CN107354768A - The preparation method of light blue cladding - Google Patents

The preparation method of light blue cladding Download PDF

Info

Publication number
CN107354768A
CN107354768A CN201710602769.4A CN201710602769A CN107354768A CN 107354768 A CN107354768 A CN 107354768A CN 201710602769 A CN201710602769 A CN 201710602769A CN 107354768 A CN107354768 A CN 107354768A
Authority
CN
China
Prior art keywords
parts
agent
preparation
scytoblastema
light
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710602769.4A
Other languages
Chinese (zh)
Inventor
唐志坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Hongxing Shoes Industry Co Ltd
Original Assignee
Guangzhou Hongxing Shoes Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Hongxing Shoes Industry Co Ltd filed Critical Guangzhou Hongxing Shoes Industry Co Ltd
Priority to CN201710602769.4A priority Critical patent/CN107354768A/en
Publication of CN107354768A publication Critical patent/CN107354768A/en
Pending legal-status Critical Current

Abstract

A kind of preparation method of light blue cladding, is related to the preparation of cladding, this method comprises the following steps：Step 1: scytoblastema changes colour, the spray liquid that changes colour uniformly is sprayed onto on scytoblastema by full-automatic spray skin machine；Step 2, finished product changes colour, the scytoblastema handled well in step 1 is placed into inside oil spout platform first, blue dye liquor is sprayed onto on scytoblastema using spray technique is molded, secondly the scytoblastema sprayed is placed into spraying on polishing machine and receives light auxiliary agent A, now the rotating speed of polishing machine is 19 revolutions per seconds, light auxiliary agent B is received in spraying again, now the rotating speed of polishing machine is 9 revolutions per seconds, finally light auxiliary agent C is received in spraying, now the rotating speed of polishing machine is 9 revolutions per seconds, pass through cladding color more saturation made from the method, comfort level can be more preferable, there is antique effect, and color and luster is unique, make color more natural, colour fixation can be more preferable.

