CN107384046A - A kind of mono-component aqueous interior wall engineering paint and preparation method thereof - Google Patents
A kind of mono-component aqueous interior wall engineering paint and preparation method thereof Download PDFInfo
- Publication number
- CN107384046A CN107384046A CN201710707526.7A CN201710707526A CN107384046A CN 107384046 A CN107384046 A CN 107384046A CN 201710707526 A CN201710707526 A CN 201710707526A CN 107384046 A CN107384046 A CN 107384046A
- Authority
- CN
- China
- Prior art keywords
- parts
- mono
- thickener
- interior wall
- aqueous interior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of mono-component aqueous interior wall engineering paint and preparation method thereof,Mono-component aqueous interior wall engineering paint includes 100 130 parts of film forming matter I,130 150 parts of film forming matter II,350 380 parts of constitution modified filler,14 parts of thickener I,12 parts of thickener II,35 parts of thickener III,13 parts of wetting agent,47 parts of dispersant I,57 parts of dispersant II,23 parts of defoamer I,12 parts of defoamer II,57 parts of antifreezing agent,20 40 parts of Chinese white,12 parts of multifunctional assistant,20 30 parts of constitution filler,12 parts of mould inhibitor,12 parts of preservative,0.1 part of essence and 265 305 parts of deionized water,Wherein,The particle diameter of constitution modified filler is more than 2000 mesh,The composite granule of internal porous.The engineering paint period of storage of the present invention is more than 18 months.
Description
Technical field
The invention belongs to paint field, in particular it relates to a kind of mono-component aqueous interior wall engineering paint and above-mentioned one pack system
The preparation method of water-based inner wall engineering paint.
Background technology
Engineering paint is applied to industry-by-industry, every field, by feat of it in our life in our life
It is seen everywhere, with reference to China's actual conditions, the developing direction of dope for inner wall of architecture should be medium and high classes engineering paint, not require nothing more than
With good scrub resistance, can opening, rheological characteristic, brushability etc., it is necessary to health type develop, be done step-by-step Diamond Search and
Residual monomers as few as possible, the original performance of coating, and nontoxic, free from extraneous odour how are improved, meets green structural material
Requirement become research staff at present required for solve the problems, such as.
Prior art is utilizing the interior wall engineering paint of the useless powder work of artificial stone, and it is thick particle occur.And after depositing a period of time
Can slowly it thicken, or even gel.
The content of the invention
In view of this, first purpose of the invention is to propose a kind of mono-component aqueous interior wall engineering paint, when it is deposited
Between it is long, it is easier to preserve.
Second object of the present invention is the preparation method for proposing above-mentioned mono-component aqueous interior wall engineering paint.
In order to solve the above technical problems, the present invention is achieved using following technical scheme：
A kind of mono-component aqueous interior wall engineering paint, include the component of following parts by weight：
The film forming matter I of 100-130 parts, the film forming matter II of 130-150 parts, the constitution modified filler of 350-380 parts, 1-4 parts
Thickener I, the thickener II of 1-2 parts, the thickener III of 3-5 parts, the wetting agent of 1-3 parts, the dispersant I of 4-7 parts, 5-7 parts
Dispersant II, defoamer I, the defoamer II of 1-2 parts, the antifreezing agent of 5-7 parts, the Chinese white, 1-2 of 20-40 parts of 2-3 parts
Part multifunctional assistant, the constitution filler of 20-30 parts, the mould inhibitor of 1-2 parts, the preservative of 1-2 parts, 0.1 part of essence and
The deionized water of 265-305 parts, wherein, constitution modified filler be particle diameter more than 2000 mesh, and the composite powder of internal porous
Body.
