CN107419566A - A kind of preparation method of terylene linen blend fabric - Google Patents

A kind of preparation method of terylene linen blend fabric Download PDF

Info

Publication number
CN107419566A
CN107419566A CN201710463054.5A CN201710463054A CN107419566A CN 107419566 A CN107419566 A CN 107419566A CN 201710463054 A CN201710463054 A CN 201710463054A CN 107419566 A CN107419566 A CN 107419566A
Authority
CN
China
Prior art keywords
preparation
water outlet
degree
blend fabric
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710463054.5A
Other languages
Chinese (zh)
Inventor
李仁华
杭红莲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongtai Henghua Weaving Co Ltd
Original Assignee
Dongtai Henghua Weaving Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongtai Henghua Weaving Co Ltd filed Critical Dongtai Henghua Weaving Co Ltd
Priority to CN201710463054.5A priority Critical patent/CN107419566A/en
Publication of CN107419566A publication Critical patent/CN107419566A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of preparation method of terylene linen blend fabric, and in particular to fabric preparing technical field, including S1：Twisting, raw material wash chopped fiber and flax by mixing spun yarn, twisting from chopped fiber and flax is washed entirely, by complete；S2：Sizing, temperature are that 80 to 90 degree are shaped；S3：Metal, deoil wax, removes the oily wax contained in polyester staple fiber yarn；S4：Chlorine floats, and chlorine drifts out water and carries out chlorine drift again, allows fiber to open completely, removes the impurity water outlet in flaxen fiber；S5：Bobbin dyeing, cool water outlet after insulation；S6：Vital staining, water inlet are warming up to 100 degree of vital stainings, are incubated water outlet, then 40 degree of twice of heating of soaping of intaking；S7：Starching, in the oiling of pulp machine pit and wax；S8：Mercerized finish, soda bath concentration are 260 to 280g/l, water outlet sizing；S9：Fabric preshrunk.The present invention has is made fabric together by the two kinds of raw material blending of terylene flax, has crease-resistant, antibacterial, hydroscopic fast-drying, has the advantages of drapability, comfortable and easy to wear.

