CN107413601A - A kind of willow basket lackering method - Google Patents
A kind of willow basket lackering method Download PDFInfo
- Publication number
- CN107413601A CN107413601A CN201710768376.0A CN201710768376A CN107413601A CN 107413601 A CN107413601 A CN 107413601A CN 201710768376 A CN201710768376 A CN 201710768376A CN 107413601 A CN107413601 A CN 107413601A
- Authority
- CN
- China
- Prior art keywords
- willow basket
- paint
- willow
- basket
- seconds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of willow basket lackering method, specially following methods:（1）Willow basket uses treatment fluid immersion oil removing after working out；（2）Dipping lacquer after baking, it is then centrifuged for drying；（3）Natural air drying, polishing.By experiment, the japanning of willow basket is carried out using the inventive method, obtained film thickness is below 72 μm, and using existing method to carry out willow basket japanning, film thickness is up to 135 μm, it is seen that uses the inventive method, paint usage amount can be greatly reduced, the paint drying time is reduced, entreprise cost is greatly reduced, is made and widelys popularize.
Description
Technical field
The invention belongs to wicker products production technical field, and in particular to a kind of willow basket lackering method.
Background technology
Wicker products raw material are extensive, the characteristics of making full use of toughness plant, focus on color and luster, skin texture, pursue natural, embody
Honest, pure and honest, the sincere moral character of the work common people.Compared with general traditional art, the subjectivity of wicker plaiting article moulding idea is more
Add protrusion, be the combination of practical technique among the people and folk industrial art, and practicality and aesthetic combination.
In the prior art, the lackering method of willow basket is that willow basket is slowly immersed in paint solution to complete japanning, but this side
Method paint consumption is big, and film thickness is big, causes drying time-consuming long, seriously restricts enterprises production efficiency.
The content of the invention
In order to solve the above problems, the invention provides a kind of willow basket lackering method.
The present invention is achieved through the following technical solutions：
A kind of willow basket lackering method, specially following steps:
（1）After willow basket is worked out, surface washing is clean, after drying up moisture, immerses and 30-45 points are soaked in 55-65 DEG C for the treatment of fluid
Clock, immersion are completed to apply the supersonic oscillations emulsification 60-90 seconds in the backward treatment fluid, then take out willow basket；The treatment fluid,
By deionized water, sodium acetate, odium stearate, sodium hydroxide 100-200 in mass ratio:2:1:It is made after 15 mixing；Willow basket is clear
Immerse in the treatment fluid and soak after wash clean, treatment fluid is alkalescence, and contains fatty acid metal salts, can effectively remove willow basket table
The fluid in face, is then handled by supersonic oscillations, further improves cleaning effect, after the willow basket japanning so handled
Make the adhesive force of paint stronger, the paint film of formation is more uniform, japanning speed faster, effect it is more preferable；
（2）By step（1）The willow basket handled well is cleaned, and uniformly toasts the 30-40 seconds using 60-70 DEG C of hot blast, is then delayed while hot
It is slow to immerse in paint solution, taken out at once after being totally submerged, be positioned over conveyer belt, be sent to centrigugal swing dryer after the 20-25 seconds, make
Excess paint is got rid of with the rotation of 60-80r/min speed；By willow basket dipping lacquer while hot, further increase paint film and form the time, make oil
Paint forms paint film with the direct contact portion rapid draing of willow basket, and redundance is thrown away by low speed rotation, and the paint thrown away is also
It can reuse and avoid wasting, greatly reduce the usage amount of paint, reduce japanning cost, while make paint drying speed
Greatly improve, improve japanning efficiency；
（3）The willow basket of drying is placed in outdoor natural air drying, by polishing, that is, completes japanning.
Further, step（1）The ultrasonic wave, frequency 25-35kHz.
Further, step（2）Excess paint is got rid of in the rotation, need to rotate the 10-15 seconds.
Further, step（2）The excess paint, refunded after collection in paint solution.
Beneficial effects of the present invention：Immersing in the treatment fluid and soak after willow basket is cleaned up, treatment fluid is alkalescence, and
Containing fatty acid metal salts, the fluid on willow basket surface can be effectively removed, then handles by supersonic oscillations, further improves
Cleaning effect, make the adhesive force of paint stronger after the willow basket japanning so handled, the paint film of formation is more uniform, japanning speed
Degree faster, effect it is more preferable；By willow basket dipping lacquer while hot, further increase paint film and form the time, paint is directly contacted with willow basket
Part rapid draing forms paint film, and redundance is thrown away by low speed rotation, and the paint thrown away can also be reused and avoided
Waste, greatly reduce the usage amount of paint, reduce japanning cost, while greatly improve paint drying speed, improve
Japanning efficiency.By experiment, using the japanning of the inventive method progress willow basket, obtained film thickness makes below 72 μm
Willow basket japanning is carried out with existing method, film thickness is up to 135 μm, it is seen that using the inventive method, oil can be greatly reduced
Usage amount is painted, the paint drying time is reduced, entreprise cost is greatly reduced, is made and widelys popularize.
Embodiment
Embodiment 1
A kind of willow basket lackering method, specially following steps:
（1）After willow basket is worked out, surface washing is clean, after drying up moisture, immerses in 55-65 DEG C for the treatment of fluid and soaks 30 minutes,
Immersion is completed to apply supersonic oscillations emulsification 60 seconds in the backward treatment fluid, then takes out willow basket；The treatment fluid, by go from
Sub- water, sodium acetate, odium stearate, sodium hydroxide in mass ratio 100:2:1:It is made after 15 mixing；
（2）By step（1）The willow basket handled well is cleaned, and is uniformly toasted 30 seconds using 60-70 DEG C of hot blast, then slowly leaching while hot
Enter to paint in solution, taken out at once after being totally submerged, be positioned over conveyer belt, be sent to centrigugal swing dryer after 20 seconds, use 60-
Excess paint is got rid of in the rotation of 80r/min speed；
（3）The willow basket of drying is placed in outdoor natural air drying, by polishing, that is, completes japanning.
