CN108457078A - Environmental-friendfilm film construction material and its manufacture craft - Google Patents

Environmental-friendfilm film construction material and its manufacture craft Download PDF

Info

Publication number
CN108457078A
CN108457078A CN201810486214.2A CN201810486214A CN108457078A CN 108457078 A CN108457078 A CN 108457078A CN 201810486214 A CN201810486214 A CN 201810486214A CN 108457078 A CN108457078 A CN 108457078A
Authority
CN
China
Prior art keywords
base fabric
environmental
baking
film construction
plasticizing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810486214.2A
Other languages
Chinese (zh)
Inventor
边晓伟
阮长青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sun Thin Cloth (shanghai) Nanometer Technology Co Ltd
Original Assignee
Sun Thin Cloth (shanghai) Nanometer Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sun Thin Cloth (shanghai) Nanometer Technology Co Ltd filed Critical Sun Thin Cloth (shanghai) Nanometer Technology Co Ltd
Priority to CN201810486214.2A priority Critical patent/CN108457078A/en
Publication of CN108457078A publication Critical patent/CN108457078A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of environmental-friendfilm film construction materials, it includes the substance of following proportioning:Base fabric 35 50%, liquid flame retardant 10 20%, silica slurry 55 70%, fluorubber 1 20%;The base fabric is woven by filament.Reasonable design, it is skillfully constructed, overcome traditional membrane material there are the shortcomings that, degradable, nontoxic, odorlessness is free of bioxin, and with spatial structure building film material tension, tear-proof is strong, high-air-tightness, soda acid, wear-resisting, high and low temperature resistance and corrosion resistance, light, surface is smooth, anti-fouling and self-cleaning, sound insulation, anti-aging, flexibility is good, fire-retardant, insulation, translucency is good, service life is long, it is widely used in the decoration of air film, membrane structure building, park, venue, process is pollution-free, energy conservation and environmental protection.