Above-mentioned composite granule, its source have three kinds：
Source one：With acryl resin, unsaturated-resin, epoxy resin, polyester resin, phenolic resin, acrylic resin,
Raw material based on polyvinyl resin, polystyrene resin etc., using special hydrogen alumina powder as filler, with polyfunctional monomer (such as
Acrylamide, N.N hydroxyacrylamides) it is cross-linking type raw material, (such as hydrogen peroxide, cross chlorine by initiator of low temperature peroxide
Acid amides) crosslinking curing is carried out, then cured product is polished, collected；Deeply broken, collection etc. crush, again again again
Homogenizing is collected, obtains particle diameter more than 2000 mesh, and the extraordinary composite granule of internal porous.
Source two：Using above-mentioned homogeneous raw material directly by extrusion molding, solidification, broken, collection method, to obtain grain
Footpath is more than 2000 mesh, and the extraordinary composite granule of internal porous.
Source three：Current numerous enterprises are made full use of in Ya Ke of the production body plane materiel as being added with special hydrogen alumina powder
Polish on power sheet material, unsaturated-resin sheet material, epoxy resin sheet material and their other shaped articles such as surface such as bathtub, core basin
Collected powder is that 400-600 mesh composite granules are raw material afterwards, then is crushed, to obtain particle diameter more than 2000 mesh,
And the extraordinary composite granule of internal porous.
Preferably, the film forming matter I is the PVA glue of 6.0-10% concentration；The film forming matter II is primary chemical
Composition is the material of copolymer in cinnamic acrylic ester, selected from D-800, GHT-1, GHT-1D, AP-658, XG-2000, XG-
One kind in 2013.
Above-mentioned film forming matter I is prepared as the special type of two layers of oil resistant up and down of acryl plates production line sheet material protection
PVA (polyvinyl alcohol) film, it is better than common polyvinyl alcohol film compactness, and water resistance and oil resistivity are much excellent, used
After take off, directly dissolved after broken with 60-80 DEG C of deionized water, controlled concentration is in 6.0-10% or so.
Preferably, the thickener I is carboxymethyl cellulose, CMS, xanthans, Casein, gelatin, first
One or more in base cellulose, hydroxyethyl cellulose, methylhydroxypropylcellulose；The thickener II is bentonite, two
One kind in silica, Attapulgite；The thickener III is acrylic acid and acrylate copolymer with carboxyl, selected from HS-
325th, the one or more in HS-663, HS-935, HS-970, HS-663, TT-935.
Preferably, the wetting agent is the condensation products that main chemical compositions are alkyl phenol and oxirane, selected from X-
405th, one kind in CF-01, OP-10, TX-10, OF-10, FN-211, FN-225.
Preferably, the dispersant I is alkyl sulfate, alkyl aryl sulfonate, polyoxyethylene-modified alkyl sulfide
One or more in acid esters, APES, polycarboxylate, polymethacrylate derivative；The dispersant II
For the one or more in sodium pyrophosphate, tertiary sodium phosphate, calgon, sodium metasilicate, sodium disilicate.
Preferably, the defoamer I is the materials that main chemical compositions are mineral oil, selected from GF-309A, BASF-
One kind in 309A, foamaster-309A, SN-DEFOAMER-309A, D-309A, WT-309A, NO-FOAM-309A；It is described
Defoamer II be main chemical compositions be polyethers material, selected from FOAMASTER 8034A, WBA-8034A, BASF-8034A,
One kind in HT-8034A, F-126, SN-DEFOANER 8034A.
Preferably, the multifunctional assistant is one kind in HX-6130, C-950, AMP-96, MA-95；It is described anti-
Jelly agent is one or both of ethylene glycol, glycerine.
Preferably, the Chinese white is the one or more in titanium dioxide, zinc white, lithopone, stibium trioxide powder；Institute
Constitution filler is stated as the one or more in talcum powder, kaolin, wollastonite, mica powder, sericite, synthetic aluminium silicate.
Preferably, the mould inhibitor is isothiazolinone derivatives, benzimidazole compound, substituted arene chemical combination
One or more in thing, release formaldehyde class compound；The preservative be organic bromine class compound, organic amine compound,
One or more in compound in triazine class.
