CN106637680A - Polytetrafluoroethylene filament non-woven fabric based on film tearing method and preparation technology thereof - Google Patents
Polytetrafluoroethylene filament non-woven fabric based on film tearing method and preparation technology thereof Download PDFInfo
- Publication number
- CN106637680A CN106637680A CN201611272561.2A CN201611272561A CN106637680A CN 106637680 A CN106637680 A CN 106637680A CN 201611272561 A CN201611272561 A CN 201611272561A CN 106637680 A CN106637680 A CN 106637680A
- Authority
- CN
- China
- Prior art keywords
- filament
- film
- fiber
- woven fabrics
- split
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polytetrafluoroethylene filament non-woven fabric based on a film tearing method. The fabric comprises a filament fiber net formed by stacking polytetrafluoroethylene fiber filaments with the average fineness being 0.2-20 dtex based on the film tearing method, the filament fiber net is compressed in a repeated acupuncture reinforcing and stretching mode, and the polytetrafluoroethylene filament non-woven fabric based on the film tearing method is formed. A preparation technology comprises the steps of 1 material preparation, 2 splitting, 3 lapping, 4 acupuncturing and 5 rolling. According to the polytetrafluoroethylene filament non-woven fabric based on the film tearing method and the preparation technology thereof, one-time molding and manufacturing are performed, the defects that in the prior art, a non-woven fabric is poor in firmness and a preparation technology is complex can be overcome, the overall strength of the filament non-woven fabric is enhanced, and the polytetrafluoroethylene filament non-woven fabric has the good water permeable and gas permeable performance and is wide in application range.
Description
Technical field
The present invention relates to field of nonwoven fabric technology, more particularly to a kind of polytetrafluoroethylfilament filament nonwoven that method is split based on film
Cloth and its preparation technology.
Background technology
The material for preparing of simple tension film is ultra-high molecular weight polyethylene, PTFE, polypropylene, PPS (polyphenylene sulfide), P84
(polyimides), wherein, PTFE is the english abbreviation of polytetrafluoroethylene (PTFE), is the king of plastics generally acknowledged in the world at present, with anti-
The advantages of ultraviolet radiation, resistance to chemical attack, wearability, polytetrafluoroethylene fibre chemical stability is fabulous, and corrosion resistance is better than
Other synthetic fibers kinds;Fiber surface has wax sense, and coefficient of friction is little;Meanwhile, also with preferable against weather and warp resistance
Property.
Non-woven fabrics is defined as non-weaving cloth again, is made up of fiber orient or random, is environment-friendly materials of new generation,
With moistureproof, ventilative, flexible, light weight, not combustion-supporting, easy decomposition, nontoxic nonirritant, rich color, cheap, capable of circulation
The features such as using again.As adopted polypropylene (pp materials) pellet for raw material, Jing high-temperature fusions, spinneret, paving guiding principle, hot pressing are batched continuously more
One-step production is formed.Cloth is called because of the outward appearance with cloth and some performances.Realize in the U.S. from nineteen forty-two early start
After industrialization production, because it has, low cost, products application big compared with conventional woven cloth simple production process, yield extensively etc.
Feature, nowadays, it has also become emerging field with the fastest developing speed in textile industry.Non-woven fabrics can be divided into by processing method difference:
Spun-bonded non-woven fabrics, spunlace non-woven cloth, heat seal non-woven fabrics, wet nonwoven fabrics, needle punched non-woven fabrics etc..Non-woven fabrics has many functionally
Excellent properties, purposes is extremely extensive, can be divided into according to its purposes:Clothes non-woven fabrics, furniture decoration/household non-woven fabrics,
Non-woven fabrics for medical healthcare, filtering material non-woven fabrics etc..
The cloth of method shaping, manufacture are tangled etc. more than the manufacture of existing non-woven fabrics using the direct hot melt adhesive of chopped fiber, machinery
Process is relatively easy, low cost. but the binding site of hot melt adhesive only occurs in fiber intersection points, advantage be have elasticity well and
Fluffy degree, has the disadvantage the cutting or directly purchase of chopped fiber, transport and personnel cost is increased, due to the spy of chopped fiber itself
There is the defect of fiber head, uneven surface in point, the non-woven fabrics prepared.