Description

The preparation method of light blue cladding
Technical field：
The present invention relates to the preparation of cladding, and in particular to a kind of preparation method of light blue cladding.
Background technology：
Leather is widely used in the surface of people's livelihood articles for use, such as tables and chairs, sofa, footwear material, clothing etc., increases people's livelihood articles for use Texture, aesthetic feeling or durability.Leather can be roughly divided into dermatine and natural leather.Natural leather, which refers to, to be taken animal fur and gives With drying, cleaning, softening, dyeing, deburring, the manufacture craft processing such as cut after, form surfacing and strong but pliable in texture skin Material.
Following 2 drawbacks be present in the finished product processed using existing processing method：1st, surface can not be repaired well Disability.Colour uneven；2nd, brightness is unnatural, and coloring effect is bad, and color disorder is asked intolerant to seeing in order to solve above-mentioned technology Topic, spy propose a kind of new technical scheme.
The content of the invention：
In place of overcoming above-mentioned the shortcomings of the prior art, and provide a kind of light blue cladding Preparation method.
The technical solution adopted by the present invention is：A kind of preparation method of light blue cladding, this method comprise the following steps：Step Rapid one, scytoblastema changes colour, and is uniformly sprayed onto the spray liquid that changes colour on scytoblastema by full-automatic spray skin machine；
Step 2: finished product changes colour, the scytoblastema handled well in step 1 is placed into inside oil spout platform first, utilizes shaping Blue dye liquor is sprayed onto on scytoblastema by spray technique, and the scytoblastema sprayed secondly is placed into spraying on polishing machine receives light auxiliary agent A, now The rotating speed of polishing machine is 19 revolutions per seconds, and light auxiliary agent B is received in spraying again, and now the rotating speed of polishing machine is 9 revolutions per seconds, and light is received in finally spraying Auxiliary agent C, now the rotating speed of polishing machine is 9 revolutions per seconds.
Described spray change colour liquid composition and parts by weight be sky blue dyestuff 20-40 parts, emulsifying agent 10-20 parts, synthesis Resin 5-15 parts, surfactant 10-20 parts, levelling agent 1-10 parts, environment-friendly type solvent 20-30 parts.
Described emulsifying agent is alkylphenol-polyethenoxy base ether formaldehyde condensation products；Described synthesis resin is by acrylic acid tree Fat, polyurethane resin, the water-based filler of self-control and synthesis cerate composition；Described surfactant is polyoxyethylene glyceride, gathered Mixing more than one or both of oxygen ethene oleate, Emulsifier EL-60 and its derivative, LABRAFIL M 1944CS Thing.
Described blue dye liquor composition and parts by weight are sky blue dyestuff 30-50 parts, the 1-10 of organic solvent containing OH parts, steady Determine agent 1-10 parts, blended wax 10-20 parts, anti-settling agent 5-15 parts, organic pigment 20-30 parts.
The composition and parts by weight of described receipts light auxiliary agent A are pigment paste palm wax 25-35 parts, natural palm wax 35-45 Part, discoloration wax 10-20 parts, hand feeling agent 10-20 parts.
The composition and parts by weight of described receipts light auxiliary agent B are transparent pigment cream 25-35 parts, synthesis resin 25-35 parts, hand Feel agent 10-20 parts, bleeding agent 20-30 parts.
Described bleeding agent is made up of environment-friendly type solvent 60%, surfactant 30% and dispersant 10%.
The described composition for receiving light auxiliary agent C and parts by weight are cobalt blue dyestuff 35-45 parts, blue or green palm wax 1-10 parts, comprehensive Resin 20-30 parts, hand feeling agent surfactant 1-10 parts, bleeding agent 20-30 parts.
Described bleeding agent is made up of environment-friendly type solvent 45%, surfactant 25% and dispersant 30%.
Described environment-friendly type solvent is dimethyl carbonate, propene carbonate, ethylene dimethyl, dimethyl glutarate, fourth The combination of one or both of diacid diformazan and the above.
Beneficial effects of the present invention are：By cladding color more saturation made from the method, comfort level can be more preferable, has imitative Ancient effect, and color and luster is unique, makes color more natural, and colour fixation can be more preferable.
Embodiment：
The present invention is further described in conjunction with specific embodiments：
Embodiment one：
A kind of preparation method of light blue cladding, this method comprise the following steps：Step 1: scytoblastema changes colour, by it is complete from The spray liquid that changes colour uniformly is sprayed onto on scytoblastema by dynamic spray skin machine；
Step 2: finished product changes colour, the scytoblastema handled well in step 1 is placed into inside oil spout platform first, utilizes shaping Blue dye liquor is sprayed onto on scytoblastema by spray technique, and the scytoblastema sprayed secondly is placed into spraying on polishing machine receives light auxiliary agent A, now The rotating speed of polishing machine is 19 revolutions per seconds, and light auxiliary agent B is received in spraying again, and now the rotating speed of polishing machine is 9 revolutions per seconds, and light is received in finally spraying Auxiliary agent C, now the rotating speed of polishing machine is 9 revolutions per seconds.
Described spray change colour liquid composition and parts by weight be 20 parts of sky blue dyestuff, 10 parts of emulsifying agent, synthesis resin 5 Part, 10 parts of surfactant, 1 part of levelling agent, 20 parts of environment-friendly type solvent.
Described blue dye liquor composition and parts by weight are 30 parts of sky blue dyestuff, 1 part of organic solvent containing OH, stabilizer 1 Part, 10 parts of blended wax, 5 parts of anti-settling agent, 20 parts of organic pigment.
The composition and parts by weight of described receipts light auxiliary agent A are 25 parts of pigment paste palm wax, 35 parts of natural palm wax, discoloration 10 parts of wax, 10 parts of hand feeling agent.
