CN107382242A - A kind of waterproof thermal-insulated partition plate and preparation method thereof - Google Patents
A kind of waterproof thermal-insulated partition plate and preparation method thereof Download PDFInfo
- Publication number
- CN107382242A CN107382242A CN201710614257.XA CN201710614257A CN107382242A CN 107382242 A CN107382242 A CN 107382242A CN 201710614257 A CN201710614257 A CN 201710614257A CN 107382242 A CN107382242 A CN 107382242A
- Authority
- CN
- China
- Prior art keywords
- parts
- partition plate
- feldspar powder
- powder
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of waterproof thermal-insulated partition plate and preparation method thereof, it is related to building material technical field, the partition plate includes following raw material：Diatom ooze, desulfurated plaster, ore tailings, modified feldspar powder, aerating aluminium powder, croci, alumina silicate fibre, tributyl phosphate, mineral wool, white glue with vinyl, inorganic aluminate water-proof agent, foaming agent, coupling agent, activator and dispersant.Its preparation method is by stirring and evenly mixing, made from moulding by casting and maintenance processing to raw material.This kind of partition plate is prepared simply, convenient material drawing, low production cost, has the advantages that light, water-fast moisture resistance is good, compression strength is high, heat preservation and soundproof effect is obvious, service life length, and application field is extensive.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of waterproof thermal-insulated partition plate and preparation method thereof.
Background technology
Building partition and interior decoration partition material are mainly common brick, and air pressure turns, and plasterboard etc., it has the shortcomings that notable,
If common brick and air pressure brick are from great, partition wall is only done on the space of a whole page for have beam, it is non-moistureproof not prevent although plasterboard is from heavy and light
Water, low intensity, service life are short.Partition plate is a kind of novel light partition wall batten, is widely used as industrial building, inhabitation
Building, the non-load bearing inner partition wall of public works, belongs to light partition wall engineering.Partition plate is especially in modern Decoration Industry
Using most, miscellaneous partition plate can be used for the space for separating house, meet different human needs.
Feldspar powder is the aluminium silicate mineral powder of the alkali metal such as potassium, sodium, calcium, barium or alkaline-earth metal, crystal structure category rack-like
Structure, it is the most important rock-forming mineral of surface rock, it has the excellent characteristics such as high, the corrosion-resistant, high temperature resistant of intensity, and it passes through
Particular step is modified, and the various aspects of performance showed improves, and is applied to building material technical field, has actively favourable
Meaning.
The content of the invention
For problems of the prior art, the invention provides a kind of waterproof thermal-insulated partition plate and preparation method thereof,
This kind of partition plate prepares simple, convenient material drawing, low production cost, has that light, water-fast moisture resistance is good, compression strength is high, protects
The advantages that warm soundproof effect is obvious, service life length, application field are extensive.
In order to achieve the above object, the present invention is achieved through the following technical solutions：
A kind of waterproof thermal-insulated partition plate, including following raw material by weight：Diatom ooze 40-60 parts, desulfurated plaster 30-
40 parts, ore tailings 20-30 parts, modified feldspar powder 20-30 parts, aerating aluminium powder 5-15 parts, croci 4-8 parts, alumina silicate
Fiber 6-10 parts, tributyl phosphate 2-4 parts, mineral wool 4-10 parts, white glue with vinyl 5-15 parts, inorganic aluminate water-proof agent 1-5 parts, foaming
Agent 1-5 parts, coupling agent 1-3 parts, activator 1-3 parts and dispersant 1-5 parts；
The modified feldspar powder is made by following steps：Feldspar powder is put into sodium carbonate and potassium permanganate mixed solution
After soaking 1-2h, drying is taken out, adds wooden sodium sulfonate equivalent to feldspar powder weight 2-4%, equivalent to feldspar powder weight 1-
3% sldium lauryl sulfate and aluminum oxide equivalent to feldspar powder weight 4-6% stir 20-30min under 300-500r/min
After grind, cross 120-160 mesh sieves produce.
