CN103468423A - Metal parts cleaning agent - Google Patents
Metal parts cleaning agent Download PDFInfo
- Publication number
- CN103468423A CN103468423A CN2013104398047A CN201310439804A CN103468423A CN 103468423 A CN103468423 A CN 103468423A CN 2013104398047 A CN2013104398047 A CN 2013104398047A CN 201310439804 A CN201310439804 A CN 201310439804A CN 103468423 A CN103468423 A CN 103468423A
- Authority
- CN
- China
- Prior art keywords
- parts
- out system
- metallic element
- element clean
- cleaning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a metal parts cleaning agent. The metal parts cleaning agent comprises the following components in parts by mass: 32-34 parts of anionic surfactant, 26-28 parts of non-ionic surfactant, 3-4 parts of inorganic base, 3-4 parts of detergency builder, 0.5-1.0 part of corrosive inhibitor, 8-10 parts of chain type polyethylene glycol, and the balance of deionized water; the anionic surfactant is alcohol ether carboxylate; the non-ionic surfactant is C12-C14 alcohol polyoxyethylene ether. The metal cleaning agent does not contain phosphorus and APEO (alkylphenol ethoxylates) surfactants, is wholly green, environmentally-friendly and harmless by adopting the environmentally-friendly surfactants, and has stronger cleansing power at low temperature and normal temperature, thus being a good metal parts cleaning agent.
Description
Technical field
The present invention relates to a kind of metallic element clean-out system.
Background technology
Metal cleaner is mainly used in the cleaning in component production, and in the surface treatments such as application, plating, degreasing is important technological process, and the degreasing degree on metallic article surface will directly have influence on the subsequent disposal quality of workpiece.Usually can add some phosphorous assistants and APEO class tensio-active agent in metal cleaner, these materials have very large harm to environment, therefore, need the metallic element clean-out system of some environmental protection of exploitation.
Summary of the invention
goal of the invention: purpose of the present invention just is to provide a kind of metallic element clean-out system.
technical scheme:for achieving the above object, the present invention has taked following technical scheme:
A kind of metallic element clean-out system is characterized in that: it is comprised of by mass parts following component:
Anion surfactant: 32-34 part;
Nonionogenic tenside: 26-28 part;
Mineral alkali: 3-4 part;
Washing assistant: 3-4 part;
Inhibiter: 0.5-1.0 part;
Chain polyoxyethylene glycol: 8-10 part; This compound is nontoxic, nonirritant, has good water-solublely, and with many organic matter components, good intermiscibility is arranged, and they have good oilness, moisture retention, dispersiveness, joins in clean-out system that to make clean-out system mix more even.
Deionized water: surplus;
Described anion surfactant is: alcohol ether carboxylate; Such tensio-active agent belongs to anion surfactant, in fact have the characteristics of negatively charged ion and nonionogenic tenside concurrently, such tensio-active agent has good characteristic of solubilizing, soil release performance, wettability, emulsifying property, dispersiveness and dispersion of calcium soap, acid and alkali-resistance, high temperature resistant, anti-hard water, can under pH value condition, use widely, and readily biodegradable, nontoxic, use safety.
Described nonionogenic tenside is: C
12-14polyoxyethylenated alcohol.The cold washing performance that such tensio-active agent tool is good and solubilising, dispersion, wettability, viscosity is low, and congealing point is low, almost the gel-free phenomenon, have the good big gun performance that disappears, and has good biological degradability, pungency to skin is low, is a kind of environmental protection, non-harmful nonionogenic tenside.
Described washing assistant is poly (sodium aspartate).
Described mineral alkali is sodium oxalate.Sodium oxalate alkalescence is comparatively gentle, little to the pungency of skin.
Described inhibiter is octadecylamine.Add inhibiter can effectively protect metallic substance, can prevent or slow down metallic material corrosion.
The preparation method of described metallic element clean-out system is: by described formula, prepared burden, first by the chain polyoxyethylene glycol, add in deionized water and stir mixing, then under room temperature, mineral alkali is added in the mixed solution of chain polyoxyethylene glycol and deionized water, after mineral alkali dissolves fully, add successively anion surfactant, nonionogenic tenside, washing assistant, inhibiter under room temperature, stir and obtain described metallic element clean-out system.
beneficial effect:adopt the present invention of technique scheme to have the following advantages:
Metal cleaner of the present invention is not phosphorous, also not containing APEO class tensio-active agent, adopting the tensio-active agent of environment-friendly type to make clean-out system generally speaking green, environmentally friendly, have stronger soil removability under low temperature, normal temperature, is a kind of good metallic element clean-out system.
Embodiment
Below by specific embodiment, the present invention is further set forth.
Embodiment 1:
According to a kind of metallic element clean-out system of the present embodiment, described metallic element clean-out system comprises following composition by weight: anion surfactant: 32 parts; Nonionogenic tenside: 26 parts; Mineral alkali sodium oxalate: 4 parts; Washing assistant poly (sodium aspartate): 4 parts; Inhibiter octadecylamine: 0.5 part; Chain polyoxyethylene glycol: 10 parts; Deionized water: surplus;
Wherein said anion surfactant is: alcohol ether carboxylate; Described nonionogenic tenside is: C
12-14polyoxyethylenated alcohol.
