CN107384214A - A kind of environment protection type wall covering ornament materials and preparation method thereof - Google Patents
A kind of environment protection type wall covering ornament materials and preparation method thereof Download PDFInfo
- Publication number
- CN107384214A CN107384214A CN201710796114.5A CN201710796114A CN107384214A CN 107384214 A CN107384214 A CN 107384214A CN 201710796114 A CN201710796114 A CN 201710796114A CN 107384214 A CN107384214 A CN 107384214A
- Authority
- CN
- China
- Prior art keywords
- parts
- ornament materials
- stirring
- mixture
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment protection type wall covering ornament materials and preparation method thereof, ornament materials component includes 40 60 parts of resin material, 10 30 parts of hydroxyethyl ether cellulose, 10 20 parts of organosilicon moisture repellent, 5 10 parts of binding agent, 8 16 parts of levelling agent, 4 12 parts of calcium zinc stabilizer, 5 10 parts of butyl titanate, 10 20 parts of expoxy propane, 10 20 parts of zingiberol ginger, 6 18 parts of 5 molecular sieves of ZSM in parts by weight, preparation method of the present invention is simple, and obtained ornament materials can reduce indoor pollution risk.
Description
Technical field
The present invention relates to ornament materials preparing technical field, specially a kind of environment protection type wall covering ornament materials and its preparation side
Method.
Background technology
Decorative paint refers to decoration and protection skin face, makes building appearance beautiful and clean, so as to reach beautification city
City's environment and the purpose for giving people salubrious space.It can also play a part of protecting building wall simultaneously, extend its service life.Wall
Face decorative paint is broadly divided into exterior coating and interior wall coating.
Easy release formaldehyde and benzene material after decorative material for wall surface use in the prior art, pollute surrounding air, Er Qiexian
Easy cracking phenomenon after some decorative paint uses.
The content of the invention
It is an object of the invention to provide a kind of environment protection type wall covering ornament materials and preparation method thereof, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides following technical scheme：A kind of environment protection type wall covering ornament materials, ornament materials
Component in parts by weight include resin material 40-60 parts, hydroxyethyl ether cellulose 10-30 parts, organosilicon moisture repellent 10-20 parts,
Binding agent 5-10 parts, levelling agent 8-16 parts, calcium zinc stabilizer 4-12 parts, butyl titanate 5-10 parts, expoxy propane 10-20 parts,
Zingiberol ginger 10-20 parts, ZSM-5 molecular sieve 6-18 parts.
Preferably, the preferable composition proportion of ornament materials component include 50 parts of resin material, 20 parts of hydroxyethyl ether cellulose,
15 parts of organosilicon moisture repellent, 8 parts of binding agent, 12 parts of levelling agent, 8 parts of calcium zinc stabilizer, 8 parts of butyl titanate, expoxy propane 15
Part, 15 parts of zingiberol ginger, 12 parts of ZSM-5 molecular sieve.
Preferably, its preparation method comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Compared with prior art, the beneficial effects of the invention are as follows：Preparation method of the present invention is simple, obtained ornament materials energy
Enough reduce indoor pollution risk；Wherein, the zingiberol ginger of addition, ZSM-5 molecular sieve being capable of the effectively benzene in sorbing material, formaldehyde
Material, prevent from polluting air；In addition, the stirring technique used in the preparation method used in the present invention can effectively prevent material
Material occur caking phenomenon, further increase convenience for construction, moreover, construction after be not in come off, cracking phenomena.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The present invention provides following technical scheme：A kind of environment protection type wall covering ornament materials, ornament materials component is in parts by weight
Including resin material 40-60 parts, hydroxyethyl ether cellulose 10-30 parts, organosilicon moisture repellent 10-20 parts, binding agent 5-10 parts, stream
Flat agent 8-16 parts, calcium zinc stabilizer 4-12 parts, butyl titanate 5-10 parts, expoxy propane 10-20 parts, zingiberol ginger 10-20 parts,
ZSM-5 molecular sieve 6-18 parts.
Embodiment one：
Ornament materials component includes 40 parts of resin material, 10 parts of hydroxyethyl ether cellulose, organosilicon moisture repellent 10 in parts by weight
Part, 5 parts of binding agent, 8 parts of levelling agent, 4 parts of calcium zinc stabilizer, 5 parts of butyl titanate, 10 parts of expoxy propane, 10 parts of zingiberol ginger,
6 parts of ZSM-5 molecular sieve.
The preparation method of the present embodiment comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Embodiment two：
Ornament materials component includes 60 parts of resin material, 30 parts of hydroxyethyl ether cellulose, organosilicon moisture repellent 20 in parts by weight
Part, 10 parts of binding agent, 16 parts of levelling agent, 12 parts of calcium zinc stabilizer, 10 parts of butyl titanate, 20 parts of expoxy propane, zingiberol ginger 20
Part, 18 parts of ZSM-5 molecular sieve.
