CN107419424A - A kind of Thermoheat hygroscopic heating fibers cloud blanket - Google Patents
A kind of Thermoheat hygroscopic heating fibers cloud blanket Download PDFInfo
- Publication number
- CN107419424A CN107419424A CN201710741571.4A CN201710741571A CN107419424A CN 107419424 A CN107419424 A CN 107419424A CN 201710741571 A CN201710741571 A CN 201710741571A CN 107419424 A CN107419424 A CN 107419424A
- Authority
- CN
- China
- Prior art keywords
- thermoheat
- fibers
- cloud
- cloud blanket
- blanket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Thermoheat hygroscopic heating fibers cloud blanket, the cloud blanket uses the suede yarn for cloud blanket with saw-tooth shaped cross section, ultra-fine, skin-core structure Thermoheat fibers, in the case where not influenceing cloud blanket its own advantages, the problems such as moisture absorption performance of cloud blanket greatly improved, make feeling of oppression and heat, easy static electrification, contamination dust is significantly improved;In addition, the present invention more optimizes the production technology of cloud blanket, the soft, antistatic of cloud blanket is further increased, fine hair is more neat, and feel is more plentiful.
Description
Technical field
The invention belongs to textile technology field, more particularly, to a kind of Thermoheat hygroscopic heating fibers cloud blanket.
Background technology
Cloud blanket be with science and technology, rapid economic development create it is a kind of with light, thin, the soft high-end product for theory.Cloud
Blanket dicoration, comfort level, service life etc. will be substantially better than traditional woollen blanket.Cloud blanket series of products have overturned woollen blanket completely
The features such as can not being machine-washed in cleaning process, and have the advantages that washing, machine-wash it is indeformable, do not influence hair side effect.
Relatively common cloud blanket species includes on the market:Composite water ripple embroiders mark cloud blanket, compound short flannel embroiders mark cloud blanket,
The compound nearly 50 kinds of specifications of three kinds of stamp cloud blanket.Cloud blanket plain color short flannel series of products are handled using advanced technologies, effectively
It ensure that product matte is neat and elastic, have the characteristics that good hand feeling, softness do not lose well-pressed, creative involvement fashion reason
Read, greatly improve product comfort level and aesthetics.Cloud blanket water ripples series of products are raw material from dacron ultrafine fiber, with spy
Different weaving process knits out height hair side style straggly, gives people that a kind of color is beautiful, strong art atmosphere of elegant, collocation
National tradition PROCESS FOR TREATMENT shows peculiar visual effect.Cloud blanket stamp series cloud blanket is by traditional woollen blanket production technology
Elite and Modern Home Textile theory perfect adaptation, using modern warp knit weaving, it is ensured that the smooth not hair loss of matte, when being equipped with brief
Modernization pattern still, even more shows its voguish style.
Dacron ultrafine fiber is selected in cloud blanket front in manufacturing process, and feel is smooth, and carpet surface has fluffy sense, while to flesh
Skin can be adapted to different coloring process, the color fastness and vividness on cloud blanket surface is effectively ensured without any stimulation, not allergy.But
It is worth noting that, traditional polyester fiber moisture pick-up properties is poor, official regain is only 0.4% or so, and process is being used in cloud blanket
Feeling of oppression and heat, while easily static electrification, contamination dust can be brought to user, influences attractive in appearance and comfortableness.And use other hygroscopicity
Good fiber(Such as viscose glue, wool)Weaved cloud blanket is difficult to possess the characteristics of light, thin, soft again.
The content of the invention
To overcome cloud blanket to bring feeling of oppression and heat, while easily static electrification, contamination dust to user using process, U.S. is influenceed
See and the problem of comfortableness, the present invention provides a kind of Thermoheat hygroscopic heating fibers cloud blanket, realize existing conventional cloud blanket gently,
The characteristics of thin, soft, there is warming, moisture absorption comfort again.
