CN107376834A - A kind of preparation method for the fishing purse seine for handling breeding pollution - Google Patents
A kind of preparation method for the fishing purse seine for handling breeding pollution Download PDFInfo
- Publication number
- CN107376834A CN107376834A CN201710775654.5A CN201710775654A CN107376834A CN 107376834 A CN107376834 A CN 107376834A CN 201710775654 A CN201710775654 A CN 201710775654A CN 107376834 A CN107376834 A CN 107376834A
- Authority
- CN
- China
- Prior art keywords
- fishing
- purse seine
- temperature
- preparation
- breeding pollution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method for the fishing purse seine for handling breeding pollution, belong to technical field of aquaculture.Zeolite is the porous aluminosilicate crystals in skeletal structure, possesses higher cation exchange capacity (CEC), the ammonia nitrogen that the present invention is gone in water removal using the cation exchange capacity (CEC) of zeolite, and lanthanum hydroxide sediment is loaded to by natural zeolite surface using liquid-phase precipitation method, prepare lanthanum hydroxide natural zeolite composite, pass through the ligand exchange between the oh group and P elements on lanthanum hydroxide surface, adsorb P elements, effectively remove nitrogen excessive in water body, the nutrients such as phosphorus, mitigate the pressure of Water Environment In Lakes, it is effectively improved the capacity of self-regulation of water environment, it is worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation method for the fishing purse seine for handling breeding pollution, belong to technical field of aquaculture.
Background technology
To encourage the development of cultivation fishery, country adjusts Fisheries Development policy energetically, using aquaculture as national fishery
The emphasis of development.Seining cultivation is not only to improve the important measures of lake output of aquatic products, or the main source of fishery economic.
With greatly developing for seining cultivation industry, national aquaculture yield cumulative year after year, particularly nearly ten years, speedup are accelerated,
But while people's aquatic products demand is met, extremely serious destruction is also brought to water environment, or even threatens lake life
The balance of state system, seriously constrain the sustainable development of enclosure culture in lake industry.
Lake is the Main Waters resource of culture fishery, and necessary material base is provided for the development of seining cultivation industry
Condition.But culture fishery the problem of some are inevitable has been met with while fast development, most serious is exactly water body
Environment is heavily polluted, and destroys the rapport between water environment and aquaculture, and this seining cultivation industry made is faced with resource
With the huge challenge of the dual restriction of environment.
Artificial bait throwing in is the important measures that enclosure culture in lake quickly improves output of aquatic products, but the bait fed is usual
Have more than 30% not by fish.The bait not utilized sink under water after by microorganism decomposition consume dissolved oxygen, and then discharge
The nutrients such as nitrogen, phosphorus, fertilizer is turned into by material circulation, polluted-water environment, changes lake water water quality.So daily ration, feeding quantity
Be continuously increased be accelerate lake eutrophication, cause lake water quality deteriorate principal element.
The aquatic animal of seining cultivation can produce a large amount of excretas and secretion, contain substantial amounts of nitrification in these materials
Thing, such as:Ammonia, urea, creatine, protein etc..According to investigations, often production 1kg fish approximately produce 162g or so excrement it is organic
Thing, mainly include 30g total nitrogens, 7g total phosphorus.A large amount of residual feed and excretas are deposited on lakebed with secretion, pass through the decomposition of microorganism
Act on, the nutrient such as nitrogen, phosphorus in releasing organics, cause lake water overnutrition to cause body eutrophication, and then pollute
Water quality.
Therefore, how to mitigate the pressure of Water Environment In Lakes, be effectively improved the capacity of self-regulation of water environment, be to realize life
The grand strategy measure of state fishery.
The content of the invention
The technical problems to be solved by the invention:For a large amount of residual feed and excretas and secretion in current seining cultivation industry
Lakebed is deposited on, by the decomposition of microorganism, the nutrient such as nitrogen, phosphorus in releasing organics, causes lake water nutrition
It is surplus to cause body eutrophication, and then the problem of polluted water, there is provided a kind of preparation for the fishing purse seine for handling breeding pollution
Method.
