CN107383842A - 一种建筑用吸音板材及其制备方法 - Google Patents
一种建筑用吸音板材及其制备方法 Download PDFInfo
- Publication number
- CN107383842A CN107383842A CN201710644645.2A CN201710644645A CN107383842A CN 107383842 A CN107383842 A CN 107383842A CN 201710644645 A CN201710644645 A CN 201710644645A CN 107383842 A CN107383842 A CN 107383842A
- Authority
- CN
- China
- Prior art keywords
- parts
- sound
- building panel
- panel material
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂13～18份、石膏5～9份、聚酰胺3～8份、聚苯乙烯泡沫塑料5～9份、纳米炭黑1～2份、煤矸石粉7～14份、胶原纤维6～13份、玻化微珠颗粒15～25份、改性粉煤灰20～30份、邻苯二甲酸二辛酯5～8份、蒙脱土7～14份、膨胀珍珠岩15～25份、十溴二苯乙烷2～3份、柠檬酸钾2～4份、腐殖酸钠0.5～1份、阻燃剂1～2份、减水剂1～2份。所述建筑用隔音板材防潮阻燃、柔韧质轻、透气性好、能循环利用、无毒无害、吸音效果好并且制造成本低等优点。
Description
技术领域
本发明属于建筑材料技术领域，具体涉及一种建筑用吸音板材及其制备方法。
背景技术
吸音板是指板状的具有吸音减噪作用的材料，主要应用于影剧院、音乐厅、博物馆、展览馆、图书馆、审讯室、画廊、拍卖厅、体育馆、报告厅、多功能厅、酒店大堂、医院、商场、学校、琴房、会议室、演播室、录音室、KTV包房、酒吧、工业厂房、机房、家庭降噪等对声学环境要求较高及高档装修的场所。现有吸音板材料也有复合型的，但是无机物料与有机物料复合的性能指标优异的较少。
发明内容
本发明提供了一种建筑用吸音板材及其制备方法，解决了上述背景技术中的问题，所述建筑用隔音板材防潮阻燃、柔韧质轻、透气性好、能循环利用、无毒无害、吸音效果好并且制造成本低等优点。
为了解决现有技术存在的问题，采用如下技术方案：
一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂13～18份、石膏5～9份、聚酰胺3～8份、聚苯乙烯泡沫塑料5～9份、纳米炭黑1～2份、煤矸石粉7～14份、胶原纤维6～13份、玻化微珠颗粒15～25份、改性粉煤灰20～30份、邻苯二甲酸二辛酯5～8份、蒙脱土7～14份、膨胀珍珠岩15～25份、十溴二苯乙烷2～3份、柠檬酸钾2～4份、腐殖酸钠0.5～1份、阻燃剂1～2份、减水剂1～2份。
优选的，所述建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂14～17份、石膏6～8份、聚酰胺5～7份、聚苯乙烯泡沫塑料6～8份、纳米炭黑1.3～1.8份、煤矸石粉9～12份、胶原纤维8～11份、玻化微珠颗粒17～23份、改性粉煤灰24～26份、邻苯二甲酸二辛酯6～7份、蒙脱土10～13份、膨胀珍珠岩18～24份、十溴二苯乙烷2.1～2.6份、柠檬酸钾2.5～3.5份、腐殖酸钠0.7～0.9份、阻燃剂1.3～1.7份、减水剂1.4～1.6份。
优选的，所述建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂15份、石膏7份、聚酰胺6份、聚苯乙烯泡沫塑料7份、纳米炭黑1.6份、煤矸石粉10份、胶原纤维9份、玻化微珠颗粒20份、改性粉煤灰25份、邻苯二甲酸二辛酯6.5份、蒙脱土12份、膨胀珍珠岩21份、十溴二苯乙烷2.4份、柠檬酸钾3.3份、腐殖酸钠0.8份、阻燃剂1.5份、减水剂1.5份。
优选的，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量 4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
优选的，所述阻燃剂为三氧化二锑。
优选的，所述减水剂为木质素磺酸钙、聚丙烯酸钠、氨基磺酸钠中的任一种。
优选的，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
一种制备所述建筑用吸音板材的方法，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以800～1000r/min的高速搅拌混合5～10分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混3～5分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为20～30%，在110～120℃下以1500～1800r/min速度搅拌5～10min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。
本发明与现有技术相比，其具有以下有益效果：
本发明所述的建筑用隔音板材防潮阻燃、柔韧质轻、透气性好、能循环利用、无毒无害、吸音效果好并且制造成本低等优点，具体如下：
（1）本发明所述的建筑用吸音板材添加玻化微珠颗粒作为原料，玻化微珠颗粒理化性能十分稳定、自重轻、耐老化耐候性强，具有优异的绝热﹑防火﹑吸音性能，显著提高吸音板材的综合性能；
