CN107474426A - 聚氯乙烯微生态农业塑料母料及由其制成的育秧盘 - Google Patents
聚氯乙烯微生态农业塑料母料及由其制成的育秧盘 Download PDFInfo
- Publication number
- CN107474426A CN107474426A CN201710668057.2A CN201710668057A CN107474426A CN 107474426 A CN107474426 A CN 107474426A CN 201710668057 A CN201710668057 A CN 201710668057A CN 107474426 A CN107474426 A CN 107474426A
- Authority
- CN
- China
- Prior art keywords
- parts
- bacillus
- polyvinyl chloride
- seedling
- plastic matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了聚氯乙烯微生态农业塑料母料及由其制成的育秧盘，该母料包括以下重量份的组分：10‑40份聚氯乙烯、15‑25份膨润土、20‑30份高岭土、10‑60份碳酸钙、0.1‑1份催化剂、0.1‑5份相容剂、0.5‑2份稳定剂和0.5‑5份润滑剂和0.5‑5份混合益生菌。制备成的育秧盘成型好，强度高，不易变形，可多次使用，易于回收，可减少育秧过程的费用成本；添加入纳米级的膨润土、高岭土、碳酸钙，具有保湿、保温功效，有利于秧苗发芽，减轻浇灌劳动强度；添加入对秧苗生长有益的益生菌，使秧苗具有一定的抗病能力，秧苗根部根须多、盘根效果好、茎粗壮、出苗率、成活率高，育秧过程基本不用施用肥料和喷洒农药，大大减少了劳动力，制备的微生态农业塑料母料和育秧盘的活菌数量高。
Description
技术领域
本发明涉及农业用塑料母料领域，具体地，涉及含有益生菌的聚氯乙烯微生态农业塑料母料及由其制成的育秧盘。
背景技术
现有的水稻育秧技术主要采用育秧盘进行育秧，待秧苗长到一定程度后，再将秧盘移植到田里。育秧是一个重要的过程，育秧过程秧苗长得好，则有利于秧苗后期的生长。育秧过程使用的育秧盘对秧苗的出芽率、生长状况也有一定的影响，因此通过改进育秧盘的情况，可以改善育秧过程秧苗的长势，提高秧苗的出芽率。
目前，农业上通常使用的育秧盘，寿命短，基本上只能使用一次，第二次再使用时质量下降，达不到育秧的要求。常用的育秧盘仅用于暂时培育秧苗，不能为秧苗成长过程提供其它养分，因此在育秧过程还需要定期施肥、喷洒杀虫剂和农药，不仅增加了劳动力，也还会影响秧苗的出苗率和成活率和出苗质量等。
因此，需要一种易耐用的，含有一定秧苗成长过程所需营养元素的育秧盘，该育秧盘能提高秧苗的出芽率和成活率，减少育苗过程中的肥料量和农药量的育秧盘。
发明内容
本发明所要解决的技术问题在于针对上述现有技术的不足，提供一种含有益生菌的塑料母料，其通过将多种益生菌添加入聚氯乙烯而制成，再由该塑料母料压延制成育秧盘，所制成的育秧盘能够提高秧苗的出芽率和成活率，减少育苗过程中的施肥量和农药量，既能保证育秧苗的健康生长，也可减少繁重的劳动力。
为解决上述技术问题，本发明采用的技术方案是：一种聚氯乙烯微生态农业塑料母料，其包括以下重量份的组分：10-40份聚氯乙烯、15-25份膨润土、20-30份高岭土、10-60份碳酸钙、0.1-1份催化剂、0.1-5份相容剂、0.5-2份稳定剂和0.5-5份润滑剂和0.5-5份混合益生菌。
优选的，所述混合益生菌包括以下质量百分数的菌种：50-60％梭状芽孢杆菌、20-40％棒状芽孢杆菌和10-20％乳酸芽孢杆菌。