The present invention is realized by following technology:
A kind of Thermoheat hygroscopic heating fibers cloud blanket, the cloud blanket are using ultra-fine and section to be zigzag
Thermoheat fibers are suede yarn, weave and form on tricot machine using dacron thread as bottom silk, and the suede yarn is by 80~120 tools
It is made up of cortex and core structure Thermoheat fibers, the cortex is synthetic fibers polymer, and the sandwich layer is received for heat accumulation
Ground rice end and the mixture of synthetic fibers polymer
For common cloud blanket using the polyester fiber that cross section is circle as knitting wool, prepared cloud blanket has the characteristics of light, thin, soft
, production cost can also be greatly lowered, but also bring the feeling of oppression and heat of cloud blanket, easy static electrification simultaneously, stain the problems such as dust.
In the present invention, inventor uses special-shaped synthetic fibers, i.e., is suede yarn with zigzag Thermoheat fibers.Prepare
The polymer of Thermoheat fibers can be PET, polyethylene, polypropylene or polyamide.Sawtooth is special-shaped to be cut
The Thermoheat fibers in face form a lot of groove, have wicking, the steam or drop discharged beneficial to human body to
Outside export, the feeling of oppression and heat of cloud blanket is greatly lowered.
In the present invention, used Thermoheat fibers not only have profiled-cross-section, and inventor is more spun using melting
Skin-core structure has been made in silk method.Cortex is synthetic fibers polymer, and its composition and the synthetic fibers of routine are no different, only in section
It is otherwise varied in shape.It is important that the design of sandwich layer, the sandwich layer composition of Thermoheat fibers is heat accumulation nanometer powder and conjunction
The mixture of fiber-fonning polymer.Heat accumulation nanometer powder uses one kind or composition in carborundum and zirconium carbide.
Delustering agent is not used in Thermoheat fibers, belongs to full lustrous fibre, and outer layer is transparent polymer, and light can be directed through and shine
Sandwich layer is mapped to, the heat accumulation nanometer powder, which can be realized, converts light energy into heat energy, improves the cloud blanket thermal property of knitted system.
Preferably, the fiber number of the Thermoheat fibers is 1~2D.
It is generally believed that synthetic fibers of the fiber number less than 3.5D are superfine fibres.In the case of identical weight, superfine fibre
With bigger specific surface area, larger specific surface area means higher surface energy, can adsorb dynamic water as much as possible
Son, the moisture pick-up properties of synthetic fibers is improved, make the easy static electrification of terylene, contamination dirt problems obtain significantly improving.Separately
Outside, the absorption of Dynamic Water molecule realizes kinetic energy and is transformed into heat energy, improve the temperature of cloud blanket to a certain extent into Static Water.
Preferably, the heat accumulation nanometer powder is one kind or composition in carborundum and zirconium carbide.
Preferably, heat accumulation nanometer powder and synthetic fibers polymer quality ratio are 1 in sandwich layer:60~80.
In theory, the lifting of the content of heat accumulation nanometer powder will be helpful to improve in Thermoheat core fiber layers
The heat accumulation thermal property of Thermoheat fibers, but during spinning, the lifting of heat accumulation nanometer powder dosage will shadow
Ring the rheological property of melt so that viscosity improves, and fiber easily produces broken end, influences spinning efficiency.Study and find through inventor,
Under identical particle diameter, heat accumulation nanometer powder and synthetic fibers polymer quality ratio are 1 in sandwich layer:Under the conditions of 60~80, melt
Spinning properties there is no too much influence, can be achieved smooth spinning requirement.
Preferably, the synthetic fibers polymer is PET, polyethylene, polypropylene or polyamide.
Preferably, the zigzag Thermoheat fibers are prepared using melt spinning, the single hole face of spinneret
Product is 0.3~0.5mm2, spinneret orifice is in regular zigzags, and the number of teeth is 15~25, a height of 0.2~0.5mm of tooth.