Description

A kind of preparation method of terylene linen blend fabric
Technical field
The present invention relates to fabric preparing technical field, and in particular to a kind of preparation method of terylene linen blend fabric.
Background technology
Linen-cotton fabric is a kind of blended yarn weaved fabric that people are most commonly encountered in life, and linen-cotton fabric is often related to being used for some And during among the environment of friction, such as mop, rag.Require higher for the anti-wear performance of linen-cotton fabric.It is untreated Linen-cotton fabric, after prolonged friction, linen-cotton fabric can produce certain abrasion, and fiber can be damaged, have impact on The performance of linen-cotton fabric.The anti-wear performance of linen-cotton fabric is improved, its loss after multiple friction is reduced, there are a variety of methods, need Will we be more deep study.
Traditional whole dyeing technique of linen-cotton fabric, including desizing, boiling-off, chlorine drift, preboarding, dyeing, drying, shaping process, First, before desizing process, removal of impurities processing is not done, the surface of fabric is more coarse, can influence whole dye effect；Secondly, drying After dry dyed shell fabrics, directly shaped, easily cause the fabric after dyeing, gauffer easily occur, further influence linen-cotton face The whole dye effect of material.
The invention discloses one to grow flax for patent flax fabric (publication date 2013.10.23, notification number CN103361830A) Fabric, including：Totally 4 kinds of raw material blending are made into and pass through dyeing for flax fiber, cotton synthetic fibre fiber, viscose filament rayon fiber and polyester fiber Agent is dyed, and mass percent of the described flax fiber in flax fabric is 35%~40%, described cotton synthetic fibre fiber Mass percent in flax fabric is 20%~25%, and mass percent of the described viscose filament yarn in flax fabric is 20%~25%, mass percent of the described polyester fiber in flax fabric is 10%~15%, and described coloring agent is Natural dyeing agent.This patent has the drawback that：It is more using raw material, and drapability is poor.
The content of the invention
Have the technical problem to be solved in the present invention is to provide one kind and face is made in the two kinds of raw material blending of terylene flax together Material, there is crease-resistant, antibacterial, hydroscopic fast-drying, have drapability, the preparation method of terylene linen blend fabric comfortable and easy to wear.
In order to solve the above-mentioned technical problem, the present invention provides a kind of preparation method of terylene linen blend fabric, including S1： Twisting, raw material wash chopped fiber and flax by mixing spun yarn, twisting from chopped fiber and flax is washed entirely, by complete；S2：Sizing, Temperature is that 80 to 90 degree are shaped；S3：Metal, deoil wax, removes the oily wax contained in polyester staple fiber yarn；S4：Chlorine floats, chlorine drift Water outlet carries out chlorine drift again, allows fiber to open completely, removes the impurity water outlet in flaxen fiber；S5：Bobbin dyeing, bobbin dyeing temperature are 125 degree Dye is scattered, and cool water outlet after insulation；S6：Vital staining, water inlet are warming up to 100 degree of vital stainings 50 to 55 minutes, insulation 35 to Water outlet in 40 minutes, then 40 degree of twice of heating of soaping of intaking；S7：Starching, in the oiling of pulp machine pit and wax；S8：Mercerized finish, burn Alkaline concentration is 260 to 280g/l, water outlet sizing；S9：Fabric preshrunk, it is ensured that preshrinking rate is less than 3%.
Preferably, the S1 with 21S fiber crops wash mixed yarn add 1 centimetre 4 sth. made by twisting.
Preferably, setting temperature is 90 degree in the S2, and sizing soaking time is to protect 45 minutes.
Preferably, the dye jitter time in the S5 is 60 minutes, is incubated 30-50 minutes.
Preferably, soaking time is 40 minutes in the S6.
Preferably, the vital staining time is 55 minutes in the S6.
Preferably, two kinds of activity is disperseed in the S6, dye material decibel disperses a kind of color, another color of activity, made Obtaining on an one thread has two kinds of colors so that Bamboo-shaped is presented in yarns, and then makes occur irregular ring on cloth cover so that face Material reaches the effect of good permeability, hydroscopic fast-drying and antibacterial.
Preferably, wax is atoleine in the S7.
Preferably, the speed of mercerized finish is 55-70 ms/min in the S8, and water outlet setting temperature is 175 degree, speed 45 ms/min.
Preferably, soda bath concentration is 260g/l in the S8.
Advantages of the present invention：
(1) two kinds of activity is disperseed, dye material decibel disperses a kind of color, another color of activity so that on an one thread There are two kinds of colors so that Bamboo-shaped is presented in yarns, and then makes occur irregular ring on cloth cover, so that fabric reaches ventilative Good, comfortable and easy to wear, the effect of hydroscopic fast-drying and antibacterial of property；
(2) terylene linen blend combines, and possesses crease-resistant, anti-bacterial wet-absorbing quick-drying, overhangs the advantages of property is preferable；
(3) easily arrange, it is comfortable and easy to wear.
Embodiment
Embodiment one
A kind of preparation method of terylene linen blend fabric of the present invention, including S1：Twisting, raw material are selected and wash chopped fiber entirely And flax, chopped fiber and flax are washed by mixing spun yarn, twisting by complete；S2：Sizing, temperature are 80 degree of sizings；S3：Metal, Deoil wax, removes the oily wax contained in polyester staple fiber yarn；S4：Chlorine floats, and chlorine drifts out water and carries out chlorine drift again, allows fiber to beat completely Open, remove the impurity water outlet in flaxen fiber；S5：Bobbin dyeing, bobbin dyeing temperature are that 125 degree of dyes are scattered, and dye jitter time is 60 minutes, is protected Cool water outlet after warm 30 minutes；S6：Vital staining, water inlet are warming up to 100 degree of vital stainings 50 minutes, are incubated water outlet in 35 minutes, Intake to soap again and heat 40 degree of twice；S7：Starching, in the oiling of pulp machine pit and wax；S8：Mercerized finish, mercerized finish speed For 55 ms/min, soda bath concentration is 280g/l, and water outlet is shaped；S9：Fabric preshrunk, it is ensured that preshrinking rate is less than 3%.
Embodiment two
A kind of preparation method of terylene linen blend fabric of the present invention, including S1：Twisting, raw material are selected and wash chopped fiber entirely And flax, chopped fiber and flax are washed by mixing spun yarn by complete, and washing mixed yarn with 21S fiber crops adds 1 centimetre of 4 sth. made by twisting；S2：Sizing, Temperature is 90 degree of sizings, and sizing soaking time is to protect 45 minutes；S3：Metal, deoil wax, removes and contains in polyester staple fiber yarn Oily wax；S4：Chlorine floats, and chlorine drifts out water and carries out chlorine drift again, allows fiber to open completely, removes the impurity water outlet in flaxen fiber；S5：Cylinder Dye, bobbin dyeing temperature is scattered for 125 degree of dyes, and dye jitter time is 60 minutes, and cool water outlet after being incubated 50 minutes；S6：Vital staining, Water inlet is warming up to 100 degree of vital stainings 55 minutes, is incubated water outlet in 40 minutes, then 40 degree of twice of heating of soaping of intaking；S7：Starching, In the oiling of pulp machine pit and wax；S8：Mercerized finish, soda bath concentration are 260g/l, and water outlet is shaped；S9：Fabric preshrunk, really Protect preshrinking rate and be less than 3%, disperse two kinds of activity, dye material decibel disperses a kind of color, another color of activity a so that yarn There are two kinds of colors on line so that Bamboo-shaped is presented in yarns, and then makes occur irregular ring on cloth cover, so that fabric reaches Good permeability, comfortable and easy to wear, the effect of hydroscopic fast-drying and antibacterial.
The preferred embodiment of innovation and creation is the foregoing is only, is not intended to limit the invention creation, it is all in this hair All any modification, equivalent and improvement made within the spirit and principle of bright creation etc., should be included in the invention Within protection domain.