Further, the partition plate includes following raw material by weight：50 parts of diatom ooze, 35 parts of desulfurated plaster,
25 parts of ore tailings, modified 25 parts of feldspar powder, 10 parts of aerating aluminium powder, 6 parts of croci, 8 parts of alumina silicate fibre, tricresyl phosphate fourth
3 parts of ester, 7 parts of mineral wool, 10 parts of white glue with vinyl, 3 parts of inorganic aluminate water-proof agent, 3 parts of foaming agent, 2 parts of coupling agent, 2 parts of activator and
2 parts of dispersant.
Further, the modified feldspar powder is made by following steps：Feldspar powder is put into sodium carbonate and potassium permanganate
After soaking 1.5h in mixed solution, drying is taken out, adds the wooden sodium sulfonate equivalent to feldspar powder weight 3%, equivalent to feldspar
After the sldium lauryl sulfate of powder weight 2% and aluminum oxide equivalent to feldspar powder weight 5% stir 125min under 400r/min
Grinding, cross 140 mesh sieves and produce.
Preferably, the foaming agent be sodium metasilicate, calcium carbonate, sodium acid carbonate, carborundum or hydrogen peroxide in one kind or
Person more than one.
Preferably, the coupling agent is in Silane coupling agent KH550, titanate esters or gamma-aminopropyl-triethoxy-silane
It is a kind of.
Preferably, the activator is one kind in calcium sulphoaluminate, alumina silicate or washing slurry.
Preferably, the dispersant is one kind in sodium tripolyphosphate, calgon or sodium pyrophosphate.
A kind of preparation method of above-mentioned waterproof thermal-insulated partition plate, is followed the steps below：
(1) the weight preparing material is pressed；
(2) desulfurated plaster and ore tailings be crushed into 100-200 mesh sieves, obtains powder, by powder, modified feldspar powder, added
Gas aluminium powder and croci mixing, weight is added than stirring 10-20min, speed of agitator 60-80r/ for 60-80% water
min；Diatom ooze, alumina silicate fibre, tributyl phosphate, mineral wool and white glue with vinyl are added, is again stirring for 1-2h；It is eventually adding surplus
Remaining raw material stirs 10-20min, obtains material；
(3) material is poured into mould, be molded by pressing mode, briquetting pressure 8-12MPa；
(4) by the plate after shaping be placed in humidity be 80%-90%, maintenance processing 4- in the environment of temperature is 38-42 DEG C
6h.
The present invention has following beneficial effect：The partition plate of the present invention prepares simple, convenient material drawing, and production cost is low
It is honest and clean, by being improved and optimizated to production and processing raw material and technique, add the compositions such as diatom ooze, modified feldspar powder, aerating aluminium powder, association
With the function affect of outer adding assistant so that finished partition plate reached light, water-fast moisture resistance is good, compression strength is high, insulation
Soundproof effect substantially waits multinomial performance index request, further, after testing, moisture permeable coefficient≤0.003g/ of this kind of partition plate
(m.s.pa), more than 240% is reduced compared to commercially available plasterboard；Its thermal conductivity factor≤0.015W/m.K, compared to commercially available stone
Cream plate reduces more than 130%；Its value of bulk density≤612.5kg/m3, 4%-12% is reduced compared to commercially available plasterboard；It is flat
Equal compression strength is 28.7MPa, and more than 97% is improved compared to commercially available plasterboard；And this kind of partition plate service life length, no
Dry linting occurs, drops off and phenomena such as crackle, application field is extensive.
Embodiment
The embodiment of the present invention is further described with reference to embodiment, following examples are only used for more
Clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
Embodiment 1
A kind of waterproof thermal-insulated partition plate, it is to be prepared to weigh following raw material：Diatom ooze 40kg, desulfurated plaster 30kg, ore tail
Sand 20kg, modified feldspar powder 20kg, aerating aluminium powder 5kg, croci 4kg, alumina silicate fibre 6kg, tributyl phosphate 2kg,
Mineral wool 4kg, white glue with vinyl 5kg, inorganic aluminate water-proof agent 1kg, foaming agent 1kg, coupling agent 1kg, activator 1kg and dispersant
1kg；
The modified feldspar powder is made by following steps：Take 20kg feldspar powder to be put into sodium carbonate to mix with potassium permanganate
After soaking 1h in solution, drying is taken out, adds the wooden sodium sulfonate equivalent to feldspar powder weight 2%, equivalent to feldspar powder weight
1% sldium lauryl sulfate and aluminum oxide equivalent to feldspar powder weight 4% are ground after stirring 20min under 300r/min, mistake
120 mesh sieves are that the modification feldspar powder needed for raw material of the present invention is made.
