CN108789179A - A kind of abrasive wheel for abrasion of steel ball formula - Google Patents
A kind of abrasive wheel for abrasion of steel ball formula Download PDFInfo
- Publication number
- CN108789179A CN108789179A CN201810535218.5A CN201810535218A CN108789179A CN 108789179 A CN108789179 A CN 108789179A CN 201810535218 A CN201810535218 A CN 201810535218A CN 108789179 A CN108789179 A CN 108789179A
- Authority
- CN
- China
- Prior art keywords
- parts
- abrasive
- abrasion
- steel ball
- wheel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to grinding wheel technical fields, specifically disclose a kind of abrasive wheel for abrasion of steel ball formula of the present invention, are made from the following raw materials in parts by weight：A kind of abrasive wheel for abrasion of steel ball formula, is made from the following raw materials in parts by weight：18~24 parts of brown corundum abrasive, 6~12 parts of white fused alumina abrasive material, 10~20 parts of silicon carbide abrasive, 20~30 parts of feldspar, 15~20 parts of clay, 2~5 parts of boron glass, 25~40 parts of bonding agent, the present invention overcomes the deficiencies in the prior art, utilize brown corundum abrasive, white fused alumina abrasive material, silicon carbide abrasive, feldspar, clay, boron glass, bonding agent produce abrasive wheel for abrasion of steel ball, not only having higher durability again has higher grinding efficiency, while heat resistance is good, the high yield rate in roasting.
Description
Technical field
The present invention relates to grinding wheel technical fields, particularly belong to a kind of abrasive wheel for abrasion of steel ball formula.
Background technology
Abrasive wheel for abrasion of steel ball be for be ground diameter 76.20mm or less spherical balls special grinding wheel, have specification it is big,
The features such as fine size, hardness are high, density is big is widely used in machinery, bearing industry.Currently, all abrasive wheel for abrasion of steel ball factories
Family is all using the compound abrasive of Brown Alundum and silicon carbide manufacture abrasive wheel for abrasion of steel ball, because mill steel sand wheel is close when being formulated design
Degree is big, hardness is high, simple to have certain limit to improve its density using improving typed pressure, thus have after requiring grinding wheel burning compared with
It is big to shrink to improve grinding wheel density.And the refractoriness of bonding agent is unsuitable higher, therefore, is such as ground using the fine granularity of single Brown Alundum
Material, because wherein impurity content is higher, grinding wheel roasting process easily entirely foams；It is suitably added silicon carbide abrasive, product can be improved
Performance, be conducive to improve product intensity and hardness.But with the development of national economy, grinding wheel is using producer to grinding steel ball sand
The requirement of wheel is higher and higher, not only requires grinding wheel to have higher durability, while also requiring it with higher grinding efficiency.
It is well known that abrasive wheel for abrasion of steel ball to be made to have higher durability, then the hardness of grinding wheel is higher, and at this moment its grinding efficiency declines；
Conversely, to improve grinding efficiency, then the hardness of grinding wheel must be reduced, durability declines.Therefore, abrasive wheel for abrasion of steel ball is not being reduced
Hardness under the premise of, improve its grinding efficiency, improve heat resistance and grinding wheel obtain yield rate, become the one of grinding wheel manufacturing
A problem.
Invention content
The object of the present invention is to provide a kind of abrasive wheel for abrasion of steel ball formulas, overcome the deficiencies in the prior art, just using palm fibre
Beautiful abrasive material, white fused alumina abrasive material, silicon carbide abrasive, feldspar, clay, boron glass, bonding agent produce abrasive wheel for abrasion of steel ball, not only have compared with
High durability has higher grinding efficiency again, while heat resistance is good, the high yield rate in roasting.
To solve the above problems, the technical solution used in the present invention is as follows：
A kind of abrasive wheel for abrasion of steel ball formula, is made from the following raw materials in parts by weight：18~24 parts of brown corundum abrasive, white fused alumina abrasive material 6
~12 parts, 10~20 parts of silicon carbide abrasive, 20~30 parts of feldspar, 15~20 parts of clay, 2~5 parts of boron glass, bonding agent
25~40 parts.
Further, it is made from the following raw materials in parts by weight：120 parts of brown corundum abrasive, 8 parts of white fused alumina abrasive material, silicon carbide
16 parts of abrasive material, 26 parts of feldspar, 17 parts of clay, 3 parts of boron glass, 30 parts of bonding agent.
Further, the bonding agent is made from the following raw materials in parts by weight：40~60 parts of silica, aluminium oxide 20~30
Part, 0.5~2 part of iron oxide, 0.1~0.5 part of calcium oxide, 1~3 part of boron oxide, 2~5 parts of manganese oxide.