Second object of the present invention is achieved by the following technical programs：
A kind of preparation method of mono-component aqueous interior wall engineering paint, comprises the following steps：
(1) most of deionized water is first added in scuffing of cylinder bore as solvent, starts dispersion machine, thickening is added under stirring at low speed
Agent I and thickener II, stirring at low speed 3-5 minutes；
(2) continue to put into wetting agent, dispersant I, dispersant II, defoamer I into its scuffing of cylinder bore, continue to stir 3-5 minutes；
(3) continue to throw multifunctional assistant, film forming matter I, antifreezing agent into scuffing of cylinder bore, stir to thickener I and be completely dissolved；
(4) dispersion machine is adjusted to medium-to-high grade rotating speed, then adds Chinese white, constitution filler, constitution modified filler successively,
Scattered 40-60 minutes at a high speed；
(5) dispersion machine is adjusted to low-grade rotating speed, adds defoamer II, film forming matter II, mould inhibitor, preservative, international odor type
Spices, the balance deionized water of thickener III, stirring 15-20 minutes produce.
The present invention have the advantage that compared with prior art for：The present invention passes through the ways such as recipe determination, refinement making
Footpath, take different measure to be improved, can reach international comprehensively with discarded artificial stone flour production is a, period of storage is more than 18
The interior wall engineering paint of the moon.Spy of the interior wall engineering paint that the present invention can utilize the useless powder of artificial stone and prepare except possessing ordinary skill paint
Point is outer, also with the function such as damp proof, sound insulation, wear-resisting, more recycles useless powder and creates a practical way, promote change to give up into
Precious realization, it is worth for social creativity.
Embodiment
The present invention is got information about to allow those skilled in the art to become apparent from, the present invention will be made below further
Explanation.
A kind of mono-component aqueous interior wall engineering paint, include the component of following parts by weight：
The film forming matter I of 100-130 parts, the film forming matter II of 130-150 parts, the constitution modified filler of 350-380 parts, 1-4 parts
Thickener I, the thickener II of 1-2 parts, the thickener III of 3-5 parts, the wetting agent of 1-3 parts, the dispersant I of 4-7 parts, 5-7 parts
Dispersant II, defoamer I, the defoamer II of 1-2 parts, the antifreezing agent of 5-7 parts, the Chinese white, 1-2 of 20-40 parts of 2-3 parts
Part multifunctional assistant, the constitution filler of 20-30 parts, the mould inhibitor of 1-2 parts, the preservative of 1-2 parts, 0.1 part of essence and
The deionized water of 265-305 parts, wherein, constitution modified filler be particle diameter more than 2000 mesh, and the composite powder of internal porous
Body.
Above-mentioned composite granule, its source have three kinds：
Source one：With acryl resin, unsaturated-resin, epoxy resin, polyester resin, phenolic resin, acrylic resin,
Raw material based on polyvinyl resin, polystyrene resin etc., using special hydrogen alumina powder as filler, with polyfunctional monomer (such as
Acrylamide, N.N hydroxyacrylamides) it is cross-linking type raw material, (such as hydrogen peroxide, cross chlorine by initiator of low temperature peroxide
Acid amides) crosslinking curing is carried out, then cured product is polished, collected；Deeply broken, collection etc. crush, again again again
Homogenizing is collected, obtains particle diameter more than 2000 mesh, and the extraordinary composite granule of internal porous.
Source two：Using above-mentioned homogeneous raw material directly by extrusion molding, solidification, broken, collection method, to obtain grain
Footpath is more than 2000 mesh, and the extraordinary composite granule of internal porous.
Source three：Current numerous enterprises are made full use of in Ya Ke of the production body plane materiel as being added with special hydrogen alumina powder
Polish on power sheet material, unsaturated-resin sheet material, epoxy resin sheet material and their other shaped articles such as surface such as bathtub, core basin
Collected powder is that 400-600 mesh composite granules are raw material afterwards, then is crushed, to obtain particle diameter more than 2000 mesh,
And the extraordinary composite granule of internal porous.
