CN107418439A - The wear resistant processing method of metallic article - Google Patents
The wear resistant processing method of metallic article Download PDFInfo
- Publication number
- CN107418439A CN107418439A CN201710539102.4A CN201710539102A CN107418439A CN 107418439 A CN107418439 A CN 107418439A CN 201710539102 A CN201710539102 A CN 201710539102A CN 107418439 A CN107418439 A CN 107418439A
- Authority
- CN
- China
- Prior art keywords
- metallic article
- parts
- spray coating
- coating liquor
- sprayed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention disclose a kind of wear resistant processing method of metallic article, and it includes pending metallic article being put into cleaning fluid, its surface clean is clean, drying, polishes;Metallic article is cooled down, spray coating liquor then is preliminarily sprayed to its surface;Then, metallic article is cooled down again, and spray coating liquor is preliminarily sprayed to its surface again, finally dried;Wherein, spray coating liquor used is sprayed twice to be made up of following raw material:Sodium sulphate, sodium carbonate, potassium chloride, boric acid, nano silicon, nano zine oxide, nanometer hydromica, rosin resin and water.The present invention utilizes the principle expanded with heat and contract with cold, metallic article is cooled down twice, sprayed twice, and by adding sodium sulphate, sodium carbonate, potassium chloride, boric acid, nano silicon, nano zine oxide, nanometer hydromica, rosin resin, so as to increase its permeability and adhesive force, the purpose for improving surface of metal product wearability is finally reached.
Description
Technical field
The present invention relates to metallic article processing technology field, more particularly to a kind of wear resistant processing method of metallic article.
Background technology
Steel Wire Products Industry includes structured metal product manufacture, metal tools manufacture, container and packaging container of metal
Manufacture, stainless steel and similar daily metallic article manufacture etc..With the progress of society and the development of science and technology, metallic article is in work
The utilization of industry, agricultural and the various fields of recent life of people is more and more extensive, also the value increasing to social creativity.
However, no matter how excellent using material, how accurate machining accuracy is, and surface of metal product is seen under the microscope
Examine, always cloth is all over pit and gap, thus the phenomenon of abrasion occurs.And due to the presence of wear phenomenon so that for it is metallurgical,
Metallic article workpiece and equipment in the industries such as mine, harbour, electric power, coal, building materials and military affairs and fail rapidly, caused by it
Economic loss is quite surprising.Therefore, how improving its abrasion resistance properties will be following desired raising metallic article quality
Key technique.
The content of the invention
The present invention provides a kind of wear resistant processing method of metallic article, and the wear resistant processing method can solve existing metal system
The problem of product wear extent is big.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is:
It comprises the following steps:
A. pending metallic article is put into cleaning fluid, its surface clean is clean, drying;
B. the metallic article by step A processing is polished with sand paper;
C. the metallic article Jing Guo step B grinding process is cooled to 5 DEG C~10 DEG C, temperature then, which is preliminarily sprayed, to its surface is
100 DEG C~150 DEG C of spray coating liquor;Then, metallic article is cooled to 5 DEG C~10 DEG C again, and its surface is preliminarily sprayed again
Temperature is 100 DEG C~150 DEG C of spray coating liquor;Wherein, it is by the raw material of following parts by weight to spray spray coating liquor used twice
It is made:4 parts~6 parts of sodium sulphate, 1 part~3 parts of sodium carbonate, 0.5 part~1 part of potassium chloride, 0.4 part~0.6 part of boric acid, nano-silica
1 part~5 parts of SiClx, 5 parts~10 parts of 1 part~5 part, nanometer hydromica of nano zine oxide, 15 parts~20 parts of rosin resin and water 5
Part~10 parts;
D. the metallic article by step C processing is incubated drying at 100 DEG C~150 DEG C.
Due to using above-mentioned technical proposal, the beneficial effect that the present invention obtains is:
Metallic article is cooled down, sprayed twice using the principle expanded with heat and contract with cold by the present invention twice, and by add sodium sulphate,
Sodium carbonate, potassium chloride, boric acid, nano silicon, nano zine oxide, nanometer hydromica, rosin resin, so as to increase its infiltration
Property and adhesive force, be finally reached improve surface of metal product wearability purpose.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only limited to
In following examples.
