CN107471760A - One kind discoloration embroidery wall cloth production technology - Google Patents
One kind discoloration embroidery wall cloth production technology Download PDFInfo
- Publication number
- CN107471760A CN107471760A CN201710676390.8A CN201710676390A CN107471760A CN 107471760 A CN107471760 A CN 107471760A CN 201710676390 A CN201710676390 A CN 201710676390A CN 107471760 A CN107471760 A CN 107471760A
- Authority
- CN
- China
- Prior art keywords
- embroidery
- cloth
- discoloration
- production technology
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind discoloration embroidery wall cloth production technology, in turn include the following steps：Weaving embroidery base fabric fabric, photosensitive colour-changing processing is carried out to embroidery base fabric fabric, digit printing is carried out to embroidery base fabric, embroidery base fabric carries out computerized embroidery, cloth and fire retardant nonwoven fabric are compound, embroidered cloth the is embroidered compound one layer of polyurethane film in side, spun-bonded non-woven fabrics side are compounded with adhesive layer, are pasted with release liners on adhesive layer, last cutting edge clot, examine, storage.A kind of discoloration embroidery wall cloth production technology involved in the present invention, different colors is presented in wall paper pattern color that can be in invention under different temperature conditionss, and wall paper pattern is made up of embroidery, has third dimension, while also there is preferable fire protection flame retarding function, use range is wide；Polyurethane film has the characteristics of ventilative, transparent visual, antibacterial.
Description
Technical field
The present invention relates to wall decoration fabric production technical field is same, especially a kind of discoloration embroidery wall cloth production technology.
Background technology
With advances in technology and the improvement of people's living standards, will to the finishing of household or the indoor wall of service location
Seek more and more higher.Wall paper, especially embroidery wall cloth are widely used as a kind of house decorative material.People are present not
Common wall paper pattern is contented just to, the pattern and color to wall paper ornament materials propose higher requirement.With people
For the requirement higher to wall paper, it is not strong pattern texture to be also present in existing wall paper decoration technique, color-variability it is not strong or
The function without antifouling waterproof etc. while with color-variability.
The content of the invention
It is an object of the invention to provide one kind discoloration embroidery wall cloth production technology, using the teaching of the invention it is possible to provide a kind of
In order to solve the above technical problems, the object of the present invention is achieved like this：A kind of discoloration embroidery wall involved in the present invention
Cloth production technology, in turn includes the following steps：
Step A, weaving embroidery base fabric fabric, carry out in big jacquard weaving designed flower pattern using filling-backed weave；
Step B, photosensitive colour-changing processing is carried out to embroidery base fabric fabric；
Step C, using digital printing process, stamp is carried out to embroidery base fabric；
Step D, computerized embroidery is carried out to the embroidery base fabric after stamp, obtains embroidered cloth；
Step E, the embroidered cloth that step D is obtained and spun-bonded non-woven fabrics are compound；
Step F, the embroidered cloth embroidery compound one layer of polyurethane film in side after compound；
Step H, the embroidered cloth spun-bonded non-woven fabrics side after step F processing is compounded with adhesive layer, and release liners are pasted with adhesive layer, are made
Into discoloration embroidery wall cloth；
Step I, embroidery wall cloth is examined, storage through cutting edge clot.
As a further illustration of the above scheme, in step A, in described weaving embroidery cloth process, choose through weft yarn
And institutional framework, it is warp thread from cotton yarn, is as weft yarn, fabric structure from cotton yarn and original liquid coloring color polyester silk
Filling-backed weave, flower pattern being designed as needed, being weaved on big jacquard, its front is the one side with flower pattern.
As a further illustration of the above scheme, described cotton yarn is 42；Described original liquid coloring color polyester silk
Fineness is 300D.
As a further illustration of the above scheme, the photosensitive colour-changing processing described in step B, is by the woven bases of step A
Cloth, it is put into photosensitive colour-changing treatment fluid, is warming up to 100-120 DEG C, programming rate is 1-3 DEG C/min；130-140 is warming up to again
DEG C, programming rate is 1-2 DEG C/min；Keeping temperature 30-60min again；Again through being naturally cooling to 60 DEG C, finally washed in clear water
Wash, 90-100 DEG C of drying.