The film forming matter I is the PVA glue of 6.0-10% concentration；The film forming matter II is that main chemical compositions are benzene second
The material of alkene-acrylate copolymer, one in D-800, GHT-1, GHT-1D, AP-658, XG-2000, XG-2013
Kind.
Above-mentioned film forming matter I is prepared as the special type of two layers of oil resistant up and down of acryl plates production line sheet material protection
PVA (polyvinyl alcohol) film, it is better than common polyvinyl alcohol film compactness, and water resistance and oil resistivity are much excellent, used
After take off, directly dissolved after broken with 60-80 DEG C of deionized water, controlled concentration is in 6.0-10% or so.
The thickener I is carboxymethyl cellulose, CMS, xanthans, Casein, gelatin, methylcellulose, hydroxyl
One or more in ethyl cellulose, methylhydroxypropylcellulose；The thickener II is bentonite, silica, recessed rod
One kind in soil；The thickener III is acrylic acid and acrylate copolymer with carboxyl, selected from HS-325, HS-663, HS-
935th, the one or more in HS-970, HS-663, TT-935；The wetting agent is that main chemical compositions are alkyl phenol and epoxy
The condensation product of ethane, one kind in X-405, CF-01, OP-10, TX-10, OF-10, FN-211, FN-225；It is described scattered
Agent I is alkyl sulfate, alkyl aryl sulfonate, polyoxyethylene-modified alkyl sulfate, APES, polycarboxylic acids
One or more in salt, polymethacrylate derivative；The dispersant II is sodium pyrophosphate, tertiary sodium phosphate, hexa metaphosphoric acid
One or more in sodium, sodium metasilicate, sodium disilicate；The defoamer I is the materials that main chemical compositions are mineral oil, is selected
From GF-309A, BASF-309A, foamaster-309A, SN-DEFOAMER-309A, D-309A, WT-309A, NO-FOAM-
One kind in 309A；The defoamer II is the materials that main chemical compositions are polyethers, selected from FOAMASTER 8034A, WBA-
One kind in 8034A, BASF-8034A, HT-8034A, F-126, SN-DEFOANER 8034A；The multifunctional assistant is
One kind in HX-6130, C-950, AMP-96, MA-95；The antifreezing agent is one or both of ethylene glycol, glycerine；Institute
Chinese white is stated as the one or more in titanium dioxide, zinc white, lithopone, stibium trioxide powder；The constitution filler is talcum powder, height
One or more in ridge soil, wollastonite, mica powder, sericite, synthetic aluminium silicate；The mould inhibitor derives for OIT
One or more in thing, benzimidazole compound, substituted arene compound, release formaldehyde class compound；The preservative is
One or more in organic bromine class compound, organic amine compound, compound in triazine class.
Further illustrated below by three embodiments.
Embodiment 1
The formula such as following table that the mono-component aqueous interior wall engineering paint of the present embodiment specifically uses
Its preparation technology and flow are as follows：
(1) deionized water 262.0kg is first added in scuffing of cylinder bore, starts dispersion machine, hydroxy ethyl fiber is added under stirring at low speed
Plain thickener 2.9kg and EW-2 bentonite thickener 1.5kg, stirring at low speed 3-5 minutes；(2) continue to put into TX- into its scuffing of cylinder bore
10 wetting agent 1.8kg, H-1900W dispersant 6.0kg, sodium pyrophosphate dispersant 5.8kg, GF-309A defoamer 2.4kg, continue
Stir 3-5 minutes；(3) continue to throw C-950 multifunctional assistants 1.5kg, 10% concentration PVA glue film forming matters of self-control into scuffing of cylinder bore
120.0kg, ethylene glycol antifreeze 6.0kg, stir to hydroxyethylcellulose thickener and are completely dissolved, about 5 minutes；(4) will divide
Scattered machine is adjusted to medium-to-high grade rotating speed, then adds R986 Chinese whites 33.0kg, kaolin constitution filler 24.0kg, constitution successively and changes
Property filler --- make extraordinary composite granule 375kg by oneself, at a high speed scattered 40-60 minutes；(5) dispersion machine is adjusted to low-grade rotating speed, added
8034A defoamer 1.5kg, GHT-1 styrene-acrylic emulsion film forming matter 140.0kg, PE-5 mould inhibitor 1.5kg, ZX-105 preservative 1.5,
International fragrant perfume 0.1kg, HS-935 thickener 4.1kg, balance deionized water 29.4kg, stir 15-20 minutes；(6) examine
It is qualified, filter and package.