In prior art, splitting method film by film and split the filament fiber for can not make non-woven fabrics, for manufacturing woven bag etc.,
While how film is split the filament fiber manufacture non-woven fabrics for, filament fiber is not cut off, be non-woven fabrics directly into the method for cloth
The new trend of technical field.
The content of the invention
For defect present in prior art or deficiency, the present invention is innovatively proposed a kind of splits the poly- of method based on film
Tetrafluoroethene continuous yarn non-woven fabrics and its preparation technology, one-shot forming manufacture, can overcome non-woven fabrics fastness in prior art it is poor,
The defects such as complicated process of preparation, making the overall dynamics of the polytetrafluoroethylfilament filament non-woven fabrics for splitting method based on film strengthens, with good
Permeable, permeability, application is extensive.
The technical scheme is that what is be achieved in that:
A kind of polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, including by average fineness for 0.2-20dtex based on
Film splits the filament web of the polytetrafluoroethylfiber fiber filaments laying of method, and the mode reinforced using repeated puncture and stretched is made
Filament web is compressed, and the polytetrafluoroethylfilament filament non-woven fabrics of method is split in formation based on film.
Preferably, the needling density of the filament web is 100-800 pins/square centimeter.
Preferably, metal fiber wire or glass fibers are mixed with the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film
Dimension silk in one or two.
Preferably, it is described composition filament in polytetrafluoroethylfiber fiber filaments shared by percentage by weight be 20-80%, institute
It is 10-35% to state percentage by weight shared by metal fiber wire, and percentage by weight shared by the glass fiber is 10-45%.
Preferably, the elongated fibers of a diameter of 0.003-0.03mm of the polytetrafluoroethylfiber fiber filaments, the metal
The elongated fibers of filametntary a diameter of 0.005-0.05mm, a diameter of 0.004-0.04mm's of the glass fiber is elongated
Fiber.
Preferably, the fiber filament constituted in polytetrafluoroethylfilament filament non-woven fabrics is that the fiber continuously not cut off is long
Silk, the length of the fiber filament, the length >=100mm of the fiber filament.
Preferably, the poly tetrafluoroethylene is one-way membrane.
The invention also discloses a kind of preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, including it is as follows
Step:
(1), get the raw materials ready:According to Production requirement, polytetrafluoroethylene (PTFE) one-way membrane is prepared according to quantity;
(2), fibrillation:The polytetrafluoroethylene (PTFE) one-way membrane Jing films of step (1) are split into device cut into 100-50000 and be based on film
Split the polytetrafluoroethylfiber fiber filaments of method;
(3), lapping:Jing films in step (2) are split into the obtained polytetrafluoroethylfiber fiber filaments for splitting method based on film of device equal
Even dispersion is simultaneously laid on lapper lace curtaining, and by the reciprocal laying of lapper lace curtaining, the polytetrafluoroethyl-ne of method is split in formation based on film
Alkene filament web is intersected with each other to be stacked on output lace curtaining;
(4), acupuncture:It is the pricker of triangle and seamed edge with hook thorn using section, by filament fiber obtained in step (3)
Net carries out acupuncture, and when several prickers are pierced into filament web, the hook thorn on pricker can be with the fibre of filament fiber net surface
Dimension passes through filament web with pricker, mutually tangles, and in the presence of frictional force, is compressed filament web, and acupuncture adds
Gu when, fiber filament departs from hook thorn and rests in the vertical state in filament web so that compressed filament web
No longer restore to the original state, according to Production requirement, reach default density for 0.2-2.5 gram/cm, formation splits method based on film
Polytetrafluoroethylfilament filament non-woven fabrics;
(5), wind:By the obtained polytetrafluoroethylfilament filament non-woven fabrics winding packing that method is split based on film of step (4).
Preferably, the needling density of the filament web is 100-800 pins/square centimeter.
