CN104275862A - Fabric with physical therapy effect - Google Patents
Fabric with physical therapy effect Download PDFInfo
- Publication number
- CN104275862A CN104275862A CN201410507420.9A CN201410507420A CN104275862A CN 104275862 A CN104275862 A CN 104275862A CN 201410507420 A CN201410507420 A CN 201410507420A CN 104275862 A CN104275862 A CN 104275862A
- Authority
- CN
- China
- Prior art keywords
- yarn
- flame retardant
- fabric
- cotton
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fabric with a physical therapy effect. The fabric comprises a surface layer (101), a first fabric layer (102) and a second fabric layer (103), wherein the first fabric layer (102) covers the outer surface of the second fabric layer (103); the surface layer (101) covers the outer surface of the first fabric layer (102); the surface layer (101) is made of carbon fibers; the first fabric layer (102) is made of mercerized wool; the second fabric layer (103) is made of chitosan fibers; and the chitosan fibers are of crossed or irregular meshed structures. The fabric with the physical therapy effect, which is disclosed by the invention, has the soft, ventilated, antistatic and health functions.
Description
Technical field
The present invention relates to a kind of fabric with physiotheraping effect.
Background technology
The various clothes clothes worn made a general reference with it by clothes, and the original idea of clothes is warming, the medium of flak jacket; And the decorative article of human body has been evolved into gradually at modern society's clothes, signify standard of living and the social status of a people time more; Simultaneously on the constant basis of clothes basic function, people more and more focus on the health-care effect of clothing to health, the new material of continuous research and development clothes, utilizes suitable technique to add in dress material by various effects of different materials, adds the functional of clothes.
The fabric of existing production clothes is generally made up of a kind of material, does not have corresponding physical therapy efficacy.
Summary of the invention
The object of the invention is to overcome above-mentioned deficiency, a kind of fabric with physiotheraping effect is provided, physiotherapy function can be produced to wearer.
The object of the present invention is achieved like this: a kind of fabric with physiotheraping effect, include top layer, the first surface bed of material and the second precoat, the outer surface of described second precoat is coated with the first surface bed of material, described first surface bed of material outer surface covers top layer, described top layer is made up of carbon fiber, the described first surface bed of material is made up of mercerized wool, and described second precoat is made up of chitin fiber, and described chitin fiber is in intersecting shape or random network structure; Described top layer is implanted with cashmere;
Described top layer is also coated with the cotton protective garment fabric layer of a high flame retardant nitrile, described fabric includes the yarn for making the cotton protective garment fabric of high flame retardant nitrile, the flame retardant polyacrylic and polyester at least containing 60% percetage by weight in described yarn;
Described yarn is made up of the component of following percetage by weight: flame retardant polyacrylic and polyester 60%, combed cotton 40%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 35%, nylon 5%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 38%, antistatic fibre 2%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 33%, nylon 5%, antistatic fibre 2%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 30%, nylon 5%, aramid fiber 3%, antistatic fibre 2%;
The described yarn for the cotton protective garment fabric of high flame retardant nitrile, when described yarn is tatting yarn, the yarn count of tatting yarn is 20S/2-45S/2, and the twist is that 77.5-86.67T/10CM, S twist with the fingers; When described yarn is stocking yarn, the yarn count of stocking yarn is 10S-40S, and the twist is that 56-66T/10CM, Z twist with the fingers.
And be provided with between the first surface bed of material and the second precoat by physiotherapy layer, this physiotherapy layer includes cotton substrate processed and spraying magnetisable coating thereon.
Compared with prior art, the invention has the beneficial effects as follows:
The cotton protective garment fabric of high flame retardant nitrile of the present invention, solve the defect in technical scheme, comprise: top layer, the first surface bed of material, second precoat, the outer surface of the second described precoat is coated with the first surface bed of material, described first surface bed of material outer surface is coated with top layer, described top layer is made up of carbon fiber, the described first surface bed of material is made up of mercerized wool, the second described precoat is made up of chitin fiber, described chitin fiber is staggered shape or random network structure, the fabric that this material above-mentioned is made, can while wearing fabric, fabric not only has flexible, breathable, anlistatig function, also has the function of health care.
Accompanying drawing explanation
Fig. 1 is a kind of structural representation with the fabric of physiotheraping effect of the present invention.
Wherein:
Top layer 101, the first surface bed of material 102 and the second precoat 103.
