CN107325405A - A kind of plastics spoon for baby - Google Patents
A kind of plastics spoon for baby Download PDFInfo
- Publication number
- CN107325405A CN107325405A CN201710648289.1A CN201710648289A CN107325405A CN 107325405 A CN107325405 A CN 107325405A CN 201710648289 A CN201710648289 A CN 201710648289A CN 107325405 A CN107325405 A CN 107325405A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- ethanol
- weight
- baby
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of plastics spoon for baby, is related to Domestic plastic product processing and fabricating technical field, it is characterised in that：It is made up of the material of following parts by weight, 17 21 parts of acrylic resin, 24 parts of basalt powder, 13 parts of pulverized limestone, 35 parts of tallow, 79 parts of ethanol, 13 parts of talcum powder, 8 11 parts of coating agent.The inventive method is reasonable, easy to make, nontoxic, service life is permanent.
Description
Technical field
The present invention relates to Domestic plastic product processing and fabricating technical field, and in particular to a kind of plastics spoon for baby.
Background technology
Plastics are, using monomer as raw material, to pass through addition polymerization or the high-molecular compound of polycondensation polymerized
(macromolecules) plastics (plastics) or resin (resin), are commonly called as, can freely change composition and body styles,
It is made up of the additive such as synthetic resin and filler, plasticizer, stabilizer, lubricant, colorant.
The main component of plastics is resin.This noun of resin is gained the name by the lipid that animals and plants secret out of, such as
Rosin, shellac etc., resin refer to the high-molecular compound not yet mixed with various additives.Resin accounts for plastics gross weight
40%~100%.The basic performance of plastics depends mainly on the person's character of resin, but additive also plays an important role.Some modelings
Material is substantially made up of synthetic resin, is free of or is contained additive, such as lucite, polystyrene less.
So-called plastics, it is one kind in synthetic resin in fact, and shape is similar with the pine resin in natural resin, by changing
Learn to do section progress artificial synthesized, and be referred to as plastics.
The species of spoon is a lot, different materials, different colors, different sizes, for different things, he
Use be also different.
And spoon for baby typically there are two kinds, one it is stainless steel spoon, two is plastics spoon, stainless steel spoon quality
Firmly, service life is relatively long, but is due to metallic article, and the temperature of spoon is just held after being placed in relatively boiling hotter food etc.
Easily rise, harm is easily brought so when feeding and is damaged to the oral cavity of baby, and the spoon of plastics comparatively longevity
Life is shorter, and unqualified now with many plastics spoon materials, often there is the harmful substance of many, and the body of baby is good for
Health brings harm.
The content of the invention
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, making side
Just a kind of permanent plastics spoon for baby of, nontoxic, service life.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of plastics spoon for baby, it is characterised in that：It is made up of the material of following parts by weight,
17-21 parts of acrylic resin, 2-4 parts of basalt powder, 1-3 parts of pulverized limestone, 3-5 parts of tallow, 7-9 parts of ethanol, cunning
1-3 parts of stone flour, 8-11 parts of coating agent；
Including following preparation process,
I basalt powder is stirred in 40-45 DEG C of iron pan with pulverized limestone mix 10-13 minutes it is uniform, during stirring
Add the pure water of material gross weight 1/14；
Acrylic resin, tallow, talcum powder are added standing 10-13 minutes in ethanol by II, are then stirred 5 minutes；
III sequentially adds the material in I, II in mixing plant, stirring mixing 7-10 minutes；
IV is uniformly applied to coating agent on mould inner wall, is put into the compound in III wherein after 3 minutes, then carries out
Shaping；
The coating agent is made up of the material of following parts by weight,
9 parts of oyster shell whiting, 5 parts of organic siliconresin, 4 parts of ester gum, 2 parts of Ludox, 5 parts of defoamer, iron oxide red 1
Part, 9 parts of ethanol, 6 parts of age resistor；
Preparation process is as follows,
I is put into oyster shell whiting immersion 5 minutes in 0.1-0.2% hydrochloric acid, is then placed in Muffle furnace and is heated to 650 DEG C,
Continue 2-3 hour, the weight of hydrochloric acid is identical with oyster shell whiting；
II is put into organic siliconresin, ester gum, Ludox, iron oxide red in ethanol, 10-13 points of stirring mixing
Clock, to uniform, then adds defoamer, continues to stir 5-8 minutes；
III adds the material in I in II, stirs 5-7 minutes, then adds age resistor, continues to stir 6-8 minutes.