In order to solve the above technical problems, the technical solution adopted by the present invention is:
A kind of preparation method for the fishing purse seine for handling breeding pollution, it is characterised in that concretely comprise the following steps:
(1)Natural zeolite is taken to be well mixed after crushing sieving with lanthanum chloride addition deionized water, pH is to 10~11 for regulation, and stirs
2~3h is staticly settled after mixing 1~2h, filters to obtain filter residue, filter residue washing and drying is obtained into composite;
(2)Take ultra-high molecular weight polyethylene to be fitted into melting extrusion in extruder after being mixed with composite, obtain melt;
(3)The melt of extrusion is cooled down and three-level stretching is carried out in the presence of carry-over pinch rolls, it is stretched to a diameter of 0.5~
1.2mm monofilament, obtains composite monofilament;
(4)Composite monofilament is placed on knot netting machine and is made into the purse seine that mesh is 10~50mm, the fishing that must handle breeding pollution is used
Purse seine.
Step(1)The mass ratio of the natural zeolite and lanthanum chloride is 5:1.
Step(2)The mass ratio of the ultra-high molecular weight polyethylene and composite is 20:1.
Step(2)The melting extrusion temperature is that preheating zone temperature is set to 120~130 DEG C, Heating Zone Temperature is set to 130~
140 DEG C, melting zone temperature is 135~145 DEG C, and transition region temperature is set to 130~140 DEG C, metering Pen Ji areas temperature is 130~
140℃。
Step(3)The three-level extensograph parameter is that one-level draft temperature is 80~90 DEG C, and draw ratio is 15~20, two level
Stretch draft temperature be 90~100 DEG C, draw ratio be 2~5, three-level draft temperature be 100~110 DEG C, draw ratio be 1~
2。
Step(2)The ultra-high molecular weight polyethylene is the ultra-high molecular weight polyethylene of molecular weight 150~1,800,000.
Compared with other method, advantageous effects are the present invention:
Zeolite is the porous aluminosilicate crystals in skeletal structure, possesses higher cation exchange capacity (CEC), present invention profit
The ammonia nitrogen gone with the cation exchange capacity (CEC) of zeolite in water removal, and lanthanum hydroxide sediment is loaded to by day using liquid-phase precipitation method
Right zeolite surface, prepare lanthanum hydroxide-natural zeolite composite, by the oh group and P elements on lanthanum hydroxide surface it
Between ligand exchange, adsorb P elements, effectively remove the nutrient such as excessive nitrogen, phosphorus in water body, mitigate Water Environment In Lakes
Pressure, be effectively improved the capacity of self-regulation of water environment, be worth of widely use.
Embodiment
Take natural zeolite to add in pulverizer to crush, cross 200 mesh sieves, obtain natural zeolite powder, take 10~20g natural zeolites
Powder, 2~4g lanthanum chlorides, add 100~200mL deionized waters in, at 30~35 DEG C, with 300~400r/min stirring 20~
30min, then with mass fraction be that 5% sodium hydroxide solution adjusts pH to 10~11, continue to staticly settle after 1~2h of stirring 2~
3h, filter residue is filtered to obtain, be transferred to after filter residue 3~5 times is washed with deionized in drying box, dried at 105~110 DEG C to perseverance
Weight, obtains composite, loads extruder after taking 200~400g ultra-high molecular weight polyethylenes, 10~20g composites well mixed
In, control melting extrusion temperature to be set to 120~130 DEG C for preheating zone temperature, Heating Zone Temperature is set to 130~140 DEG C, melting zone
Temperature is 135~145 DEG C, and transition region temperature is set to 130~140 DEG C, and metering Pen Ji areas temperature is 130~140 DEG C, obtains melt,
The melt of extrusion is cooled down and stretched in the presence of carry-over pinch rolls, one-level draft temperature is 80~90 DEG C, stretching times
Number is 15~20, and secondary drawing draft temperature is 90~100 DEG C, and draw ratio is 2~5, and three-level draft temperature is 100~110
DEG C, draw ratio is 1~2, is stretched to a diameter of 0.5~1.2mm, obtains composite monofilament, and composite monofilament is placed on knot netting machine
The purse seine that mesh is 10~50mm is made into, the fishing purse seine of breeding pollution must be handled.