Further, step（1）The ultrasonic wave, frequency 25-35kHz.
Further, step（2）Excess paint is got rid of in the rotation, need to rotate the 10-15 seconds.
Further, step（2）The excess paint, refunded after collection in paint solution.
Embodiment 2
A kind of willow basket lackering method, specially following steps:
（1）After willow basket is worked out, surface washing is clean, after drying up moisture, immerses in 55-65 DEG C for the treatment of fluid and soaks 45 minutes,
Immersion is completed to apply supersonic oscillations emulsification 90 seconds in the backward treatment fluid, then takes out willow basket；The treatment fluid, by go from
Sub- water, sodium acetate, odium stearate, sodium hydroxide in mass ratio 200:2:1:It is made after 15 mixing；
（2）By step（1）The willow basket handled well is cleaned, and is uniformly toasted 40 seconds using 60-70 DEG C of hot blast, then slowly leaching while hot
Enter to paint in solution, taken out at once after being totally submerged, be positioned over conveyer belt, be sent to centrigugal swing dryer after 25 seconds, use 60-
Excess paint is got rid of in the rotation of 80r/min speed；
（3）The willow basket of drying is placed in outdoor natural air drying, by polishing, that is, completes japanning.
Further, step（1）The ultrasonic wave, frequency 25-35kHz.
Further, step（2）Excess paint is got rid of in the rotation, need to rotate the 10-15 seconds.
Further, step（2）The excess paint, refunded after collection in paint solution.
Embodiment 3
A kind of willow basket lackering method, specially following steps:
（1）After willow basket is worked out, surface washing is clean, after drying up moisture, immerses in 55-65 DEG C for the treatment of fluid and soaks 40 minutes,
Immersion is completed to apply supersonic oscillations emulsification 80 seconds in the backward treatment fluid, then takes out willow basket；The treatment fluid, by go from
Sub- water, sodium acetate, odium stearate, sodium hydroxide in mass ratio 150:2:1:It is made after 15 mixing；
（2）By step（1）The willow basket handled well is cleaned, and is uniformly toasted 35 seconds using 60-70 DEG C of hot blast, then slowly leaching while hot
Enter to paint in solution, taken out at once after being totally submerged, be positioned over conveyer belt, be sent to centrigugal swing dryer after 23 seconds, use 60-
Excess paint is got rid of in the rotation of 80r/min speed；
（3）The willow basket of drying is placed in outdoor natural air drying, by polishing, that is, completes japanning.
Further, step（1）The ultrasonic wave, frequency 25-35kHz.
Further, step（2）Excess paint is got rid of in the rotation, need to rotate the 10-15 seconds.
Further, step（2）The excess paint, refunded after collection in paint solution.
Control group
Existing willow basket immerses the lackering method of paint solution.
Determine the film thickness of above-mentioned 4 kinds of willow baskets lackering method formation respectively using film thickness instrument, many experiments are average
As a result such as table 1：
Table 1
| Film thickness（μm） | |
| Embodiment 1 | 72 |
| Embodiment 2 | 65 |
| Embodiment 3 | 70 |
| Control group | 135 |
As shown in Table 1, the japanning of willow basket is carried out using the inventive method, obtained film thickness uses existing below 72 μm
There is method to carry out willow basket japanning, film thickness is up to 135 μm, it is seen that using the inventive method, can greatly reduce paint makes
Dosage, the paint drying time is reduced, entreprise cost is greatly reduced, be made and widely popularize.
Claims (5)
1. a kind of willow basket lackering method, it is characterised in that be specially following steps:
（1）After willow basket is worked out, surface washing is clean, after drying up moisture, immerses and 30-45 points are soaked in 55-65 DEG C for the treatment of fluid
Clock, immersion are completed to apply the supersonic oscillations emulsification 60-90 seconds in the backward treatment fluid, then take out willow basket；The treatment fluid,
By deionized water, sodium acetate, odium stearate, sodium hydroxide 100-200 in mass ratio:2:1:It is made after 15 mixing；
（2）By step（1）The willow basket handled well is cleaned, and uniformly toasts the 30-40 seconds using 60-70 DEG C of hot blast, is then delayed while hot
It is slow to immerse in paint solution, taken out at once after being totally submerged, be positioned over conveyer belt, be sent to centrigugal swing dryer after the 20-25 seconds, make
Excess paint is got rid of with the rotation of 60-80r/min speed；
（3）The willow basket of drying is placed in outdoor natural air drying, by polishing, that is, completes japanning.
A kind of 2. willow basket lackering method according to claim 1, it is characterised in that:Step（1）The treatment fluid, by go from
Sub- water, sodium acetate, odium stearate, sodium hydroxide in mass ratio 150:2:1:It is made after 15 mixing.
A kind of 3. willow basket lackering method according to claim 1, it is characterised in that:Step（1）The ultrasonic wave, frequency are
25-35kHz。
A kind of 4. willow basket lackering method according to claim 1, it is characterised in that:Step（2）It is unnecessary that the rotation is got rid of
Paint, need to rotate the 10-15 seconds.
A kind of 5. willow basket lackering method according to claim 1, it is characterised in that:Step（2）The excess paint, through receiving
Refunded after collection in paint solution.