CN107447331A - Staple fibre blended yarn weaved fabric - Google Patents
Staple fibre blended yarn weaved fabric Download PDFInfo
- Publication number
- CN107447331A CN107447331A CN201710912533.0A CN201710912533A CN107447331A CN 107447331 A CN107447331 A CN 107447331A CN 201710912533 A CN201710912533 A CN 201710912533A CN 107447331 A CN107447331 A CN 107447331A
- Authority
- CN
- China
- Prior art keywords
- staple fibre
- weaved fabric
- blended yarn
- fibre blended
- yarn weaved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of staple fibre blended yarn weaved fabric, and by warp thread and weft yarn, braiding is made the staple fibre blended yarn weaved fabric mutually, and the warp thread is formed by the silk fiber blended weaving of 40 60wt% milk protein fibers and 40 60wt%.The present invention provides a kind of staple fibre blended yarn weaved fabric, has the advantages that soft, sucting wet air permeability is good, chemical proofing is good.
Description
Technical field
The present invention relates to a kind of staple fibre blended yarn weaved fabric.
Background technology
With the continuous development of scientific technology, meet that the textile fabric of the different needs of people emerges in an endless stream, to meet to disappear
The demand of the person of expense, more and more important effect is played in daily life.Staple fibre is two major classes of chemical fibre
One of.Raw material is done with some natural polymers or derivatives thereof, weaving solution is made after dissolving, is then spun into fibre
Dimension, bamboo, timber, bagasse, cotton seed suede etc. are all the raw materials for manufacturing staple fibre.Existing fabric function when wearing is most
It is relatively simple, often feel relatively simple when people wear, and also do not possess some to contribute to the function of health, relatively
Shortcoming.
The content of the invention
The present invention provides a kind of artificial fibre for having the advantages that soft, sucting wet air permeability is good, chemical proofing is good
Tie up blended yarn weaved fabric.
The technical scheme is that：A kind of staple fibre blended yarn weaved fabric, the staple fibre blended yarn weaved fabric is by warp thread
Weave mutually and be made with weft yarn, the warp thread by 40-60wt% milk protein fibers and 40-60wt% it is silk fiber blended weaving and
A diameter of 9.07 μm, fiber number 113dtex that yarn is pricked for dragon into, described weft yarn, density are 37.7/cm, the polytetrafluoro
A diameter of 70.33 μm of the compound fine line of vinyl, fiber number 657dtex, density are 46.3/cm, the staple fibre blending
The preparation technology of fabric is raw material（Dispensing）Cutting is batched in → heating → extruding → filtering → casing → stretching → networking hot rolling →
→ weigh → examine → pack → be put in storage.
In a preferred embodiment of the present invention, the density of the tencel fiber about 1.40g/cm3.
In a preferred embodiment of the present invention, the fiber number of the milk protein fiber is 200~385dtex.
The present invention a kind of staple fibre blended yarn weaved fabric, have it is soft, sucting wet air permeability is good, chemical proofing is good
The advantages that.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly defined so as to be made to protection scope of the present invention.
Wherein, by warp thread and weft yarn, braiding is made the staple fibre blended yarn weaved fabric mutually, and the warp thread is by 40-
60wt% milk protein fibers and the silk fiber blended weavings of 40-60wt% form, and described weft yarn pricks a diameter of of yarn for dragon
9.07 μm, fiber number 113dtex, density is 37.7/cm, a diameter of 70.33 μm of the compound fine line of PTFE base,
Fiber number is 657dtex, and density is 46.3/cm, and the preparation technology of the staple fibre blended yarn weaved fabric is raw material（Dispensing）→ plus
Heat → extruding → filtering → casing → stretching → networking hot rolling →, which is batched, cuts → weighing → and examines → packaging → to be put in storage.
Further illustrate, the density about 1.40g/cm3 of the tencel fiber, the fiber number of the milk protein fiber is 200
~385dtex.
Further illustrating, PTFE composites pressure in molding process is very big to its density and intensity effect.
Pressure is big, and the space in composite is few, and density is big, and tensile strength is big, but too high pressure can destroy the knot of glass cloth
Structure.In our current research, compressing processing temperature is controlled at 250 DEG C with thermocouple, and pressure is 70atm, the space of material
Volume is seldom, while glass cloth is also intact.PTFE resins are heated to 311 ~ 344 DEG C and start to melt.Melting
During, not only mutually wind, also occur between molecular resin and glass cloth surface modified molecules mutual between molecular resin
Effect, this transmission acted through between molecule and molecule can be distributed in whole composite so that glass cloth increases
Strong later PTFE melting temperature accordingly improves.The mechanical performance that composite is not only after glass cloth enhancing is changed
Kind, heat resistance is more preferable.Too high or too low glass cloth content all can reduce the tensile strength of composite.When compound
When material is acted on by extraneous stress, stress is transmitted by the interface of fiber and resin, is diffused into resin body,
Avoid stress concentration.Therefore, interface plays an important role to the mechanical property of composite.PTFE matrix resins and glass
Between fiber interface size, interface binding power be control composite materials property important parameter, too high or too low, glass
Fiber cloth content is unfavorable for the formation at interface between matrix resin and reinforcing material, only when glass fabric content is 40%
During left and right, interfacial combined function is best between matrix resin and reinforcing material..The present invention provides a kind of staple fibre blending face
Material, has the advantages that soft, sucting wet air permeability is good, chemical proofing is good.
The embodiment of the present invention, but protection scope of the present invention is not limited thereto, any to be familiar with this area
Technical staff disclosed herein technical scope in, the change or replacement that can expect without creative work should all be contained
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should be with protection model that claims are limited
Enclose and be defined.
Claims (3)
- A kind of 1. staple fibre blended yarn weaved fabric, it is characterised in that：The staple fibre blended yarn weaved fabric is mutual by warp thread and weft yarn Braiding is made, and the warp thread is formed by the silk fiber blended weaving of 40-60wt% milk protein fibers and 40-60wt%, described Weft yarn pricks a diameter of 9.07 μm, fiber number 113dtex of yarn for dragon, and density is 37.7/cm, and the PTFE base is compound A diameter of 70.33 μm of fine line, fiber number 657dtex, density are 46.3/cm, the preparation of the staple fibre blended yarn weaved fabric Technique is raw material（Dispensing）→ heating → extruding → filtering → casing → stretching → networking hot rolling →, which is batched, cuts → weighing → and examines Test → pack → be put in storage.
- 2. staple fibre blended yarn weaved fabric according to claim 1, it is characterised in that：The density of the tencel fiber is about 1.40g/cm3。
- 3. staple fibre blended yarn weaved fabric according to claim 1, it is characterised in that：The fiber number of the milk protein fiber is 200~385dtex.