Example 1
Take natural zeolite to add in pulverizer to crush, cross 200 mesh sieves, obtain natural zeolite powder, take 10g natural zeolite powders, 2g chlorinations
Lanthanum, add in 100mL deionized waters, at 30 DEG C, 20min is stirred with 300r/min, then with mass fraction be 5% sodium hydroxide
Solution adjusts pH to 10, continues to staticly settle 2h after stirring 1h, filters to obtain filter residue, be transferred to after filter residue 3 times is washed with deionized
In drying box, dried at 105 DEG C to constant weight, obtain composite, take 200g ultra-high molecular weight polyethylenes, 10g composites mix
It is fitted into after closing uniformly in extruder, controls melting extrusion temperature to be set to 120 DEG C for preheating zone temperature, Heating Zone Temperature is set to 130
DEG C, melting zone temperature is 135 DEG C, and transition region temperature is set to 130 DEG C, and metering Pen Ji areas temperature is 130 DEG C, obtains melt, will extrude
Melt cooled down and stretched in the presence of carry-over pinch rolls, one-level draft temperature be 80 DEG C, draw ratio 15, two level
It is 90 DEG C to stretch draft temperature, and draw ratio 2, three-level draft temperature is 100 DEG C, draw ratio 1, is stretched to a diameter of
1.2mm, composite monofilament is obtained, composite monofilament is placed on knot netting machine and is made into the purse seine that mesh is 10mm, obtains processing breeding pollution
Fishing purse seine.
Example 2
Take natural zeolite to add in pulverizer to crush, cross 200 mesh sieves, obtain natural zeolite powder, take 15g natural zeolite powders, 3g chlorinations
Lanthanum, add in 150mL deionized waters, at 32 DEG C, 25min is stirred with 350r/min, then with mass fraction be 5% sodium hydroxide
Solution adjusts pH to 11, continues to staticly settle 3h after stirring 2h, filters to obtain filter residue, be transferred to after filter residue 4 times is washed with deionized
In drying box, dried at 108 DEG C to constant weight, obtain composite, take 300g ultra-high molecular weight polyethylenes, 15g composites mix
It is fitted into after closing uniformly in extruder, controls melting extrusion temperature to be set to 125 DEG C for preheating zone temperature, Heating Zone Temperature is set to 135
DEG C, melting zone temperature is 136 DEG C, and transition region temperature is set to 135 DEG C, and metering Pen Ji areas temperature is 135 DEG C, obtains melt, will extrude
Melt cooled down and stretched in the presence of carry-over pinch rolls, one-level draft temperature be 85 DEG C, draw ratio 18, two level
It is 95 DEG C to stretch draft temperature, and draw ratio 3, three-level draft temperature is 105 DEG C, draw ratio 1, is stretched to a diameter of
0.8mm, composite monofilament is obtained, composite monofilament is placed on knot netting machine and is made into the purse seine that mesh is 10mm, obtains processing breeding pollution
Fishing purse seine.
Example 3
Take natural zeolite to add in pulverizer to crush, cross 200 mesh sieves, obtain natural zeolite powder, take 20g natural zeolite powders, 4g chlorinations
Lanthanum, add in 200mL deionized waters, at 35 DEG C, 30min is stirred with 400r/min, then with mass fraction be 5% sodium hydroxide
Solution adjusts pH to 11, continues to staticly settle 3h after stirring 2h, filters to obtain filter residue, be transferred to after filter residue 5 times is washed with deionized
In drying box, dried at 110 DEG C to constant weight, obtain composite, take 400g ultra-high molecular weight polyethylenes, 20g composites mix
It is fitted into after closing uniformly in extruder, controls melting extrusion temperature to be set to 130 DEG C for preheating zone temperature, Heating Zone Temperature is set to 140
DEG C, melting zone temperature is 145 DEG C, and transition region temperature is set to 140 DEG C, and metering Pen Ji areas temperature is 140 DEG C, obtains melt, will extrude
Melt cooled down and stretched in the presence of carry-over pinch rolls, one-level draft temperature be 90 DEG C, draw ratio 20, two level
It is 100 DEG C to stretch draft temperature, and draw ratio 5, three-level draft temperature is 110 DEG C, draw ratio 2, is stretched to a diameter of
0.5mm, composite monofilament is obtained, composite monofilament is placed on knot netting machine and is made into the purse seine that mesh is 10mm, obtains processing breeding pollution
Fishing purse seine.
