CN107366061A - A kind of production method of superpower stretch socks - Google Patents

A kind of production method of superpower stretch socks Download PDF

Info

Publication number
CN107366061A
CN107366061A CN201610313533.4A CN201610313533A CN107366061A CN 107366061 A CN107366061 A CN 107366061A CN 201610313533 A CN201610313533 A CN 201610313533A CN 107366061 A CN107366061 A CN 107366061A
Authority
CN
China
Prior art keywords
fabric
superpower
socks
ultra
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610313533.4A
Other languages
Chinese (zh)
Inventor
储国平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yixing Yidie Knitting Co Ltd
Original Assignee
Yixing Yidie Knitting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yixing Yidie Knitting Co Ltd filed Critical Yixing Yidie Knitting Co Ltd
Priority to CN201610313533.4A priority Critical patent/CN107366061A/en
Publication of CN107366061A publication Critical patent/CN107366061A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of production method of superpower stretch socks, comprise the following steps：A. in spinning machine symmetrical two-way feeding ultra-fine nylon fiber, after in spinning machine, symmetrical two-way feeds ultra-fine spandex fibre in addition, through shredding and drafting blending into cylinder yarn；B., cylinder yarn is woven into the fabric of preparation making socks；C. by fabric kiering；D. the fabric after kiering is subjected to dyeing processing；E. the fabric after dyeing washed, dried, pressed；F. superpower stretch socks are made in the general cutting of above-mentioned fabric and sewing.The superpower stretch socks ultra-fine nylon fiber and ultra-fine spandex fibre can be supplied to the good elasticity of socks, gas permeability and comfortableness, are especially suitable for people and worn in motion by blending resultant yarn.

Description

A kind of production method of superpower stretch socks
Technical field
The present invention relates to socks production field, more particularly to a kind of life of superpower stretch socks
Production method.
Background technology
Socks are one of most important necessitys in daily life.Socks are using textile fabric as raw material, are interweaved by multigroup yarn into the fabric with loop construction.With the increasingly raising of living standard, people are when selecting personal socks, in addition to warming foot protection function, more focus on the comfortableness and feature of socks, the stretch socks overwhelming majority in the market is woven socks, and processing method has two kinds：One kind is that another kind is to carry out cladding weaving to ultra-fine cotton fiber, flaxen fiber or chemical fibre elastic filament on cotton knitting machine to ultra-fine cotton fiber, flaxen fiber or the short fine progress of chemical fibre plating-knitted or local stiffening on cotton knitting machine.Due to using traditional weaving method, although being significantly reduced on thickness, integral, flexible is poor, is not appropriate for people and is worn in motion.
The content of the invention
The purpose of the present invention is exactly to solve the problems of the prior art, there is provided a kind of elasticity is strong, comfortable and easy to wear, is particularly suitable for the production method of superpower stretch socks worn in motion.
In order to solve the above technical problems, the present invention is achieved through the following technical solutions：
A kind of production method of superpower stretch socks, comprises the following steps：
A. in spinning machine symmetrical two-way feeding ultra-fine nylon fiber, after in spinning machine, symmetrical two-way feeds ultra-fine spandex fibre in addition, through shredding and drafting blending into cylinder yarn；
B., cylinder yarn is woven into the fabric of preparation making socks；
C. fabric is immersed in the kiering solution being made up of caustic soda and help experienced agent 3~5 hours；
D. the fabric after kiering is subjected to dyeing processing；
E. the fabric after dyeing washed, dried, pressed；
F. superpower stretch socks are made in the general cutting of above-mentioned fabric and sewing.
Further, described dyeing treatment temperature is 85 DEG C, and the time is 35 minutes.
Further, described drying and processing temperature is 100 DEG C, and the time is 60 minutes.
The beneficial effects of the invention are as follows：Ultra-fine nylon fiber and ultra-fine spandex fibre can be supplied to the good elasticity of socks, gas permeability and comfortableness, are especially suitable for people and worn in motion by blending resultant yarn.
Embodiment
With reference to specific embodiment, the present invention will be described in detail.
A kind of production method of superpower stretch socks of the present embodiment, comprises the following steps：
A. in spinning machine symmetrical two-way feeding ultra-fine nylon fiber, after in spinning machine, symmetrical two-way feeds ultra-fine spandex fibre in addition, through shredding and drafting blending into cylinder yarn；
B., cylinder yarn is woven into the fabric of preparation making socks；
C. fabric is immersed in the kiering solution being made up of caustic soda and help experienced agent 3~5 hours；
D. the fabric after kiering is subjected to dyeing processing, dyeing treatment temperature is 85 DEG C, and the time is 35 minutes；
E. the fabric after dyeing washed, dried, pressed, drying and processing temperature is 100 DEG C, and the time is 60 minutes；
F. superpower stretch socks are made in the general cutting of above-mentioned fabric and sewing.
The present invention is not limited to above-mentioned preferred forms; anyone can draw other various forms of products under the enlightenment of the present invention; however, make any change in its shape or structure, and it is every that there is technical scheme identical or similar to the present application, each fall within protection scope of the present invention.

Claims (3)

1. a kind of production method of superpower stretch socks, it is characterised in that comprise the following steps：
A. in spinning machine symmetrical two-way feeding ultra-fine nylon fiber, after in spinning machine, symmetrical two-way feeds ultra-fine spandex fibre in addition, through shredding and drafting blending into cylinder yarn；
B., cylinder yarn is woven into the fabric of preparation making socks；
C. fabric is immersed in the kiering solution being made up of caustic soda and help experienced agent 3~5 hours；
D. the fabric after kiering is subjected to dyeing processing；
E. the fabric after dyeing washed, dried, pressed；
F. superpower stretch socks are made in the general cutting of above-mentioned fabric and sewing.
A kind of 2. production method of superpower stretch socks according to claim 1, it is characterised in that：Described dyeing treatment temperature is 85 DEG C, and the time is 35 minutes.
A kind of 3. production method of superpower stretch socks according to claim 1, it is characterised in that：Described drying and processing temperature is 100 DEG C, and the time is 60 minutes.
CN201610313533.4A 2016-05-12 2016-05-12 A kind of production method of superpower stretch socks Pending CN107366061A (en)