Wherein, above-mentioned foaming agent uses sodium metasilicate；Coupling agent uses Silane coupling agent KH550；Activator uses sulphur aluminium
Sour calcium；Dispersant uses sodium tripolyphosphate.
A kind of preparation method of above-mentioned waterproof thermal-insulated partition plate, is followed the steps below：
(1) desulfurated plaster and ore tailings first be crushed into 100 mesh sieves, obtains powder；Again by powder, modified feldspar powder plus
Gas aluminium powder and croci mixing, weight is added than stirring 10min, speed of agitator 60r/min for 60% water；Afterwards plus
Enter diatom ooze, alumina silicate fibre, tributyl phosphate, mineral wool and white glue with vinyl, be again stirring for 1h；It is eventually adding surplus stock stirring
10min, obtain material；
(2) material is poured into mould, be molded by pressing mode, briquetting pressure 8MPa；
(3) plate after shaping is placed in humidity is 80%, maintenance processing 4h is made in the environment of temperature is 38 DEG C
The waterproof thermal-insulated partition plate of invention.
Embodiment 2
A kind of waterproof thermal-insulated partition plate, it is to be prepared to weigh following raw material：Diatom ooze 50kg, desulfurated plaster 35kg, ore tail
Sand 25kg, modified feldspar powder 25kg, aerating aluminium powder 10kg, croci 6kg, alumina silicate fibre 8kg, tributyl phosphate 3kg,
Mineral wool 7kg, white glue with vinyl 10kg, inorganic aluminate water-proof agent 3kg, foaming agent 3kg, coupling agent 2kg, activator 2kg and dispersant
2kg；
The modified feldspar powder is made by following steps：Take 25kg feldspar powder to be put into sodium carbonate to mix with potassium permanganate
After soaking 1.5h in solution, drying is taken out, adds the wooden sodium sulfonate equivalent to feldspar powder weight 3%, equivalent to feldspar powder weight
The sldium lauryl sulfate of amount 2% and grind after stirring 25min under 400r/min equivalent to the aluminum oxide of feldspar powder weight 5%,
Cross the modification feldspar powder needed for the i.e. obtained raw material of the present invention of 140 mesh sieves.
Wherein, above-mentioned foaming agent uses sodium acid carbonate；Coupling agent uses titanate esters；Activator alumina silicate；Dispersant is adopted
Use calgon.
A kind of preparation method of above-mentioned waterproof thermal-insulated partition plate, is followed the steps below：
(1) desulfurated plaster and ore tailings first be crushed into 150 mesh sieves, obtains powder；Again by powder, modified feldspar powder plus
Gas aluminium powder and croci mixing, weight is added than stirring 15min, speed of agitator 70r/min for 70% water；Afterwards plus
Enter diatom ooze, alumina silicate fibre, tributyl phosphate, mineral wool and white glue with vinyl, be again stirring for 1.5h；Surplus stock is eventually adding to stir
12min is mixed, obtains material；
(2) material is poured into mould, be molded by pressing mode, briquetting pressure 10MPa；
(3) plate after shaping is placed in humidity is 85%, maintenance processing 5h is made in the environment of temperature is 40 DEG C
The waterproof thermal-insulated partition plate of invention.