优选的，所述混合益生菌包括以下质量百分数的菌种：55％梭状芽孢杆菌、30％棒状芽孢杆菌和15％乳酸芽孢杆菌。
优选的，所述梭状芽孢杆菌包括以下质量百分数的菌种：18-25％地衣芽孢杆菌、35-45％枯草芽孢杆菌和37-42％解淀粉芽孢杆菌。
本发明的枯草芽孢杆和解淀粉芽孢杆菌可以是公知，如中国微生物菌种保藏中心的，保藏编号为CGMCC NO.13643的解淀粉芽孢杆菌，保藏编号为CGMCC NO.13642的枯草芽孢杆。
优选的，所述棒状芽孢杆菌包括以下质量百分数的菌种：30-40％侧孢芽孢杆菌和60-70％苏云金芽孢杆菌。
优选的，所述乳酸芽孢杆菌包括以下质量百分数的菌种：10-20％丁酸芽孢杆菌和80-90％乙酸芽孢杆菌。
本发明的菌株可以是公知，例如，由广东惠州立博生物科技有限公司提供的地衣芽孢杆菌、河南益康生物有限公司提供的侧孢芽孢杆菌、广州芭农生物科技公司提供的苏云金芽孢杆菌、山东苏柯汉生物工程股份有限公司提供的丁酸芽孢杆菌和乙酸芽孢杆菌。
优选的，所述催化剂是偶氮二丁腈或异丙苯过氧化氢；所述相容剂是EVA或PEO；所述稳定剂是有机锡类；所述润滑剂是高级醇类。
所述的有机锡类是硫醇锡，高级醇类是十六碳醇。
所述膨润土、高岭土和碳酸钙的粒径均为纳米级。添加纳米级粒径的膨润土、高岭土和碳酸钙，这些物料具有保湿、吸水和保温功效，有利于提高秧苗的发芽率，减轻浇灌的劳动强度。
本发明还提供了聚氯乙烯微生态农业塑料母料的制备方法，包括以下步骤：
1)将各纯菌种分别振荡发酵培养；
2)将步骤1)中经发酵培养后的各纯菌种离心分离；
3)将步骤2)中离心得到的各纯菌种放入种子罐中，进行扩大培养；
4)将步骤3)扩大培养得到的各纯菌种放入发酵锅进行发酵培养；
5)将步骤4)发酵培养得到的各纯菌种离心分离；
6)将步骤5)中离心得到的各纯菌种混合，得到混合菌；
7)将混合菌与膨润土、高岭土、碳酸钙吸收混合，干燥、粉碎、研磨成为混合菌粉体；
8)在反应釜内依次添加入聚氯乙烯、催化剂、相溶剂、稳定剂和润滑剂，在80-120℃温度下，搅拌1-5小时,冷却放料，得到混合物料；
9)将步骤8)得到的混合物料放入造粒挤出机中，挤出造粒，得到颗粒状的聚氯乙烯微生态农业塑料母料。
具体的，各种菌的培养如下：
1.地衣芽孢杆菌的培养：
从广东惠州立博生物科技有限公司取回菌种扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到地衣芽孢杆菌。
2.枯草芽孢杆菌的培养：
从保藏中心取回保藏编号为CGMCC NO.13642的枯草芽孢杆菌扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到枯草芽孢杆菌。
3.解淀粉芽孢杆菌的培养：
从保藏中心取回保藏编号为CGMCC NO.13643的解淀粉芽孢杆菌扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到解淀粉芽孢杆菌。
4.侧孢芽孢杆菌的培养：
从河南益康生物有限公司提供的取回菌种扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到侧孢芽孢杆菌。
5.苏云金芽孢杆菌的培养：
从广州芭农生物科技公司取回菌种扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到苏云金芽孢杆菌。
6.丁酸芽孢杆菌的培养：
从山东苏柯汉生物工程股份有限公司取回菌种扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到丁酸芽孢杆菌。
7.乙酸芽孢杆菌的培养：
从山东苏柯汉生物工程股份有限公司取回菌种扩大培养。
