CN107593765A - A kind of mould proof handling process of sound insulation beam - Google Patents
A kind of mould proof handling process of sound insulation beam Download PDFInfo
- Publication number
- CN107593765A CN107593765A CN201710752772.4A CN201710752772A CN107593765A CN 107593765 A CN107593765 A CN 107593765A CN 201710752772 A CN201710752772 A CN 201710752772A CN 107593765 A CN107593765 A CN 107593765A
- Authority
- CN
- China
- Prior art keywords
- sound insulation
- insulation beam
- mould proof
- parts
- handling process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mould proof handling process of sound insulation beam, the mould inhibitor used in the mould proof handling process of sound insulation beam includes 50~60 parts of 10~13 parts of sodium fluoride, 5~8 parts of sodium citrate, 3~8 parts of penta sodium pentachlorophenate, 2~5 parts of borax, 5~10 parts of sodium alginate and water, and the mould proof handling process of sound insulation beam comprises the following steps：1) is cleaned：It is clean that each raw material of sound insulation beam is subjected to hot water washing；2) is air-dried：Each raw material of wash clean is carried out drying air-dried steam；3) high pressure steam sterilizations：The various single-layer pads synthesized are washed away using high pressure steam sterilization rifle；4) soaks：Single-layer pad is put into the solution of mould inhibitor and soaked；5) is dried：Drying in oven is put into after immersion, the mould proof handling process of sound insulation beam of the present invention has the characteristics of safe and non-toxic, green, strong to sound insulation beam permeability, can effectively suppress the mould inside sound insulation beam, and there is good anchorage and durability, the stable prospect of product quality is good.
Description
Technical field
The present invention relates to the mould proof processing technology field of pad, and in particular to a kind of mould proof handling process of sound insulation beam.
Background technology
Sound insulation beam preserved under the environmental condition of warm moist and using when easily by mould corrode go mouldy, and
After mould invasion sound insulation beam, make permeability increase of the liquid to sound insulation beam, the erosion to sound insulation beam can be promoted,
Influence the performance of sound insulation beam.Therefore for the sound insulation beam handicraft using sound insulation beam as primary raw material, mould proof place
Manage particularly significant.The mould inhibitor for being usually used in sound insulation beam handicraft at present often has certain toxicity, and contactee is good for
Be present potential risk in health, be short of in terms of safety and environmental protection.And the stability and anchorage of conventional mould inhibitor are poor, easily
It is lost in, mould proof durability is bad.With the economic development and improvement of living standards, consumer is to green requirement
Also gradually lifting, therefore, environmentally friendly, economy and durability new product is developed, there are huge market prospects.
The content of the invention
To solve the above problems, the present invention proposes a kind of mould proof handling process of sound insulation beam.
To realize the object of the invention, the technical scheme of use is：A kind of mould proof handling process of sound insulation beam, the sound insulation
The mould proof handling process of beam comprises the following steps：
1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate heat
Water, adds appropriate cleaning agent, opens low-speed mixer and is stirred, cleans 2~3 times back and forth, and each scavenging period is 45~
60min；
2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by sound insulation beam
Each raw material carry out drying air-dried steam, each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；
3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is washed away 1 using high pressure steam sterilization rifle~
3min, all microorganisms being deposited with inside multiple sound insulation beam are killed, and remove its residue；
4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, in adding after mould proof agent solution
Immersion, open low-speed mixer and be stirred, soak 1~3 day；
5) is dried：Multiple sound insulation beam after immersion, which is put into low temperature baking oven, is dried, until multiple sound insulation damping
Moisture concentration inside pad is 10~15wt%.
Preferably, the temperature control of hot water is 50~60 DEG C in the mould proof treatment process steps 1 of the sound insulation beam.
Preferably, the stir speed (S.S.) of low-speed mixer is arranged to 300 in the mould proof treatment process steps 1 of the sound insulation beam
~800r/min.
Preferably, the high steam party that the mould proof mesohigh of the treatment process steps 3 sterilizing rifle of the sound insulation beam uses
Temperature setting is 120~140 DEG C.
Preferably, the mould inhibitor used in the mould proof treatment process steps 4 of the sound insulation beam includes sodium fluoride 10~13
Part, 5~8 parts of sodium citrate, 3~8 parts of penta sodium pentachlorophenate, 2~5 parts of borax, 5~10 parts of sodium alginate and 50~60 parts of water.
Preferably, the stir speed (S.S.) of low-speed mixer is arranged to 300 in the mould proof treatment process steps 4 of the sound insulation beam
~500r/min.
Preferably, the drying temperature in the mould proof treatment process steps 5 of the sound insulation beam in low temperature baking oven is arranged to 50
~60 DEG C.
Beneficial effects of the present invention are：The mould proof handling process of sound insulation beam of the present invention has safe and non-toxic, green
The characteristics of, it is strong to sound insulation beam permeability, it can effectively suppress the mould inside sound insulation beam, and there is good set
Property and durability, anti-mold effect it is lasting, product quality is stable, and application prospect is good.