Beneficial effects of the present invention are：It is nontoxic after material mixing, human body is not damaged, and coating agent is being used
When ensure that mould and material are separated without forming attachment, will not damage mould, and mix material high temperature resistant,
Non-conducting high temperature, and baby likes beating thing, the hardness of product is high but is not easily broken, and life of product is long.The present invention
Method is reasonable, easy to make, nontoxic, service life is permanent.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
A kind of plastics spoon for baby, it is characterised in that：It is made up of the material of following parts by weight,
19 parts of acrylic resin, 3 parts of basalt powder, 1 part of pulverized limestone, 3 parts of tallow, 8 parts of ethanol, 1 part of talcum powder, parcel
8 parts of agent；
Including following preparation process,
I basalt powder is stirred in 4 DEG C of iron pan with pulverized limestone mix 11 minutes it is uniform, material is added during stirring
The pure water of gross weight 1/14；
Acrylic resin, tallow, talcum powder are added standing 12 minutes in ethanol by II, are then stirred 5 minutes；
III sequentially adds the material in I, II in mixing plant, stirring mixing 8 minutes；
IV is uniformly applied to coating agent on mould inner wall, is put into the compound in III wherein after 3 minutes, then carries out
Shaping；
The coating agent is made up of the material of following parts by weight,
9 parts of oyster shell whiting, 5 parts of organic siliconresin, 4 parts of ester gum, 2 parts of Ludox, 5 parts of defoamer, iron oxide red 1
Part, 9 parts of ethanol, 6 parts of age resistor；
Preparation process is as follows,
I is put into oyster shell whiting immersion 5 minutes in 0.1-% hydrochloric acid, is then placed in Muffle furnace and is heated to 650 DEG C, continues
2 hours, the weight of hydrochloric acid is identical with oyster shell whiting；
II is put into organic siliconresin, ester gum, Ludox, iron oxide red in ethanol, stirring mixing 10 minutes, extremely
Uniformly, defoamer is then added, continues to stir 6 minutes；
III adds the material in I in II, stirs 7 minutes, then adds age resistor, continues to stir 7 minutes.
Embodiment 2
A kind of plastics spoon for baby, it is characterised in that：It is made up of the material of following parts by weight,
20 parts of acrylic resin, 3 parts of basalt powder, 2 parts of pulverized limestone, 5 parts of tallow, 7 parts of ethanol, 2 parts of talcum powder, parcel
9 parts of agent；
Including following preparation process,
I basalt powder is stirred in 43 DEG C of iron pan with pulverized limestone mix 11 minutes it is uniform, material is added during stirring
Expect the pure water of gross weight 1/14；
Acrylic resin, tallow, talcum powder are added standing 12 minutes in ethanol by II, are then stirred 5 minutes；
III sequentially adds the material in I, II in mixing plant, stirring mixing 9 minutes；
IV is uniformly applied to coating agent on mould inner wall, is put into the compound in III wherein after 3 minutes, then carries out
Shaping；
The coating agent is made up of the material of following parts by weight,
9 parts of oyster shell whiting, 5 parts of organic siliconresin, 4 parts of ester gum, 2 parts of Ludox, 5 parts of defoamer, iron oxide red 1
Part, 9 parts of ethanol, 6 parts of age resistor；
Preparation process is as follows,
I is put into oyster shell whiting immersion 5 minutes in 0.1-% hydrochloric acid, is then placed in Muffle furnace and is heated to 650 DEG C, continues
2 hours, the weight of hydrochloric acid is identical with oyster shell whiting；
II is put into organic siliconresin, ester gum, Ludox, iron oxide red in ethanol, stirring mixing 10 minutes, extremely
Uniformly, defoamer is then added, continues to stir 6 minutes；
III adds the material in I in II, stirs 7 minutes, then adds age resistor, continues to stir 7 minutes.
The product of embodiment 1 and embodiment 2 is subjected to data experiment, its physics and chemical property is measured, data by
Shown in following table,
| Soft durometer | Intensity | Whether there is toxin | Resistance to elevated temperatures | |
| Embodiment 1 | It is softer | It is high | Nothing | ≤340℃ |
| Embodiment 2 | It is moderate | In | Nothing | ≤305℃ |
Note：Soft durometer is divided into：It is soft, softer, moderate, harder, hard；Intensity is divided into：It is high, medium and low；
Soft durometer be spoon for tooth, the soft or hard degree of the sensation of gum, intensity is bend resistance, measuring body ability.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of plastics spoon for baby, it is characterised in that：It is made up of the material of following parts by weight,
17-21 parts of acrylic resin, 2-4 parts of basalt powder, 1-3 parts of pulverized limestone, 3-5 parts of tallow, 7-9 parts of ethanol, talcum powder
1-3 parts, 8-11 parts of coating agent；
Including following preparation process,
I basalt powder is stirred in 40-45 DEG C of iron pan with pulverized limestone mix 10-13 minutes it is uniform, added during stirring
The pure water of material gross weight 1/14；
Acrylic resin, tallow, talcum powder are added standing 10-13 minutes in ethanol by II, are then stirred 5 minutes；
III sequentially adds the material in I, II in mixing plant, stirring mixing 7-10 minutes；
IV is uniformly applied to coating agent on mould inner wall, is put into wherein the compound in III after 3 minutes, then carries out into
Type.
2. a kind of plastics spoon for baby according to claim 1, it is characterised in that：The coating agent is by following weight
The material of part is made,
9 parts of oyster shell whiting, 5 parts of organic siliconresin, 4 parts of ester gum, 2 parts of Ludox, 5 parts of defoamer, 1 part of iron oxide red, second
9 parts of alcohol, 6 parts of age resistor；
Preparation process is as follows,
I is put into oyster shell whiting immersion 5 minutes in 0.1-0.2% hydrochloric acid, is then placed in Muffle furnace and is heated to 650 DEG C, continues
2-3 hour, the weight of hydrochloric acid is identical with oyster shell whiting；
II is put into organic siliconresin, ester gum, Ludox, iron oxide red in ethanol, stirring mixing 10-13 minutes, extremely
Uniformly, defoamer is then added, continues to stir 5-8 minutes；
III adds the material in I in II, stirs 5-7 minutes, then adds age resistor, continues to stir 6-8 minutes.