CN107382374A - A kind of preparation technology that ice crack is formed on ceramic mobile phone shell - Google Patents
A kind of preparation technology that ice crack is formed on ceramic mobile phone shell Download PDFInfo
- Publication number
- CN107382374A CN107382374A CN201710568156.3A CN201710568156A CN107382374A CN 107382374 A CN107382374 A CN 107382374A CN 201710568156 A CN201710568156 A CN 201710568156A CN 107382374 A CN107382374 A CN 107382374A
- Authority
- CN
- China
- Prior art keywords
- mobile phone
- embryo
- phone shell
- ice crack
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation technology that ice crack is formed on ceramic mobile phone shell, it is characterized in that porcelain embryo is fabricated to mobile phone shelly by this method, the surface of porcelain embryo is coated into following prescription again and does obtained glaze, proembryo is obtained, then carries out proembryo secondary the mobile phone shell with ice crack effect to be made:Albite:65 75, kaolin:1.5 3, quartz:12 16, lime stone:68, tin oxide:1‑1.4.The technique enables to the surface of phone housing to form the effect of ice crack crackle, and realizes that easy, Con trolling index is simple and feasible, low manufacture cost, is easy to implement large-scale production.
Description
Technical field
The present invention relates to mobile phone shell field, more particularly to a kind of method that ice crack effect is formed on ceramic manual casing.
Background technology
With the popularization of smart mobile phone, the application of mobile phone shell is also increasingly wider, and people not only protect mobile phone using mobile phone shell
It is injury-free, also there is installing effect.
On July 19th, 2011, first item ceramic package mobile phone came out in Jing Dezhen, and the mobile phone shell is by more than 1300 degree high temperature
Firing forms, and not only environmental protection, wearability are high, also great ornamental value.However, the ceramic manual casing is carried out using nano material
Fire, with high costs, preparation technology is complicated, it is difficult to realizes and produces in enormous quantities.
Later, people were improved this, produced the ceramic manual casing of low cost, and ceramic manual casing is typically to pass through
High temperature biscuiting and low temperature sinter are fired twice, turn into that whiteness is high, transparency is good, porcelain is fine and smooth, the bright smooth porcelain of glaze paint, but
It is, it is well known that the pattern of ceramic is difficult to batch duplicating, and two ways realizes the figure in mobile phone shell again now
Case, the first be need in advance pottery embryo on it is drawn can just be fired, second is by being printed again on mobile phone shell surface
Brush or the mode of one coating of adhesion is realized, and for current ceramic manual casing, the cost of manufacture of the mobile phone shell of the first
It is too high, it is difficult to be received by ordinary consumer, second seems that production technique is inferior, and coating can usually fall because of abrasion
Fall, largely effect on the aesthetic property of mobile phone shell.
The making of ice crack effect, it is to form a kind of preparation technology of crackle on the surface of ceramics, i.e., China is found out
So-called hacking, produced with Song Dynasty taxi driver brother's kiln the most famous, because its line piece such as ice ruptures, sliver stacking, have third dimension and be referred to as.
The principle of hacking is:First, base mud extends in a certain direction during shaping, the arrangement of molecule have impact on.Second, base, the glaze coefficient of expansion
Difference, pottery are burnt till in the cooling procedure after terminating, and tire glaze starts to shrink at, and tire glaze shrinks and is more or less the same during beginning, but with
The reduction of temperature, because the coefficient of expansion is different, tire glaze, which shrinks, differs increasing, and glaze contraction is more, and tire contraction is few, glaze is produced one
Kind tensile stress, as a result causes glaze paint to ftracture.Tire glaze coefficient of expansion difference is bigger, and hacking is more, otherwise fewer.If the expansion of glaze
Coefficient is less than the coefficient of expansion of tire, glaze just not hacking.But traditional hacking technique is lost, people can only burn once in a while at present
The ceramics with ice crack effect are made, and by the present of geographical position.As patent application 02120521.3 discloses one kind
The preparation method of celadon frostwork glaze and products thereof, this method glaze composition are:Yellow * glaze soil 25~35%, Zijin soil
8~5%, feldspar powder 35~25%, talcum powder 3~6%, lime stone 14~19%, bamboo township glaze soil 15~10%, this method is adopted
Raw material can only be produced in specific region, and yield is small, and are limited by indexs such as temperature, and production cost is high, it is difficult to real
Now mass produce.
The content of the invention
For weak point present in above-mentioned technology, the present invention provides a kind of formation ice crack on ceramic mobile phone shell
Preparation technology, the technique enable to the surface of phone housing to form the effect of ice crack crackle.
It is another object of the present invention to provide a kind of preparation technology that ice crack is formed on ceramic mobile phone shell, the work
Skill realizes that easy, Con trolling index is simple and feasible, is easy to implement large-scale production.
To achieve the above object, the present invention is realized in.