Preferably, the Denier range of the polytetrafluoroethylfiber fiber filaments that method is split based on film is in 0.2-20dtex, strength
Scope is in 2.5-6.5cN/dtex.
Compared with prior art, the beneficial effects of the present invention is:
The invention discloses a kind of polytetrafluoroethylfilament filament non-woven fabrics and its preparation technology that method is split based on film, the technique by
Film is split method and directly polytetrafluoroethylene (PTFE) one-way membrane is split into device by film and is cut into the polytetrafluoroethylfiber fiber filaments that method is split based on film,
Subsequently prepare again during non-woven fabrics without the need for cut staple long filament, compared with the non-woven fabrics of other technique productions, a step into
The mode of type, saves traditional fibre cutting, opens bag, staple card lapping operation, saves the production of artificial and product
Cost, reduces the transit link of chopped fiber, also prevent secondary pollution of the chopped fiber in transportation.
The polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film of the present invention, one-shot forming manufacture, can overcome existing skill
Non-woven fabrics fastness is poor in art, complicated process of preparation, increase the defects such as human cost, makes the polytetrafluoroethylene (PTFE) for splitting method based on film long
The overall dynamics of silk non-woven fabrics strengthens, with good flexibility, water penetration, permeability etc., meanwhile, overcome traditional short fibre
The defect that fiber head is excessive in dimension non-woven fabrics, surface is not smooth enough, application is extensive.
Specific embodiment
With reference to specific embodiment, technical scheme is clearly and completely described, it is clear that retouched
The embodiment stated is only a part of embodiment of the invention, rather than the embodiment of whole.Based on the embodiment in the present invention, this
The every other embodiment that field those of ordinary skill is obtained under the premise of creative work is not made, belongs to the present invention
The scope of protection.
The invention provides a kind of polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, including being 0.2- by average fineness
The filament web of the polytetrafluoroethylfiber fiber filaments laying that method is split based on film of 20dtex, using repeated puncture reinforce and
The mode of stretching is compressed filament web, and the polytetrafluoroethylfilament filament non-woven fabrics of method is split in formation based on film;Filament fiber
The needling density of net is 100-800 pins/square centimeter;Metal is mixed with the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film
One or two in filament or glass fiber, wherein, constitute weight shared by the polytetrafluoroethylfiber fiber filaments in filament
Amount percentage is 20-80%, percentage by weight shared by metal fiber wire is 10-35%, percentage by weight shared by glass fiber
For 10-45%;Elongated fibers, the metal that a diameter of 0.003-0.03mm of the polytetrafluoroethylfiber fiber filaments of method is split based on film is fine
Elongated fibers, the elongated fibers of a diameter of 0.004-0.04mm of glass fiber of a diameter of 0.005-0.05mm of dimension silk;
The fiber filament that split in the polytetrafluoroethylfilament filament non-woven fabrics of method based on film of composition is the fiber filament continuously not cut off, the fibre
The length of dimension long filament, the length >=100mm of the fiber filament.
Embodiment 1:
A kind of preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, is comprised the steps:
(1), get the raw materials ready:According to Production requirement, polytetrafluoroethylene (PTFE) one-way membrane is prepared according to quantity;
(2), fibrillation:The polytetrafluoroethylene (PTFE) one-way membrane Jing films of step (1) are split into device and cuts into 10000-200000 foundation
The polytetrafluoroethylfiber fiber filaments of method are split in film, the Denier range of the polytetrafluoroethylfiber fiber filaments is in 0.5dtex, strength model
It is trapped among 4.5cN/dtex;
(3), lapping:Jing films in step (2) are split into the obtained polytetrafluoroethylfiber fiber filaments for splitting method based on film of device equal
Even dispersion is simultaneously laid on lapper lace curtaining, and by the reciprocal laying of lapper lace curtaining, the polytetrafluoroethyl-ne of method is split in formation based on film
Alkene filament web is intersected with each other to be stacked on output lace curtaining;
(4), acupuncture:It is the pricker of triangle and seamed edge with hook thorn using section, by filament fiber obtained in step (3)
Net carries out acupuncture, and the needling density of filament web is 100 pins/square centimeter;When several prickers are pierced into filament web,
Hook thorn on pricker can pass through filament web with the fiber of filament fiber net surface with pricker, mutually tangle, in frictional force
In the presence of, filament web is compressed, during pinprick reinforcement, fiber filament departs from hook thorn and rests on length in the vertical state
In silk fiber net so that compressed filament web no longer restores to the original state, according to Production requirement, reaching default density is
0.2 gram/cm, the polytetrafluoroethylfilament filament non-woven fabrics of method is split in formation based on film;
(5), wind:By the obtained polytetrafluoroethylfilament filament non-woven fabrics winding packing that method is split based on film of step (4).