（2）本发明所述的建筑用吸音板材添加膨胀珍珠岩作为原料，具有轻质、柔韧、孔隙大的特点；添加蒙脱土、改性粉煤灰等，使板材料坚韧耐磨，原料之间相互协同作用，使得本发明所述的吸音板材强度高，耐腐蚀，抗氧化，加工性能好。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
本实施例涉及一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂13份、石膏5份、聚酰胺3份、聚苯乙烯泡沫塑料5份、纳米炭黑1份、煤矸石粉7份、胶原纤维6份、玻化微珠颗粒15份、改性粉煤灰20份、邻苯二甲酸二辛酯5份、蒙脱土7份、膨胀珍珠岩15份、十溴二苯乙烷2份、柠檬酸钾2份、腐殖酸钠0.5份、阻燃剂1份、减水剂1份。
其中，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量 4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
其中，所述阻燃剂为三氧化二锑。
其中，所述减水剂为木质素磺酸钙。
其中，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
一种制备述建筑用吸音板材的方法，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以800r/min的高速搅拌混合5分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混3分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为20%，在110℃下以1500r/min速度搅拌5min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。
实施例2
本实施例涉及一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂18份、石膏9份、聚酰胺8份、聚苯乙烯泡沫塑料9份、纳米炭黑2份、煤矸石粉14份、胶原纤维13份、玻化微珠颗粒25份、改性粉煤灰30份、邻苯二甲酸二辛酯8份、蒙脱土14份、膨胀珍珠岩25份、十溴二苯乙烷3份、柠檬酸钾4份、腐殖酸钠1份、阻燃剂2份、减水剂2份。
其中，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量 4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
其中，所述阻燃剂为三氧化二锑。
其中，所述减水剂为聚丙烯酸钠。
其中，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
一种制备述建筑用吸音板材的方法，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以1000r/min的高速搅拌混合10分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混5分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为30%，在120℃下以1800r/min速度搅拌10min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。
实施例3
本实施例涉及一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂14份、石膏6份、聚酰胺5份、聚苯乙烯泡沫塑料6份、纳米炭黑1.3份、煤矸石粉9份、胶原纤维8份、玻化微珠颗粒17份、改性粉煤灰24份、邻苯二甲酸二辛酯6份、蒙脱土10份、膨胀珍珠岩18份、十溴二苯乙烷2.1份、柠檬酸钾2.5份、腐殖酸钠0.7份、阻燃剂1.3份、减水剂1.4份。
其中，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量 4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
其中，所述阻燃剂为三氧化二锑。
其中，所述减水剂为氨基磺酸钠。
其中，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
一种制备述建筑用吸音板材的方法，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以850r/min的高速搅拌混合6分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混4分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为22%，在113℃下以1600r/min速度搅拌7min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。
实施例4
本实施例涉及一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂17份、石膏8份、聚酰胺7份、聚苯乙烯泡沫塑料8份、纳米炭黑1.8份、煤矸石粉12份、胶原纤维11份、玻化微珠颗粒23份、改性粉煤灰26份、邻苯二甲酸二辛酯7份、蒙脱土13份、膨胀珍珠岩24份、十溴二苯乙烷2.6份、柠檬酸钾3.5份、腐殖酸钠0.9份、阻燃剂1.7份、减水剂1.6份。
其中，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量 4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
