CN107376905B - 一种可降解甲醛的Ag/ZnO复合材料的制备方法 - Google Patents
一种可降解甲醛的Ag/ZnO复合材料的制备方法 Download PDFInfo
- Publication number
- CN107376905B CN107376905B CN201710806052.1A CN201710806052A CN107376905B CN 107376905 B CN107376905 B CN 107376905B CN 201710806052 A CN201710806052 A CN 201710806052A CN 107376905 B CN107376905 B CN 107376905B
- Authority
- CN
- China
- Prior art keywords
- zno
- nano particles
- composite material
- zno composite
- material capable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本申请公开了一种在可见光下就可以降解甲醛的Ag/ZnO复合材料的制备方法，包括以下步骤：(1)制备纳米ZnO颗粒；(2)Ag/ZnO的制备：通过物理气相沉积将Ag纳米颗粒均匀的分散在步骤(1)得到的ZnO纳米颗粒上，形成Ag/ZnO复合纳米颗粒。并可以进一步包含步骤(3)：将步骤(2)制备的Ag/ZnO复合纳米颗粒和椰壳活性碳以及聚乙烯混合，烧结成富含Ag/ZnO纳米颗粒的烧结活性碳颗粒。所得到的Ag/ZnO复合材料本申请通过银纳米粒子在可见光下的表面等离子共振效应突破了现有产品只有在紫外光下才能起到光催化效果的技术瓶颈，光催化效果好，简洁，高效。
Description
技术领域
本申请涉及一种光催化剂的制备方法，具体涉及一种可降解甲醛的Ag/ZnO复合材料的制备方法。
背景技术
光催化技术以半导体纳米材料二氧化钛TiO2为代表，利用自然光即可催化分解细菌和污染物，具有高催化活性、良好的化学稳定性和热稳定性、无二次污染、无刺激性、安全无毒等特点，且能长期有益于生态自然环境，是最具有开发前景的绿色环保催化剂之一。
氧化锌ZnO是一种具有卓越性能的新型宽禁带、高激发能的半导体材料，特殊的电子结构使它具有优异的电、磁、光等效应。氧化锌与二氧化钛相比，二者禁带宽度相当，但氧化锌生产工艺简单、成本低廉，因此成为目前被广泛研究的光催化半导体材料。然而，低量子产率和缺乏可见光利用阻碍了ZnO的实际应用。在ZnO粒子表面沉积贵金属是一种有效的半导体光催化剂改性方法，贵金属的掺杂可改变体系中的电子分布，使纳米半导体产生晶格缺陷和杂质能级，从而改善光量子效率，提高氧化还原能力，扩大光谱吸收范围。贵金属掺杂半导体能有效提高光生电荷与光生空穴的分离，是当前光催化剂改性研究中的一个热点。目前的研究中，银掺杂氧化锌复合光催化剂的主要合成方法有水热法、激光加热法、浸渍光解法、火焰喷雾热解法及光化学沉积法等。例如，CN1795970A公开了一种用于室温条件下催化完全氧化低浓度甲醛的高活性催化剂，该催化剂由金属氧化物为主体，在金属氧化物上负载贵金属组分构成，其中，金属氧化物组分可以是下列的金属氧化物群中至少一种，前述贵金属组分可以是下列的贵金属群中至少一种。金属氧化物：二氧化铈、二氧化锆、二氧化钛、三氧化二铝、三氧化二镧、氧化镁、氧化锌、氧化钙、氧化铜；贵金属群：铂、金、铑、钯、银；制备过程中贵金属组分可通过用各自的可溶的化合物水溶液以众所周知的浸渍法、沉淀法、溶胶-凝胶法负载于金属氧化物上。
但是，现有市面上流行的光触媒只能在紫外线的条件下才能发挥作用，或是用杂化方式，比如氮杂化，改变导带位置，从而可以吸收可见光来进行光催化。
发明内容
针对现有技术存在的上述不足，本发明的目的在于提供一种可降解甲醛的Ag/ZnO复合材料的制备方法。
为实现以上目的，本发明提供的一种可降解甲醛的Ag/ZnO复合材料的制备方法，采用如下技术方案：
