行快速改性处理，使纤维表面粗糙度增加并接枝大量活性基团，有助于聚甲醛材料在玄武岩纤维表面进行化学键合和机械铆合，提高了玄武岩纤维与聚甲醛材料的相容性。
2、本发明聚甲醛材料增强专用玄武岩纤维的制备方法，直接采用浸润剂对纤维原丝进行改性处理，将纤维的生产和改性合二为一，简化了生产步骤，节约了生产成本，缩短了生产周期。
3、本发明聚甲醛材料增强专用玄武岩纤维，表面粗糙度大并接枝有大量活性基团，玄武岩纤维与聚甲醛材料之间的化学键合和机械铆合能力强，与聚甲醛材料的相容性好，能在聚甲醛材料中大量添加和应用。
具体实施方式
下面结合试验例及具体实施方式对本发明作进一步的详细描述。但不应将此理解为本发明上述主题的范围仅限于以下的实施例，凡基于本发明内容所实现的技术均属于本发明的范围。
实施例1
（1）将玄武岩矿石进行粉碎处理，得到粒径为0.5mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1250℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在2000m/min的速度下进行拉丝，得到直径为15μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为60℃的浸润剂中进行浸润处理；浸润剂组成为：15重量份含有二甲基次磷酸钠︰草酸按质量比6︰2混合而成的改性剂、50重量份的丁二烯树脂成膜剂、20重量份的乙醇、20重量份的水、10重量份的硅烷偶联剂和3重量份的硬脂酸甲酯；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
实施例2
（1）将玄武岩矿石进行粉碎处理，得到粒径为1.0mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1350℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在2500m/min的速度下进行拉丝，得到直径为4μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为70℃的浸润剂中进行浸润处理；浸润剂组成为：10重量份含有苯-1，4-二甲基次磷酸钾︰亚硫酸按质量比5︰1混合而成的改性剂、60重量份的丁二烯树脂成膜剂、20重量份的乙醇、20重量份的水、15重量份的硅烷偶联剂和1重量份的硬脂酸锌；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
实施例3
（1）将玄武岩矿石进行粉碎处理，得到粒径为0.1mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1100℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在3000m/min的速度下进行拉丝，得到直径为2μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为80℃的浸润剂中进行浸润处理；浸润剂组成为：20重量份含有乙基甲基次磷酸钠︰乙酸按质量比8︰3混合而成的改性剂、40重量份的丁二烯树脂成膜剂、20重量份的乙醇、30重量份的水、5重量份的硅烷偶联剂和5重量份的硬脂酸甲酯；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
实施例4
（1）将玄武岩矿石进行粉碎处理，得到粒径为2mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1500℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在1500m/min的速度下进行拉丝，得到直径为50μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为50℃的浸润剂中进行浸润处理；浸润剂组成为：10重量份含有甲基苯基次磷酸钠︰乙二酸按质量比5︰3混合而成的改性剂、40重量份的丁二烯树脂成膜剂、20重量份的乙醇、10重量份的水、5重量份的硅烷偶联剂和5重量份的硬脂酸锌；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
对比例1
（1）将玄武岩矿石进行粉碎处理，得到粒径为0.5mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1250℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在2000m/min的速度下进行拉丝，得到直径为4μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为60℃的浸润剂中进行浸润处理；浸润剂组成为：50重量份的丁二烯树脂成膜剂、20重量份的乙醇、20重量份的水、10重量份的硅烷偶联剂和3重量份的硬脂酸甲酯；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到玄武岩纤维。
对比例2