Embodiment 3
A kind of waterproof thermal-insulated partition plate, it is to be prepared to weigh following raw material：Diatom ooze 60kg, desulfurated plaster 40kg, ore tail
Sand 30kg, modified feldspar powder 30kg, aerating aluminium powder 15kg, croci 8kg, alumina silicate fibre 10kg, tributyl phosphate
4kg, mineral wool 10kg, white glue with vinyl 15kg, inorganic aluminate water-proof agent 5kg, foaming agent 5kg, coupling agent 3kg, activator 3kg and point
Powder 5kg；
The modified feldspar powder is made by following steps：Take 30kg feldspar powder to be put into sodium carbonate to mix with potassium permanganate
After soaking 2h in solution, drying is taken out, adds the wooden sodium sulfonate equivalent to feldspar powder weight 4%, equivalent to feldspar powder weight
3% sldium lauryl sulfate and aluminum oxide equivalent to feldspar powder weight 6% are ground after stirring 30min under 500r/min, mistake
160 mesh sieves are that the modification feldspar powder needed for raw material of the present invention is made.
Wherein, above-mentioned foaming agent uses two kinds of mixtures of calcium carbonate and carborundum, and mass ratio between the two is 3:
1；Coupling agent uses gamma-aminopropyl-triethoxy-silane；Activator uses washing slurry；Dispersant uses sodium pyrophosphate.
A kind of preparation method of above-mentioned waterproof thermal-insulated partition plate, is followed the steps below：
(1) desulfurated plaster and ore tailings first be crushed into 200 mesh sieves, obtains powder；Again by powder, modified feldspar powder plus
Gas aluminium powder and croci mixing, weight is added than stirring 20min, speed of agitator 80r/min for 80% water；Afterwards plus
Enter diatom ooze, alumina silicate fibre, tributyl phosphate, mineral wool and white glue with vinyl, be again stirring for 2h；It is eventually adding surplus stock stirring
20min, obtain material；
(2) material is poured into mould, be molded by pressing mode, briquetting pressure 12MPa；
(3) plate after shaping is placed in humidity is 90%, maintenance processing 6h is made in the environment of temperature is 42 DEG C
The waterproof thermal-insulated partition plate of invention.
Embodiment 4
A kind of waterproof thermal-insulated partition plate, it is to be prepared to weigh following raw material：Diatom ooze 50kg, desulfurated plaster 35kg, ore tail
Sand 25kg, modified feldspar powder 25kg, aerating aluminium powder 10kg, croci 6kg, alumina silicate fibre 8kg, tributyl phosphate 3kg,
Mineral wool 7kg, white glue with vinyl 10kg, inorganic aluminate water-proof agent 3kg, foaming agent 3kg, coupling agent 2kg, activator 2kg and dispersant
2kg；
The modified feldspar powder is made by following steps：Take 25kg feldspar powder to be put into sodium carbonate to mix with potassium permanganate
After soaking 1h in solution, drying is taken out, adds the wooden sodium sulfonate equivalent to feldspar powder weight 4%, equivalent to feldspar powder weight
1% sldium lauryl sulfate and aluminum oxide equivalent to feldspar powder weight 6% are ground after stirring 30min under 300r/min, mistake
120 mesh sieves are that the modification feldspar powder needed for raw material of the present invention is made.
Wherein, above-mentioned foaming agent uses hydrogen peroxide；Coupling agent uses Silane coupling agent KH550；Activator uses water
Pulp washing；Dispersant uses sodium tripolyphosphate.
A kind of preparation method of above-mentioned waterproof thermal-insulated partition plate, is followed the steps below：
(1) desulfurated plaster and ore tailings first be crushed into 100 mesh sieves, obtains powder；Again by powder, modified feldspar powder plus
Gas aluminium powder and croci mixing, weight is added than stirring 10min, speed of agitator 60r/min for 80% water；Afterwards plus
Enter diatom ooze, alumina silicate fibre, tributyl phosphate, mineral wool and white glue with vinyl, be again stirring for 2h；It is eventually adding surplus stock stirring
10min, obtain material；
(2) material is poured into mould, be molded by pressing mode, briquetting pressure 8MPa；
(3) plate after shaping is placed in humidity is 90%, maintenance processing 4h is made in the environment of temperature is 38 DEG C
The waterproof thermal-insulated partition plate of invention.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God any modification, equivalent substitution and improvements made etc., should be included in the scope of the protection with principle.