一种可降解甲醛的Ag/ZnO复合材料的制备方法，包括以下步骤：
(1)制备纳米ZnO颗粒：将Zn(NO3)2溶液边搅拌边加入NaOH溶液，静置，将生成的沉淀物进行过滤，洗涤，并烘干，再将干燥好的沉淀物放在马弗炉里焙烧，冷却后研磨，得到ZnO纳米颗粒；
(2)Ag/ZnO的制备：通过物理气相沉积将Ag纳米颗粒均匀的分散在步骤(1)得到的ZnO纳米颗粒上，形成Ag/ZnO复合纳米颗粒。
优选的，进一步包含步骤(3)：将步骤(2)制备的Ag/ZnO复合纳米颗粒和椰壳活性碳以及聚乙烯混合，烧结成富含Ag/ZnO纳米颗粒的烧结活性碳颗粒。
进一步地，所述步骤(2)中，物理气相沉积过程中，首先抽真空至0.05帕，并保持真空度不低于0.1Pa。
优选的，所述步骤(2)中，ZnO和Ag的质量比为20：1。
优选的，所述步骤(1)中Zn(NO3)2溶液的浓度为1mol/L，NaOH溶液的浓度为2mol/L，Zn(NO3)2溶液与NaOH溶液的体积比为1:1。
优选的，所述步骤(3)中Ag/ZnO复合纳米颗粒、椰壳活性碳以及聚乙烯的质量比为1：100：2。
优选的，所述步骤(3)中烧结条件为：压力为2个大气压，温度为220℃，烧结时间为3小时。
本申请所述的物理气相沉积也即PVD(Physical Vapor Deposition)，是指在真空条件下，采用低电压、大电流的电弧放电技术，利用气体放电使靶材蒸发并使被蒸发物质与气体都发生电离，利用电场的加速作用，使被蒸发物质及其反应产物沉积在工件上。
发明人发现，将银纳米颗粒以PVD方式分散在ZnO纳米颗粒上，不仅能够使分散更加均匀，而且能够形成特殊的Ag/ZnO复合纳米结构，这种Ag/ZnO的复合结构，在可见光的情况下，银纳米颗粒可以产生表面等离子体共振，可以将被自身激发的活性电子传输到ZnO的导带上，银纳米颗粒会留下活性正电荷，可以氧化降解甲醛等有机物。
在紫外光存在条件下，ZnO纳米颗粒在紫外光照射下所产生的活性电子和正电荷空穴，以及从银纳米颗粒得到的活性电子，同样可以降解有机物，具有杀菌和消毒的作用。
根据本申请方法制备得到的可降解甲醛的Ag/ZnO复合材料，可以用于室内空气处理，例如做成成品放置在室内，车内或是其它场所内，可以降解甲醛，吸附空气中的粉尘和其它有害杂质；也可以和空气净化器结合，达到空气的全方位净化。
根据本申请方法制备得到的可降解甲醛Ag/ZnO复合材料，可以用于降解甲醛。
与现有技术相比，本申请具有以下有益效果：
(1)ZnO纳米颗粒上进行PVD方式将银纳米颗粒均匀分散进行装饰，使银纳米颗粒更为均匀的分散在ZnO纳米颗粒上，Ag/ZnO纳米组合结构显示出更高的可见光和紫外(UV)光吸收，对甲醛降解的光催化活性显著提高。银纳米颗粒的等离子体共振(SPR)，显著改善了光激发ZnO的电荷分离。通过银纳米粒子在可见光下的表面等离子共振效应突破了现有产品只有在紫外光下才能起到光催化效果的技术瓶颈。
(2)将Ag/ZnO复合纳米颗粒和椰壳活性碳以及粘合剂聚乙烯烧结在一块，形成富含Ag/ZnO复合纳米颗粒的烧结活性碳颗粒，让Ag/ZnO纳米颗粒更为有效的附着在活性碳上，发挥其光催化的效果。
(3)本申请Ag/ZnO复合纳米结构利用了金属纳米颗粒的表面等离子体共振，从而在金属纳米颗粒上产生活性电子和空穴，从而提高整个系统光催化效果，可以在可见光下进行甲醛的降解，简洁，高效。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述，本发明的其它特征、目的和优点将会变得更明显：
图1为本申请Ag/ZnO纳米颗粒工作原理图；
1-导带；2-价带；3-可见光；4-紫外光。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进。这些都属于本发明的保护范围。
实施例1
一种可以降解甲醛的Ag/ZnO复合材料的制备方法，包括以下步骤：