The preparation method of this metallic element clean-out system is as follows:
By described formula, prepared burden, first by the chain polyoxyethylene glycol, add in deionized water and stir mixing, then under room temperature, mineral alkali is added in the mixed solution of chain polyoxyethylene glycol and deionized water, after mineral alkali dissolves fully, add successively anion surfactant, nonionogenic tenside, washing assistant, inhibiter under room temperature, stir and obtain described metallic element clean-out system.
Embodiment 2:
According to a kind of metallic element clean-out system of the present embodiment, described metallic element clean-out system comprises following composition by weight: anion surfactant: 33 parts; Nonionogenic tenside: 27 parts; Mineral alkali sodium oxalate: 3 parts; Lotion poly (sodium aspartate): 4 parts; Inhibiter octadecylamine: 0.8 part; Chain polyoxyethylene glycol: 9 parts; Deionized water: surplus;
Wherein said anion surfactant is: alcohol ether carboxylate; Described nonionogenic tenside is: C
12-14polyoxyethylenated alcohol.
The preparation method of this metallic element clean-out system is as follows:
By described formula, prepared burden, first by the chain polyoxyethylene glycol, add in deionized water and stir mixing, then under room temperature, mineral alkali is added in the mixed solution of chain polyoxyethylene glycol and deionized water, after mineral alkali dissolves fully, add successively anion surfactant, nonionogenic tenside, washing assistant, inhibiter under room temperature, stir and obtain described metallic element clean-out system.
Embodiment 3:
According to a kind of metallic element clean-out system of the present embodiment, described metallic element clean-out system comprises following composition by weight: anion surfactant: 34 parts; Nonionogenic tenside: 28 parts; Mineral alkali sodium oxalate: 4 parts; Washing assistant poly (sodium aspartate): 3 parts; Erosion agent octadecylamine: 1.0 parts; Chain polyoxyethylene glycol: 8 parts; Deionized water: surplus;
Wherein said anion surfactant is: alcohol ether carboxylate; Described nonionogenic tenside is: C
12-14polyoxyethylenated alcohol.
The preparation method of this metallic element clean-out system is as follows:
By described formula, prepared burden, first by the chain polyoxyethylene glycol, add in deionized water and stir mixing, then under room temperature, mineral alkali is added in the mixed solution of chain polyoxyethylene glycol and deionized water, after mineral alkali dissolves fully, add successively anion surfactant, nonionogenic tenside, washing assistant, inhibiter under room temperature, stir and obtain described metallic element clean-out system.
Metallic element clean-out system of the present invention needs dilute with water 10-20 doubly in use, and the metallic element that then will clean is immersed in soaking at room temperature 30-60 minute in washing lotion, then cleans, and after cleaning, washes once again, finally dries and gets final product.
Metallic element clean-out system of the present invention replaces APEO class tensio-active agent in the past with the tensio-active agent of environment-friendly type, and the washing assistant of use is also phosphorus-free adjuvant, and phosphate-free metal cleaner environmental protection of the present invention like this, pollution-free and cleansing power is strong.
It is only below several specific embodiment of the present invention; should understand these embodiment only is not used in and limits the scope of the invention for the present invention is described; after having read the present invention; those skilled in the art all fall within claims of the present invention to the modification of the various equivalent form of values of the present invention and limit, and protection scope of the present invention should be as the criterion with claim of the present invention.
Claims (5)
1. a metallic element clean-out system, it is characterized in that: it is comprised of by mass parts following component:
Anion surfactant: 32-34 part;
Nonionogenic tenside: 26-28 part;
Mineral alkali: 3-4 part;
Washing assistant: 3-4 part;
Inhibiter: 0.5-1.0 part;
Chain polyoxyethylene glycol: 8-10 part;
Deionized water: surplus;
Described anion surfactant is: alcohol ether carboxylate;
Described nonionogenic tenside is: C
12-14polyoxyethylenated alcohol.
2. metallic element clean-out system according to claim 1, it is characterized in that: described washing assistant is poly (sodium aspartate).
3. metallic element clean-out system according to claim 1, it is characterized in that: described mineral alkali is sodium oxalate.
4. metallic element clean-out system according to claim 1, it is characterized in that: described inhibiter is octadecylamine.
5. the preparation method of a metallic element clean-out system as claimed in claim 1, it is characterized in that this preparation method is: prepared burden by described formula, first by the chain polyoxyethylene glycol, add in deionized water and stir mixing, then under room temperature, mineral alkali is added in the mixed solution of chain polyoxyethylene glycol and deionized water, after mineral alkali dissolves fully, add successively anion surfactant, nonionogenic tenside, washing assistant, inhibiter under room temperature, stir and obtain described metallic element clean-out system.