Preferably, the production stage of the cloud blanket is as follows:
1)Select raw material:Selection Thermoheat fibers are suede yarn, 150~200D/120~144F dacron thread as bottom silk,
By weight percentage, suede yarn 70~78%, bottom silk 22~30%;
2)Weaving:Complete to weave using tricot machine, wherein 14~18mm of knocking-over bar gauge, the high 3~5mm of hair, fabric weight are 300
~450g/m2;
3)Preliminary finish:Bristle is carried out after 130~140 DEG C of 25~45s of preliminary drying, bristle finishes, clot;
4)Stamp:Prepare print paste and stamp is carried out to cloud blanket;
5)Drying;The cloud blanket that stamp finishes is transferred to drying in baking oven, and drying temperature is 140~150 DEG C, and criteria thus the drying time is 10~
15min;
6)Steaming and color fixing:Using evaporate method to stamp cloud blanket carry out fixation, color fixing temperature be 130~135 DEG C, the time be 25~
30min;
7)Washing:Stamp cloud blanket that fixation finishes is immersed in 30~40 DEG C of water lotions and washed, in water lotion containing 0.1~
0.2g/L antistatic additive and 0.1~0.2g/L neutral detergent;
8)Soft treatment:By cloud blanket after washing with bath raio 1:Carried out in 10~15 immersion amino-silicone oil softening agent dressing liquids soft
Supple-settlement, the dosage of amino-silicone oil softening agent are the 5~8% of fabric weight, the temperature of amino-silicone oil softening agent dressing liquid for 45~
55℃;
9)Scald and cut:Fabric after soft treatment is subjected to bristle after 130~140 DEG C of 30~40s of preliminary drying, bristle finishes, successively
Scalded by 165~170 DEG C, 155~160 DEG C, three of 145~150 DEG C and cut combination machine, speed is 12~15m/min;Scald and cut weight
Multiple operation is twice;
10)Finished product:The cloud blanket cut-parts after cutting will be scalded, bound edge gets product Thermoheat hygroscopic heating fibers cloud blankets.
Relative to the production technology of traditional cloud blanket, the composition and knot of the invention according to the Thermoheat fibers spinned
Structure feature, through adjusting processing parameter repeatedly, the production of Thermoheat hygroscopic heating fibers cloud blankets is set smoothly to enter
OK.In addition, scalding in shearing process, traditional method use 1~2 boiling hot shearing machine, scalds for 1 time and to cut, in the present invention, inventor uses 3
Scald shearing machine, 2 times scald cut, the results showed that, obtained cloud blanket fine hair is more neat, and feel is more plentiful.
The beneficial effects of the present invention are:1)Design and use with saw-tooth shaped cross section, ultra-fine Thermoheat fibers
For the suede yarn of cloud blanket, in the case where not influenceing cloud blanket its own advantages, the moisture absorption performance of cloud blanket greatly improved, make sultry
The problems such as sense, easy static electrification, contamination dust, is significantly improved;2)Design and use the Thermoheat of skin-core structure fine
Dimension, sandwich layer using heat accumulation nanometer powder and synthetic fibers polymer mixture, heat accumulation nanometer powder have good heat absorption and
The characteristics of heat accumulation, improve the thermal property of cloud blanket.3)The production technology of cloud blanket is optimized, further increases the soft of cloud blanket
Soft, antistatic, fine hair is more neat, and feel is more plentiful.
Embodiment
The present invention is further illustrated below.
Embodiment 1
A kind of Thermoheat hygroscopic heating fibers cloud blanket obtained by the present embodiment, is using ultra-fine and section to be zigzag
Thermoheat fibers are suede yarn, weave and form on tricot machine using dacron thread as bottom silk.Suede yarn by 80 have cortex and
Core structure Thermoheat fibers(Fiber number is 1D)Composition, the raw material of cortex are PET, the original of sandwich layer
Expect the mixture for zirconium carbide nanometer powder and PET.Zirconium carbide nanometer powder is with gathering to benzene two in sandwich layer
The mass ratio of formic acid second diester is 1:60.Thermoheat fibers are prepared by melt spinning.