Further, the bonding agent is made from the following raw materials in parts by weight：45 parts of silica, 23 parts of aluminium oxide, iron oxide
0.9 part, 0.3 part of calcium oxide, 2.1 parts of boron oxide, 4 parts of manganese oxide.
Further, the brown corundum abrasive, white fused alumina abrasive material, silicon carbide abrasive granularity are F170~F220
Compared with prior art, implementation result of the invention is as follows by the present invention：
A kind of abrasive wheel for abrasion of steel ball formula of the present invention, using brown corundum abrasive, white fused alumina abrasive material, silicon carbide abrasive, feldspar glues
Soil, boron glass, bonding agent produce abrasive wheel for abrasion of steel ball, and not only having higher durability again has higher grinding efficiency, while resistance to
Good in thermal property, the high yield rate in roasting.
Specific implementation mode
With reference to embodiment, the invention will be further described, but the present invention is not limited to these instances, and is being de-
Under the premise of from present inventive concept, carried out by it is any improvement be within the scope of the present invention.
Embodiment 1
A kind of abrasive wheel for abrasion of steel ball formula of the present invention, is made from the following raw materials in parts by weight：A kind of abrasive wheel for abrasion of steel ball formula,
It is made from the following raw materials in parts by weight：18~24 parts of brown corundum abrasive, 6~12 parts of white fused alumina abrasive material, silicon carbide abrasive 10~
20 parts, 20~30 parts of feldspar, 15~20 parts of clay, 2~5 parts of boron glass, 25~40 parts of bonding agent.
Further, the bonding agent is made from the following raw materials in parts by weight：40~60 parts of silica, aluminium oxide 20~30
Part, 0.5~2 part of iron oxide, 0.1~0.5 part of calcium oxide, 1~3 part of boron oxide, 2~5 parts of manganese oxide.
Further, the brown corundum abrasive, white fused alumina abrasive material, silicon carbide abrasive granularity are F170~F220
Embodiment 2
A kind of abrasive wheel for abrasion of steel ball formula of the present invention, is made from the following raw materials in parts by weight：120 parts of brown corundum abrasive, white fused alumina mill
8 parts of material, 16 parts of silicon carbide abrasive, 26 parts of feldspar, 17 parts of clay, 3 parts of boron glass, 30 parts of bonding agent.
The bonding agent is made from the following raw materials in parts by weight：45 parts of silica, 23 parts of aluminium oxide, 0.9 part of iron oxide, oxygen
Change 0.3 part of calcium, 2.1 parts of boron oxide, 4 parts of manganese oxide.
The brown corundum abrasive, white fused alumina abrasive material, silicon carbide abrasive granularity are F170~F220
Above content is only to present inventive concept example and explanation, affiliated those skilled in the art are to being retouched
The specific embodiment stated does various modifications or additions or substitutes by a similar method, as long as it does not deviate from the concept of invention
Or beyond the scope defined by this claim, it is within the scope of protection of the invention.
Claims (5)
1. a kind of abrasive wheel for abrasion of steel ball formula, it is characterised in that：It is made from the following raw materials in parts by weight：Brown corundum abrasive 18~24
Part, 6~12 parts of white fused alumina abrasive material, 10~20 parts of silicon carbide abrasive, 20~30 parts of feldspar, 15~20 parts of clay, boron glass
2~5 parts of glass, 25~40 parts of bonding agent.
2. a kind of abrasive wheel for abrasion of steel ball formula according to claim 1, it is characterised in that：By the raw material system of following parts by weight
At：120 parts of brown corundum abrasive, 8 parts of white fused alumina abrasive material, 16 parts of silicon carbide abrasive, 26 parts of feldspar, 17 parts of clay, boron glass
3 parts of glass, 30 parts of bonding agent.
3. according to a kind of abrasive wheel for abrasion of steel ball formula of claims 1 or 2 any one of them, it is characterised in that：The bonding agent
It is made from the following raw materials in parts by weight：40~60 parts of silica, 20~30 parts of aluminium oxide, 0.5~2 part of iron oxide, calcium oxide 0.1
~0.5 part, 1~3 part of boron oxide, 2~5 parts of manganese oxide.
4. according to a kind of abrasive wheel for abrasion of steel ball formula of claim 3 any one of them, it is characterised in that：The bonding agent is by following
The raw material of parts by weight is made：45 parts of silica, 23 parts of aluminium oxide, 0.9 part of iron oxide, 0.3 part of calcium oxide, 2.1 parts of boron oxide, oxygen
Change 4 parts of manganese.
5. according to a kind of abrasive wheel for abrasion of steel ball formula of claims 1 or 2 any one of them, it is characterised in that：The Brown Alundum
Abrasive material, white fused alumina abrasive material, silicon carbide abrasive granularity are F170~F2201.