The composition and parts by weight of described receipts light auxiliary agent B are 25 parts of transparent pigment cream, 25 parts of synthesis resin, hand feeling agent 10 Part, 20 parts of bleeding agent.
Described bleeding agent is made up of environment-friendly type solvent 60%, surfactant 30% and dispersant 10%.
The described composition for receiving light auxiliary agent C and parts by weight are 35 parts of cobalt blue dyestuff, 1 part of blue or green palm wax, synthesis resin 20 parts, 1 part of hand feeling agent surfactant, 20 parts of bleeding agent.
Described bleeding agent is made up of environment-friendly type solvent 45%, surfactant 25% and dispersant 30%.
Embodiment two：
A kind of preparation method of light blue cladding, this method comprise the following steps：Step 1: scytoblastema changes colour, by it is complete from The spray liquid that changes colour uniformly is sprayed onto on scytoblastema by dynamic spray skin machine；
Step 2: finished product changes colour, the scytoblastema handled well in step 1 is placed into inside oil spout platform first, utilizes shaping Blue dye liquor is sprayed onto on scytoblastema by spray technique, and the scytoblastema sprayed secondly is placed into spraying on polishing machine receives light auxiliary agent A, now The rotating speed of polishing machine is 19 revolutions per seconds, and light auxiliary agent B is received in spraying again, and now the rotating speed of polishing machine is 9 revolutions per seconds, and light is received in finally spraying Auxiliary agent C, now the rotating speed of polishing machine is 9 revolutions per seconds.
Described spray change colour liquid composition and parts by weight be 30 parts of sky blue dyestuff, 15 parts of emulsifying agent, synthesis resin 10 Part, 15 parts of surfactant, 5 parts of levelling agent, 25 parts of environment-friendly type solvent.
Described blue dye liquor composition and parts by weight are 40 parts of sky blue dyestuff, 5 parts of organic solvent containing OH, stabilizer 5 Part, 15 parts of blended wax, 10 parts of anti-settling agent, 25 parts of organic pigment.
The composition and parts by weight of described receipts light auxiliary agent A are 30 parts of pigment paste palm wax, 40 parts of natural palm wax, discoloration 15 parts of wax, 15 parts of hand feeling agent.
The composition and parts by weight of described receipts light auxiliary agent B are 30 parts of transparent pigment cream, 30 parts of synthesis resin, hand feeling agent 15 Part, 25 parts of bleeding agent.
Described bleeding agent is made up of environment-friendly type solvent 60%, surfactant 30% and dispersant 10%.
The described composition for receiving light auxiliary agent C and parts by weight are 40 parts of cobalt blue dyestuff, 5 parts of blue or green palm wax, synthesis resin 25 parts, 5 parts of hand feeling agent surfactant, 25 parts of bleeding agent.
Described bleeding agent is made up of environment-friendly type solvent 45%, surfactant 25% and dispersant 30%.
Embodiment three：
A kind of preparation method of light blue cladding, this method comprise the following steps：Step 1: scytoblastema changes colour, by it is complete from The spray liquid that changes colour uniformly is sprayed onto on scytoblastema by dynamic spray skin machine；
Step 2: finished product changes colour, the scytoblastema handled well in step 1 is placed into inside oil spout platform first, utilizes shaping Blue dye liquor is sprayed onto on scytoblastema by spray technique, and the scytoblastema sprayed secondly is placed into spraying on polishing machine receives light auxiliary agent A, now The rotating speed of polishing machine is 19 revolutions per seconds, and light auxiliary agent B is received in spraying again, and now the rotating speed of polishing machine is 9 revolutions per seconds, and light is received in finally spraying Auxiliary agent C, now the rotating speed of polishing machine is 9 revolutions per seconds.
Described spray change colour liquid composition and parts by weight be 40 parts of sky blue dyestuff, 20 parts of emulsifying agent, synthesis resin 15 Part, 20 parts of surfactant, 10 parts of levelling agent, 30 parts of environment-friendly type solvent.
Described blue dye liquor composition and parts by weight are 50 parts of sky blue dyestuff, 10 parts of organic solvent containing OH, stabilizer 10 parts, 20 parts of blended wax, 15 parts of anti-settling agent, 30 parts of organic pigment.
The composition and parts by weight of described receipts light auxiliary agent A are 35 parts of pigment paste palm wax, 45 parts of natural palm wax, discoloration 20 parts of wax, 20 parts of hand feeling agent.
The composition and parts by weight of described receipts light auxiliary agent B are 35 parts of transparent pigment cream, 35 parts of synthesis resin, hand feeling agent 20 Part, 30 parts of bleeding agent.
Described bleeding agent is made up of environment-friendly type solvent 60%, surfactant 30% and dispersant 10%.
The described composition for receiving light auxiliary agent C and parts by weight are 45 parts of cobalt blue dyestuff, 10 parts of blue or green palm wax, synthesis resin 30 parts, 10 parts of hand feeling agent surfactant, 30 parts of bleeding agent.
Described bleeding agent is made up of environment-friendly type solvent 45%, surfactant 25% and dispersant 30%.
Using effect is tested：
This research is handled cladding by randomly selecting 100 claddings, investigates the effect of this method each side.Test Project standards of grading are：Very satisfied 5 points, 4 points are satisfied with, general 3 points, is unsatisfied with 2 points, very dissatisfied 1 point.Wherein common group For common processing method；
In summary, the present invention its not only can effectively color saturation, reparation leather scar effect and color and luster problem, And it is safe to use, healthy, effective, colour fixation is also more preferable.The preparation method is by being made to the processing method of conventional leather Breakthrough adjustment, the proportioning of some unique raw material and raw material is equally added during adjustment, make entirely to make Preparation Method is more smooth, and effect is apparent.
For those skilled in the art, it is various corresponding can be made according to above technical scheme and design for other Change and deformation, and all these change and deformation should all belong within the protection domain of the claims in the present invention.