As a further illustration of the above scheme, described photosensitive colour-changing solution includes photosensitive colour-changing agent, thickener, disperseed
Agent；Described photosensitive colour-changing agent Wei spirooxazine sensitising agents, mass percent 10-20%；Described dispersant is still scattered
Agent polyacrylic acid sodium salt, mass percent 1-2%；Described thickener is fiber-like thickener, mass percent 1-5%；
Surplus is water.
As a further illustration of the above scheme, the fire retardant nonwoven fabric described in step E is fire-retardant spunlace non-woven cloth or resistance
Fire spun-bonded non-woven fabrics.
As a further illustration of the above scheme, raw material used in described fire-retardant spunlace non-woven cloth is that anti-flaming viscose is fine
Dimension, weight per square meter are 50-90 grams；The specification of the FRC is 1.56dtex*38mm.
As a further illustration of the above scheme, described fire-retardant spun-bonded non-woven fabrics are the production in terylene spun-bonded non-woven fabrics
During, addition 10-15% environmentally friendly polypropylene fibre flame-retardant master batch, the weight per square meter of fire-retardant spun-bonded non-woven fabrics in the raw material of melting
For 30-80 grams.
The beneficial effects of the invention are as follows：A kind of discoloration embroidery wall cloth production technology involved in the present invention, can be in invention
Wall paper pattern color different colors is presented under different temperature conditionss, wall paper pattern is made up of embroidery, has third dimension,
While also there is preferable fire protection flame retarding function, use range is wide；Polyurethane film has the characteristics of ventilative, transparent visual, antibacterial.
Embodiment
With reference to specific embodiment, the present invention is further described.
Embodiment one
A kind of discoloration embroidery wall cloth production technology involved by the present embodiment, in turn includes the following steps.
Step A, weaving embroidery base fabric fabric；In weaving embroidery cloth process, choose through weft yarn and institutional framework, from cotton
Yarn is warp thread, and from cotton yarn and original liquid coloring color polyester silk as weft yarn, fabric structure is filling-backed weave, according to need
Flower pattern is designed, its front is the one side with flower pattern.Selected cotton yarn is 42；The fineness of original liquid coloring color polyester silk
For 300D.
Effective range of choice of table organization and inner tissue used in the present embodiment is the twill or satin weave in basic stitch,
The warp thread of selected table organization and inner tissue, the Weaving Cycle number of weft yarn are identical, between 5 and 48, i.e., corresponding to tissue follow
Ring is between 5 × 5 to 48 × 48.Table organization is identical with the Weaving Cycle number of inner tissue or into integral multiple relation, and one
The latitude of outer weft floats length in Weaving Cycle or latitude floating number is greater than the floating length of latitude or latitude floating number of back weft.
Step B, photosensitive colour-changing processing is carried out to embroidery base fabric fabric；Photosensitive colour-changing processing, is by the woven bases of step A
Cloth, it is put into photosensitive colour-changing treatment fluid, is warming up to 100 DEG C, programming rate is 1 DEG C/min；130 DEG C are warming up to again, heating speed
Spend for 1 DEG C/min；Keeping temperature 30min again；Again through being naturally cooling to 60 DEG C, finally washed in clear water, 90 DEG C of drying.
Photosensitive colour-changing solution includes photosensitive colour-changing agent, thickener, dispersant；Described photosensitive colour-changing agent Wei spirooxazine light
Quick dose, mass percent 10%；Described dispersant is still dispersant polyacrylic acid sodium salt, mass percent 1%；It is described
Thickener be fiber-like thickener, mass percent 1%；Surplus is water.
Step C, using digital printing process, stamp is carried out to embroidery base fabric；Enter line number in scrim surfaces with reactive dye
Code stamp, mainly the ground portion for fabric of embroidering is painted, flower portion is not painted, and digit printing is engaged with flower portion, is formed new
Pattern, give people a kind of good visual experience.
Step D, computerized embroidery is carried out to the embroidery base fabric after stamp, obtains embroidered cloth；In the profile that digit printing is sketched the contours of
In the range of embroidered, embroider out designed switch pattern.