Embodiment 2:
A kind of preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, is comprised the steps:
(1), get the raw materials ready:According to Production requirement, polytetrafluoroethylene (PTFE) one-way membrane is prepared according to quantity;
(2), fibrillation:The polytetrafluoroethylene (PTFE) one-way membrane Jing films of step (1) are split into device and cuts into 30000-300000 foundation
The polytetrafluoroethylfiber fiber filaments of method are split in film, the Denier range of the polytetrafluoroethylfiber fiber filaments is in 15dtex, strength model
It is trapped among 3.5cN/dtex;
(3), lapping:Jing films in step (2) are split into the obtained polytetrafluoroethylfiber fiber filaments for splitting method based on film of device equal
Even dispersion is simultaneously laid on lapper lace curtaining, and by the reciprocal laying of lapper lace curtaining, the polytetrafluoroethyl-ne of method is split in formation based on film
Alkene filament web is intersected with each other to be stacked on output lace curtaining;
(4), acupuncture:It is the pricker of triangle and seamed edge with hook thorn using section, by filament fiber obtained in step (3)
Net carries out acupuncture, and the needling density of filament web is 550 pins/square centimeter;When several prickers are pierced into filament web,
Hook thorn on pricker can pass through filament web with the fiber of filament fiber net surface with pricker, mutually tangle, in frictional force
In the presence of, filament web is compressed, during pinprick reinforcement, fiber filament departs from hook thorn and rests on length in the vertical state
In silk fiber net so that compressed filament web no longer restores to the original state, according to Production requirement, reaching default density is
1.5 grams/cm, the polytetrafluoroethylfilament filament non-woven fabrics of method is split in formation based on film;
(5), wind:By the obtained polytetrafluoroethylfilament filament non-woven fabrics winding packing that method is split based on film of step (4).
Embodiment 3:
A kind of preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, is comprised the steps:
(1), get the raw materials ready:According to Production requirement, polytetrafluoroethylene (PTFE) one-way membrane is prepared according to quantity;
(2), fibrillation:The polytetrafluoroethylene (PTFE) one-way membrane Jing films of step (1) are split into device and cuts into 50000-500000 foundation
The polytetrafluoroethylfiber fiber filaments of method are split in film,
(3), lapping:Jing films in step (2) are split into the obtained polytetrafluoroethylfiber fiber filaments for splitting method based on film of device equal
Even dispersion is simultaneously laid on lapper lace curtaining, and by the reciprocal laying of lapper lace curtaining, the polytetrafluoroethyl-ne of method is split in formation based on film
Alkene filament web is intersected with each other to be stacked on output lace curtaining;The Denier range of the polytetrafluoroethylfiber fiber filaments exists
20dtex, strength scope is in 4.0cN/dtex;
(4), acupuncture:It is the pricker of triangle and seamed edge with hook thorn using section, by filament fiber obtained in step (3)
Net carries out acupuncture, and the needling density of filament web is 800 pins/square centimeter;When several prickers are pierced into filament web,
Hook thorn on pricker can pass through filament web with the fiber of filament fiber net surface with pricker, mutually tangle, in frictional force
In the presence of, filament web is compressed, during pinprick reinforcement, fiber filament departs from hook thorn and rests on length in the vertical state
In silk fiber net so that compressed filament web no longer restores to the original state, according to Production requirement, reaching default density is
2.5 grams/cm, the polytetrafluoroethylfilament filament non-woven fabrics of method is split in formation based on film;
(5), wind:By the obtained polytetrafluoroethylfilament filament non-woven fabrics winding packing that method is split based on film of step (4).
