CN107382227A - 一种诱生负离子的蛭石板及其制备方法 - Google Patents

一种诱生负离子的蛭石板及其制备方法 Download PDF

Info

Publication number
CN107382227A
CN107382227A CN201710700885.XA CN201710700885A CN107382227A CN 107382227 A CN107382227 A CN 107382227A CN 201710700885 A CN201710700885 A CN 201710700885A CN 107382227 A CN107382227 A CN 107382227A
Authority
CN
China
Prior art keywords
anion
tourmaline
nano
vermiculite
vermiculite board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710700885.XA
Other languages
English (en)
Inventor
杨卓舒
纪勇
段晓
张军华
马春羽
甄瑞成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hebei Zhuoda Building Materials Research Institute Co Ltd
Original Assignee
Hebei Zhuoda Building Materials Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hebei Zhuoda Building Materials Research Institute Co Ltd filed Critical Hebei Zhuoda Building Materials Research Institute Co Ltd
Priority to CN201710700885.XA priority Critical patent/CN107382227A/zh
Publication of CN107382227A publication Critical patent/CN107382227A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种诱生负离子的蛭石板，包括以下质量百分比的组分：膨胀蛭石40‑50％、快硬硫铝酸盐水泥10‑20％、纳米电气石10‑20％、纳米二氧化钛5‑10％、超细硬质酸钙5‑10％、超细滑石粉5‑10％、纤维素5‑8％、石英砂10‑20％；本发明通过纳米电气石、纳米二氧化钛、超细硬质酸钙、超细滑石粉的合理配置，提高了负离子的诱生效果，可持久释放负离子，诱生负离子效率高、能够净化甲醛等污染物、吸放湿好、透气性好、防火隔音、防腐蚀霉变、生产制备成本低，且电气石含量较少，通过添加有效的辐射屏蔽剂，降低了电气石存在的放射性可能，更环保健康是一种绿色生态建筑产品。