Detailed description of the invention
See Fig. 1, a kind of fabric with physiotheraping effect that the present invention relates to and the clothing utilizing this fabric to make, the cotton protective garment fabric of high flame retardant nitrile of the present invention, include top layer 101, the first surface bed of material 102 and the second precoat 103, the outer surface of described second precoat 103 is coated with the first surface bed of material 102, the described first surface bed of material 102 outer surface covers top layer 101, described top layer 101 is made up of carbon fiber, the described first surface bed of material 102 is made up of mercerized wool, described second precoat 103 is made up of chitin fiber, described chitin fiber is in intersecting shape or random network structure.
Preferably, described top layer 101 is made up of carbon fiber, and durable acid-proof, alkali prevention, anticorrosion are antistatic, and described top layer 101 is implanted with cashmere, to increase feel.
Preferably, the described first surface bed of material 102 is made up of mercerized wool, and gloss is soft, soft texture, and hygroscopicity is strong, good permeability, comfortable and stickyly have general utility functions and make human body keep salubrious, has good heat resistance.
Preferably, described second precoat 103 is made up of chitin fiber, and chitin fiber has antibacterial and deodouring function, to the nursing function of skin, to the supplemental treatment function of allergic skin, to the defencive function of environment, and anti-static function.
Preferably, described chitin fiber is staggered shape or random network structure, this fiber good permeability.
Preferably, described carbon fiber polyacrylonitrile fibre, pitch fibers, viscose or phenolic fibre obtain through carbonization.
Preferably, described top layer and the first surface bed of material 102 and the second precoat 103, be bonded together by adhesive, each layer can be linked together more closely.
Preferably, the thickness of the cotton protective garment fabric of described high flame retardant nitrile is 0.25-0.40mm, and fabric is light, not thick and heavy.
The cotton protective garment fabric of high flame retardant nitrile of the present invention, solve the defect in technical scheme, comprise: top layer, the first surface bed of material, second precoat, the outer surface of the second described precoat is coated with the first surface bed of material, described first surface bed of material outer surface is coated with top layer, described top layer is made up of carbon fiber, the described first surface bed of material is made up of mercerized wool, the second described precoat is made up of chitin fiber, described chitin fiber is staggered shape or random network structure, the fabric that this material above-mentioned is made, can while wearing fabric, fabric not only has flexible, breathable, anlistatig function, also has the function of health care.
Described top layer 101 is also coated with the cotton protective garment fabric layer of a high flame retardant nitrile, the cotton protective garment fabric of this high flame retardant nitrile includes the yarn for making the cotton protective garment fabric of high flame retardant nitrile, the flame retardant polyacrylic and polyester at least containing 60% percetage by weight in described yarn;
The described yarn for the cotton protective garment fabric of high flame retardant nitrile can adopt following steps spinning gained: pick up → blowing → comb and parallel cotton fibers prior to spinning → in advance also → combing → drafting → rove → spun yarn → winder → doubling → double twisting of spend → distributing cotton.
As the preferred embodiment of the yarn for the cotton protective garment fabric of high flame retardant nitrile of the present invention, described yarn is also containing combed cotton; As the more preferably embodiment of the yarn for the cotton protective garment fabric of high flame retardant nitrile of the present invention, described yarn is made up of the component of following percetage by weight: flame retardant polyacrylic and polyester 60%, combed cotton 40%; Or flame retardant polyacrylic and polyester 60%, combed cotton 35%, nylon 5%; Or flame retardant polyacrylic and polyester 60%, combed cotton 38%, antistatic fibre 2%; Or flame retardant polyacrylic and polyester 60%, combed cotton 33%, nylon 5%, antistatic fibre 2%; Or flame retardant polyacrylic and polyester 60%, combed cotton 30%, nylon 5%, aramid fiber 3%, antistatic fibre 2%.
As the preferred embodiment of the yarn for the cotton protective garment fabric of high flame retardant nitrile of the present invention, the flame retardant polyacrylic and polyester that described yarn is 100% by percetage by weight forms.
Yarn for the cotton protective garment fabric of high flame retardant nitrile of the present invention, when described yarn is tatting yarn, the yarn count of tatting yarn is 20S/2-45S/2, and the twist is that 77.5-86.67T/10CM, S twist with the fingers; When described yarn is stocking yarn, the yarn count of stocking yarn is 10S-40S, and the twist is that 56-66T/10CM, Z twist with the fingers.