培养过程设备及仪器：高温消毒锅一台；恒温水塔一台/套；管式离心机一台/套；超净灭菌柜一台/套；THZ-92A台式恒温振荡器(振荡幅度25mm)一台/套；显微镜一台；培养皿、玻璃仪器一批。
培育及生产过程：斜面培养基：牛肉膏：0.2-1.0％；蛋白冻：0.5-1.0％；营养琼脂：0.5-1.0％；NaCl：0.1-0.5％，余量为水。
发酵培养基：豆粕：1-5％；玉米粉：1-3％；玉米浆：0.2-1.0％；KHPO4：0.1-0.3％；余量为水。
发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在30-80℃200r/min下振荡培养10-40h。
将发酵培养后的菌种经离心机分离，进入100L种子罐中，在40-80℃下扩大培养8-12小时，接着进入1000L发酵锅进行发酵24-48小时，检验合格后，进入离心机分离，得到丁酸芽孢杆菌。
本发明还提供了一种育秧盘，所述育秧盘由聚氯乙烯微生态农业塑料母料经挤压成型制成。
本发明还提供了育秧盘的制备方法，包括以下步骤：
1)将聚氯乙烯微生态农业塑料母料放入压延机中进行压片，温度控制为150-210℃，得到片材；
2)将步骤1)中得到的片材放入育秧盘成型机中，温度控制为130-150℃，挤压成型，得到育秧盘。
制备得到的聚氯乙烯微生态农业塑料母料含有丰富的益生菌，可直接将其作为肥料投入农作物的根部，可以改善土壤的板结状况，增加土壤的肥力，补充农作物的肥料，使农作物茁壮生长，根茎发达，提高了农作物的抗倒伏能力，也可以减少农作物生长过程的施肥量和喷药量，是一种新型环保的育苗方式。
本发明的有益效果是：本发明的由聚氯乙烯微生态农业塑料母料制备成的育秧盘成型好，强度高，不易变形，可多次使用，易于回收，可减少育秧过程的费用成本；添加入纳米级的膨润土、高岭土、碳酸钙具有保湿、保温功效，有利于秧苗发芽，减轻浇灌劳动强度；添加入对秧苗生长有益的益生菌，使秧苗具有一定的抗病能力，秧苗根部根须多、盘根效果好、茎粗壮、出苗率、成活率高，育秧过程基本不用施用肥料和喷洒农药，大大减少了劳动力。制备的微生态农业塑料母料和育秧盘的活菌数量高，微生态农业母料成活菌数量为500-1000亿/克；育秧盘成活菌数量为100万/克以上。
附图说明
图1为采用本发明制备的育秧盘培育的秧苗生长22天的长势照片；
图2为采用常规毯式盘培育的秧苗生长22天的长势照片；
图3为采用本发明制备的育秧盘和常规毯式盘培育的秧苗生长相同天数(15天)的盘根情况的照片；
图4为采用本发明制备的育秧盘和常规毯式盘培育的秧苗生长10天的长势情况的照片；
图5为采用本发明制备的育秧盘培育的秧苗的根系生长情况照片；
图6为采用常规毯式盘培育的秧苗的根系生长情况照片。
具体实施方式
下面通实施例，对本发明的技术方案做进一步的详细描述。
实施例1
一种聚氯乙烯微生态农业塑料母料，其包括以下重量份的组分：10份聚氯乙烯、15份膨润土、20份高岭土、10份碳酸钙、0.1份异丙苯过氧化氢、0.1份EVA、0.5份硫醇锡、0.5份十六碳醇和0.5份混合益生菌。所述混合益生菌包括以下质量百分数的菌种：50％梭状芽孢杆菌、40％棒状芽孢杆菌和10％乳酸芽孢杆菌。
其中，梭状芽孢杆菌包括以下质量百分数的菌种：20％地衣芽孢杆菌、40％枯草芽孢杆菌和40％解淀粉芽孢杆菌；棒状芽孢杆菌包括以下质量百分数的菌种：32％侧孢芽孢杆菌和68％苏云金芽孢杆菌；乳酸芽孢杆菌包括以下质量百分数的菌种：15％丁酸芽孢杆菌和85％乙酸芽孢杆菌。
聚氯乙烯微生态农业塑料母料的制备方法，包括以下步骤：
1)将各纯菌种分别振荡发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在40℃，200r/min下，振荡培养30h，其中，各纯菌种分别是地衣芽孢杆菌、枯草芽孢杆菌、解淀粉芽孢杆菌、侧孢芽孢杆菌、苏云金芽孢杆菌、丁酸芽孢杆菌或乙酸芽孢杆菌；