Description

Environmental-friendfilm film construction material and its manufacture craft
Technical field
The present invention relates to building material fields, and in particular to a kind of environmental-friendfilm film construction material and its manufacture craft.
Background technology
Some large-scale athletic competition venue, showground, departure hall, shopping centers etc. building, from 70 Just replace traditional building steel brick mixed structure from age with the membrane material structure of large span, but these membrane material structures all rely on into Mouthful, it is not only expensive, a large amount of foreign exchanges are needed, and more important is import membrane materials unsatisfactory in quality, service life Short, tension, tearing toughness are low, exceeded containing bioxin, it is not possible to degrade, weatherability is poor, and clean surfaces performance is of short duration, reflectivity Poor, inflammable, the easy sound-absorbing of energy, soundproof effect are poor.
Traditional material disadvantage, most of the membrane structure material on the current international market of substitute is all that cannot degrade and contain The exceeded product of bioxin causes pollution to environment.
Invention content
To solve the above problems, a kind of environmental-friendfilm film construction material of present invention proposition and its manufacture craft, reasonable design, design It is ingenious, overcome traditional membrane material there are the shortcomings that, degradable, nontoxic, odorlessness, be free of bioxin, and have space structure Building film material tension, tear-proof are strong, high-air-tightness, soda acid, wear-resisting, high and low temperature resistance and corrosion resistance, light, surface is smooth, it is antifouling from Clean, sound insulation, anti-aging, flexibility is good, fire-retardant, insulation, translucency is good, service life is long, is widely used in air film, membrane structure is built Build, park, venue decoration, process is pollution-free, energy conservation and environmental protection.
A kind of environmental-friendfilm film construction material, it includes the substance of following proportioning:Base fabric 35-50%, liquid flame retardant 10- 20%, silica slurry 55-70%, fluorubber 1-20%;The base fabric is woven by filament.
A kind of manufacture craft of environmental-friendfilm film construction material, it includes the following steps:
1)Base fabric makes
Filament carries out being woven into base fabric.
2)Environmentally friendly membrane material prepares
It by silica slurry, liquid flame retardant, is mixed evenly according to the ratio, then mixture is coated in base fabric, coating Base fabric afterwards coats and toasts in triplicate plasticizing by the baking plasticizing of baking oven high humidity.
3)Surface treatment
Toasted plasticizing base fabric carries out fluorubber anti-pollution processing by the liquid fluorubber being arranged in large cylinder.
4)Toast sulfidization molding
Baking oven high humidity baking temperature is set as 170 DEG C~230 DEG C, baking vulcanization time is 20~30min, will be in step 3 The base fabric handled well be put into baking oven carry out baking vulcanization form dry film, then dry film is put into high temperature furnace again, 120 DEG C~ 10~20min of solid phase reaction at a temperature of 180 DEG C forms environmental-friendfilm film construction material.
Above-mentioned technical proposal is improved further and is refined, coats and toasts in triplicate in step 2 plasticizing, mix It closes and forms four layer stackup space structures between object and base fabric.
Traditional Environmental-protection membrane building material is compared, the method have the advantages that, according to environmental-friendfilm film raw material of building materials characteristic, the invention Environmental-friendfilm film construction material is degradable, nontoxic, odorlessness, is free of bioxin and with spatial structure building film material tension, tear-proof By force, high-air-tightness, soda acid, wear-resisting, high and low temperature resistance and corrosion resistance, light, surface is smooth, anti-fouling and self-cleaning, sound insulation, anti-aging, flexible Property it is good, fire-retardant, insulation, translucency is good, service life is long, be widely used in air film, membrane structure building, park, venue, decoration etc. Building, process is pollution-free, energy conservation and environmental protection.
Specific implementation mode
A kind of environmental-friendfilm film construction material, it includes the substance of following proportioning:Base fabric 35-50%, liquid flame retardant 10- 20%, silica slurry 55-70%, fluorubber 1-20%;The base fabric is woven by filament.
A kind of manufacture craft of environmental-friendfilm film construction material, it includes the following steps:
1)Base fabric makes
Filament carries out being woven into base fabric.
2)Environmentally friendly membrane material prepares
It by silica slurry, liquid flame retardant, is mixed evenly according to the ratio, then mixture is coated in base fabric, coating Base fabric afterwards coats and toasts in triplicate plasticizing by the baking plasticizing of baking oven high humidity.
3)Surface treatment
Toasted plasticizing base fabric carries out fluorubber anti-pollution processing by the liquid fluorubber being arranged in large cylinder.
4)Toast sulfidization molding
Baking oven high humidity baking temperature is set as 170 DEG C~230 DEG C, baking vulcanization time is 20~30min, will be in step 3 The base fabric handled well be put into baking oven carry out baking vulcanization form dry film, then dry film is put into high temperature furnace again, 120 DEG C~ 10~20min of solid phase reaction at a temperature of 180 DEG C forms environmental-friendfilm film construction material.
Plasticizing is coated and toasted in triplicate in step 2, forms four layer stackup space structures between mixture and base fabric.
Due to the finiteness of literal expression, and objectively there is unlimited concrete structure, for the common of the art For technical staff, without departing from the principle of the present invention, several improvement, retouching or variation can also be made, it can also Above-mentioned technical characteristic is combined in the right way;These improve retouching, variation or combination, or not improved by invention Design and technical solution directly apply to other occasions, are regarded as protection scope of the present invention.

Claims (3)

1. a kind of environmental-friendfilm film construction material, it is characterised in that:It includes the substance of following proportioning:Base fabric 35-50%, liquid resistance Fire agent 10-20%, silica slurry 55-70%, fluorubber 1-20%;The base fabric is woven by filament.
2. a kind of manufacture craft of environmental-friendfilm film construction material, it is characterised in that:It includes the following steps
1)Base fabric makes
Filament carries out being woven into base fabric;
2)Environmentally friendly membrane material prepares
It by silica slurry, liquid flame retardant, is mixed evenly according to the ratio, then mixture is coated in base fabric, coating Base fabric afterwards coats and toasts in triplicate plasticizing by the baking plasticizing of baking oven high humidity;
3)Surface treatment
Toasted plasticizing base fabric carries out fluorubber anti-pollution processing by the liquid fluorubber being arranged in large cylinder;
4)Toast sulfidization molding
Baking oven high humidity baking temperature is set as 170 DEG C~230 DEG C, baking vulcanization time is 20~30min, will be in step 3 The base fabric handled well be put into baking oven carry out baking vulcanization form dry film, then dry film is put into high temperature furnace again, 120 DEG C~ 10~20min of solid phase reaction at a temperature of 180 DEG C forms environmental-friendfilm film construction material.
3. a kind of manufacture craft of environmental-friendfilm film construction material according to claim 2, it is characterised in that:It weighs in step 2 It is multiple to coat and toast three times plasticizing, four layer stackup space structures are formed between mixture and base fabric.
CN201810486214.2A 2018-05-21 2018-05-21 Environmental-friendfilm film construction material and its manufacture craft Pending CN108457078A (en)