CN107446497A - The barrier coating that a kind of plastics spoon uses when making - Google Patents

The barrier coating that a kind of plastics spoon uses when making Download PDF

Info

Publication number
CN107446497A
CN107446497A CN201710647680.XA CN201710647680A CN107446497A CN 107446497 A CN107446497 A CN 107446497A CN 201710647680 A CN201710647680 A CN 201710647680A CN 107446497 A CN107446497 A CN 107446497A
Authority
CN
China
Prior art keywords
parts
minutes
stirred
weight
ethanol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710647680.XA
Other languages
Chinese (zh)
Inventor
刘立平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jieshou City Hongli Plastic Co Ltd
Original Assignee
Jieshou City Hongli Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jieshou City Hongli Plastic Co Ltd filed Critical Jieshou City Hongli Plastic Co Ltd
Priority to CN201710647680.XA priority Critical patent/CN107446497A/en
Publication of CN107446497A publication Critical patent/CN107446497A/en
Pending legal-status Critical Current

Abstract

The barrier coating that a kind of plastics spoon uses when making, it is related to Domestic plastic product processing technical field, it is characterised in that：It is made up of the material of following parts by weight, 9 12 parts of ethanol, 9 14 parts of oyster shell whiting, 58 parts of organic siliconresin, 47 parts of ester gum, 13 parts of silicone oil, 69 parts of defoamer, 36 parts of polyamide wax, 7 10 parts of auxiliary agent, 36 parts of blender.The inventive method is reasonable, easy to operate, noresidue is without attachment.