2)将步骤1)中经发酵培养后的各纯菌种离心分离；
3)将步骤2)中离心得到的各纯菌种放入100L种子罐中，在40℃下进行扩大培养12小时；
4)将步骤3)扩大培养得到的各纯菌种放入1000L发酵锅进行发酵培养32小时；
5)将步骤4)发酵培养得到的各纯菌种离心分离；
6)将步骤5)中离心得到的各纯菌种混合，得到混合菌；
7)将混合菌与膨润土、高岭土、碳酸钙吸收混合，干燥、粉碎、研磨成为混合菌粉体；
8)在反应釜内依次添加入聚氯乙烯、异丙苯过氧化氢、EVA、硫醇锡和十六碳醇，在90℃温度下，搅拌4小时,冷却放料，得到混合物料；
9)将步骤8)得到的混合物料放入造粒挤出机中，挤出造粒，得到颗粒状的聚氯乙烯微生态农业塑料母料。
一种育秧盘，由聚氯乙烯微生态农业塑料母料经挤压成型制成。
育秧盘的制备方法，包括以下步骤：
1)将聚氯乙烯微生态农业塑料母料放入压延机中进行压片，温度控制为150℃，得到片材；
2)将步骤1)中得到的片材放入育秧盘成型机中，温度控制为150℃，挤压成型，得到育秧盘。
实施例2
一种聚氯乙烯微生态农业塑料母料，其包括以下重量份的组分：20份聚氯乙烯、18份膨润土、20份高岭土、20份碳酸钙、0.3份偶氮二丁腈、1份PEO、1份硫醇锡、1份十六碳醇和1份混合益生菌。所述混合益生菌包括以下质量百分数的菌种：58％梭状芽孢杆菌、30％棒状芽孢杆菌和12％乳酸芽孢杆菌。
其中，梭状芽孢杆菌包括以下质量百分数的菌种：18％地衣芽孢杆菌、45％枯草芽孢杆菌和37％解淀粉芽孢杆菌；棒状芽孢杆菌包括以下质量百分数的菌种：30％侧孢芽孢杆菌和70％苏云金芽孢杆菌；乳酸芽孢杆菌包括以下质量百分数的菌种：10％丁酸芽孢杆菌和90％乙酸芽孢杆菌。
聚氯乙烯微生态农业塑料母料的制备方法，包括以下步骤：
1)将各纯菌种分别振荡发酵培养：采用500ml三角瓶，内装50ml发酵培养基，在60℃，200r/min下，振荡培养20h，其中，各纯菌种分别是地衣芽孢杆菌、枯草芽孢杆菌、解淀粉芽孢杆菌、侧孢芽孢杆菌、苏云金芽孢杆菌、丁酸芽孢杆菌或乙酸芽孢杆菌；
2)将步骤1)中经发酵培养后的各纯菌种离心分离；
3)将步骤2)中离心得到的各纯菌种放入100L种子罐中，在60℃下进行扩大培养10小时；
4)将步骤3)扩大培养得到的各纯菌种放入1000L发酵锅进行发酵培养40小时；
5)将步骤4)发酵培养得到的各纯菌种离心分离；
6)将步骤5)中离心得到的各纯菌种混合，得到混合菌；
7)将混合菌与膨润土、高岭土、碳酸钙吸收混合，干燥、粉碎、研磨成为混合菌粉体；
8)在反应釜内依次添加入聚氯乙烯、偶氮二丁腈、PEO、硫醇锡和十六碳醇，在100℃温度下，搅拌3小时,冷却放料，得到混合物料；
9)将步骤8)得到的混合物料放入造粒挤出机中，挤出造粒，得到颗粒状的聚氯乙烯微生态农业塑料母料。
一种育秧盘，由聚氯乙烯微生态农业塑料母料经挤压成型制成。
育秧盘的制备方法，包括以下步骤：
1)将聚氯乙烯微生态农业塑料母料放入压延机中进行压片，温度控制为200℃，得到片材；
2)将步骤1)中得到的片材放入育秧盘成型机中，温度控制为150℃，挤压成型，得到育秧盘。
实施例3
一种聚氯乙烯微生态农业塑料母料，其包括以下重量份的组分：25份聚氯乙烯、20份膨润土、25份高岭土、30份碳酸钙、0.8份偶氮二丁腈、3份EVA、1份硫醇锡、2份十六碳醇和2份混合益生菌。所述混合益生菌包括以下质量百分数的菌种：55％梭状芽孢杆菌、30％棒状芽孢杆菌和15％乳酸芽孢杆菌。
其中，梭状芽孢杆菌包括以下质量百分数的菌种：23％地衣芽孢杆菌、38％枯草芽孢杆菌和39％解淀粉芽孢杆菌；棒状芽孢杆菌包括以下质量百分数的菌种：35％侧孢芽孢杆菌和65％苏云金芽孢杆菌；乳酸芽孢杆菌包括以下质量百分数的菌种：15％丁酸芽孢杆菌和85％乙酸芽孢杆菌。