A kind of preparation technology that ice crack is formed on ceramic mobile phone shell, it is characterised in that porcelain embryo is fabricated to hand by this method
Casing shape, then the surface of porcelain embryo is coated into following prescription (parts by weight) and does obtained glaze, proembryo is obtained, then enters proembryo
Row is secondary to be made the mobile phone shell with ice crack effect:
Guixi porcelain stone:30-35 parts
Kaolin:41-47 parts
Zijin soil:13-18 parts
Quartz:3-5 parts.
The raw material such as Guixi porcelain stone, kaolin, quartz and Zijin soil are all readily available, and will not be influenceed by the place of production,
Cost of manufacture can be greatly lowered, and utilize the coefficient of expansion difference between various components, particularly Guixi porcelain stone and kaolinite
The difference of physical expansion coefficient between soil, Zijin soil, the expansion coefficient difference between glaze and porcelain embryo is increased, in the burning of ceramics
Formed during system and pass through secondary firing, good ice crack effect can be formed.
Further, the Guixi porcelain stone dosage is preferably 32-34 parts.
Further, the kaolin dosage is preferably 44-45 parts.
Further, the Zijin soil dosage is preferably 15-16 parts.
Further, the quartzy dosage is preferably 3.8-4.2 parts.
Methods described, its first by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be dried, remove into embryo
Part moisture content in embryo, biscuiting is then carried out, removed completely into the moisture content in embryo;Fully remove being carried out into embryo at glazing for moisture content
Manage (glazing), be dried after glazing, obtain proembryo, proembryo is subjected to secondary firing, you can the hand with ice crack effect is made
Casing.
Further, this method also includes embryo process of repairing, and the embryo process of repairing is located at before glazing, i.e., after biscuiting, mobile phone
Shell can be deformed, and now carried out repairing embryo processing, then carried out glazing.
The preparation technology that ice crack is formed on ceramic mobile phone shell that the present invention is realized, the Guixi porcelain stone of use, kaolinite
The raw material such as soil, quartz and Zijin soil are all readily available, and will not be influenceed by the place of production, can be greatly lowered and be fabricated to
This, and it is different using the coefficient of expansion between various components, particularly the physics between Guixi porcelain stone and kaolin, Zijin soil is swollen
The difference of swollen coefficient, the expansion coefficient difference between glaze and porcelain embryo is increased, formed in the sintering procedure of ceramics by secondary
Fire, good ice crack effect can be formed.
Brief description of the drawings
Fig. 1 is the preparation flow figure of the present invention.
Embodiment
In order to more clearly state the present invention, the present invention is further described below in conjunction with the accompanying drawings.
Refer to shown in Fig. 1, the preparation technology that ice crack is formed on ceramic mobile phone shell that the present invention realizes, its feature exists
Porcelain embryo is fabricated to mobile phone shelly in this method, then the surface of porcelain embryo is coated into following prescription (weight percent hundred) and does obtained glaze
Material, proembryo is obtained, then carry out proembryo secondary the mobile phone shell with ice crack effect to be made:
Guixi porcelain stone:30-35 parts
Kaolin:41-47 parts
Zijin soil:13-18 parts
Quartz:3-5 parts.
Further, the Guixi porcelain stone dosage is preferably 32-34 parts.
Further, the kaolin dosage is preferably 44-45 parts.
Further, the Zijin soil dosage is preferably 15-16 parts.
Further, the quartzy dosage is preferably 3.8-4.2 parts.
The method realized of the present invention, first by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be done into embryo
It is dry, remove into the part moisture content in embryo, then carry out biscuiting, remove completely into the moisture content in embryo;After biscuiting, mobile phone shell can produce
Deformation, now carry out repairing embryo processing;After repairing embryo, abundant removal moisture content is subjected to glazing treatment (glazing) into embryo, glazing is laggard
Row drying, proembryo is obtained, proembryo is subjected to secondary firing, you can the mobile phone shell with ice crack effect is made.
Embodiment one.
First by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be dried into embryo, and remove into the part in embryo
Moisture content, biscuiting is then carried out, removed completely into the moisture content in embryo;After biscuiting, mobile phone shell can be deformed, and now carry out repairing at embryo
Reason;After repairing embryo, abundant removal moisture content is subjected to glazing treatment (glazing) into embryo, is dried after glazing, proembryo is obtained, by original
Embryo carries out secondary firing, and at 1500 °, the time is 1 hour, you can the mobile phone shell with ice crack effect is made for firing temperature control.
During glazing, glaze is made according to following formula:
Guixi porcelain stone:30 parts
Kaolin:41 parts
Zijin soil:13 parts
Quartz:3 parts.
Embodiment two.