Description

The barrier coating that a kind of plastics spoon uses when making
Technical field
The present invention relates to Domestic plastic product to process technical field, and in particular to a kind of plastics spoon uses when making Barrier coating.
Background technology
Plastics are the high-molecular compounds that are formed by addition polymerization or polycondensation polymerized using monomer as raw material (macromolecules) plastics (plastics) or resin (resin), are commonly called as, can freely change composition and body styles, It is made up of the additive such as synthetic resin and filler, plasticizer, stabilizer, lubricant, colorant.
The main component of plastics is resin.This noun of resin is gained the name by the lipid that animals and plants secret out of, such as Rosin, shellac etc., resin refer to the high-molecular compound not yet with various additives mixing.Resin accounts for plastics gross weight 40%~100%.The basic performance of plastics depends mainly on the person's character of resin, but additive also plays an important role.Some modelings Material is substantially made up of synthetic resin, is free of or is contained additive, such as lucite, polystyrene less.
So-called plastics, it is one kind in synthetic resin in fact, and shape is similar with the pine resin in natural resin, by changing It is artificial synthesized to learn to do section progress, and is referred to as plastics.
The species of spoon is a lot, different materials, different colors, different sizes, for different things, he Use be also different.
And be a very important product with the spoon of plastic production, and the scope used is very wide, but Due to material itself and the reason for mold material etc., residue attachment is often had after production during production On mould, and clear up it is very inconvenient, and delay it is follow-up continue to produce, substantial amounts of time and manpower can be wasted Deng.
The content of the invention
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, operation side Just the barrier coating used when, a kind of plastics spoon of the noresidue without attachment makes.
The technical problems to be solved by the invention are realized using following technical scheme：
The barrier coating that a kind of plastics spoon uses when making, it is characterised in that：It is made up of the material of following parts by weight,
Ethanol 9-12 parts, oyster shell whiting 9-14 parts, organic siliconresin 5-8 parts, ester gum 4-7 parts, silicone oil 1-3 parts, disappear Infusion 6-9 parts, polyamide wax 3-6 parts, auxiliary agent 7-10 parts, blender 3-6 parts；
Comprise the following steps that,
Oyster shell whiting is put into 0.1-0.2% hydrochloric acid and soaked 5 minutes by I, is then placed in Muffle furnace and is heated to 650 DEG C, Continue 2-3 hour, the weight of hydrochloric acid is identical with the weight of oyster shell whiting, it is to be heated after the completion of 1 hour add blender and stir Mix 10-14 minutes；
II is put into organic siliconresin, ester gum, silicone oil, defoamer, polyamide wax in ethanol, is stirred 10- 14 minutes, to uniform；
III in the addition of the material in I II, will be stirred 5-7 minutes adds auxiliary agent afterwards, continues to be stirred 11-14 points Clock；
IV will can be used after the material left 30 minutes after stirring, uniformly be applied to mould inner wall during use；
The auxiliary agent is made up of the material of following parts by weight,
8 parts of ethanol, 0.5 part of hydrofluoric acid, 1 part of titanium dioxide, 1 part of poly- glutaric acid propylene glycol ester, 0.5 part of coal tar, gelatin 4 Part, 7 parts of age resistor；
Production method includes,
Titanium dioxide, gelatin are put into iron pan and are stirred 12 minutes by I, add the pure of material gross weight 1/18 during stirring Water；
Hydrofluoric acid, poly- glutaric acid propylene glycol ester, coal tar are put into ethanol and stand 8 minutes by II, are then stirred 5 minutes；
III is put into the material in I and II in mixing plant, is stirred 7 minutes, then adds age resistor and continues stirring 8 Minute；
The blender is made up of the material of following parts by weight,
1 part of Chinese ephedra, 3 parts of Radix Isatidis, 2 parts of cassia twig, 3 parts of perilla leaf, 1 part of ginseng, 2 parts of reed rhizome, 3 parts of ginger, 1 part of pseudo-ginseng, 2 parts of the coptis；
Preparation method：Above-mentioned material is rinsed well with clear water, is then cut into sheet, natural drying shines surface water mark It is dry, the distillation processing that 5-6 hours are carried out in distillation equipment is then placed in, then remaining impurity, material are removed, stay the liquid after distillation Body.
Beneficial effects of the present invention are：The material of mixing effectively can protect mould not corroded, and can produce During ensure mould in material do not bonded with mould, can once be completed during demoulding, and do not have on mould There is remaining attachment, ensure the integrality and clean level of mould, and the material smeared can be to the product of in-mold molding Play a protective role, certain anti-old, antioxygen can be played a part of, extend the service life of product.The inventive method rationally, Easy to operate, noresidue is without attachment.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below One step illustrates the present invention.
Embodiment 1
The barrier coating that a kind of plastics spoon uses when making, it is characterised in that：It is made up of the material of following parts by weight,
It is 11 parts of ethanol, 12 parts of oyster shell whiting, 7 parts of organic siliconresin, 5 parts of ester gum, 1 part of silicone oil, 8 parts of defoamer, poly- 4 parts of amide waxe, 7 parts of auxiliary agent, 4 parts of blender；
Comprise the following steps that,
Oyster shell whiting is put into 0.1% hydrochloric acid and soaked 5 minutes by I, is then placed in Muffle furnace and is heated to 650 DEG C, continues 2 Individual hour, the weight of hydrochloric acid is identical with the weight of oyster shell whiting, it is to be heated after the completion of 1 hour add blender and be stirred 12 points Clock；
II is put into organic siliconresin, ester gum, silicone oil, defoamer, polyamide wax in ethanol, is stirred 12 points Clock, to uniform；
III adds the material in I in II, adds auxiliary agent after being stirred 6 minutes, continues to be stirred 11 minutes；
IV will can be used after the material left 30 minutes after stirring, uniformly be applied to mould inner wall during use；
The auxiliary agent is made up of the material of following parts by weight,
8 parts of ethanol, 0.5 part of hydrofluoric acid, 1 part of titanium dioxide, 1 part of poly- glutaric acid propylene glycol ester, 0.5 part of coal tar, gelatin 4 Part, 7 parts of age resistor；
Production method includes,
Titanium dioxide, gelatin are put into iron pan and are stirred 12 minutes by I, add the pure of material gross weight 1/18 during stirring Water；
Hydrofluoric acid, poly- glutaric acid propylene glycol ester, coal tar are put into ethanol and stand 8 minutes by II, are then stirred 5 minutes；
III is put into the material in I and II in mixing plant, is stirred 7 minutes, then adds age resistor and continues stirring 8 Minute；
The blender is made up of the material of following parts by weight,
1 part of Chinese ephedra, 3 parts of Radix Isatidis, 2 parts of cassia twig, 3 parts of perilla leaf, 1 part of ginseng, 2 parts of reed rhizome, 3 parts of ginger, 1 part of pseudo-ginseng, 2 parts of the coptis；
Preparation method：Above-mentioned material is rinsed well with clear water, is then cut into sheet, natural drying shines surface water mark It is dry, the distillation processing that 5-6 hours are carried out in distillation equipment is then placed in, then remaining impurity, material are removed, stay the liquid after distillation Body.
Embodiment 2
The barrier coating that a kind of plastics spoon uses when making, it is characterised in that：It is made up of the material of following parts by weight,
It is 12 parts of ethanol, 12 parts of oyster shell whiting, 7 parts of organic siliconresin, 4 parts of ester gum, 5 parts of silicone oil, 6 parts of defoamer, poly- 4 parts of amide waxe, 8 parts of auxiliary agent, 5 parts of blender；
Comprise the following steps that,
Oyster shell whiting is put into 0.2% hydrochloric acid and soaked 5 minutes by I, is then placed in Muffle furnace and is heated to 650 DEG C, continues 2 Individual hour, the weight of hydrochloric acid is identical with the weight of oyster shell whiting, it is to be heated after the completion of 1 hour add blender and be stirred 12 points Clock；
II is put into organic siliconresin, ester gum, silicone oil, defoamer, polyamide wax in ethanol, is stirred 13 points Clock, to uniform；
III adds the material in I in II, adds auxiliary agent after being stirred 6 minutes, continues to be stirred 13 minutes；
IV will can be used after the material left 30 minutes after stirring, uniformly be applied to mould inner wall during use；
The auxiliary agent is made up of the material of following parts by weight,
8 parts of ethanol, 0.5 part of hydrofluoric acid, 1 part of titanium dioxide, 1 part of poly- glutaric acid propylene glycol ester, 0.5 part of coal tar, gelatin 4 Part, 7 parts of age resistor；
Production method includes,
Titanium dioxide, gelatin are put into iron pan and are stirred 12 minutes by I, add the pure of material gross weight 1/18 during stirring Water；
Hydrofluoric acid, poly- glutaric acid propylene glycol ester, coal tar are put into ethanol and stand 8 minutes by II, are then stirred 5 minutes；
III is put into the material in I and II in mixing plant, is stirred 7 minutes, then adds age resistor and continues stirring 8 Minute；
The blender is made up of the material of following parts by weight,
1 part of Chinese ephedra, 3 parts of Radix Isatidis, 2 parts of cassia twig, 3 parts of perilla leaf, 1 part of ginseng, 2 parts of reed rhizome, 3 parts of ginger, 1 part of pseudo-ginseng, 2 parts of the coptis；
Preparation method：Above-mentioned material is rinsed well with clear water, is then cut into sheet, natural drying shines surface water mark It is dry, the distillation processing that 5-6 hours are carried out in distillation equipment is then placed in, then remaining impurity, material are removed, stay the liquid after distillation Body.
The product of embodiment 1 and embodiment 2 is subjected to experimental analysis, carried out for its physical property and chemical property Data comparison, such as following table：
Toxicity Adhesion strength Corrosion resistance
Embodiment 1 Nothing Nothing Have
Embodiment 2 Nothing Nothing Have
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (3)