聚氯乙烯微生态农业塑料母料的制备方法和育秧盘的制备方法与实施例1的方法一样。
实施例4
一种聚氯乙烯微生态农业塑料母料，其包括以下重量份的组分：30份聚氯乙烯、22份膨润土、26份高岭土、45份碳酸钙、0.6份异丙苯过氧化氢、2.5份EVA、1.5份硫醇锡、3份十六碳醇和3份混合益生菌。所述混合益生菌包括以下质量百分数的菌种：52％梭状芽孢杆菌、28％棒状芽孢杆菌和20％乳酸芽孢杆菌。
其中，梭状芽孢杆菌包括以下质量百分数的菌种：22％地衣芽孢杆菌、36％枯草芽孢杆菌和42％解淀粉芽孢杆菌；棒状芽孢杆菌包括以下质量百分数的菌种：38％侧孢芽孢杆菌和62％苏云金芽孢杆菌；乳酸芽孢杆菌包括以下质量百分数的菌种：16％丁酸芽孢杆菌和84％乙酸芽孢杆菌。
聚氯乙烯微生态农业塑料母料的制备方法和育秧盘的制备方法与实施例2的方法一样。
实施例5
一种聚氯乙烯微生态农业塑料母料，其包括以下重量份的组分：40份聚氯乙烯、25份膨润土、30份高岭土、55份碳酸钙、1份异丙苯过氧化氢、4份PEO、2份硫醇锡、5份十六碳醇和5份混合益生菌。所述混合益生菌包括以下质量百分数的菌种:60％梭状芽孢杆菌、26％棒状芽孢杆菌和14％乳酸芽孢杆菌。
其中，梭状芽孢杆菌包括以下质量百分数的菌种：25％地衣芽孢杆菌、35％枯草芽孢杆菌和40％解淀粉芽孢杆菌；棒状芽孢杆菌包括以下质量百分数的菌种：40％侧孢芽孢杆菌和60％苏云金芽孢杆菌；乳酸芽孢杆菌包括以下质量百分数的菌种：17％丁酸芽孢杆菌和83％乙酸芽孢杆菌。
聚氯乙烯微生态农业塑料母料的制备方法和育秧盘的制备方法与实施例2的方法一样。
采用常用的活菌平板计数法检测实施例1-5制备的聚氯乙烯微生态农业塑料母料和育秧盘的成活菌数量，其中制备的微生态农业塑料母料和育秧盘的活菌数量高，微生态农业母料成活菌数量为500-1000亿/克；育秧盘成活菌数量为100万/克以上。
实施例6
此例为采用本发明制备的育秧盘进行育苗效果研究。
为探索研究本发明制备的育秧盘的育苗效果，为实践生产应用提供依据。以常规毯式盘为对照组，开展了育苗效果对比试验。试验对秧苗株高、叶龄、根数、地上地下干重、鲜重等进行调查。
1、试验材料
本发明制备的育秧盘
常规毯式盘(市场购买)
2、试验地点
勤得利农场科技园区(黑龙江省同江市)
3、试验设计
试验设在一个大棚内，试验样品量为300-500盘。水稻品种选用龙粳31和龙粳46，按照水稻生产技术规程标准进行常规秧田管理，将本发明制备的育秧盘的育苗效果与常规毯式盘的育苗效果进行对比。
4、调查分析
试验处理于3月20日摆盘，4月7日播种，观察发现，采用本发明制备的育秧盘培育的秧苗出苗时间为4月11日，而采用常规毯式盘培育的秧苗出苗时间为4月14日。移栽前，5月10日调查两种育秧盘的育苗效果，考察的秧苗素质包括株高、根数、叶龄、地上、地下干重、鲜重等。所得平均结果如下表1所示。
表1秧苗素质调查
从表1中可以看出，采用本发明的育秧盘培育的秧苗株高比常规毯式盘培育的秧苗高2.5cm，秧苗叶龄多0.5个叶，根数多3条，茎基宽多0.4mm，地上百株鲜重多6.7g，地下百株鲜重多2.1g。综上所述，采用本发明的育秧盘育苗可以增加秧苗的株高，采用本发明的育秧盘培育的秧苗的各项指标均高于采用常规毯式盘培育的秧苗。
图1为采用本发明制备的育秧盘培育的秧苗生长22天的长势照片，图2为采用常规毯式盘培育的秧苗生长22天的长势照片。对比图1和图2可知，采用本发明制备的育秧盘培育的秧苗长势很好，长得比较浓密，叶片无孔洞；而常规毯式盘培育的秧苗长势稍微差点，植株较矮，叶片偏黄。