Description

一种诱生负离子的蛭石板及其制备方法
技术领域
本发明涉及一种建筑材料，尤其是一种诱生负离子的蛭石板及其制备方法。
背景技术
随着人们的生活水平的提高和健康环保意识的增强，对家居装饰装修的材料的选材和使用提出了更高的要求。在竞争日益家具的室内装修材料上如何满足人们的使用要求成为了各大厂商优先考虑的问题。
蛭石板是一种新型的无机材料，以膨胀蛭石为主要原料，与一定比例的无机粘合剂混合，经过一系列工序加工而成的具有耐高温、防火、绿色环保、绝热、隔音、不含有害物质的板材。蛭石板同时具有韧性好、易加工、外观美观高贵等特点，非常适合作为装饰材料。蛭石板是用膨胀蛭石和一定剂量的黏合剂，经过热压或是冷压而制成的板材。该板材具有保温、隔热、防火等特点。此产品可以用在防火门芯，壁炉内衬，墙体材料。但是纯蛭石板由于是膨胀蛭石颗粒通过粘合剂粘结成板状的，虽然质轻，但是制作工艺复杂，目前国内外生产的蛭石板生产工艺是以人工辅料，输送通过热压成型，其缺点是人工费用过高，产量低，生产成本高。
在社会污染日益严重，人们生活环境日益恶化的今天，随着人们越来越注重健康，绿色生态建筑材料成了新材料研究的重点方向。绿色生态建筑材料是指那些具有良好的使用性能和优良的环境协调性的材料。良好的环境协调性是指资源、能源消耗少，环境污染小，再生循环利用率高。在人们越来越注重健康的今天，负氧离子(被誉为空气中的维生素)含量，甲醛、TVOC、放射性、PM2.5等含量越来越被人们所看重。
目前社会使用较多功能性产品如硅藻泥涂料、藻钙板等，主体使用的原料是硅藻泥，资源消耗大，产品虽然具有一定的释放负氧离子的功能，但其释放量低，净化甲醛、调节气候等作用也不是很明显。同时现在推销很广的空气净化气产品，主体是采用电激发原理产生负氧离子，能耗很大，而且同时产生对人体有害的臭氧，且产品的甲醛、PM2.5的净化效果也很难达到国家标准的75％以上。
负氧离子被誉为“空气维生素”，有利于人体的身心健康。它主要是通过人的神经系统及血液循环能对人的机体生理活动产生影响，负氧离子可让人体的毛细管扩张，从而起到促进血液循环促进再生细胞组织的作用。且还可防止细胞氧化，就是所谓的防止老化，促进新陈代谢，提高免疫力。此外也有着除昧，防止细菌生长，防霉，储热等效果。电气石可释放负氧离子，但是电气石释放负氧离子的速率低、浓度低，不能满足需求。
目前，CN201310604099.1公开了一种可释放负氧离子的蛭石板及其制备方法，然而所得诱生负离子蛭石板诱生负离子效率低，所用原材料电气石存在微量放射性，电气石含量较大会对人体造成伤害。
发明内容
针对现有技术中存在的不足，本发明的目的是提供一种可高效诱生负离子的蛭石板及其制备方法，本发明可持久释放负离子，诱生负离子效率高、净化甲醛等污染物、且电气石含量较少，更环保健康。
为了实现本发明目的，本发明通过以下技术方案实现：
一种诱生负离子的蛭石板，包括以下质量百分比的组分：膨胀蛭石40-50％、快硬硫铝酸盐水泥10-20％、纳米电气石10-20％、纳米二氧化钛5-10％、超细硬质酸钙5-10％、超细滑石粉5-10％、纤维素5-8％、石英砂10-20％。
所述诱生负离子的蛭石板，包括以下质量百分比的组分：膨胀蛭石40-45％、快硬硫铝酸盐水泥10-15％、纳米电气石10-15％、纳米二氧化钛5-8％、超细硬质酸钙5-8％、超细滑石粉5-8％、纤维素5-6％、石英砂10-15％。
所述诱生负离子的蛭石板，包括以下质量百分比的组分：膨胀蛭石40％、快硬硫铝酸盐水泥15％、纳米电气石10％、纳米二氧化钛5％、超细硬质酸钙5％、超细滑石粉5％、纤维素5％、石英砂15％。
所述诱生负离子的蛭石板的制备方法，包括以下步骤：
(1)称取膨胀蛭石、快硬硫铝酸盐水泥、纳米电气石、纳米二氧化钛、超细硬质酸钙、超细滑石粉、纤维素、石英砂，按质量百分比混合成粉料，加水搅拌5-10分钟成浆料；
(2)将搅拌均匀的浆料流入到皮带中，输送滚筒压粘浆制自成型；
(3)成型后的产品先常温养护6-8小时，然后蒸压10-12小时，烘干。
所述步骤(1)中粉料与水的质量比为7:3。
所述步骤(3)中蒸压温度为80-100℃。
所述步骤(3)中烘干温度为100-120℃，烘干时间5-8小时。
本发明的有益效果：本发明提供一种诱生负离子的蛭石板及其制备方法，通过纳米电气石、纳米二氧化钛、超细硬质酸钙、超细滑石粉的合理配置，提高了负离子的诱生效果，可持久释放负离子，诱生负离子效率高、能够净化甲醛等污染物、吸放湿好、透气性好、防火隔音、防腐蚀霉变、生产制备成本低，且电气石含量较少，通过添加有效的辐射屏蔽剂，降低了电气石存在的放射性可能，更环保健康是一种绿色生态建筑产品。
具体实施方式
以下通过具体实施例对本发明做进一步的详细阐述。
实施例1
(1)按质量百分比称取膨胀蛭石40％、快硬硫铝酸盐水泥15％、纳米电气石10％、纳米二氧化钛5％、超细硬质酸钙5％、超细滑石粉5％、纤维素5％、石英砂15％，混合成粉料；
(2)粉料与水的质量比按照7:3混合，搅拌10分钟直至均匀成浆料；
(3)将搅拌均匀的浆料流入到皮带中，输送滚筒压粘浆制自成型；
(4)成型后的产品先常温养护6小时，然后100℃蒸压10小时，最后以100℃烘干温度烘6小时，即可制得诱生负离子的蛭石板。
实施例2
(1)按质量百分比称取膨胀蛭石40％、快硬硫铝酸盐水泥10％、纳米电气石12.5％、纳米二氧化钛7.5％、超细硬质酸钙7.5％、超细滑石粉7.5％、纤维素5％、石英砂10％，混合成粉料；
(2)粉料与水的质量比按照7:3混合，搅拌10分钟直至均匀成浆料；
(3)将搅拌均匀的浆料流入到皮带中，输送滚筒压粘浆制自成型；
(4)成型后的产品先常温养护8小时，然后80℃蒸压12小时，最后以120℃烘干温度烘5小时，即可制得诱生负离子的蛭石板。
对比例
(1)依据CN201310604099.1公开的诱生负离子的蛭石板的制备方法，按体积百分含量称取膨胀蛭石55％、纤维素7％、石英砂25％、水泥12.6％、电气石0.4％；
(2)将上述原料通过搅拌器混合、搅拌均匀；
(3)将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；
(4)成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时，即可制得诱生负离子的蛭石板。
以上实施例、对比例制得的负离子蛭石板性能经实验室检测，测试结果如下表：
表2为面积200mm*400mm的负离子蛭石板在温度25℃，湿度75％RH，测定时间为100s，有害物质的检测结果
从以上实施例和对比例可以看出，对比例中的负离子蛭石板与实施例的组分不同、含量不同，从负离子蛭石板的性能测试结果表可以发现，对比例对应的蛭石板性能一般，释放的负离子量相对较少，而实施例中对应的蛭石板释放的负离子量明显较多，尤其是实施例1，同时，对比例中对有害气体的吸附效果也不理想，说明本发明负离子蛭石板组分和含量对蛭石板实现大量负离子的释放和有效吸附有害气体具有非常关键的意义。
本发明提供一种诱生负离子的蛭石板及其制备方法，通过纳米电气石、纳米二氧化钛、超细硬质酸钙、超细滑石粉的合理配置，提高了负离子的诱生效果，可持久释放负离子，诱生负离子效率高、能够净化甲醛等污染物、吸放湿好、透气性好、防火隔音、防腐蚀霉变、生产制备成本低，且电气石含量较少，通过添加有效的辐射屏蔽剂，降低了电气石存在的放射性可能，更环保健康是一种绿色生态建筑产品。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书的保护范围为准。