Brief description of the drawings
Fig. 1 is the raw material proportioning table of the mould inhibitor of the mould proof handling process of sound insulation beam of the present invention.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
Embodiment 1
It refer to shown in Fig. 1, the invention provides a kind of scheme：A kind of mould proof handling process of sound insulation beam, it is described every
The mould proof handling process of sound beam comprises the following steps：
1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate temperature
For 50 DEG C of hot water, appropriate cleaning agent is added, low-speed mixer is opened and is stirred with 300r/min stir speed (S.S.), back and forth
Cleaning 2 times, each scavenging period is 45min；
2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by sound insulation beam
Each raw material carry out drying air-dried steam, each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；
3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is steamed using the high pressure that vapor (steam) temperature is 120 DEG C
Vapour sterilizing rifle washes away min, kills all microorganisms being deposited with inside multiple sound insulation beam, and remove its residue；
4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, in adding after mould proof agent solution
Immersion, open low-speed mixer and be stirred with 300r/min stir speed (S.S.), soaked 1 day；
5) is dried：Multiple sound insulation beam after immersion is put into low temperature baking oven and dried at a temperature of 50 DEG C, directly
Moisture concentration inside to multiple sound insulation beam is 10wt%.
Wherein, the mould inhibitor used in the mould proof treatment process steps 4 of the sound insulation beam includes 13 parts of sodium fluoride, lemon
60 parts of sour 8 parts of sodium, 8 parts of penta sodium pentachlorophenate, 5 parts of borax, 10 parts of sodium alginate and water.
Embodiment 2
It refer to shown in Fig. 1, the invention provides a kind of scheme：A kind of mould proof handling process of sound insulation beam, it is described every
The mould proof handling process of sound beam comprises the following steps：
1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate temperature
For 60 DEG C of hot water, appropriate cleaning agent is added, low-speed mixer is opened and is stirred with 800r/min stir speed (S.S.), back and forth
Cleaning 3 times, each scavenging period is 60min；
2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by sound insulation beam
Each raw material carry out drying air-dried steam, each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；
3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is steamed using the high pressure that vapor (steam) temperature is 140 DEG C
Vapour sterilizing rifle washes away 3min, kills all microorganisms being deposited with inside multiple sound insulation beam, and remove its residue；
4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, in adding after mould proof agent solution
Immersion, open low-speed mixer and be stirred with 500r/min stir speed (S.S.), soaked 3 days；
5) is dried：Multiple sound insulation beam after immersion is put into low temperature baking oven and dried at a temperature of 60 DEG C, directly
Moisture concentration inside to multiple sound insulation beam is 15wt%.
Wherein, the mould inhibitor used in the mould proof treatment process steps 4 of the sound insulation beam includes 13 parts of sodium fluoride, lemon
60 parts of sour 8 parts of sodium, 8 parts of penta sodium pentachlorophenate, 5 parts of borax, 10 parts of sodium alginate and water.
Embodiment 3
It refer to shown in Fig. 1, the invention provides a kind of scheme：A kind of mould proof handling process of sound insulation beam, it is described every
The mould proof handling process of sound beam comprises the following steps：
1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate temperature
For 50 DEG C of hot water, appropriate cleaning agent is added, low-speed mixer is opened and is stirred with 300r/min stir speed (S.S.), back and forth
Cleaning 2 times, each scavenging period is 45min；
2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by sound insulation beam
Each raw material carry out drying air-dried steam, each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；
3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is steamed using the high pressure that vapor (steam) temperature is 120 DEG C
Vapour sterilizing rifle washes away 1min, kills all microorganisms being deposited with inside multiple sound insulation beam, and remove its residue；
4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, in adding after mould proof agent solution
Immersion, open low-speed mixer and be stirred with 300r/min stir speed (S.S.), soaked 1 day；
5) is dried：Multiple sound insulation beam after immersion is put into low temperature baking oven and dried at a temperature of 50 DEG C, directly
Moisture concentration inside to multiple sound insulation beam is 10wt%.
Wherein, the mould inhibitor used in the mould proof treatment process steps 4 of the sound insulation beam includes 10 parts of sodium fluoride, lemon
50 parts of sour 5 parts of sodium, 3 parts of penta sodium pentachlorophenate, 2 parts of borax, 5 parts of sodium alginate and water.
Embodiment 4
It refer to shown in Fig. 1, the invention provides a kind of scheme：A kind of mould proof handling process of sound insulation beam, it is described every
The mould proof handling process of sound beam comprises the following steps：
1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate temperature
For 60 DEG C of hot water, appropriate cleaning agent is added, low-speed mixer is opened and is stirred with 800r/min stir speed (S.S.), back and forth
Cleaning 3 times, each scavenging period is 60min；
2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by sound insulation beam
Each raw material carry out drying air-dried steam, each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；
3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is steamed using the high pressure that vapor (steam) temperature is 140 DEG C
Vapour sterilizing rifle washes away 3min, kills all microorganisms being deposited with inside multiple sound insulation beam, and remove its residue；
4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, in adding after mould proof agent solution
Immersion, open low-speed mixer and be stirred with 500r/min stir speed (S.S.), soaked 3 days；
5) is dried：Multiple sound insulation beam after immersion is put into low temperature baking oven and dried at a temperature of 60 DEG C, directly
Moisture concentration inside to multiple sound insulation beam is 15wt%.