The preparation method of the present embodiment comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Embodiment three：
Ornament materials component includes 45 parts of resin material, 13 parts of hydroxyethyl ether cellulose, organosilicon moisture repellent 12 in parts by weight
Part, 6 parts of binding agent, 9 parts of levelling agent, 6 parts of calcium zinc stabilizer, 6 parts of butyl titanate, 12 parts of expoxy propane, 12 parts of zingiberol ginger,
8 parts of ZSM-5 molecular sieve.
The preparation method of the present embodiment comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Example IV：
Ornament materials component includes 55 parts of resin material, 28 parts of hydroxyethyl ether cellulose, organosilicon moisture repellent 18 in parts by weight
Part, 8 parts of binding agent, 14 parts of levelling agent, 11 parts of calcium zinc stabilizer, 9 parts of butyl titanate, 18 parts of expoxy propane, zingiberol ginger 18
Part, 16 parts of ZSM-5 molecular sieve.
The preparation method of the present embodiment comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Embodiment five：
Ornament materials component includes 55 parts of resin material, 25 parts of hydroxyethyl ether cellulose, organosilicon moisture repellent 16 in parts by weight
Part, 8 parts of binding agent, 14 parts of levelling agent, 10 parts of calcium zinc stabilizer, 7 parts of butyl titanate, 16 parts of expoxy propane, zingiberol ginger 14
Part, 14 parts of ZSM-5 molecular sieve.
The preparation method of the present embodiment comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Embodiment six：
Ornament materials component includes 50 parts of resin material, 20 parts of hydroxyethyl ether cellulose, organosilicon moisture repellent 15 in parts by weight
Part, 8 parts of binding agent, 12 parts of levelling agent, 8 parts of calcium zinc stabilizer, 8 parts of butyl titanate, 15 parts of expoxy propane, 15 parts of zingiberol ginger,
12 parts of ZSM-5 molecular sieve.
The preparation method of the present embodiment comprises the following steps：
A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min
20min, obtain mixture A；
B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve
Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring
After 60min, mixture B is obtained；
C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.
Preparation method of the present invention is simple, and obtained ornament materials can reduce indoor pollution risk；Wherein, the zingiberol of addition
Ginger, ZSM-5 molecular sieve can the effectively benzene in sorbing material, formaldehyde material, prevent from polluting air；In addition, adopted in the present invention
The stirring technique used in preparation method can effectively prevent material from caking phenomenon occurs, and further increase construction just
Profit, moreover, construction after be not in come off, cracking phenomena.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
- A kind of 1. environment protection type wall covering ornament materials, it is characterised in that：Ornament materials component includes resin material 40- in parts by weight 60 parts, hydroxyethyl ether cellulose 10-30 parts, organosilicon moisture repellent 10-20 parts, binding agent 5-10 parts, levelling agent 8-16 parts, calcium Zinc stabilizer 4-12 parts, butyl titanate 5-10 parts, expoxy propane 10-20 parts, zingiberol ginger 10-20 parts, ZSM-5 molecular sieve 6-18 Part.
- A kind of 2. environment protection type wall covering ornament materials according to claim 1, it is characterised in that：Ornament materials component is preferable Composition proportion includes 50 parts of resin material, 20 parts of hydroxyethyl ether cellulose, 15 parts of organosilicon moisture repellent, 8 parts of binding agent, levelling agent 12 parts, 8 parts of calcium zinc stabilizer, 8 parts of butyl titanate, 15 parts of expoxy propane, 15 parts of zingiberol ginger, 12 parts of ZSM-5 molecular sieve.
- 3. realize a kind of preparation method of environment protection type wall covering ornament materials described in claim 1, it is characterised in that：Its preparation side Method comprises the following steps：A, by resin material, hydroxyethyl ether cellulose, organosilicon moisture repellent, binding agent, low speed in agitator tank is added after mixing and is stirred Mix, stir speed (S.S.) is 200 revs/min, and levelling agent, calcium zinc stabilizer are sequentially added in whipping process, is stood after stirring 30min 20min, obtain mixture A；B, stirring at low speed in agitator tank, stirring are added after mixing butyl titanate, expoxy propane, zingiberol ginger, ZSM-5 molecular sieve Speed is 500 revs/min, and mixture A is added in whipping process, stir speed (S.S.) is slowly increased into 1500 revs/min afterwards, stirring After 60min, mixture B is obtained；C, mixture B is placed after standing 24h at normal temperatures, that is, obtains ornament materials.