Step E, the embroidered cloth that step D is obtained and fire retardant nonwoven fabric are compound；Fire retardant nonwoven fabric can be fire-retardant spunlace non-woven cloth or
Fire-retardant spun-bonded non-woven fabrics, selected for fire-retardant spunlace non-woven cloth in the present embodiment, raw material used in fire-retardant spunlace non-woven cloth
For FRC, weight per square meter is 50 grams；The specification for firing viscose rayon is 1.56dtex*38mm.Embroidered cloth and flame-retardant water
The Combined Mining of prick nonwoven cloth is compound with PU glue.
Step F, the embroidered cloth embroidery compound one layer of polyurethane film in side after compound.
Step H, to the embroidered cloth after step F processing, fire-retardant spunlace non-woven cloth side is compounded with adhesive layer, pasted on adhesive layer
There are release liners, discoloration embroidery wall cloth is made.Adhesive layer is EVA adhesive film, is carried out by way of hot pressing with fire-retardant spunlace non-woven cloth
Compound, selected EVA adhesive film is thickness between 0.01mm, and fusing point is more than 70 DEG C.
Step I, embroidery wall cloth is examined, storage through cutting edge clot.
Embodiment two
A kind of discoloration embroidery wall cloth production technology involved by the present embodiment, in turn includes the following steps.
Step A, weaving embroidery base fabric fabric；In weaving embroidery cloth process, choose through weft yarn and institutional framework, from cotton
Yarn is warp thread, and from cotton yarn and original liquid coloring color polyester silk as weft yarn, fabric structure is filling-backed weave, according to need
Flower pattern is designed, its front is the one side with flower pattern.Selected cotton yarn is 42；The fineness of original liquid coloring color polyester silk
For 300D.
Effective range of choice of table organization and inner tissue used in the present embodiment is the twill or satin weave in basic stitch,
The warp thread of selected table organization and inner tissue, the Weaving Cycle number of weft yarn are identical, between 5 and 48, i.e., corresponding to tissue follow
Ring is between 5 × 5 to 48 × 48.Table organization is identical with the Weaving Cycle number of inner tissue or into integral multiple relation, and one
The latitude of outer weft floats length in Weaving Cycle or latitude floating number is greater than the floating length of latitude or latitude floating number of back weft.
Step B, photosensitive colour-changing is carried out to embroidery base fabric fabric；Photosensitive colour-changing processing, is by the woven fabrics of step A, puts
Enter into photosensitive colour-changing treatment fluid, be warming up to 120 DEG C, programming rate is 3 DEG C/min；140 DEG C are warming up to again, programming rate 2
℃/min；Keeping temperature 60min again；Again through being naturally cooling to 60 DEG C, finally washed in clear water, 100 DEG C of drying.
Photosensitive colour-changing solution includes photosensitive colour-changing agent, thickener, dispersant；Described photosensitive colour-changing agent Wei spirooxazine light
Quick dose, mass percent 20%；Described dispersant is still dispersant polyacrylic acid sodium salt, mass percent 2%；It is described
Thickener be fiber-like thickener, mass percent 5%；Surplus is water.
Step C, using digital printing process, stamp is carried out to embroidery base fabric；Enter line number in scrim surfaces with reactive dye
Code stamp, mainly the ground portion for fabric of embroidering is painted, flower portion is not painted, and digit printing is engaged with flower portion, is formed new
Pattern, give people a kind of good visual experience.
Step D, computerized embroidery is carried out to the embroidery base fabric after stamp, obtains embroidered cloth；In the profile that digit printing is sketched the contours of
In the range of embroidered, embroider out designed switch pattern.
Step E, the embroidered cloth that step D is obtained and fire retardant nonwoven fabric are compound；Fire retardant nonwoven fabric can be fire-retardant spunlace non-woven cloth or
Fire-retardant spun-bonded non-woven fabrics, selected in the present embodiment is terylene spun-bonded for fire-retardant anti-bonded non-woven fabrics, fire-retardant spun-bonded non-woven fabrics
In the production process of non-woven fabrics, 15% environmentally friendly polypropylene fibre flame-retardant master batch is added in the raw material of melting, fire-retardant spun-bonded non-woven fabrics are put down
Square meter Chong Liang is 80 grams.
Embroidered cloth and the Combined Mining of fire-retardant spun-bonded non-woven fabrics are compound with PU glue.