The production stage of cloud blanket is as follows:
1)Select raw material:It is suede yarn to select Thermoheat fibers, and 150D/120F dacron thread is as bottom silk, by weight percentage
Than meter, suede yarn 70%, bottom silk 30%;
2)Weaving:Complete to weave using tricot machine, wherein knocking-over bar gauge 14mm, the high 3mm of hair, fabric weight are 300g/m2;
3)Preliminary finish:Bristle is carried out after 130 DEG C of preliminary drying 45s, bristle finishes, clot;
4)Stamp:Prepare print paste and stamp is carried out to cloud blanket;
5)Drying;The cloud blanket that stamp finishes is transferred to drying in baking oven, and drying temperature is 140 DEG C, criteria thus the drying time 15min;
6)Steaming and color fixing:Method is evaporated using high pressure fixation is carried out to stamp cloud blanket, color fixing temperature is 130 DEG C, and the time is
30min;
7)Washing:The stamp cloud blanket that fixation finishes is immersed in 30 DEG C of water lotions and washed, contains 0.1g/L's in water lotion
Antistatic additive(It is commercially available)With 0.1g/L neutral detergent(It is commercially available);
8)Soft treatment:By cloud blanket after washing with bath raio 1:Soft place is carried out in 10 immersion amino-silicone oil softening agent dressing liquids
Reason, the dosage of amino-silicone oil softening agent are the 5% of fabric weight, and the temperature of amino-silicone oil softening agent dressing liquid is 45 DEG C;
9)Scald and cut:Fabric after soft treatment is subjected to bristle after 130 DEG C of preliminary drying 40s, bristle finishes, pass sequentially through 165 DEG C,
155 DEG C, three of 145 DEG C scald and cut combination machine, speed 12m/min;Scald to cut and repeat twice;
10)Finished product:The cloud blanket cut-parts after cutting will be scalded, bound edge gets product Thermoheat hygroscopic heating fibers cloud blankets.
According to GB/T 6503-2008《Chemical fibre regain test method》Standard is to prepared by the present embodiment
Thermoheat hygroscopic heating fibers cloud blankets are tested, and the regain for measuring Thermoheat hygroscopic heating fibers cloud blankets is
3.6%, the regain is far above the 0.4% of ordinary polyester fiber official regain, illustrates the obtained Thermoheat of this implementation
Hygroscopic heating fibers cloud blanket has good moisture pick-up properties.
Embodiment 2
A kind of Thermoheat hygroscopic heating fibers cloud blanket obtained by the present embodiment, is using ultra-fine and section to be zigzag
Thermoheat fibers are suede yarn, weave and form on tricot machine using dacron thread as bottom silk.Suede yarn by 120 have cortex and
Core structure Thermoheat fibers(Fiber number is 2D)Composition, the raw material of cortex are PET, the original of sandwich layer
Expect for nanometer silicon carbide powder and polyacrylic mixture.Nanometer silicon carbide powder and polyacrylic mass ratio are 1 in sandwich layer:
80.Thermoheat fibers are prepared by melt spinning.
The production stage of cloud blanket is as follows:
1)Select raw material:It is suede yarn to select Thermoheat fibers, and 200D/144F dacron thread is as bottom silk, by weight percentage
Than meter, suede yarn 78%, bottom silk 22%;
2)Weaving:Complete to weave using tricot machine, wherein knocking-over bar gauge 16mm, the high 5mm of hair, fabric weight are 450g/m2;
3)Preliminary finish:Bristle is carried out after 140 DEG C of preliminary drying 25s, bristle finishes, clot;
4)Stamp:Prepare print paste and stamp is carried out to cloud blanket;
5)Drying;The cloud blanket that stamp finishes is transferred to drying in baking oven, and drying temperature is 150 DEG C, criteria thus the drying time 10min;
6)Steaming and color fixing:Method is evaporated using high pressure fixation is carried out to stamp cloud blanket, color fixing temperature is 135 DEG C, and the time is
25min;
7)Washing:The stamp cloud blanket that fixation finishes is immersed in 40 DEG C of water lotions and washed, contains 0.2g/L's in water lotion
The neutral detergent of antistatic additive and 0.2g/L;
8)Soft treatment:By cloud blanket after washing with bath raio 1:Soft place is carried out in 15 immersion amino-silicone oil softening agent dressing liquids
Reason, the dosage of amino-silicone oil softening agent are the 8% of fabric weight, and the temperature of amino-silicone oil softening agent dressing liquid is 55 DEG C;
9)Scald and cut:Fabric after soft treatment is subjected to bristle after 140 DEG C of preliminary drying 30s, bristle finishes, pass sequentially through 170 DEG C,
160 DEG C, three of 150 DEG C scald and cut combination machine, speed 15m/min;Scald to cut and repeat twice;
10)Finished product:The cloud blanket cut-parts after cutting will be scalded, bound edge gets product Thermoheat hygroscopic heating fibers cloud blankets.