Claims (10)

  1. A kind of 1. preparation method of light blue cladding, it is characterised in that：This method comprises the following steps：Step 1: scytoblastema changes colour, The spray liquid that changes colour uniformly is sprayed onto on scytoblastema by full-automatic spray skin machine；
    Step 2: finished product changes colour, the scytoblastema handled well in step 1 is placed into inside oil spout platform first, sprays skill using shaping Blue dye liquor is sprayed onto on scytoblastema by art, and the scytoblastema sprayed secondly is placed into spraying on polishing machine receives light auxiliary agent A, now polishes The rotating speed of machine is 19 revolutions per seconds, and light auxiliary agent B is received in spraying again, and now the rotating speed of polishing machine is 9 revolutions per seconds, and light auxiliary agent is received in finally spraying C, now the rotating speed of polishing machine is 9 revolutions per seconds.
  2. 2. the preparation method of light blue cladding according to claim 1, it is characterised in that：Described spray is changed colour the composition of liquid And parts by weight be sky blue dyestuff 20-40 parts, emulsifying agent 10-20 parts, synthesis resin 5-15 parts, surfactant 10-20 parts, Levelling agent 1-10 parts, environment-friendly type solvent 20-30 parts.
  3. 3. the preparation method of light blue cladding according to claim 2, it is characterised in that：Described emulsifying agent is alkyl phenol Polyoxyethylene ether formaldehyde condensation products；Described synthesis resin is by acrylic resin, polyurethane resin, the water-based filler of self-control and conjunction Formed into cerate；Described surfactant be polyoxyethylene glyceride, polyoxyethylene oleate, Emulsifier EL-60 and its Mixture more than one or both of derivative, LABRAFIL M 1944CS.
  4. 4. the preparation method of light blue cladding according to claim 1, it is characterised in that：Described blue dye liquor composition and Parts by weight are sky blue dyestuff 30-50 parts, the 1-10 of organic solvent containing OH parts, stabilizer 1-10 parts, blended wax 10-20 parts, anti- Heavy agent 5-15 parts, organic pigment 20-30 parts.
  5. 5. the preparation method of light blue cladding according to claim 1, it is characterised in that：Described receipts light auxiliary agent A into Part and parts by weight are pigment paste palm wax 25-35 parts, natural palm wax 35-45 parts, discoloration wax 10-20 parts, hand feeling agent 10-20 Part.
  6. 6. the preparation method of light blue cladding according to claim 1, it is characterised in that：Described receipts light auxiliary agent B into Part and parts by weight are transparent pigment cream 25-35 parts, synthesis resin 25-35 parts, hand feeling agent 10-20 parts, bleeding agent 20-30 parts.
  7. 7. the preparation method of light blue cladding according to claim 6, it is characterised in that：Described bleeding agent is by environment-friendly type Solvent 60%, surfactant 30% and dispersant 10% form.
  8. 8. the preparation method of light blue cladding according to claim 1, it is characterised in that：It is described receive light auxiliary agent C into Part and parts by weight are cobalt blue dyestuff 35-45 parts, blue or green palm wax 1-10 parts, synthesis resin 20-30 parts, hand feeling agent surface-active Agent 1-10 parts, bleeding agent 20-30 parts.
  9. 9. the preparation method of light blue cladding according to claim 8, it is characterised in that：Described bleeding agent is by environment-friendly type Solvent 45%, surfactant 25% and dispersant 30% form.
  10. 10. the preparation method of the light blue cladding according to claim 7 or 9, it is characterised in that：Described environment-friendly type solvent For one or both of dimethyl carbonate, propene carbonate, ethylene dimethyl, dimethyl glutarate, succinic acid diformazan and Combination above.
CN201710602769.4A 2017-07-21 2017-07-21 The preparation method of light blue cladding Pending CN107354768A (en)