Embodiment 2
The formula such as following table that the mono-component aqueous interior wall engineering paint of the present embodiment specifically uses
Its preparation technology and flow are as follows：
(1) deionized water 255.0kg is first added in scuffing of cylinder bore, starts dispersion machine, QD-300 fibers is added under stirring at low speed
Plain thickener 3.0kg and EW-2 bentonite thickener 1.5kg, stirring at low speed 3-5 minutes；(2) continue to put into OF- into its scuffing of cylinder bore
10 wetting agent 1.7kg, alkyl sulfate dispersant 5.8kg, calgon dispersant 6.0kg, BASF-309A defoamer
2.6kg, continue to stir 3-5 minutes；(3) continue to throw AMP-96 multifunctional assistants 1.3kg, 10% concentration PVA of self-control into scuffing of cylinder bore
Glue film forming matter 120.0kg, ethylene glycol antifreeze 6.0kg, stir to QD-300 cellulose thickeners and are completely dissolved, about 5 points
Clock；(4) dispersion machine is adjusted to medium-to-high grade rotating speed, then adds R996 Chinese whites 30.0kg, kaolin constitution filler successively
27.0kg, constitution modified filler --- make extraordinary composite granule 375kg by oneself, at a high speed scattered 40-60 minutes；(5) dispersion machine is adjusted to
Low-grade rotating speed, add BASF-8034A defoamer 1.5kg, XG-2000 styrene-acrylic emulsion film forming matter 140.0kg, PE-5 mould inhibitors
1.5kg, ZX-105 preservative 1.5, international fragrant perfume 0.1kg, HS-935 thickener 3.8kg, balance deionized water 36.7kg,
Stir 15-20 minutes；(6) it is qualified to examine, and filters and packages.
Embodiment 3
The formula such as following table that the mono-component aqueous interior wall engineering paint of the present embodiment specifically uses
Its preparation technology and flow are as follows：
(1) deionized water 265.0kg is first added in scuffing of cylinder bore, starts dispersion machine, methylhydroxypropyl is added under stirring at low speed
Cellulose thickener 2.7kg and EW-2 bentonite thickener 1.5kg, stirring at low speed 3-5 minutes；(2) continue to throw into its scuffing of cylinder bore
Enter X-405 wetting agents 2.0kg, alkyl aryl sulfonate dispersant 6.1kg, tertiary sodium phosphate dispersant 5.7kg, 309A defoamer
2.5kg, continue to stir 3-5 minutes；(3) continue to throw MA-95 multifunctional assistants 1.4kg, 10% concentration PVA glue of self-control into scuffing of cylinder bore
MJPZ thing 120.0kg, ethylene glycol antifreeze 6.0kg, stir to methylhydroxypropylcellulose thickener and are completely dissolved, and about 5
Minute；(4) dispersion machine is adjusted to medium-to-high grade rotating speed, then adds R966 Chinese whites 32.0kg, kaolin constitution filler successively
25.0kg, constitution modified filler --- make extraordinary composite granule 375kg by oneself, at a high speed scattered 40-60 minutes；(5) dispersion machine is adjusted to
Low-grade rotating speed, add HT-8034A defoamer 1.5kg, GHT-1D styrene-acrylic emulsion film forming matter 140.0kg, PE-5 mould inhibitors
1.5kg, ZX-105 preservative 1.5, international fragrant perfume 0.1kg, HS-935 thickener 4.0kg, balance deionized water 26.5kg,
Stir 15-20 minutes；(6) it is qualified to examine, and filters and packages.