The present invention also provides a kind of bobbin yarn-dying method of yarn described above, and described method comprises the steps: base yarn → loose type coning → dress yarn → pre-treatment → dyeing → post processing → dehydration → oven dry → network look cylinder → packaging; Described pre-treatment is for carry out cleaning kiering with bleeding agent and soda ash; Described dyeing comprises 2 steps, and the 1st step dye of positive ion dyes to polyacrylic and polyester fiber, and the 2nd step reactive dye dye to cotton fiber.
As the preferred embodiment of the yarn bobbin yarn-dying method for the cotton protective garment fabric of high flame retardant nitrile of the present invention, during dye fluorescein color:
The described dye of positive ion contains the component of following percetage by weight: cation Y10GFF0.6-0.8%, cation Y7GL0.005-0.01%;
Dye of positive ion auxiliary agent contains following component: acetic acid 0.2-0.5g/L and levelling agent 0.2-0.5g/L;
Described reactive dye contain the component of following percetage by weight: reactive dye YHD-8GL0.3-0.6%, reactive dye TBG1900.0005-0.002%;
Reactive dye auxiliary agent contains following component: sodium chloride 30-50g/L, sodium carbonate 10-30g/L.
As the preferred embodiment of the yarn bobbin yarn-dying method for the cotton protective garment fabric of high flame retardant nitrile of the present invention, during dye fluorescent orange color:
The described dye of positive ion contains the component of following percetage by weight: cation 10GFF0.4 ~ 0.7%, cation 5GN0.05 ~ 0.085%;
Dye of positive ion auxiliary agent contains following component: acetic acid 0.2-0.5g/L and levelling agent 0.2-0.5g/L;
Described reactive dye contain the component of following percetage by weight: reactive dye CF-GN2 ~ 2.8%, reactive dye HD-8GL0.15 ~ 0.25%;
Reactive dye auxiliary agent contains following component: sodium chloride 30-50g/L, sodium carbonate 10-30g/L.
As the preferred embodiment of the yarn bobbin yarn-dying method for the cotton protective garment fabric of high flame retardant nitrile of the present invention, during dye black:
The described dye of positive ion contains the component of following percetage by weight: Y x-GL0.6-0.8 %, Rx-GRL0.1-0.5% and B x-BL0.7-0.9%;
Dye of positive ion auxiliary agent contains following component: acetic acid 0.3-0.5g/L, levelling agent 0.3-0.5g/L;
Described reactive dye contain the component of following percetage by weight: Y M3R150 % 0.2-0.6 %, R3BNJ0.1-0.4% and B KG10-20%;
Reactive dye auxiliary agent contains following component: sodium chloride 50-80g/L, sodium carbonate 10-30g/L.
As the preferred embodiment of the yarn bobbin yarn-dying method for the cotton protective garment fabric of high flame retardant nitrile of the present invention, during dye navy blue:
The described dye of positive ion contains the component of following percetage by weight: Y x-GL0.2-0.4 %, Rx-GRL0.1-0.5% and B x-BL1-2%;
Dye of positive ion auxiliary agent contains following component: acetic acid 0.3-0.5g/L, levelling agent 0.3-0.5g/L;
Described reactive dye contain the component of following percetage by weight: Y M3R150 % 0.3-0.6 %, R3BNJ0.4-0.8% and B KG1-2%;
Reactive dye auxiliary agent contains following component: sodium chloride 50-80g/L, sodium carbonate 10-30g/L.
As the preferred embodiment of the yarn bobbin yarn-dying method for the cotton protective garment fabric of high flame retardant nitrile of the present invention, the described 1st step dye of positive ion dyes to polyacrylic and polyester fiber: the dye of positive ion is prepared dissolving, be heated to 70 DEG C, add dye of positive ion auxiliary agent, running 5-10min, is warming up to and boils in 60min, dye of boiling 60min, slowly be cooled to about 60 DEG C with cold water, get after doing confirmation of checking colors, carry out loose colour cleaning technique;
2nd step reactive dye dye to cotton fiber: add the reactive dye that dissolved in advance and fill natrium carbonicum calcinatum, regulate pH=9, be warming up to 60 DEG C, insulation dyeing 30min, add reactive dye auxiliary agent common salt and sodium carbonate equably several times, make pH=4-9, fixation treatment 30min, again get and do confirmation color; By the loose colour on soaping agent cleaning fiber after confirmation.
