CN107353018A - 一种铁钩浇注料 - Google Patents
一种铁钩浇注料 Download PDFInfo
- Publication number
- CN107353018A CN107353018A CN201710418551.3A CN201710418551A CN107353018A CN 107353018 A CN107353018 A CN 107353018A CN 201710418551 A CN201710418551 A CN 201710418551A CN 107353018 A CN107353018 A CN 107353018A
- Authority
- CN
- China
- Prior art keywords
- castable
- cement
- al2o3
- alundum
- cleek
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种铁钩浇注料,所述的铁钩浇注料由如下组分按重量百分比组成:65‑75%的三氧化二铝主料,12‑18%的碳化硅,3‑7%的水泥,1‑5%的聚丙烯纤维,0.5‑1.5%的复合型外加剂,2‑5%的碳粉,1‑4%的超细粉,以上各组分的重量百分比以100%为准;所述的三氧化二铝主料由刚玉与矾土按照4‑6:4‑6的比例组成;所述的水泥为硅酸盐或铝酸钙水泥中的至少一种;所述的复合型外加剂由柠檬酸水溶液、化学纯磷酸三钠溶液以及木质素磺酸钙溶液按照2‑3.5:1.25‑1.5:1‑2比例混合而成;所述的超细粉由活性三氧化二铝微粉和氧化硅微粉按照1‑5:5‑10的比例混合而成;所述的聚丙烯纤维的直径5‑10微米,长度4‑8毫米;它具有强度高,抗侵蚀,耐冲刷,不粘渣,通铁量高,施工性能优良等特点。
Description
技术领域
本发明涉及一种铁钩浇注料,主要适用于大、中、小型高炉及冲天炉和矿热炉出铁钩的现场施工浇注,属于炉体浇注料技术领域。
背景技术
国内大型高炉多采用Al2O3-SiC-C质低水泥浇注料,其流动性好、耐火度高,浇注体致密性好、强度高,因此铁沟抗侵蚀、抗冲刷、使用寿命长;但该材料的最大问题是浇注后需要养护且不能过快速度烘烤,否则会出现强度低和爆炸爆裂等现象。而单出铁口的中、小型高炉,其铁沟需要快速修补,施工时间不能大于每次出铁的间隔时间。由于这种近乎苛刻的要求,上述普通的Al2O3-SiC-C质低水泥浇注料很难适用于该类型的高炉。所以,绝大多数单出铁口高炉都在使用免烘烤铁沟捣打料,该铁沟捣打料能够满足高炉出铁不需要烘烤或快速烘烤的要求,但它存在体积密度偏小,耐压强度偏低,抗侵蚀能力较差,抗冲刷能力更差,且维修频繁、劳动强度大、不符合环保要求等缺点。
大型铁沟浇注料能够使铁沟延长寿命,但不能满足施工要求;免烘烤铁沟捣打料虽然能够满足施工要求,却又无法使铁沟达到较长的寿命。
发明内容
本发明的目的在于克服现有技术存在的不足,而提供一种强度高,抗侵蚀,耐冲刷,不粘渣,通铁量高,施工性能优良的铁钩浇注料。
本发明的目的是通过如下技术方案来完成的,一种铁钩浇注料,所述的铁钩浇注料由如下组分按重量百分比组成:
三氧化二铝主料 65-75%,
碳化硅 12-18%,
水泥 3-7%,
聚丙烯纤维 1-5%,
复合型外加剂 0.5-1.5%,
碳粉 2-5%,
超细粉 1-4%,
以上各组分的重量百分比以100%为准。
作为优选:所述的浇注料由如下组分按重量百分比组成:
三氧化二铝主料 70%,
碳化硅 15%,
水泥 5%,
聚丙烯纤维 3%,
复合型外加剂 1%,
碳粉 3.5%,
超细粉 2.5%。
作为优选:所述的三氧化二铝主料由刚玉与矾土按照4-6:4-6的比例组成;所述的水泥为硅酸盐或铝酸钙水泥中的至少一种;所述的复合型外加剂由柠檬酸水溶液、化学纯磷酸三钠溶液以及木质素磺酸钙溶液按照2-3.5:1.25-1.5:1-2比例混合而成;所述的超细粉由活性三氧化二铝微粉和氧化硅微粉按照1-5:5-10的比例混合而成;所述的聚丙烯纤维的直径5-10微米,长度4-8毫米。
本发明具有强度高,抗侵蚀,耐冲刷,不粘渣,通铁量高,施工性能优良,成型后经养护及烘烤无明显裂纹,粘结性能好,整体使用寿命长等特点。