其中，所述阻燃剂为三氧化二锑。
其中，所述减水剂为木质素磺酸钙。
其中，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
一种制备述建筑用吸音板材的方法，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以900r/min的高速搅拌混合7分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混4分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为25%，在115℃下以1650r/min速度搅拌7min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。
实施例5
本实施例涉及一种建筑用吸音板材，包括如下重量份的原料：热塑性苯酚树脂15份、石膏7份、聚酰胺6份、聚苯乙烯泡沫塑料7份、纳米炭黑1.6份、煤矸石粉10份、胶原纤维9份、玻化微珠颗粒20份、改性粉煤灰25份、邻苯二甲酸二辛酯6.5份、蒙脱土12份、膨胀珍珠岩21份、十溴二苯乙烷2.4份、柠檬酸钾3.3份、腐殖酸钠0.8份、阻燃剂1.5份、减水剂1.5份。
其中，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量 4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
其中，所述阻燃剂为三氧化二锑。
其中，所述减水剂为聚丙烯酸钠。
其中，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
一种制备述建筑用吸音板材的方法，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以950r/min的高速搅拌混合8分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混4分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为28%，在119℃下以1700r/min速度搅拌9min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (8)
1.一种建筑用吸音板材，其特征在于，包括如下重量份的原料：热塑性苯酚树脂13～18份、石膏5～9份、聚酰胺3～8份、聚苯乙烯泡沫塑料5～9份、纳米炭黑1～2份、煤矸石粉7～14份、胶原纤维6～13份、玻化微珠颗粒15～25份、改性粉煤灰20～30份、邻苯二甲酸二辛酯5～8份、蒙脱土7～14份、膨胀珍珠岩15～25份、十溴二苯乙烷2～3份、柠檬酸钾2～4份、腐殖酸钠0.5～1份、阻燃剂1～2份、减水剂1～2份。
2.根据权利要求1所述的建筑用吸音板材，其特征在于，包括如下重量份的原料：热塑性苯酚树脂14～17份、石膏6～8份、聚酰胺5～7份、聚苯乙烯泡沫塑料6～8份、纳米炭黑1.3～1.8份、煤矸石粉9～12份、胶原纤维8～11份、玻化微珠颗粒17～23份、改性粉煤灰24～26份、邻苯二甲酸二辛酯6～7份、蒙脱土10～13份、膨胀珍珠岩18～24份、十溴二苯乙烷2.1～2.6份、柠檬酸钾2.5～3.5份、腐殖酸钠0.7～0.9份、阻燃剂1.3～1.7份、减水剂1.4～1.6份。
3.根据权利要求1所述的建筑用吸音板材，其特征在于，包括如下重量份的原料：热塑性苯酚树脂15份、石膏7份、聚酰胺6份、聚苯乙烯泡沫塑料7份、纳米炭黑1.6份、煤矸石粉10份、胶原纤维9份、玻化微珠颗粒20份、改性粉煤灰25份、邻苯二甲酸二辛酯6.5份、蒙脱土12份、膨胀珍珠岩21份、十溴二苯乙烷2.4份、柠檬酸钾3.3份、腐殖酸钠0.8份、阻燃剂1.5份、减水剂1.5份。
4.根据权利要求1所述的建筑用吸音板材，其特征在于，所述改性粉煤灰由以下方法制得：先将粉煤灰在100℃烘箱中烘干，然后将烘干后的粉煤灰放入高速捏合机中，加入相当于粉煤灰重量4％的铝酸酯偶联剂、3％的木质磺酸钠、3％的柠檬酸三乙酯、2％的液体石蜡和4％的滑石粉，高速混合后，烘干，粉碎研磨成超细粉末即可。
5.根据权利要求1所述的建筑用吸音板材，其特征在于，所述阻燃剂为三氧化二锑。
6.根据权利要求1所述的建筑用吸音板材，其特征在于，所述减水剂为木质素磺酸钙、聚丙烯酸钠、氨基磺酸钠中的任一种。
7.根据权利要求1所述的建筑用吸音板材，其特征在于，所述胶原纤维是将经过预处理的废革料按一定浓度在磨浆机中磨浆制备得到的。
8.一种制备权利要求1～7任一项所述建筑用吸音板材的方法，其特征在于，包括如下步骤：
（1）按上述配方称取热塑性苯酚树脂、石膏、聚酰胺、聚苯乙烯泡沫塑料、纳米炭黑、煤矸石粉、胶原纤维、玻化微珠颗粒、改性粉煤灰、邻苯二甲酸二辛酯、蒙脱土、膨胀珍珠岩、十溴二苯乙烷、柠檬酸钾、腐殖酸钠、阻燃剂、减水剂，备用；
（2）将石膏、纳米炭黑、煤矸石粉及改性粉煤灰放入搅拌机中搅拌混合均匀，再加入玻化微珠颗粒、蒙脱土及膨胀珍珠岩，以800～1000r/min的高速搅拌混合5～10分钟；
（3）将热塑性苯酚树脂、聚酰胺、聚苯乙烯泡沫塑料及邻苯二甲酸二辛酯混合，边搅拌边加热，初混3～5分钟，然后进入高速混合机中加入步骤（2）所得的混合物以及其余剩余成分，并加水，使其含水量为20～30%，在110～120℃下以1500～1800r/min速度搅拌5～10min，物料冷却至常温待用；
（4）将步骤（3）所得的混合粉末置于模具压制成型，脱模后蒸汽养护，即得所述建筑用吸音板材。