CN107385463A - One Albatra metal environment-protection brightening cleaning agent and preparation method thereof - Google Patents
One Albatra metal environment-protection brightening cleaning agent and preparation method thereof Download PDFInfo
- Publication number
- CN107385463A CN107385463A CN201710633393.3A CN201710633393A CN107385463A CN 107385463 A CN107385463 A CN 107385463A CN 201710633393 A CN201710633393 A CN 201710633393A CN 107385463 A CN107385463 A CN 107385463A
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- mixed
- builder
- albatra metal
- metal environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of chemical surface cleaning agent, especially Albatra metal environment-protection brightening cleaning agent and preparation method thereof.Wherein, the component of cleaning agent and mass percent are：Organic base 5 10%, inorganic base 10 20%, polyalcohols 20 30%, polyethers 25 35%, builder 1 5%.The present invention after being mixed organic base, inorganic base, polyalcohols, polyethers and builder and water etc. according to certain part by weight by that can form with cleaning degree, brightness and the superior cleaning agent of antioxygenic property, due to not containing strong acid and oxidizing species in cleaning agent, the pollutant containing heavy metal ion will not be produced when carrying out surface cleaning processing to copper and copper alloy, thus be advantageous to improve copper and its working environment of alloy treatment, save enterprise's production cost.
Description
Technical field
The present invention relates to a kind of chemical surface cleaning agent, especially an Albatra metal environment-protection brightening cleaning agent and its preparation side
Method.
Background technology
It is well known that copper and its alloy are one of non-ferrous metals very close with human relation, it is widely used in
Electrically, in the field such as light industry, machine-building, building industry, national defence or on smart electronicses equipment.Due to copper or
Copper alloy its surface during production can have various organic and inorganic pollution, typically pass through oil removing, polishing, protection
Etc. the processing of several procedures, especially in link is polished, traditional cleaning method big city uses substantial amounts of strong acid or Strong oxdiative
Agent, and the use of strong acid or strong oxidizer and because of heavy metal ion caused by it, will necessarily increase the generation of pollutant, lead
Working environment is caused to be deteriorated, energy consumption increase；Simultaneously, it is also desirable to the special waste water disposal facility of enterprise configuration, so as to greatly increase
Enterprise production cost.
The content of the invention
For above-mentioned the shortcomings of the prior art, one of purpose of the invention is to provide Albatra metal environmental protection
Bright cleaning agent；Second object of the present invention is to provide a kind of preparation method for above-mentioned cleaning agent.
To achieve these goals, first technical scheme using of the present invention for：
One Albatra metal environment-protection brightening cleaning agent, the component and mass percent of cleaning agent are：It is organic base 5-10%, inorganic
Alkali 10-20%, polyalcohols 20-30%, polyethers 25-35%, surplus are water and builder.
As one of preferred scheme, the builder includes 2-3% corrosion inhibiter and 1-2% levelling dispersant.
As one of preferred scheme, the corrosion inhibiter is imidazoles, and the levelling dispersant is fluorocarbon surfactant.
Second technical scheme that the present invention uses for：
The preparation method of one Albatra metal environment-protection brightening cleaning agent, it comprises the following steps：
A, polyalcohols and polyethers are well mixed by quality proportioning, obtain mixed once liquid；
B, add organic base by quality proportioning in mixed once liquid and be well mixed, obtain secondary mixed liquor；
C, add builder by quality proportioning in secondary mixed liquor and be well mixed, obtain mixed liquor three times；
D, inorganic base is added to the water by quality proportioning and dissolved, obtain four mixed liquors, four mixed liquors are cooled down
To less than 40 DEG C；
E, it mixed liquor will be mixed evenly three times with four mixed liquors, and obtain five mixed liquors, five mixed liquors are cold
But it is filled with water to prescribed volume to benefit after less than 40 DEG C, you can obtain the cleaning agent.
As a result of such scheme, the present invention is by by organic base, inorganic base, polyalcohols, polyethers and builder and water
Deng can be formed after being mixed according to certain part by weight with cleaning degree, brightness and the superior cleaning of antioxygenic property
Agent, will not when carrying out surface cleaning processing to copper and copper alloy due to not containing strong acid and oxidizing species in cleaning agent
The pollutant containing heavy metal ion is produced, thus is advantageous to improve copper and its working environment of alloy treatment, saves enterprise's life
Produce cost；The cheap environmental protection of its constituent cost, prepares that convenient and swift, cleaning performance is notable, have very strong practical value with
Market popularization value.