According to GB/T 6503-2008《Chemical fibre regain test method》Standard is to prepared by the present embodiment
Thermoheat hygroscopic heating fibers cloud blankets are tested, and the regain for measuring Thermoheat hygroscopic heating fibers cloud blankets is
3.2%, the regain is far above 0.0%, the 0.4% of ordinary polyester fiber official regain of normal polypropylene fiber official regain,
Illustrate that the obtained Thermoheat hygroscopic heating fibers cloud blankets of this implementation have good moisture pick-up properties.
Embodiment 3
A kind of Thermoheat hygroscopic heating fibers cloud blanket obtained by the present embodiment, is using ultra-fine and section to be zigzag
Thermoheat fibers are suede yarn, weave and form on tricot machine using dacron thread as bottom silk.Suede yarn by 130 have cortex and
Core structure Thermoheat fibers(Fiber number is 1.5D)Composition, the raw material of cortex is PET, sandwich layer
Raw material is the mixture of nanometer silicon carbide powder and polyamide.The mass ratio of nanometer silicon carbide powder and polyamide is 1 in sandwich layer:
70.Thermoheat fibers are prepared by melt spinning.
The production stage of cloud blanket is as follows:
1)Select raw material:It is suede yarn to select Thermoheat fibers, and 180D/136F dacron thread is as bottom silk, by weight percentage
Than meter, suede yarn 75%, bottom silk 25%;
2)Weaving:Complete to weave using tricot machine, wherein knocking-over bar gauge 15mm, the high 4mm of hair, fabric weight are 350g/m2;
3)Preliminary finish:Bristle is carried out after 135 DEG C of preliminary drying 35s, bristle finishes, clot;
4)Stamp:Prepare print paste and stamp is carried out to cloud blanket;
5)Drying;The cloud blanket that stamp finishes is transferred to drying in baking oven, and drying temperature is 145 DEG C, criteria thus the drying time 12min;
6)Steaming and color fixing:Method is evaporated using high pressure fixation is carried out to stamp cloud blanket, color fixing temperature is 132 DEG C, and the time is
28min;
7)Washing:The stamp cloud blanket that fixation finishes is immersed in 35 DEG C of water lotions and washed, contains 0.15g/L's in water lotion
The neutral detergent of antistatic additive and 0.15g/L;
8)Soft treatment:By cloud blanket after washing with bath raio 1:Soft place is carried out in 12 immersion amino-silicone oil softening agent dressing liquids
Reason, the dosage of amino-silicone oil softening agent are the 6% of fabric weight, and the temperature of amino-silicone oil softening agent dressing liquid is 50 DEG C;
9)Scald and cut:Fabric after soft treatment is subjected to bristle after 135 DEG C of preliminary drying 35s, bristle finishes, pass sequentially through 168 DEG C,
158 DEG C, three of 148 DEG C scald and cut combination machine, speed 13m/min;Scald to cut and repeat twice;
10)Finished product:The cloud blanket cut-parts after cutting will be scalded, bound edge gets product Thermoheat hygroscopic heating fibers cloud blankets.
According to GB/T 6503-2008《Chemical fibre regain test method》Standard is to prepared by the present embodiment
Thermoheat hygroscopic heating fibers cloud blankets are tested, and the regain for measuring Thermoheat hygroscopic heating fibers cloud blankets is
7.2%, the regain is far above the 4.5% of common polyamide fiber official regain, ordinary polyester fiber official regain
0.4%, illustrate that the obtained Thermoheat hygroscopic heating fibers cloud blankets of this implementation have good moisture pick-up properties.