First by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be dried into embryo, and remove into the part in embryo
Moisture content, biscuiting is then carried out, removed completely into the moisture content in embryo;After biscuiting, mobile phone shell can be deformed, and now carry out repairing at embryo
Reason;After repairing embryo, abundant removal moisture content is subjected to glazing treatment (glazing) into embryo, is dried after glazing, proembryo is obtained, by original
Embryo carries out secondary firing, and at 1500 °, the time is 1 hour, you can the mobile phone shell with ice crack effect is made for firing temperature control.
During glazing, glaze is made according to following formula:
Guixi porcelain stone:35 parts
Kaolin:47 parts
Zijin soil:18 parts
Quartz:5 parts.
Embodiment three.
First by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be dried into embryo, and remove into the part in embryo
Moisture content, biscuiting is then carried out, removed completely into the moisture content in embryo;After biscuiting, mobile phone shell can be deformed, and now carry out repairing at embryo
Reason;After repairing embryo, abundant removal moisture content is subjected to glazing treatment (glazing) into embryo, is dried after glazing, proembryo is obtained, by original
Embryo carries out secondary firing, and at 1500 °, the time is 1 hour, you can the mobile phone shell with ice crack effect is made for firing temperature control.
During glazing, glaze is made according to following formula:
Guixi porcelain stone:32 parts
Kaolin:44 parts
Zijin soil:15 parts
Quartz:3.8 part.
Example IV.
First by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be dried into embryo, and remove into the part in embryo
Moisture content, biscuiting is then carried out, removed completely into the moisture content in embryo;After biscuiting, mobile phone shell can be deformed, and now carry out repairing at embryo
Reason;After repairing embryo, abundant removal moisture content is subjected to glazing treatment (glazing) into embryo, is dried after glazing, proembryo is obtained, by original
Embryo carries out secondary firing, and at 1500 °, the time is 1 hour, you can the mobile phone shell with ice crack effect is made for firing temperature control.
During glazing, glaze is made according to following formula:
Guixi porcelain stone:34 parts
Kaolin:45 parts
Zijin soil:16 parts
Quartz:4.2 part.
Therefore, the preparation technology that ice crack is formed on ceramic mobile phone shell that the present invention is realized, the Guixi porcelain stone of use,
The raw material such as kaolin, quartz and Zijin soil are all readily available, and will not be influenceed by the place of production, and making can be greatly lowered
Cost, and utilize the coefficient of expansion difference between various components, the particularly physics between Guixi porcelain stone and kaolin, Zijin soil
The difference of the coefficient of expansion, the expansion coefficient difference between glaze and porcelain embryo is increased, formed in the sintering procedure of ceramics and pass through two
Secondary firing, good ice crack effect can be formed.
Disclosed above is only several specific embodiments of the present invention, but the present invention is not limited to this, any ability
What the technical staff in domain can think change should all fall into protection scope of the present invention.
Claims (8)
1. a kind of preparation technology that ice crack is formed on ceramic mobile phone shell, it is characterised in that porcelain embryo is fabricated to mobile phone by this method
Shelly, then the surface of porcelain embryo is coated into following prescription and does obtained glaze, proembryo is obtained, proembryo then is carried out into secondary fire makes
Into the mobile phone shell with ice crack effect:
Guixi porcelain stone:30-35
Kaolin:41-47
Zijin soil:13-18
Quartz:3-5.
2. the preparation technology according to claim 1 that ice crack is formed on ceramic mobile phone shell, it is characterised in that Guixi porcelain
Stone dosage is preferably 32-34 parts.
3. the preparation technology according to claim 1 that ice crack is formed on ceramic mobile phone shell, it is characterised in that the height
Ridge soil dosage is preferably 44-45 parts.
4. the preparation technology according to claim 1 that ice crack is formed on ceramic mobile phone shell, it is characterised in that the purple
The native dosage of gold is preferably 15-16 parts.
5. the preparation technology according to claim 1 that ice crack is formed on ceramic mobile phone shell, it is characterised in that the stone
English dosage is preferably 3.8-4.2 parts.
6. the preparation technology according to claim 1 that ice crack is formed on ceramic mobile phone shell, it is characterised in that the side
Method, its first by porcelain embryo according to the shape fabricating of mobile phone shell into embryo, then will be dried into embryo, and remove into the part water in embryo
Part, biscuiting is then carried out, is removed completely into the moisture content in embryo;Fully remove moisture content carries out glazing treatment into embryo, and glazing is laggard
Row drying, proembryo is obtained, proembryo is subjected to secondary firing, you can the mobile phone shell with ice crack effect is made.
7. the preparation technology according to claim 6 that ice crack is formed on ceramic mobile phone shell, it is characterised in that this method
Also include embryo process of repairing, the embryo process of repairing is located at before glazing, i.e., after biscuiting, mobile phone shell can be deformed, and now be carried out
Embryo processing is repaiied, is then carrying out glazing.
8. the preparation technology according to claim 6 that ice crack is formed on ceramic mobile phone shell, it is characterised in that secondary burning
System, at 1500 °, the time is 1 hour for firing temperature control.