  1. A kind of 1. barrier coating that plastics spoon uses when making, it is characterised in that：It is made up of the material of following parts by weight,
    Ethanol 9-12 parts, oyster shell whiting 9-14 parts, organic siliconresin 5-8 parts, ester gum 4-7 parts, silicone oil 1-3 parts, defoamer 6-9 parts, polyamide wax 3-6 parts, auxiliary agent 7-10 parts, blender 3-6 parts；
    Comprise the following steps that,
    Oyster shell whiting is put into 0.1-0.2% hydrochloric acid and soaked 5 minutes by I, is then placed in Muffle furnace and is heated to 650 DEG C, is continued 2-3 hour, the weight of hydrochloric acid is identical with the weight of oyster shell whiting, it is to be heated after the completion of 1 hour add blender and be stirred 10-14 minutes；
    II is put into organic siliconresin, ester gum, silicone oil, defoamer, polyamide wax in ethanol, is stirred 10-14 points Clock, to uniform；
    III in the addition of the material in I II, will be stirred 5-7 minutes adds auxiliary agent afterwards, continues to be stirred 11-14 minutes；
    IV will can be used after the material left 30 minutes after stirring, uniformly be applied to mould inner wall during use.
  2. 2. the barrier coating that a kind of plastics spoon according to claim 1 uses when making, it is characterised in that：The auxiliary agent It is made up of the material of following parts by weight,
    It is 8 parts of ethanol, 0.5 part of hydrofluoric acid, 1 part of titanium dioxide, 1 part of poly- glutaric acid propylene glycol ester, 0.5 part of coal tar, 4 parts of gelatin, anti- Old 7 parts of agent；
    Production method includes,
    Titanium dioxide, gelatin are put into iron pan and are stirred 12 minutes by I, and the pure water of material gross weight 1/18 is added during stirring；
    Hydrofluoric acid, poly- glutaric acid propylene glycol ester, coal tar are put into ethanol and stand 8 minutes by II, are then stirred 5 minutes；
    III is put into the material in I and II in mixing plant, is stirred 7 minutes, then adds age resistor and continues stirring 8 minutes .
  3. 3. the barrier coating that a kind of plastics spoon according to claim 1 uses when making, it is characterised in that：The mediation Agent is made up of the material of following parts by weight,
    1 part of Chinese ephedra, 3 parts of Radix Isatidis, 2 parts of cassia twig, 3 parts of perilla leaf, 1 part of ginseng, 2 parts of reed rhizome, 3 parts of ginger, 1 part of pseudo-ginseng, the coptis 2 Part；
    Preparation method：Above-mentioned material to be rinsed well with clear water, is then cut into sheet, natural drying dries surface water mark, The distillation processing that 5-6 hours are carried out in distillation equipment is then placed in, then remaining impurity, material are removed, stay the liquid after distillation.
CN201710647680.XA 2017-08-01 2017-08-01 The barrier coating that a kind of plastics spoon uses when making Pending CN107446497A (en)