The present invention also provide a kind of adopt bobbin yarn-dying method yarn dyeing described above after the dyed yarn that obtains.
The present invention also provides a kind of and adopts the cotton protective garment fabric of the high flame retardant nitrile of yarn weaving described above.The method for weaving of described fabric comprises dyed yarn and spells the antistatic long filament step of sth. made by twisting.The cotton protective garment fabric of the high flame retardant nitrile of yarn weaving described above is adopted to meet European Union ecological textile OKO-TEX STANDARD100 standard; Meet European Union flame retardant textiles EN11612, EN11611 standard; Meet the safety warning garment EN471 standard of EU criteria association height visibility, meet European Union antistatic EN1149 standard; Meet safety warning garment (the ANSI)/ISEA-107 standard of the flame retardant textiles ASTM F-1506 standard of U.S.'s detection and materials association, ASTM F1595/F standard and ANSI's height visibility.
Finally, the present invention also provides a kind of protective clothes adopting the cotton protective garment fabric of high flame retardant nitrile described above to make;
Be provided with between the above-mentioned first surface bed of material and the second precoat by physiotherapy layer, this physiotherapy layer includes cotton substrate processed and spraying magnetisable coating thereon, thus provides continual physiotheraping effect by magnetisable coating to human body;
Compared with prior art, the yarn for the cotton protective garment fabric of high flame retardant nitrile of the present invention, select the fibers such as Vinyon N or Vinyon N and combed cotton to match obtained, greatly, fire resistance is good for intensity; Yarn bobbin yarn-dying method of the present invention, when dyeing, color fastness is good; Dyed yarn is spelled and twisted with the fingers antistatic long filament is that antistatic long filament is woven in fabric inside completely, adopts the fabric of yarn weaving described above, and antistatic effect is better, and more attractive in appearance; Can not burn away after leaving burning things which may cause a fire disaster with the protective clothes that this fabric is obtained, without melting, without molten drop, wearer's second hurt can not be caused, meet European Union ecological textile OKO-TEX STANDARD100 standard; Meet European Union flame retardant textiles EN11612, EN11611 standard; Meet the safety warning garment EN471 standard of EU criteria association height visibility, meet European Union antistatic EN1149 standard; Meet safety warning garment (the ANSI)/ISEA-107 standard of the flame retardant textiles ASTM F-1506 standard of U.S.'s detection and materials association, ASTM F1595/F standard and ANSI's height visibility.
Claims (1)
1. one kind has the fabric of physiotheraping effect, it is characterized in that: described fabric includes top layer (101), the first surface bed of material (102) and the second precoat (103), the outer surface of described second precoat (103) is coated with the first surface bed of material (102), the described first surface bed of material (102) outer surface covers top layer (101), described top layer (101) is made up of carbon fiber, the described first surface bed of material (102) is made up of mercerized wool, described second precoat (103) is made up of chitin fiber, described chitin fiber is in intersecting shape or random network structure, (101) are implanted with cashmere on described top layer,
Described top layer (101) is also coated with the cotton protective garment fabric layer of a high flame retardant nitrile, described fabric includes the yarn for making the cotton protective garment fabric of high flame retardant nitrile, the flame retardant polyacrylic and polyester at least containing 60% percetage by weight in described yarn;
Described yarn is made up of the component of following percetage by weight: flame retardant polyacrylic and polyester 60%, combed cotton 40%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 35%, nylon 5%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 38%, antistatic fibre 2%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 33%, nylon 5%, antistatic fibre 2%;
Or flame retardant polyacrylic and polyester 60%, combed cotton 30%, nylon 5%, aramid fiber 3%, antistatic fibre 2%;
The described yarn for the cotton protective garment fabric of high flame retardant nitrile, when described yarn is tatting yarn, the yarn count of tatting yarn is 20S/2-45S/2, and the twist is that 77.5-86.67T/10CM, S twist with the fingers; When described yarn is stocking yarn, the yarn count of stocking yarn is 10S-40S, and the twist is that 56-66T/10CM, Z twist with the fingers; Be provided with between the first surface bed of material and the second precoat by physiotherapy layer, this physiotherapy layer includes cotton substrate processed and spraying magnetisable coating thereon.