Claims (7)
- A kind of 1. Thermoheat hygroscopic heating fibers cloud blanket, it is characterised in that the Thermoheat hygroscopic heating fibers It by zigzag Thermoheat fibers of ultra-fine and section is suede yarn that cloud blanket, which is, is knitted using dacron thread as bottom silk on tricot machine To make and form, the suede yarn is made up of 80~120 Thermoheat fibers, and the Thermoheat fibers have skin-core structure, The cortex of Thermoheat fibers is synthetic fibers polymer, and sandwich layer is the mixing of heat accumulation nanometer powder and synthetic fibers polymer Thing.
- 2. a kind of Thermoheat hygroscopic heating fibers cloud blanket according to claim 1, it is characterised in that described The fiber number of Thermoheat fibers is 1~2D.
- A kind of 3. Thermoheat hygroscopic heating fibers cloud blanket according to claim 1 or 2, it is characterised in that the storage Hot nanometer powder is one or both of carborundum, zirconium carbide.
- 4. a kind of Thermoheat hygroscopic heating fibers cloud blanket according to claim 1 or 2, it is characterised in that in sandwich layer Heat accumulation nanometer powder is 1 with synthetic fibers polymer quality ratio:60~80.
- A kind of 5. Thermoheat hygroscopic heating fibers cloud blanket according to claim 1 or 2, it is characterised in that the conjunction Fiber-fonning polymer is PET, polyethylene, polypropylene or polyamide.
- 6. a kind of Thermoheat hygroscopic heating fibers cloud blanket according to claim 1 or 2, it is characterised in that described Thermoheat fibers are prepared using melt spinning, and the single hole area of spinneret is 0.3~0.5mm2, spinneret orifice is in rule Zigzag, the number of teeth are 15~25, a height of 0.2~0.5mm of tooth.
- 7. a kind of Thermoheat hygroscopic heating fibers cloud blanket according to claim 1 or 2, it is characterised in that described The production stage of Thermoheat hygroscopic heating fibers cloud blankets is as follows:1)Select raw material:Selection Thermoheat fibers are suede yarn, 150~200D/120~144F dacron thread as bottom silk, By weight percentage, suede yarn 70~78%, bottom silk 22~30%;2)Weaving:Complete to weave using tricot machine, wherein 14~18mm of knocking-over bar gauge, the high 3~5mm of hair, fabric weight are 300 ~450g/m2;3)Preliminary finish:Bristle is carried out after 130~140 DEG C of 25~45s of preliminary drying, bristle finishes, clot;4)Stamp:Prepare print paste and stamp is carried out to cloud blanket;5)Drying;The cloud blanket that stamp finishes is transferred to drying in baking oven, and drying temperature is 140~150 DEG C, and criteria thus the drying time is 10~ 15min;6)Steaming and color fixing:Using evaporate method to stamp cloud blanket carry out fixation, color fixing temperature be 130~135 DEG C, the time be 25~ 30min;7)Washing:Stamp cloud blanket that fixation finishes is immersed in 30~40 DEG C of water lotions and washed, in water lotion containing 0.1~ 0.2g/L antistatic additive and 0.1~0.2g/L neutral detergent;8)Soft treatment:By cloud blanket after washing with bath raio 1:Carried out in 10~15 immersion amino-silicone oil softening agent dressing liquids soft Supple-settlement, the dosage of amino-silicone oil softening agent are the 5~8% of fabric weight, the temperature of amino-silicone oil softening agent dressing liquid for 45~ 55℃;9)Scald and cut:Fabric after soft treatment is subjected to bristle after 130~140 DEG C of 30~40s of preliminary drying, bristle finishes, successively Scalded by 165~170 DEG C, 155~160 DEG C, three of 145~150 DEG C and cut combination machine, speed is 12~15m/min;Scald and cut weight Multiple operation is twice;10)Finished product:The cloud blanket cut-parts after cutting will be scalded, bound edge gets product Thermoheat hygroscopic heating fibers cloud blankets.