The assay of product made from above-described embodiment 1-3：
Drying time：2h or so；
Water resistance：96h or so, it is without exception；
Alkali resistance：48h or so, it is without exception；
Abrasion resistance：Surpass 1000 times；
Viscosity：99.4KU or so；
Article characteristic：
Paint film is fine and smooth, fungicidal properties is superior, covering power is good；
Scrubbing resistance far super national standard more than 1000 times (can reach 3-4 times of like product), remaining index reaches Standard.
It should be noted that one of source of above-mentioned composite granule filler is voluntarily to be prepared, it includes as follows
The component of parts by weight：
The friendship of the matrix of powder material of 6-9 parts, the powder stuffing of 17-22 parts, 0.1~0.2 part of difunctional or trifunctional
Connection type raw material, 0.02~0.03 part of asymmetric organic peroxide low temperature curing agent, 0.01~0.02 part of solidification trigger
Agent, 0.01~0.02 part of accelerator and 1~2 part of pigment；Wherein, the matrix of powder material is resin slurry, the powder
Filler is special hydrogen alumina powder, and the resin slurry is acryl resin, unsaturated-resin, epoxy resin, polyester resin, phenol
One kind in urea formaldehyde, acrylic resin, polyvinyl resin, polystyrene resin, the concentration of resin slurry is 10~15%, institute
The cross-linking type raw material for stating difunctional or trifunctional is acrylamide, one or two kinds of, the institute in N.N hydroxyacrylamides
State asymmetric organic peroxide low temperature curing agent to be hydrogen peroxide, cross one or both of chloroamide, the pigment is
Titanium dioxide either phthalocyanine blue or phthalocyanine green, selected according to the color of product；The curing initiator is cyclohexanone peroxide, institute
It is cobalt naphthenate to state accelerator.
Specific preparation method is as follows：
(1) matrix of powder material made from dissolving or pre-polymerization and special hydrogen alumina powder are delivered to fully mixed among mixing kettle
Close, while the color of whole material reconciled with pigment, then add into mixing kettle difunctional or trifunctional cross-linking type raw material,
Asymmetric organic peroxide low temperature curing agent, curing initiator and accelerator；Then pour into a mould or extrude in glass mold
Or on steel band, cross-linking and curing reaction is carried out at 30-50 DEG C, 30-90 minutes are reacted, obtain the tabular for being easy to polishing broken
Solid material；(2) board-like entity material is subjected to continuous polish and is crushed to the coarse powder of 100-400 mesh, coarse powder collected standby；
(3) coarse powder is subjected to fine gtinding with ultra-fine grinding mill, obtains fineness as 2000 mesh and the fine powder of the above, fine powder is collected；
(4) metering packing is carried out to fine powder.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
Those familiar with the art the invention discloses technical scope in, change or replacement can be readily occurred in, should all be contained
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should be based on the protection scope of the described claims.
Claims (10)
1. a kind of mono-component aqueous interior wall engineering paint, it is characterised in that include the component of following parts by weight：
The film forming matter I of 100-130 parts, the film forming matter II of 130-150 parts, 350-380 parts constitution modified filler, 1-4 parts increasing
Thick dose I, the thickener II of 1-2 parts, the thickener III of 3-5 parts, the wetting agent of 1-3 parts, the dispersant I of 4-7 parts, 5-7 parts point
Powder II, the defoamer I of 2-3 parts, the defoamer II of 1-2 parts, the antifreezing agent of 5-7 parts, the Chinese white of 20-40 parts, 1-2 parts
Multifunctional assistant, the constitution filler of 20-30 parts, the mould inhibitor of 1-2 parts, the preservative of 1-2 parts, 0.1 part of essence and 265-
305 parts of deionized water, wherein, constitution modified filler be particle diameter more than 2000 mesh, and the composite granule of internal porous.
2. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the film forming matter I is 6.0-
The PVA glue of 10% concentration；The film forming matter II is the materials that main chemical compositions are copolymer in cinnamic acrylic ester, is selected
From one kind in D-800, GHT-1, GHT-1D, AP-658, XG-2000, XG-2013.
3. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the thickener I is carboxymethyl
Cellulose, CMS, xanthans, Casein, gelatin, methylcellulose, hydroxyethyl cellulose, methylhydroxypropylcellulose
In one or more；The thickener II is one kind in bentonite, silica, Attapulgite；The thickener III is band
The acrylic acid and acrylate copolymer of carboxyl, in HS-325, HS-663, HS-935, HS-970, HS-663, TT-935
One or more.
4. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the wetting agent is primary chemical
Composition is the condensation product of alkyl phenol and oxirane, selected from X-405, CF-01, OP-10, TX-10, OF-10, FN-211, FN-
One kind in 225.
5. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the dispersant I is alkyl sulfide
Acid esters, alkyl aryl sulfonate, polyoxyethylene-modified alkyl sulfate, APES, polycarboxylate, poly- methyl-prop
One or more in gadoleic acid derivative；The dispersant II be sodium pyrophosphate, tertiary sodium phosphate, calgon, sodium metasilicate,
One or more in sodium disilicate.
6. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the defoamer I is mainization
Point material for being mineral oil is studied, selected from GF-309A, BASF-309A, foamaster-309A, SN-DEFOAMER-309A, D-
One kind in 309A, WT-309A, NO-FOAM-309A；The defoamer II is the materials that main chemical compositions are polyethers, is selected from
One in FOAMASTER 8034A, WBA-8034A, BASF-8034A, HT-8034A, F-126, SN-DEFOANER 8034A
Kind.
7. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the multifunctional assistant is HX-
6130th, one kind in C-950, AMP-96, MA-95；The antifreezing agent is one or both of ethylene glycol, glycerine.
8. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the Chinese white is titanium white
One or more in powder, zinc white, lithopone, stibium trioxide powder；The constitution filler is talcum powder, kaolin, wollastonite, mica
One or more in powder, sericite, synthetic aluminium silicate.
9. mono-component aqueous interior wall engineering paint according to claim 1, it is characterised in that the mould inhibitor is isothiazoline
One or more in ketone derivatives, benzimidazole compound, substituted arene compound, release formaldehyde class compound；It is described anti-
Rotten agent is the one or more in organic bromine class compound, organic amine compound, compound in triazine class.
10. the preparation method of the mono-component aqueous interior wall engineering paint according to claim any one of 1-9, it is characterised in that
Comprise the following steps：
(1) most of deionized water is first added in scuffing of cylinder bore as solvent, starts dispersion machine, thickener I is added under stirring at low speed
With thickener II, stirring at low speed 3-5 minutes；
(2) continue to put into wetting agent, dispersant I, dispersant II, defoamer I into its scuffing of cylinder bore, continue to stir 3-5 minutes；
(3) continue to throw multifunctional assistant, film forming matter I, antifreezing agent into scuffing of cylinder bore, stir to thickener I and be completely dissolved；
(4) dispersion machine is adjusted to medium-to-high grade rotating speed, then adds Chinese white, constitution filler, constitution modified filler successively, at a high speed
Scattered 40-60 minutes；
(5) dispersion machine is adjusted to low-grade rotating speed, add defoamer II, film forming matter II, mould inhibitor, preservative, international fragrant perfume,
The balance deionized water of thickener III, stirring 15-20 minutes produce.