Embodiment
Embodiments of the invention are described in detail below, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Albatra metal environment-protection brightening cleaning agent provided in an embodiment of the present invention, its component and mass percent are：It is organic
Alkali 5-10%, inorganic base 10-20%, polyalcohols 20-30%, polyethers 25-35%, surplus are water and builder.Thus, by will be upper
State can be obtained after material composition is mixed according to certain part by weight it is excellent with cleaning degree, brightness and antioxygenic property
Cleaning agent more, due to not containing strong acid and oxidizing species in cleaning agent, carried out to copper and copper alloy at surface clean
The pollutant containing heavy metal ion will not be produced during reason, thus is advantageous to improve copper and its working environment of alloy treatment, section
About enterprise's production cost.
As one of preferred scheme, the builder of the present embodiment preferably selects when carrying out mixed configuration with other components
With 2-3% corrosion inhibiter and 1-2% levelling dispersant.
As one of preferred scheme, the corrosion inhibiter of the present embodiment is preferably imidazoles, and levelling dispersant is preferably then
Fluorocarbon surfactant.
By the physicochemical property detection to cleaning agent, its outward appearance (state of matter, color etc.) is：Colourless transparent liquid, its
Without obvious penetrating odor, its pH value is 12.5-14.Used through actual test, and to copper alloy, stainless steel surfaces greasy dirt and
Various glue residues have extremely strong cleansing power, will not corrode workpiece and brightness is good, and have to copper alloy very good
Antioxidant effect.
Based on the constituent of above-mentioned cleaning agent, to ensure the cleaning performance of cleaning agent, the present embodiment additionally provides one kind
The preparation method of copper alloy environment-protection brightening cleaning agent, it comprises the following steps：
A, polyalcohols and polyethers are pressed into quality proportioning (i.e.：Foregoing constituent mass percentage) it is well mixed, once mixed
Close liquid；
B, add organic base by quality proportioning in mixed once liquid and be well mixed, obtain secondary mixed liquor；
C, add builder by quality proportioning in secondary mixed liquor and be well mixed, obtain mixed liquor three times；
D, inorganic base is added to the water by quality proportioning and dissolved, obtain four mixed liquors, four mixed liquors are cooled down
To less than 40 DEG C；
E, it mixed liquor will be mixed evenly three times with four mixed liquors, and obtain five mixed liquors, five mixed liquors are cold
But it is filled with water to prescribed volume to benefit after less than 40 DEG C, you can obtain the cleaning agent.
Require, only needed in sequence due to will not relate to complicated and accurate humiture, pressure etc. in whole method and step
Carry out mixed processing and can obtain cleaning agent, therefore the flow of preparation section can be simplified, realize that the preparation of automatic assembly line formula is made
Industry, advantageously reduce the manufacturing cost of cleaning agent.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the scope of the invention, every utilization
The equivalent structure or equivalent flow conversion that description of the invention is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (4)
- A 1. Albatra metal environment-protection brightening cleaning agent, it is characterised in that：The component and mass percent of cleaning agent be：Organic base 5- 10%th, inorganic base 10-20%, polyalcohols 20-30%, polyethers 25-35%, surplus are water and builder.
- 2. Albatra metal environment-protection brightening cleaning agent as claimed in claim 1, it is characterised in that：The builder includes 2- 3% corrosion inhibiter and 1-2% levelling dispersant.
- 3. Albatra metal environment-protection brightening cleaning agent as claimed in claim 2, it is characterised in that：The corrosion inhibiter is imidazoles, The levelling dispersant is fluorocarbon surfactant.
- 4. the preparation method of an Albatra metal environment-protection brightening cleaning agent, it is characterised in that：It comprises the following steps：A, polyalcohols and polyethers are well mixed by quality proportioning, obtain mixed once liquid；B, add organic base by quality proportioning in mixed once liquid and be well mixed, obtain secondary mixed liquor；C, add builder by quality proportioning in secondary mixed liquor and be well mixed, obtain mixed liquor three times；D, inorganic base is added to the water by quality proportioning and dissolved, obtain four mixed liquors, four mixed liquors are cooled to 40 Below DEG C；E, it mixed liquor will be mixed evenly three times with four mixed liquors, and obtain five mixed liquors, five mixed liquors are cooled to Mended after less than 40 DEG C and be filled with water to prescribed volume, you can obtain the cleaning agent.