具体实施方式
下面将结合具体实施例对本发明作详细的介绍:本发明所述的一种铁钩浇注料,所述的铁钩浇注料由如下组分按重量百分比组成:
三氧化二铝主料 65-75%,
碳化硅 12-18%,
水泥 3-7%,
聚丙烯纤维 1-5%,
复合型外加剂 0.5-1.5%,
碳粉 2-5% ,
超细粉 1-4%,
以上各组分的重量百分比以100%为准。
所述的三氧化二铝主料由刚玉与矾土按照4-6:4-6的比例组成;所述的水泥为硅酸盐或铝酸钙水泥中的至少一种;所述的复合型外加剂由柠檬酸水溶液、化学纯磷酸三钠溶液以及木质素磺酸钙溶液按照2-3.5:1.25-1.5:1-2比例混合而成;所述的超细粉由活性三氧化二铝微粉和氧化硅微粉按照1-5:5-10的比例混合而成;所述的聚丙烯纤维的直径5-10微米,长度4-8毫米。
本发明所述的复合型外加剂中配制的柠檬酸溶液的浓度0.075%,磷酸三钠溶液的浓度0.05%,木质素酸钙溶液的浓度0.03%。
复合型外加剂能够在一定程度上阻碍了水泥的水化,使得水泥水化更加有序,水化形成的结构更加密实,磷酸盐成分的加入在熟料相表面形成了不浮性磷酸盐,降低了开放孔的数量,增加了封闭孔的数量,因此可以提高混凝土,也即浇注料的抗渗性和抗冻融性。另外复合型外加剂中的木质素磺酸盐属于阴离子型高分子表面活性剂,具有半胶体性质,可以在水泥水化产物之间形成膜状胶结层,该胶结层可与水化产物相互填充,相互交织,使得硬化体的孔隙率减少,密实度增加,从而使浇注料的强度得到提高。
实施例1:本发明所述的所述的浇注料由如下组分按重量百分比组成:70%的三氧化二铝主料,其中刚玉与矾土各半混合组成;15%的碳化硅;5%硅酸盐水泥;3%的聚丙烯纤维,聚丙烯纤维的直径8微米,长度5.5毫米;1%的复合型外加剂,其中0.5%柠檬酸水溶液、0.23%化学纯磷酸三钠以及0.27%木质素磷酸钙;3.5%的碳粉;2.5%的超细粉,其中包括0.75%的活性三氧化二铝微粉和1.75%的氧化硅微粉。
实施例2:本发明所述的浇注料由如下组分按重量百分比组成:65%的三氧化二铝主料,其中60%的刚玉与40%的矾土混合组成;16%的碳化硅;6 %硅酸盐水泥;4%的聚丙烯纤维,聚丙烯纤维的10微米,长度8毫米;1.5%的复合型外加剂,其中0.55%柠檬酸水溶液、0.4%化学纯磷酸三钠以及0.55%木质素磷酸钙;4%的碳粉;3.5%的超细粉,其中包括1.75%的活性三氧化二铝微粉和1.75%的氧化硅微粉。
实施例3:本发明所述的浇注料由如下组分按重量百分比组成:75%的三氧化二铝主料,其中40%的刚玉与60%的矾土混合组成;14%的碳化硅;4 %硅酸盐水泥;2%的聚丙烯纤维,聚丙烯纤维的5微米,长度4毫米;0.5%的复合型外加剂,其中0.3%柠檬酸水溶液、0.11%化学纯磷酸三钠以及0.09%木质素磷酸钙;3%的碳粉;1.5%的超细粉,其中包括0.14%的活性三氧化二铝微粉和1.36%的氧化硅微粉。
本发明的其它实施例可以在上述实施例的基础上,通过数值的简单替换即可获得无数个实施例,且这种替换是本领域技术人员能够简单实现并实施的。
Claims (3)
1.一种铁钩浇注料,其特征在于所述的铁钩浇注料由如下组分按重量百分比组成:
三氧化二铝主料 65-75%,
碳化硅 12-18%,
水泥 3-7%,
聚丙烯纤维 1-5%,
复合型外加剂 0.5-1.5%,
碳粉 2-5%,
超细粉 1-4%,
以上各组分的重量百分比以100%为准。
2.根据权利要求1所述的铝碳化硅浇注料,其特征在于所述的浇注料由如下组分按重量百分比组成:
三氧化二铝主料 70%,
碳化硅 15%,
水泥 5%,
聚丙烯纤维 3%,
复合型外加剂 1%,
碳粉 3.5%,
超细粉 2.5%。
3.根据权利要求1或2所述的铝碳化硅浇注料,其特征在于所述的三氧化二铝主料由刚玉与矾土按照4-6:4-6的比例组成;所述的水泥为硅酸盐或铝酸钙水泥中的至少一种;所述的复合型外加剂由柠檬酸水溶液、化学纯磷酸三钠溶液以及木质素磺酸钙溶液按照2-3.5:1.25-1.5:1-2比例混合而成;所述的超细粉由活性三氧化二铝微粉和氧化硅微粉按照1-5:5-10的比例混合而成;所述的聚丙烯纤维的直径5-10微米,长度4-8毫米。