Claims (7)

1.一种诱生负离子的蛭石板，其特征在于，包括以下质量百分比的组分：膨胀蛭石40-50％、快硬硫铝酸盐水泥10-20％、纳米电气石10-20％、纳米二氧化钛5-10％、超细硬质酸钙5-10％、超细滑石粉5-10％、纤维素5-8％、石英砂10-20％。
2.根据权利要求1所述的一种诱生负离子的蛭石板，其特征在于：包括以下质量百分比的组分：膨胀蛭石40-45％、快硬硫铝酸盐水泥10-15％、纳米电气石10-15％、纳米二氧化钛5-8％、超细硬质酸钙5-8％、超细滑石粉5-8％、纤维素5-6％、石英砂10-15％。
3.根据权利要求1所述的一种诱生负离子的蛭石板，其特征在于：包括以下质量百分比的组分：膨胀蛭石40％、快硬硫铝酸盐水泥15％、纳米电气石10％、纳米二氧化钛5％、超细硬质酸钙5％、超细滑石粉5％、纤维素5％、石英砂15％。
4.根据权利要求1-3任一所述诱生负离子的蛭石板的制备方法，其特征在于，包括以下步骤：
(1)称取膨胀蛭石、快硬硫铝酸盐水泥、纳米电气石、纳米二氧化钛、超细硬质酸钙、超细滑石粉、纤维素、石英砂，按质量百分比混合成粉料，加水搅拌5-10分钟成浆料；
(2)将搅拌均匀的浆料流入到皮带中，输送滚筒压粘浆制自成型；
(3)成型后的产品先常温养护6-8小时，然后蒸压10-12小时，烘干。
5.根据权利要求4所述的诱生负离子的蛭石板的制备方法，其特征在于，所述步骤(1)中粉料与水的质量比为7:3。
6.根据权利要求4所述的诱生负离子的蛭石板的制备方法，其特征在于，所述步骤(3)中蒸压温度为80-100℃。
7.根据权利要求4所述的诱生负离子的蛭石板的制备方法，其特征在于，所述步骤(3)中烘干温度为100-120℃，烘干时间5-8小时。
CN201710700885.XA 2017-08-16 2017-08-16 一种诱生负离子的蛭石板及其制备方法 Pending CN107382227A (zh)