Embodiment 1 --- metallic article it is wear-resisting go out processing method
It comprises the following steps:
A. pending metallic article is put into cleaning fluid, its surface clean is clean, drying;
B. the metallic article by step A processing is polished with sand paper;
C. the metallic article Jing Guo step B grinding process is cooled to 5 DEG C, it is 100 DEG C then its surface to be preliminarily sprayed temperature
Spray coating liquor;Then, metallic article is cooled to 5 DEG C again, and its surface is preliminarily sprayed again the spray coating liquor that temperature is 100 DEG C;
Wherein, spray coating liquor used is sprayed twice to be prepared from the following raw materials in parts by weight:4 parts of sodium sulphate, 1 part of sodium carbonate, chlorine
Change 0.5 part of potassium, 0.4 part of boric acid, 1 part of nano silicon, 5 parts of 1 part, nanometer hydromica of nano zine oxide, 15 parts of rosin resin
And 5 parts of water;
D. the metallic article by step C processing is incubated drying at 100 DEG C.
After testing, normal temperature wear extent≤1cm of the surface of metal product after the present embodiment is handled3。
Embodiment 2 --- metallic article it is wear-resisting go out processing method
It comprises the following steps:
A. pending metallic article is put into cleaning fluid, its surface clean is clean, drying;
B. the metallic article by step A processing is polished with sand paper;
C. the metallic article Jing Guo step B grinding process is cooled to 10 DEG C, it is 150 DEG C then its surface to be preliminarily sprayed temperature
Spray coating liquor;Then, metallic article is cooled to 10 DEG C again, and its surface is preliminarily sprayed again the spray coating liquor that temperature is 150 DEG C;
Wherein, spray coating liquor used is sprayed twice to be prepared from the following raw materials in parts by weight:6 parts of sodium sulphate, 3 parts of sodium carbonate, chlorine
Change 1 part of potassium, 0.6 part of boric acid, 5 parts of nano silicon, 10 parts of 5 part, nanometer hydromica of nano zine oxide, 20 parts of rosin resin with
And 10 parts of water;
D. the metallic article by step C processing is incubated drying at 150 DEG C.
After testing, normal temperature wear extent≤1cm of the surface of metal product after the present embodiment is handled3。
Embodiment 3 --- metallic article it is wear-resisting go out processing method
It comprises the following steps:
A. pending metallic article is put into cleaning fluid, its surface clean is clean, drying;
B. the metallic article by step A processing is polished with sand paper;
C. the metallic article Jing Guo step B grinding process is cooled to 8 DEG C, it is 120 DEG C then its surface to be preliminarily sprayed temperature
Spray coating liquor;Then, metallic article is cooled to 8 DEG C again, and its surface is preliminarily sprayed again the spray coating liquor that temperature is 120 DEG C;
Wherein, spray coating liquor used is sprayed twice to be prepared from the following raw materials in parts by weight:5 parts of sodium sulphate, 2 parts of sodium carbonate, chlorine
Change 0.8 part of potassium, 0.5 part of boric acid, 4 parts of nano silicon, 8 parts of 4 part, nanometer hydromica of nano zine oxide, 19 parts of rosin resin
And 8 parts of water;
D. the metallic article by step C processing is incubated drying at 120 DEG C.
After testing, normal temperature wear extent≤1cm of the surface of metal product after the present embodiment is handled3。
Claims (1)
1. a kind of wear resistant processing method of metallic article, it is characterised in that comprise the following steps:
A. pending metallic article is put into cleaning fluid, its surface clean is clean, drying;
B. the metallic article by step A processing is polished with sand paper;
C. the metallic article Jing Guo step B grinding process is cooled to 5 DEG C~10 DEG C, temperature then, which is preliminarily sprayed, to its surface is
100 DEG C~150 DEG C of spray coating liquor;Then, metallic article is cooled to 5 DEG C~10 DEG C again, and its surface is preliminarily sprayed again
Temperature is 100 DEG C~150 DEG C of spray coating liquor;Wherein, it is by the raw material of following parts by weight to spray spray coating liquor used twice
It is made:4 parts~6 parts of sodium sulphate, 1 part~3 parts of sodium carbonate, 0.5 part~1 part of potassium chloride, 0.4 part~0.6 part of boric acid, nano-silica
1 part~5 parts of SiClx, 5 parts~10 parts of 1 part~5 part, nanometer hydromica of nano zine oxide, 15 parts~20 parts of rosin resin and water 5
Part~10 parts;
D. the metallic article by step C processing is incubated drying at 100 DEG C~150 DEG C.