The preferred embodiment of invention is the foregoing is only, not to limit the present invention, all spirit in the present invention
Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (10)
1. a kind of polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film, it is characterised in that include that by average fineness be 0.2-
The filament web of the polytetrafluoroethylfiber fiber filaments laying that method is split based on film of 20dtex, using repeated puncture reinforce and
The mode of stretching is compressed filament web, and the polytetrafluoroethylfilament filament non-woven fabrics of method is split in formation based on film.
2. the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 1, it is characterised in that the long filament
The needling density of fleece is 100-800 pins/square centimeter.
3. the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 1, it is characterised in that described to be based on
Film splits one or two that be mixed with the polytetrafluoroethylfilament filament non-woven fabrics of method in metal fiber wire or glass fiber.
4. the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 2, it is characterised in that the composition
Percentage by weight shared by polytetrafluoroethylfiber fiber filaments in filament be 20-80%, weight hundred shared by the metal fiber wire
Divide than being 10-35%, percentage by weight shared by the glass fiber is 10-45%.
5. the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 3, it is characterised in that described poly- four
The elongated fibers of a diameter of 0.003-0.03mm of PVF fiber filament, a diameter of 0.005- of the metal fiber wire
The elongated fibers of 0.05mm, the elongated fibers of a diameter of 0.004-0.04mm of the glass fiber.
6. the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 1, it is characterised in that the composition
Fiber filament in polytetrafluoroethylfilament filament non-woven fabrics is the fiber filament continuously not cut off, and the length of the fiber filament is not
Deng the length >=100mm of the fiber filament.
7. the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 1, it is characterised in that described poly- four
Fluoride film is one-way membrane.
8. the preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to any one of claim 1-7,
Characterized in that, comprising the steps:
(1), get the raw materials ready:According to Production requirement, polytetrafluoroethylene (PTFE) one-way membrane is prepared according to quantity;
(2), fibrillation:The polytetrafluoroethylene (PTFE) one-way membrane Jing films of step (1) are split device and cut into 100-50000 and be based on film and splits method
Polytetrafluoroethylfiber fiber filaments;
(3), lapping:Jing films in step (2) are split into the obtained polytetrafluoroethylfiber fiber filaments for splitting method based on film of device uniformly to divide
Dissipate and be laid on lapper lace curtaining, by the reciprocal laying of lapper lace curtaining, formation is long based on the polytetrafluoroethylene (PTFE) that film splits method
Silk fiber net is intersected with each other to be stacked on output lace curtaining;
(4), acupuncture:It is the pricker of triangle and seamed edge with hook thorn using section, filament web obtained in step (3) is entered
The hand-manipulating of needle is pierced, when several prickers are pierced into filament webs, the hook thorn on pricker can with the fiber of filament fiber net surface with
Pricker passes through filament web, mutually tangles, and in the presence of frictional force, is compressed filament web, during pinprick reinforcement,
Fiber filament departs from hook thorn and rests in the vertical state in filament web so that compressed filament web is no longer extensive
Shape is restored, according to Production requirement, default density is reached for 0.2-2.5 gram/cm, the polytetrafluoro of method is split in formation based on film
Ethene continuous yarn non-woven fabrics;
(5), wind:By the obtained polytetrafluoroethylfilament filament non-woven fabrics winding packing that method is split based on film of step (4).
9. the preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 8, its feature is existed
In the needling density of the filament web is 100-800 pins/square centimeter.
10. the preparation technology of the polytetrafluoroethylfilament filament non-woven fabrics that method is split based on film according to claim 8, its feature is existed
In, in 0.2-20dtex, strength scope is in 2.5- for the Denier range of the polytetrafluoroethylfiber fiber filaments that method is split based on film
6.5cN/dtex。