Claims (10)

1. a kind of preparation method of terylene linen blend fabric, it is characterised in that comprise the following steps：
S1：Twisting, raw material wash chopped fiber and flax by mixing spun yarn, twisting from chopped fiber and flax is washed entirely, by complete；
S2：Sizing, temperature are that 80 to 90 degree are shaped；
S3：Metal, deoil wax, removes the oily wax contained in polyester staple fiber yarn；
S4：Chlorine floats, and chlorine drifts out water and carries out chlorine drift again, allows fiber to open completely, removes the impurity water outlet in flaxen fiber；
S5：Bobbin dyeing, bobbin dyeing temperature are that 125 degree of dyes are scattered, and cool water outlet after insulation；
S6：Vital staining, water inlet are warming up to 100 degree of vital stainings 50 to 55 minutes, are incubated water outlet in 35 to 40 minutes, then soap of intaking Wash 40 degree of twice of heating；
S7：Starching, in the oiling of pulp machine pit and wax；
S8：Mercerized finish, soda bath concentration are 260 to 280g/l, water outlet sizing；
S9：Fabric preshrunk, it is ensured that preshrinking rate is less than 3%.
A kind of 2. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：S1 is numb with 21S Wash mixed yarn and add 1 centimetre of 4 sth. made by twisting.
A kind of 3. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Shaped in S2 warm Spend for 90 degree, sizing soaking time is to protect 45 minutes.
A kind of 4. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Dye point in S5 It is 60 minutes to dissipate the time, is incubated 30-50 minutes.
A kind of 5. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：When being incubated in S6 Between be 40 minutes.
A kind of 6. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Activity dye in S6 The color time is 55 minutes.
A kind of 7. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Disperse to live in S6 Property two kinds, dye material decibel disperses a kind of color, another color of activity.
A kind of 8. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Wax is liquid in S7 Body paraffin.
A kind of 9. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Mercerising is whole in S8 The speed of reason is 55-70 ms/min, and water outlet setting temperature is 175 degree, 45 ms/min of speed.
A kind of 10. preparation method of terylene linen blend fabric according to claim 1, it is characterised in that：Caustic soda in S8 Solution concentration is 260g/l.
CN201710463054.5A 2017-06-19 2017-06-19 A kind of preparation method of terylene linen blend fabric Pending CN107419566A (en)