(1)制备纳米ZnO颗粒：量取1mol/LZn(NO3)2的溶液50mL放入200ml烧杯里，边搅拌边加入50mL2mol/L NaOH溶液。静置一天时间。将生成的沉淀过滤，洗涤，80℃烘箱中烘干。将干燥好的沉淀放在马弗炉里焙烧3h。冷却后研磨即可得ZnO纳米颗粒；
(2)Ag/ZnO的制备：通过物理气相沉积将Ag纳米颗粒均匀的分散在步骤(1)制的ZnO纳米颗粒上，形成Ag/ZnO复合纳米颗粒，物理气相沉积过程中，首先抽真空至0.05帕，并保持真空度不低于0.1Pa，ZnO和Ag的质量比为20：1。
将本实施例制备得到的Ag/ZnO复合纳米颗粒放置于反应器中，进行甲醛处理的试验，结果表面甲醛降解率为90％。
如图1所示，本申请制备得到的这种Ag/ZnO的复合结构，可以在可见光3的情况下，Ag纳米颗粒位于ZnO纳米颗粒的表面，ZnO纳米颗粒中一部分为导带1，一部分为价带2，银纳米颗粒可以产生表面等离子体共振，可以将被自身激发的活性电子传输到ZnO的导带1上，银纳米颗粒会留下活性正电荷，可以氧化降解甲醛等有机物。同时，ZnO纳米颗粒在紫外光4照射下所产生的活性电子和正电荷空穴，以及从银纳米颗粒得到的活性电子，同样可以降解有机物，具有杀菌和消毒的作用。
实施例2
一种可以降解甲醛的Ag/ZnO复合材料的制备方法，包括以下步骤：
(1)制备纳米ZnO颗粒：量取1mol/LZn(NO3)2的溶液50mL放入200ml烧杯里，边搅拌边加入50mL2mol/L NaOH溶液。静置一天时间。将生成的沉淀过滤，洗涤，80℃烘箱中烘干。将干燥好的沉淀放在马弗炉里焙烧3h。冷却后研磨即可得ZnO纳米颗粒；
(2)Ag/ZnO的制备：通过物理气相沉积将Ag纳米颗粒均匀的分散在步骤(1)制的ZnO纳米颗粒上，形成Ag/ZnO复合纳米颗粒，物理气相沉积过程中，首先抽真空至0.05帕，并保持真空度不低于0.1Pa，ZnO和Ag的质量比为20：1；
(3)将步骤(2)制备的Ag/ZnO复合纳米颗粒和椰壳活性碳以及聚乙烯混合，其中Ag/ZnO复合纳米颗粒、椰壳活性碳以及聚乙烯的质量比为1：100：2，在压力为2个大气压，220℃条件下，烧结成富含Ag/ZnO纳米颗粒的烧结活性碳颗粒，3个小时。
将本实施例制备得到的Ag/ZnO复合纳米颗粒放置于反应器中，进行甲醛处理的试验，结果表面甲醛降解率为93％。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (6)
1.一种可降解甲醛的Ag/ZnO复合材料的制备方法，其特征在于，包括以下步骤：
(1)制备纳米ZnO颗粒：将Zn(NO3)2溶液边搅拌边加入NaOH溶液，静置，将生成的沉淀物进行过滤，洗涤，并烘干，再将干燥好的沉淀物放在马弗炉里焙烧，冷却后研磨，得到ZnO纳米颗粒；
(2)Ag/ZnO的制备：通过物理气相沉积将Ag纳米颗粒均匀的分散在步骤(1)得到的ZnO纳米颗粒上，形成Ag/ZnO复合纳米颗粒。
进一步包含步骤(3)：将步骤(2)制备的Ag/ZnO复合纳米颗粒和椰壳活性碳以及聚乙烯混合，烧结成富含Ag/ZnO纳米颗粒的烧结活性碳颗粒；
所述步骤(2)中，物理气相沉积的操作过程中，首先抽真空至0.05帕，并保持真空度不低于0.1Pa；
所述步骤(2)中，ZnO和Ag的质量比为20：1；
所述步骤(3)中Ag/ZnO复合纳米颗粒、椰壳活性碳以及聚乙烯的质量比为1：100：2。
2.根据权利要求1所述的可降解甲醛的Ag/ZnO复合材料的制备方法，其特征在于，所述步骤(1)中Zn(NO3)2溶液的浓度为1mol/L，NaOH溶液的浓度为2mol/L。
3.根据权利要求1所述的可降解甲醛的Ag/ZnO复合材料的制备方法，其特征在于，所述步骤(1)中Zn(NO3)2溶液与NaOH溶液的体积比为1:1。
4.根据权利要求1所述的可降解甲醛的Ag/ZnO复合材料的制备方法，其特征在于，所述步骤(3)中烧结条件为：压力为2个大气压，温度为220℃，烧结时间为3小时。
5.根据权利要求1～3任一项所述方法制备得到的可降解甲醛的Ag/ZnO复合材料用于室内空气处理。
6.根据权利要求1～3任一项所述方法制备得到的可降解甲醛的Ag/ZnO复合材料用于降解甲醛。