Step F, the embroidered cloth embroidery compound one layer of polyurethane film in side after compound.
Step H, to the embroidered cloth after step F processing, fire-retardant spunlace non-woven cloth side is compounded with adhesive layer, pasted on adhesive layer
There are release liners, discoloration embroidery wall cloth is made.Adhesive layer is EVA adhesive film, is carried out by way of hot pressing with fire-retardant spunlace non-woven cloth
Compound, selected EVA adhesive film is thickness between 0.1mm, and fusing point is more than 70 DEG C.
Step I, embroidery wall cloth is examined, storage through cutting edge clot.
Preferred embodiment of the invention described in detail above.It should be appreciated that one of ordinary skill in the art without
Creative work can is needed to make many modifications and variations according to the design of the present invention.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical scheme, all should be in the protection domain being defined in the patent claims.
Claims (8)
1. one kind discoloration embroidery wall cloth production technology, it is characterised in that in turn include the following steps：
Step A, weaving embroidery base fabric fabric, carry out in big jacquard weaving designed flower pattern using filling-backed weave；
Step B, photosensitive colour-changing processing is carried out to embroidery base fabric fabric；
Step C, using digital printing process, stamp is carried out to embroidery base fabric；
Step D, computerized embroidery is carried out to the embroidery base fabric after stamp, obtains embroidered cloth；
Step E, the embroidered cloth that step D is obtained and fire retardant nonwoven fabric are compound；
Step F, the embroidered cloth embroidery compound one layer of polyurethane film in side after compound；
Step H, the embroidered cloth spun-bonded non-woven fabrics side after step F processing is compounded with adhesive layer, and release liners are pasted with adhesive layer, are made
Into discoloration embroidery wall cloth；
Step I, embroidery wall cloth is examined, storage through cutting edge clot.
2. discoloration embroidery wall cloth production technology as claimed in claim 1, it is characterised in that in step A, described weaving embroidery
In cloth process, choose through weft yarn and institutional framework, be warp thread from cotton yarn, made from cotton yarn and original liquid coloring color polyester silk
For weft yarn, its front is the one side with flower pattern.
3. discoloration embroidery wall cloth production technology as claimed in claim 2, it is characterised in that described cotton yarn is 42；It is described
The fineness of original liquid coloring color polyester silk be 300D.
4. discoloration embroidery wall cloth production technology as claimed in claim 1, it is characterised in that the photosensitive colour-changing described in step B
Processing, is by the woven fabrics of step A, is put into photosensitive colour-changing treatment fluid, be warming up to 100-120 DEG C, programming rate 1-3
℃/min；130-140 DEG C is warming up to again, and programming rate is 1-2 DEG C/min；Keeping temperature 30-60min again；Again through Temperature fall
To 60 DEG C, finally washed in clear water, 90-100 DEG C of drying.
5. discoloration embroidery wall cloth production technology as claimed in claim 4, it is characterised in that described photosensitive colour-changing solution includes
Photosensitive colour-changing agent, thickener, dispersant；Described photosensitive colour-changing agent Wei spirooxazine sensitising agents, mass percent 10-20%；
Described dispersant is still dispersant polyacrylic acid sodium salt, mass percent 1-2%；Described thickener increases for fiber-like
Thick dose, mass percent 1-5%；Surplus is water.
6. discoloration embroidery wall cloth production technology as claimed in claim 1, it is characterised in that the fire-retardant nonwoven described in step E
Cloth is fire-retardant spunlace non-woven cloth or fire-retardant spun-bonded non-woven fabrics.
7. discoloration embroidery wall cloth production technology as claimed in claim 6, it is characterised in that described fire-retardant spunlace non-woven cloth institute
The raw material used is FRC, and weight per square meter is 50-90 grams；The specification of the FRC is
1.56dtex*38mm。
8. discoloration embroidery wall cloth production technology as claimed in claim 6, it is characterised in that described fire-retardant spun-bonded non-woven fabrics are
In the production process of terylene spun-bonded non-woven fabrics, 10-15% environmentally friendly polypropylene fibre flame-retardant master batch is added in the raw material of melting, it is fire-retardant
The weight per square meter of spun-bonded non-woven fabrics is 30-80 grams.