Reference examples:The polyethylene fishing purse seine of Hunan Wang Ye Co., Ltds production.
The fishing of example and reference examples is detected with purse seine, specific testing result such as table 1.
Table 1
Detection project | Example 1 | Example 2 | Example 3 | Reference examples |
Ammonia nitrogen absorption amount(mg/g) | 1.0 | 1.3 | 1.2 | Nothing |
Phosphorus adsorbance(mg/g) | 2.4 | 2.9 | 2.5 | Nothing |
Fracture strength(MPa) | 1011 | 1054 | 1020 | 720 |
Knot strength(MPa) | 437 | 455 | 442 | 401 |
As shown in Table 1, the fishing of processing breeding pollution prepared by the present invention is good with purse seine mechanical strength, can effectively remove mistake in water body
The nutrients such as the nitrogen of amount, phosphorus, mitigate the pressure of Water Environment In Lakes, are effectively improved the capacity of self-regulation of water environment, are worth pushing away
It is wide to use.
Claims (6)
1. the preparation method of the fishing purse seine of kind of processing breeding pollution, it is characterised in that concretely comprise the following steps:
(1)Natural zeolite is taken to be well mixed after crushing sieving with lanthanum chloride addition deionized water, pH is to 10~11 for regulation, and stirs
2~3h is staticly settled after mixing 1~2h, filters to obtain filter residue, filter residue washing and drying is obtained into composite;
(2)Take ultra-high molecular weight polyethylene to be fitted into melting extrusion in extruder after being mixed with composite, obtain melt;
(3)The melt of extrusion is cooled down and three-level stretching is carried out in the presence of carry-over pinch rolls, it is stretched to a diameter of 0.5~
1.2mm monofilament, obtains composite monofilament;
(4)Composite monofilament is placed on knot netting machine and is made into the purse seine that mesh is 10~50mm, the fishing that must handle breeding pollution is used
Purse seine.
A kind of 2. preparation method of fishing purse seine for handling breeding pollution as claimed in claim 1, it is characterised in that step
(1)The mass ratio of the natural zeolite and lanthanum chloride is 5:1.
A kind of 3. preparation method of fishing purse seine for handling breeding pollution as claimed in claim 1, it is characterised in that step
(2)The mass ratio of the ultra-high molecular weight polyethylene and composite is 20:1.
A kind of 4. preparation method of fishing purse seine for handling breeding pollution as claimed in claim 1, it is characterised in that step
(2)The melting extrusion temperature is that preheating zone temperature is set to 120~130 DEG C, and Heating Zone Temperature is set to 130~140 DEG C, melting zone
Temperature is 135~145 DEG C, and transition region temperature is set to 130~140 DEG C, and metering Pen Ji areas temperature is 130~140 DEG C.
A kind of 5. preparation method of fishing purse seine for handling breeding pollution as claimed in claim 1, it is characterised in that step
(3)The three-level extensograph parameter is that one-level draft temperature is 80~90 DEG C, and draw ratio is 15~20, secondary drawing draft temperature
For 90~100 DEG C, draw ratio is 2~5, and three-level draft temperature is 100~110 DEG C, and draw ratio is 1~2.
A kind of 6. preparation method of fishing purse seine for handling breeding pollution as claimed in claim 1, it is characterised in that step
(2)The ultra-high molecular weight polyethylene is the ultra-high molecular weight polyethylene of molecular weight 150~1,800,000.