CN107415006A - A kind of method for preventing woodwork from ftractureing - Google Patents
A kind of method for preventing woodwork from ftractureing Download PDFInfo
- Publication number
- CN107415006A CN107415006A CN201710849617.4A CN201710849617A CN107415006A CN 107415006 A CN107415006 A CN 107415006A CN 201710849617 A CN201710849617 A CN 201710849617A CN 107415006 A CN107415006 A CN 107415006A
- Authority
- CN
- China
- Prior art keywords
- woodwork
- parts
- soak
- ftractureing
- preventing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of method for preventing woodwork from ftractureing, including following operating procedure：（1）Woodwork after shaping is heat-treated using water vapour；（2）Woodwork through Overheating Treatment is immediately placed in immersion treatment in soak；（3）After the soak for disposing wood product surface, after carrying out drying and processing to it, finished product.The method provided by the invention for preventing woodwork from ftractureing, effectively can prevent woodwork from ftractureing, effectively improve the quality of woodwork.
Description
Technical field
The invention belongs to woodwork preparing technical field, and in particular to a kind of method for preventing woodwork from ftractureing.
Background technology
Woodwork is using timber as raw material, and by processing and fabricating, the product formed, woodwork is broadly divided into following several
Major class：Furniture woodwork, office woodwork, technique woodwork, gardening woodwork, life woodwork, also present high-tech wood
Product.Woodwork is during use, and especially gardening woodwork drenches with rain and be exposed to the sun, it is easy to which that ftractures shows for a long time
As.
The content of the invention
In order to solve the above-mentioned technical problem, the present invention provides a kind of method for preventing woodwork from ftractureing.
The present invention is achieved by the following technical solutions.
A kind of method for preventing woodwork from ftractureing, including following operating procedure：
（1）Woodwork after shaping is heat-treated using water vapour；
（2）Woodwork through Overheating Treatment is immediately placed in immersion treatment in soak, wherein soak is by following parts by weight
Component is made：4 heptyl iodide 8-12 parts, dinonyl phthalate 18-22 parts, frankincense gum 6-9 parts, morpholine fatty acid salt
Fruit wax 16-20 parts, ethanol 80-90 parts, water 130-150 parts；
（3）After the soak for disposing wood product surface, after carrying out drying and processing to it, finished product.
Specifically, above-mentioned steps（1）The time of middle steam treatment is 2-4 hours.
Specifically, above-mentioned steps（2）Middle soak is made of following methods：By 4 heptyl iodide, phthalic acid
After two nonyl esters, frankincense gum, Morpholine fatty acid salt fruit wax are sequentially added into ethanol, continuation adds water thereto, after being well mixed,
Soak is made.
Specifically, above-mentioned steps（3）During middle drying and processing, temperature during drying is 105-110 DEG C, and the time of drying is 2-
3 hours.
Technical scheme more than, the beneficial effects of the invention are as follows：
A kind of method for preventing woodwork from ftractureing provided by the invention, first passes through vapours processing, can effectively lift timber
Intensity, and can effectively strengthens the infiltration capacity of soak, strengthens the action effect of soak；Soak provided by the invention,
After frankincense gum, Morpholine fatty acid salt fruit wax synergy, the adhesion of woodwork interior molecules can be effectively lifted, lifts timber
Consistency, and then effectively improve the performance of the crack resistence of timber；4 heptyl iodide, dinonyl phthalate collaboration are made
With rear, the uniformity of soak distribution can be effectively lifted, and then improves the action effect of soak, woodwork is improved and prevents
The performance of cracking.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, following examples are carried out to the present invention
It is further described.It should be appreciated that specific embodiment party example described herein is not used to limit only to explain the present invention
The fixed present invention.
Embodiment 1
A kind of method for preventing woodwork from ftractureing, including following operating procedure：
（1）Woodwork after shaping is heat-treated using water vapour；
（2）Woodwork through Overheating Treatment is immediately placed in immersion treatment in soak, wherein soak is by following parts by weight
Component is made：8 parts of 4 heptyl iodide, 18 parts of dinonyl phthalate, 6 parts of frankincense gum, 16 parts of Morpholine fatty acid salt fruit wax,
80 parts of ethanol, 130 parts of water；
（3）After the soak for disposing wood product surface, after carrying out drying and processing to it, finished product.
Specifically, above-mentioned steps（1）The time of middle steam treatment is 2 hours.
