CN100560323C - A kind of pnenolic aldehyde bakelite holder acid washing burr removal technology - Google Patents
A kind of pnenolic aldehyde bakelite holder acid washing burr removal technology Download PDFInfo
- Publication number
- CN100560323C CN100560323C CNB2007101931320A CN200710193132A CN100560323C CN 100560323 C CN100560323 C CN 100560323C CN B2007101931320 A CNB2007101931320 A CN B2007101931320A CN 200710193132 A CN200710193132 A CN 200710193132A CN 100560323 C CN100560323 C CN 100560323C
- Authority
- CN
- China
- Prior art keywords
- pnenolic aldehyde
- aldehyde bakelite
- bakelite holder
- holder
- soaked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of pnenolic aldehyde bakelite holder acid washing burr removal technology is to prepare by mixed acid solution: 2~4%HNO
3, 4~5%H
2SO
4, 4~5%H
3PO
4, 2~4%CrO
3, 82~88% distilled water; Pnenolic aldehyde bakelite holder is put into 75~85 ℃ mixed acid solution and was soaked 1~5 minute, takes out retainer and puts into clear water and soaked 30~50 seconds; 5% sodium carbonate liquor that pnenolic aldehyde bakelite holder after handling is put into 55 ℃~65 ℃ soaked 1~3 minute; With in the alkali and after pnenolic aldehyde bakelite holder put into mobile clear water and washed 4~8 minutes; Pnenolic aldehyde bakelite holder was put into the supersonic wave cleaning machine ultrasonic cleaning 5~10 minutes; Pnenolic aldehyde bakelite holder after the ultrasonic cleaning put into 110 ℃~120 ℃ dry 3~5 hours of thermostatic drying chamber.Solve pnenolic aldehyde bakelite holder and can only adopt artificial removal's Burr Problem, had good practical function.
Description
Technical field
The invention belongs to the engineering plastic surface processing technology field, specially refer to a kind of pnenolic aldehyde bakelite holder acid washing burr removal technology.
Background technology
Pnenolic aldehyde bakelite holder is usually used on high speed, the precision bearing, the removal of the burr that in the mechanical processing process of pnenolic aldehyde bakelite holder, produces at present, big and retainer product wall thickness mainly adopts is the method for vibration finishing for size, promptly use abrasive material, abrasive particle to remove the burr of retainer.For thin-walled, miniature or retainer product that structural shape is special,, can only adopt manually method to remove the burr of retainer at present because its mechanical strength is lower.
Summary of the invention
At above-mentioned existing problems, the present invention proposes a kind of pnenolic aldehyde bakelite holder acid washing burr removal technology, this technology is not only simple and efficient but also can guarantee product quality.
For achieving the above object, the present invention has adopted following technical scheme:
Described pnenolic aldehyde bakelite holder acid washing burr removal technology is by preparing a kind of mixed acid solution, pnenolic aldehyde bakelite holder is soaked in mixed acid solution, and pass through alkali neutralization, water flushing, ultrasonic cleaning, dehydration with the removal of retainer burr, its technical process is as follows:
I, mixed acid solution
Mixed acid solution constitutes by weight percentage: 2~4%HNO
3, 4~5%H
2SO
4, 4~5%H
3PO
4, 2~4%CrO
3, 82~88% distilled water;
II, acid treatment
The mixed acid solution that pnenolic aldehyde bakelite holder is put into 75 ℃~85 ℃ soaked 1~5 minute, and the taking-up retainer is put into clear water and soaked 30~50 seconds;
III, alkali neutralization
5% sodium carbonate liquor that pnenolic aldehyde bakelite holder after handling is put into 55 ℃~65 ℃ soaked 1~3 minute;
IV, water flushing
With in the alkali and after pnenolic aldehyde bakelite holder put into mobile clear water and washed 4~8 minutes;
V, ultrasonic cleaning
Pnenolic aldehyde bakelite holder was put into the supersonic wave cleaning machine ultrasonic cleaning 5~10 minutes;
VI, dehydration
Pnenolic aldehyde bakelite holder after the ultrasonic cleaning put into 110 ℃~120 ℃ dry 3~5 hours of thermostatic drying chamber.