（1）将玄武岩矿石进行粉碎处理，得到粒径为0.5mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1250℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在2000m/min的速度下进行拉丝，得到直径为4μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为60℃的浸润剂中进行浸润处理；浸润剂组成为：15重量份含有二甲基次磷酸钠︰草酸按质量比6︰4混合而成的改性剂、50重量份的丁二烯树脂成膜剂、20重量份的乙醇、20重量份的水、10重量份的硅烷偶联剂和3重量份的硬脂酸甲酯；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
对比例3
（1）将玄武岩矿石进行粉碎处理，得到粒径为0.5mm的玄武岩矿石粉体；
（2）将步骤1得到粉体加热，在1250℃温度下进行熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液在2000m/min的速度下进行拉丝，得到直径为4μm的玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝在温度为60℃的浸润剂中进行浸润处理；浸润剂组成为：15重量份含有二甲基次磷酸钠︰草酸按质量比10︰1混合而成的改性剂、50重量份的丁二烯树脂成膜剂、20重量份的乙醇、20重量份的水、10重量份的硅烷偶联剂和3重量份的硬脂酸甲酯；
（5）将步骤4得到的经过浸润处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维。
将上述实施例1-4和对比例1-3中所制备得到的玄武岩纤维进行性能测试和聚甲醛塑料（断裂伸长率15%，缺口冲击强度7.6 KJ/m2，成型收缩率2.0-3.5%）增强（玄武岩纤维用量为聚甲醛质量的30%）实验，记录实验结果，记录数据如下：
| 编号 | 拉伸强度（MPa） | 断裂伸长率（%） | 改性后聚甲醛塑料缺口冲击强度（KJ/m<sup>2</sup>） | 改性后聚甲醛塑料断裂伸长率（%） | 改性后聚甲醛塑料成型收缩率（%） |
| 实施例1 | 3850 | 2.6 | 15.3 | 35 | 0.5-0.9 |
| 实施例2 | 3810 | 2.4 | 15.0 | 38 | 0.5-0.9 |
| 实施例3 | 3820 | 2.5 | 14.9 | 37 | 0.5-0.9 |
| 对比例1 | 3940 | 2.6 | 9.4 | 23 | 1.1-1.6 |
| 对比例2 | 3510 | 1.8 | 8.6 | 16 | 0.7-1.3 |
| 对比例3 | 3620 | 2.3 | 8.5 | 19 | 0.8-1.5 |
对上述实验数据分析可知，实施例1-4中采用本发明技术方案制备得到的玄武岩纤维拉申强度和断裂伸长率好，与聚甲醛塑料的相容性好，对聚甲醛塑料增强效果显著；而对比例1制备方法中使用的浸润剂为常规浸润剂，制备得到的玄武岩纤维表面光滑、活性基团少，与聚甲醛材料相容性差，与聚甲醛材料的化学键合和机械铆合能力弱，对聚甲醛材料增强作用显著减弱；对比例2制备方法中使用的浸润剂不是本发明中所保护的浸润剂组分配比用量，草酸用量过大，浸润剂对玄武岩纤维表面侵蚀过渡，对玄武岩纤维结构造成破坏，导致玄武岩纤维的拉伸强度和断裂伸长率显著降低，从而对聚甲醛纤维的增强作用也显著下降；对比例3制备方法中使用的浸润剂不是本发明中所保护的浸润剂组分配比用量，草酸用量过小，浸润剂对玄武岩纤维表面活化作用减弱，玄武岩纤维表面接枝的活性基团少，与聚甲醛材料的化学键合能力弱，对聚甲醛材料增强作用显著减弱。
Claims (7)
1.一种聚甲醛材料增强专用玄武岩纤维的制备方法，其特征在于，包括以下步骤：
（1）将玄武岩矿石进行粉碎处理，得到玄武岩矿石粉体；
（2）将步骤1得到粉体加热，熔融，形成纺丝熔液；
（3）将步骤2得到的纺丝熔液进行拉丝，得到玄武岩纤维原丝；
（4）将步骤3得到的玄武岩纤维原丝用浸润剂进行浸润改性处理；
（5）将步骤4得到的经过浸润改性处理的原丝进行退解、并捻，得到聚甲醛材料增强专用玄武岩纤维；
所述浸润剂包括以下重量份组分：40-60份的成膜剂、5-15份的偶联剂、1-5份润滑剂、10-20份的改性剂、30-50份的溶剂；改性剂包括质量比为5-8︰1-3的次磷酸盐和酸；
所述次磷酸盐为二甲基次磷酸盐、乙基甲基次磷酸盐、甲基正丙基次磷酸盐、甲烷二甲基次磷酸盐、苯-1，4-二甲基次磷酸盐、甲基苯基次磷酸盐或二苯基次磷酸盐的一种或多种；
所述酸为亚硫酸、草酸、甲酸、乙酸、乙二酸中的一种或多种；
所述成膜剂为丁二烯树脂成膜剂。
2.根据权利要求1所述的制备方法，其特征在于，步骤2中熔融温度控制在1100-1500℃。
3.根据权利要求1所述的制备方法，其特征在于，步骤3中玄武岩纤维原丝直径控制在2-50μm。
4.根据权利要求1所述的制备方法，其特征在于，所述偶联剂为含有醛基、醚基中一种或多种基团的改性硅烷偶联剂。
5.根据权利要求1所述的制备方法，其特征在于，所述溶剂为乙醇的水溶液。
6.根据权利要求1所述的制备方法，其特征在于，步骤4中浸润剂温度控制在50-80℃。
7.一种聚甲醛材料增强专用玄武岩纤维，其特征在于，是通过权利要求1-6任一项所述的制备方法制备得到的。