Specifically, above-mentioned steps（2）Middle soak is made of following methods：By 4 heptyl iodide, phthalic acid
After two nonyl esters, frankincense gum, Morpholine fatty acid salt fruit wax are sequentially added into ethanol, continuation adds water thereto, after being well mixed,
Soak is made.
Specifically, above-mentioned steps（3）During middle drying and processing, temperature during drying is 105 DEG C, and the time of drying is 2 hours.
The treated woodwork of the present embodiment, is placed in outdoor environment, after 12 months, the phenomenon that does not ftracture.
Embodiment 2
A kind of method for preventing woodwork from ftractureing, including following operating procedure：
（1）Woodwork after shaping is heat-treated using water vapour；
（2）Woodwork through Overheating Treatment is immediately placed in immersion treatment in soak, wherein soak is by following parts by weight
Component is made：10 parts of 4 heptyl iodide, 20 parts of dinonyl phthalate, 8 parts of frankincense gum, Morpholine fatty acid salt fruit wax 18
Part, 85 parts of ethanol, 140 parts of water；
（3）After the soak for disposing wood product surface, after carrying out drying and processing to it, finished product.
Specifically, above-mentioned steps（1）The time of middle steam treatment is 3 hours.
Specifically, above-mentioned steps（2）Middle soak is made of following methods：By 4 heptyl iodide, phthalic acid
After two nonyl esters, frankincense gum, Morpholine fatty acid salt fruit wax are sequentially added into ethanol, continuation adds water thereto, after being well mixed,
Soak is made.
Specifically, above-mentioned steps（3）During middle drying and processing, temperature during drying is 108 DEG C, and the time of drying is small for 2.5
When.
The treated woodwork of the present embodiment, is placed in outdoor environment, after 12 months, the phenomenon that does not ftracture.
Embodiment 3
A kind of method for preventing woodwork from ftractureing, including following operating procedure：
（1）Woodwork after shaping is heat-treated using water vapour；
（2）Woodwork through Overheating Treatment is immediately placed in immersion treatment in soak, wherein soak is by following parts by weight
Component is made：12 parts of 4 heptyl iodide, 22 parts of dinonyl phthalate, 9 parts of frankincense gum, Morpholine fatty acid salt fruit wax 20
Part, 90 parts of ethanol, 150 parts of water；
（3）After the soak for disposing wood product surface, after carrying out drying and processing to it, finished product.
Specifically, above-mentioned steps（1）The time of middle steam treatment is 4 hours.
Specifically, above-mentioned steps（2）Middle soak is made of following methods：By 4 heptyl iodide, phthalic acid
After two nonyl esters, frankincense gum, Morpholine fatty acid salt fruit wax are sequentially added into ethanol, continuation adds water thereto, after being well mixed,
Soak is made.
Specifically, above-mentioned steps（3）During middle drying and processing, temperature during drying is 110 DEG C, and the time of drying is 3 hours.
The treated woodwork of the present embodiment, is placed in outdoor environment, after 12 months, the phenomenon that does not ftracture.
Claims (4)
- A kind of 1. method for preventing woodwork from ftractureing, it is characterised in that including following operating procedure：（1）Woodwork after shaping is heat-treated using water vapour；（2）Woodwork through Overheating Treatment is immediately placed in immersion treatment in soak, wherein soak is by following parts by weight Component is made：4 heptyl iodide 8-12 parts, dinonyl phthalate 18-22 parts, frankincense gum 6-9 parts, morpholine fatty acid salt Fruit wax 16-20 parts, ethanol 80-90 parts, water 130-150 parts；（3）After the soak for disposing wood product surface, after carrying out drying and processing to it, finished product.
- 2. according to a kind of method for preventing woodwork from ftractureing described in claim 1, it is characterised in that above-mentioned steps（1）In The time of steam treatment is 2-4 hours.
- 3. according to a kind of method for preventing woodwork from ftractureing described in claim 1, it is characterised in that above-mentioned steps（2）In Soak is made of following methods：By 4 heptyl iodide, dinonyl phthalate, frankincense gum, morpholine fatty acid salt fruit After wax is sequentially added into ethanol, continuation adds water thereto, and after being well mixed, soak is made.
- 4. according to a kind of method for preventing woodwork from ftractureing described in claim 1, it is characterised in that above-mentioned steps（3）In During drying and processing, temperature during drying is 105-110 DEG C, and the time of drying is 2-3 hours.