Wherein, the mould inhibitor used in the mould proof treatment process steps 4 of the sound insulation beam includes 10 parts of sodium fluoride, lemon
50 parts of sour 5 parts of sodium, 3 parts of penta sodium pentachlorophenate, 2 parts of borax, 5 parts of sodium alginate and water.
Embodiment 5
It refer to shown in Fig. 1, the invention provides a kind of scheme：A kind of mould proof handling process of sound insulation beam, it is described every
The mould proof handling process of sound beam comprises the following steps：
1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate temperature
For 55 DEG C of hot water, appropriate cleaning agent is added, low-speed mixer is opened and is stirred with 500r/min stir speed (S.S.), back and forth
Cleaning 3 times, each scavenging period is 50min；
2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by sound insulation beam
Each raw material carry out drying air-dried steam, each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；
3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is steamed using the high pressure that vapor (steam) temperature is 130 DEG C
Vapour sterilizing rifle washes away 2min, kills all microorganisms being deposited with inside multiple sound insulation beam, and remove its residue；
4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, in adding after mould proof agent solution
Immersion, open low-speed mixer and be stirred with 400r/min stir speed (S.S.), soaked 2 days；
5) is dried：Multiple sound insulation beam after immersion is put into low temperature baking oven and dried at a temperature of 55 DEG C, directly
Moisture concentration inside to multiple sound insulation beam is 13wt%.
Wherein, the mould inhibitor used in the mould proof treatment process steps 4 of the sound insulation beam includes 12 parts of sodium fluoride, lemon
55 parts of sour 7 parts of sodium, 5 parts of penta sodium pentachlorophenate, 4 parts of borax, 7 parts of sodium alginate and water.
In the present invention, the mould proof handling process of sound insulation beam of the present invention has the characteristics of safe and non-toxic, green, right
Sound insulation beam permeability is strong, can effectively suppress the mould inside sound insulation beam, and with good anchorage and durable
Property, anti-mold effect is lasting, and product quality is stable, and application prospect is good.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
- A kind of 1. mould proof handling process of sound insulation beam, it is characterised in that：The mould proof handling process of sound insulation beam include with Lower step：1) is cleaned：Each raw material of sound insulation beam is poured into service sink, toward service sink inside add appropriate hot water, add Enter appropriate cleaning agent, open low-speed mixer and be stirred, clean 2~3 times back and forth, each scavenging period is 45~60min；2) is air-dried：Each raw material of wash clean is rinsed using clear water, after the completion of flushing, by each of sound insulation beam Raw material is carried out drying air-dried steam, and each raw material of sound insulation beam is made to the multiple sound insulation beam that can be split；3) high pressure steam sterilizations：Each individual layer of multiple sound insulation beam is washed away into 1~3min using high pressure steam sterilization rifle, All microorganisms being deposited with inside multiple sound insulation beam are killed, and remove its residue；4) soaks：Each single-layer pad of multiple sound insulation beam is put into fermentation vat, adds middle leaching after mould proof agent solution Bubble, open low-speed mixer and be stirred, soak 1~3 day；5) is dried：Multiple sound insulation beam after immersion, which is put into low temperature baking oven, is dried, until in multiple sound insulation beam The moisture concentration in portion is 10~15wt%.
- A kind of 2. mould proof handling process of sound insulation beam according to claim 1, it is characterised in that：The sound insulation beam The temperature control of hot water is 50~60 DEG C in mould proof treatment process steps 1.
- A kind of 3. mould proof handling process of sound insulation beam according to claim 1, it is characterised in that：The sound insulation beam The stir speed (S.S.) of low-speed mixer is arranged to 300~800r/min in mould proof treatment process steps 1.
- A kind of 4. mould proof handling process of sound insulation beam according to claim 1, it is characterised in that：The sound insulation beam The temperature setting for the high steam party that the mould proof mesohigh for the treatment of process steps 3 sterilizing rifle uses is 120~140 DEG C.
- A kind of 5. mould proof handling process of sound insulation beam according to claim 1, it is characterised in that：The sound insulation beam The mould inhibitor used in mould proof treatment process steps 4 includes 10~13 parts of sodium fluoride, 5~8 parts of sodium citrate, penta sodium pentachlorophenate 3~8 Part, 2~5 parts of borax, 5~10 parts of sodium alginate and 50~60 parts of water.
- A kind of 6. mould proof handling process of sound insulation beam according to claim 1, it is characterised in that：The sound insulation beam The stir speed (S.S.) of low-speed mixer is arranged to 300~500r/min in mould proof treatment process steps 4.
- A kind of 7. mould proof handling process of sound insulation beam according to claim 1, it is characterised in that：The sound insulation beam Drying temperature in mould proof treatment process steps 5 in low temperature baking oven is arranged to 50~60 DEG C.