Claims (8)
1. a kind of waterproof thermal-insulated partition plate, it is characterised in that including following raw material by weight：Diatom ooze 40-60 parts, take off
Sulphur gypsum 30-40 parts, ore tailings 20-30 parts, modified feldspar powder 20-30 parts, aerating aluminium powder 5-15 parts, croci 4-8
Part, alumina silicate fibre 6-10 parts, tributyl phosphate 2-4 parts, mineral wool 4-10 parts, white glue with vinyl 5-15 parts, inorganic aluminate water-proof agent
1-5 parts, foaming agent 1-5 parts, coupling agent 1-3 parts, activator 1-3 parts and dispersant 1-5 parts；
The modified feldspar powder is made by following steps：Feldspar powder is put into sodium carbonate with being soaked in potassium permanganate mixed solution
After 1-2h, drying is taken out, adds wooden sodium sulfonate equivalent to feldspar powder weight 2-4%, equivalent to feldspar powder weight 1-3%'s
Sldium lauryl sulfate and aluminum oxide equivalent to feldspar powder weight 4-6% are ground after stirring 20-30min under 300-500r/min
Mill, cross 120-160 mesh sieves and produce.
2. a kind of waterproof thermal-insulated partition plate according to claim 1, it is characterised in that including following original by weight
Material：50 parts of diatom ooze, 35 parts of desulfurated plaster, 25 parts of ore tailings, modified 25 parts of feldspar powder, 10 parts of aerating aluminium powder, brown iron oxide
6 parts of end, 8 parts of alumina silicate fibre, 3 parts of tributyl phosphate, 7 parts of mineral wool, 10 parts of white glue with vinyl, 3 parts of inorganic aluminate water-proof agent, foaming
2 parts of 3 parts of agent, 2 parts of coupling agent, 2 parts of activator and dispersant.
3. a kind of waterproof thermal-insulated partition plate according to claim 1, it is characterised in that the modified feldspar powder passes through following
Step is made：Feldspar powder is put into after soaking 1.5h in sodium carbonate and potassium permanganate mixed solution, takes out drying, add equivalent to
The wooden sodium sulfonate of feldspar powder weight 3%, the sldium lauryl sulfate equivalent to feldspar powder weight 2% and equivalent to feldspar powder weight
5% aluminum oxide is ground after stirring 125min under 400r/min, is crossed 140 mesh sieves and is produced.
4. a kind of waterproof thermal-insulated partition plate according to claim 1, it is characterised in that the foaming agent is sodium metasilicate, carbon
It is one or more than one kinds of in sour calcium, sodium acid carbonate, carborundum or hydrogen peroxide.
5. a kind of waterproof thermal-insulated partition plate according to claim 1, it is characterised in that the coupling agent is silane coupler
One kind in KH550, titanate esters or gamma-aminopropyl-triethoxy-silane.
A kind of 6. waterproof thermal-insulated partition plate according to claim 1, it is characterised in that the activator be calcium sulphoaluminate,
One kind in alumina silicate or washing slurry.
7. a kind of waterproof thermal-insulated partition plate according to claim 1, it is characterised in that the dispersant is tripolyphosphate
One kind in sodium, calgon or sodium pyrophosphate.
A kind of 8. preparation method of waterproof thermal-insulated partition plate as described in claim 1-7 any one, it is characterised in that including
Following steps：
(1) the weight preparing material is pressed；
(2) desulfurated plaster and ore tailings be crushed into 100-200 mesh sieves, obtains powder, by powder, modified feldspar powder, aerating aluminium
Powder and croci mixing, weight is added than stirring 10-20min, speed of agitator 60-80r/min for 60-80% water；
Diatom ooze, alumina silicate fibre, tributyl phosphate, mineral wool and white glue with vinyl are added, is again stirring for 1-2h；It is eventually adding remaining original
Material stirring 10-20min, obtains material；
(3) material is poured into mould, be molded by pressing mode, briquetting pressure 8-12MPa；
(4) plate after shaping is placed in humidity is 80%-90%, maintenance processing 4-6h is i.e. in the environment of temperature is 38-42 DEG C
Can.