图3为采用本发明制备的育秧盘和常规毯式盘培育的秧苗生长相同天数(15天)的盘根情况的照片，左边为采用本发明制备的育秧盘培育的秧苗的盘根情况，右边为采用常规毯式盘培育的秧苗的盘根情况。对比可知，采用本发明制备的育秧盘培育的秧苗的根系十分发达，根系层叠地盘在育秧盘的杯中，有利于移栽后秧苗的快速生长。
图4为采用本发明制备的育秧盘和常规毯式盘培育的秧苗生长10天的长势情况的照片，左边为采用本发明制备的育秧盘培育的秧苗的长势情况，右边为采用常规毯式盘培育的秧苗的长势情况。对比可知，采用本发明制备的育秧盘培育的秧苗的长势好，秧苗比较壮，植株比较高，根系比较发达；而采用常规毯式盘培育的秧苗长得比较细小，根系欠发达。
图5为采用本发明制备的育秧盘培育的秧苗的根系生长情况照片，图6采用常规毯式盘培育的秧苗的根系生长情况照片，其中图5和图6的秧苗的株高相同。对比可知，采用本发明制备的育秧盘培育的秧苗的根数多，根系长，而采用常规毯式盘培育的秧苗的根数较少，根系较短。
Claims (10)
1.一种聚氯乙烯微生态农业塑料母料，其特征在于，包括以下重量份的组分：10-40份聚氯乙烯、15-25份膨润土、20-30份高岭土、10-60份碳酸钙、0.1-1份催化剂、0.1-5份相容剂、0.5-2份稳定剂和0.5-5份润滑剂和0.5-5份混合益生菌。
2.根据权利要求1所述的聚氯乙烯微生态农业塑料母料，其特征在于，所述混合益生菌包括以下质量百分数的菌种：50-60％梭状芽孢杆菌、20-40％棒状芽孢杆菌和10-20％乳酸芽孢杆菌。
3.根据权利要求1所述的聚氯乙烯微生态农业塑料母料，其特征在于，所述混合益生菌包括以下质量百分数的菌种：55％梭状芽孢杆菌、30％棒状芽孢杆菌和15％乳酸芽孢杆菌。
4.根据权利要求2或3所述的聚氯乙烯微生态农业塑料母料，其特征在于，所述梭状芽孢杆菌包括以下质量百分数的菌种：18-25％地衣芽孢杆菌、35-45％枯草芽孢杆菌和37-42％解淀粉芽孢杆菌。
5.根据权利要求2或3所述的聚氯乙烯微生态农业塑料母料，其特征在于，所述棒状芽孢杆菌包括以下质量百分数的菌种：30-40％侧孢芽孢杆菌和60-70％苏云金芽孢杆菌。
6.根据权利要求2或3所述的聚氯乙烯微生态农业塑料母料，其特征在于，所述乳酸芽孢杆菌包括以下质量百分数的菌种：10-20％丁酸芽孢杆菌和80-90％乙酸芽孢杆菌。
7.根据权利要求1所述的聚氯乙烯微生态农业塑料母料，其特征在于，所述催化剂是偶氮二丁腈或异丙苯过氧化氢；所述相容剂是EVA或PEO；所述稳定剂是有机锡类；所述润滑剂是高级醇类。
8.权利要求1-7中任一项所述的聚氯乙烯微生态农业塑料母料的制备方法，其特征在于，包括以下步骤：
1)将各纯菌种分别振荡发酵培养；
2)将步骤1)中经发酵培养后的各纯菌种离心分离；
3)将步骤2)中离心得到的各纯菌种放入种子罐中，进行扩大培养；
4)将步骤3)扩大培养得到的各纯菌种放入发酵锅进行发酵培养；
5)将步骤4)发酵培养得到的各纯菌种离心分离；
6)将步骤5)中离心得到的各纯菌种混合，得到混合菌；
7)将混合菌与膨润土、高岭土、碳酸钙吸收混合，干燥、粉碎、研磨成为混合菌粉体；
8)在反应釜内依次添加入聚氯乙烯、催化剂、相溶剂、稳定剂和润滑剂，在80-120℃温度下，搅拌1-5小时,冷却放料，得到混合物料；
9)将步骤8)得到的混合物料放入造粒挤出机中，挤出造粒，得到颗粒状的聚氯乙烯微生态农业塑料母料。
9.一种育秧盘，其特征在于，所述育秧盘由权利要求1-7中任一项所述的聚氯乙烯微生态农业塑料母料经挤压成型制成。
10.权利要求9所述的育秧盘的制备方法，其特征在于，包括以下步骤：
1)将权利要求1-7中任一项所述的聚氯乙烯微生态农业塑料母料放入压延机中进行压片，得到片材；
2)将步骤1)中得到的片材放入育秧盘成型机中，挤压成型，得到育秧盘。