Because adopt aforesaid technical scheme, the present invention has following superiority:
The invention solves thin-walled, pnenolic aldehyde bakelite holder product miniature or that structural shape is special can only adopt manually method to remove the problem of the burr of retainer at present, not only guarantee product quality but also improved operating efficiency greatly, had good practical function.The present invention also can be used for the pnenolic aldehyde bakelite holder product of size than big and wall thickness.
The specific embodiment
Embodiment 1
61804 pnenolic aldehyde bakelite holders are of a size of: Ф 28 * Ф 24.5 * 6, retainer structural shape are crown type.The implementation process that its burr is removed is:
I, mixed acid solution
Mixed acid solution constitutes by weight percentage: 4%HNO
3, 5%H
2SO
4, 5%H
3PO
4, 4%CrO
3, 82% distilled water.
II, acid treatment
The acid solution that pnenolic aldehyde bakelite holder is put into 85 ℃ soaked 4 minutes, took out retainer and put into clear water immersion 50 seconds.
III, alkali neutralization
5% sodium carbonate liquor that pnenolic aldehyde bakelite holder after the acid treatment is put into 65 ℃ soaked 3 minutes.
IV, water flushing
With in the alkali and after pnenolic aldehyde bakelite holder put into mobile clear water flushing 7 minutes.
V, ultrasonic cleaning
Pnenolic aldehyde bakelite holder was put into the supersonic wave cleaning machine ultrasonic cleaning 8 minutes.
VI, dehydration
Pnenolic aldehyde bakelite holder after the ultrasonic cleaning put into 120 ℃ dry 5 hours of thermostatic drying chamber.
Embodiment 2
1000087 pnenolic aldehyde bakelite holders are of a size of: Ф 7 * Ф 4.5 * 3, and the implementation process that its burr is removed is:
I, mixed acid solution
Mixed acid solution constitutes by weight percentage: 2%HNO
3, 4%H
2SO
4, 4%H
3PO
4, 2%CrO
3, 88% distilled water.
II, acid treatment
The acid solution that pnenolic aldehyde bakelite holder is put into 75 ℃ soaked 1 minute, took out retainer and put into clear water immersion 30 seconds.
III, alkali neutralization
5% sodium carbonate liquor that pnenolic aldehyde bakelite holder after the acid treatment is put into 55 ℃ soaked 1 minute.
IV, water flushing
With in the alkali and after pnenolic aldehyde bakelite holder put into mobile clear water flushing 4 minutes.
V, ultrasonic cleaning
Pnenolic aldehyde bakelite holder was put into the supersonic wave cleaning machine ultrasonic cleaning 5 minutes.
VI, dehydration
Pnenolic aldehyde bakelite holder after the ultrasonic cleaning put into 110 ℃ dry 3 hours of thermostatic drying chamber.
Claims (1)
1, a kind of pnenolic aldehyde bakelite holder acid washing burr removal technology, it is characterized in that: this deburring technology is by preparing a kind of mixed acid solution, pnenolic aldehyde bakelite holder is soaked in mixed acid solution, and pass through alkali neutralization, water flushing, ultrasonic cleaning, dehydration with the removal of retainer burr, its technical process is as follows:
I, mixed acid solution
Mixed acid solution constitutes by weight percentage: 2~4%HNO
3, 4~5%H
2SO
4, 4~5%H
3PO
4, 2~4%CrO
3, 82~88% distilled water;
II, acid treatment
The mixed acid solution that pnenolic aldehyde bakelite holder is put into 75 ℃~85 ℃ soaked 1~5 minute, and the taking-up retainer is put into clear water and soaked 30~50 seconds;
III, alkali neutralization
5% sodium carbonate liquor that pnenolic aldehyde bakelite holder after handling is put into 55 ℃~65 ℃ soaked 1~3 minute;
IV, water flushing
With in the alkali and after pnenolic aldehyde bakelite holder put into mobile clear water and washed 4~8 minutes;
V, ultrasonic cleaning
Pnenolic aldehyde bakelite holder was put into the supersonic wave cleaning machine ultrasonic cleaning 5~10 minutes;
VI, dehydration
Pnenolic aldehyde bakelite holder after the ultrasonic cleaning put into 110 ℃~120 ℃ dry 3~5 hours of thermostatic drying chamber.