CN107345029A - Laser carving master batch, can laser marking be high flows high brilliant black polypropene composition and preparation method thereof - Google Patents
Laser carving master batch, can laser marking be high flows high brilliant black polypropene composition and preparation method thereof Download PDFInfo
- Publication number
- CN107345029A CN107345029A CN201710488854.2A CN201710488854A CN107345029A CN 107345029 A CN107345029 A CN 107345029A CN 201710488854 A CN201710488854 A CN 201710488854A CN 107345029 A CN107345029 A CN 107345029A
- Authority
- CN
- China
- Prior art keywords
- master batch
- laser
- laser marking
- polypropene composition
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of laser carving master batch, and it is using polypropylene as master batch carrier, including accounts for the inorganic oxide of gross weight 15~25% according to the weight percentage of raw materials.Also disclose that one kind can laser marking be high flows high brilliant black polypropene composition, it is based on parts by weight of raw materials including following component:1~5 part of laser carving master batch, 71.4~90.4 parts of acrylic resin, 2~5 parts of C5 Petropols, 5~15 parts of barium sulfate, 0.1~0.4 part of nucleator, 0.2~0.6 part of antioxidant, 1~2 part of toner, 0.3~0.6 part of lubricant.The laser carving master batch of the present invention is used in mixed way by sensitising agent and inorganic oxide, so as to significantly improve the laser carving master batch as can the definition of laser marking and the whiteness of mark word after active ingredient in laser marking polypropene composition.The present invention can the polypropene composition of laser marking there is high fluidity, highlighted blackness, the high whiteness of laser mark and fine definition, ensure that the outward appearance mark of product after final laser marking is not easy to be destroyed.Said composition has good application prospect on household appliances shell.
Description
Technical field
The present invention relates to polymer modification field, more particularly to a kind of laser carving master batch, gathering containing the laser carving master batch
Propylene compositions and preparation method thereof.
Background technology
At present, the technology of printing mark is many on plastic goods, such as silk-screen printing, trans-printing, gold stamping.These sides
The equal metal surface printing of method, due to scraping or chemical contamination in commodity storage, handling process, causes mark to grind off or disappear, together
When the inefficient and high deficiency of cost also be present.With concern of the people to environmental protection, emerging laser labeling method just gradually takes
For above several prods labeling method.Laser marking is a kind of new labeling method, and the technology is swashed using the continuous of high-energy
Light beam is acted on frosting, is made the flash evapn of entry material, is caused entry material that Chemical Physics change occurs by luminous energy
Change, or moieties are burnt up by luminous energy, show the pattern and word of required etching, lacking for traditional character printing method can be avoided
Fall into, be widely used in each based article lettering.
Polypropylene material is using relatively extensively on household electrical appliance, and general household electrical appliances all use traditional surface printing technology at present,
Easily there is the phenomenon ground off in mark, has at present using laser marking technique to improve the fixing of mark, traditional " white with black
The blackness of the material of word " laser marking in itself is not black enough, the wrongly written or mispronounced character whiteness deficiency that laser marking comes out;If polypropylene material
Blackness and brightness increase, the wrongly written or mispronounced character that laser marking goes out is not white enough, not enough clearly, while in order to improve the Injection moldability of material
And various thin-walled property products applications are useful in, also there is higher requirement to the mobile performance of polypropylene material.If can solve
The glossiness of black polypropylene material, blackness, laser mark whiteness and definition, material flowability etc. take into account problem, material simultaneously
Material can be promoted and apply on high end home electric appliance casing.
The content of the invention
It is an object of the invention to for above-mentioned the deficiencies in the prior art, there is provided a kind of laser carving master batch and to contain the laser carving female
The polypropene composition of grain, while the preparation method of the laser carving master batch and polypropene composition is provided.
The technical solution used in the present invention is:A kind of laser carving master batch, it is using polypropylene as master batch carrier, including by raw material
Percentage by weight meter accounts for the inorganic oxide of gross weight 15~25%.
As the further improvement of such scheme, the inorganic oxide in diatomite, aluminum oxide, mica powder extremely
Few one kind.
As the further improvement of such scheme, the laser carving master batch according to the weight percentage of raw materials by 70~80% poly- third
Alkene, 15~25% inorganic oxide and 3~7% sensitising agent LS8835 compositions.
As the further improvement of such scheme, the polypropylene is the HOPP resin of high-crystallinity, and it is melted
Flow rate > 30g/10min.
A kind of preparation method of laser carving master batch as described above, it is to add each component to mix according to the weight percentage of raw materials
Conjunction machine is well mixed, and is then added in double screw extruder, the extruding pelletization after melt blending under 200~220 DEG C of processing temperatures.Enter
One step, the well mixed mixing time is 2~5min.
Another technical scheme for being taken of the present invention is:One kind can the high high brilliant black Polypropylene compositions of flowing of laser marking
Thing, it is based on parts by weight of raw materials including following component:
Wherein, described laser carving master batch is heretofore described using polypropylene as master batch carrier, including by raw material weight
Percentages account for the self-control laser carving master batch of the inorganic oxide of gross weight 15~25%.
As the further improvement of such scheme, the toner is by EG is red, 136 yellow, transparent purplish blue and the green compoundings of 5B form.
The toner utilizes red, yellow, primary colors toner system by composition material mixing color into black, and it uses carbon mother with traditional
Larger difference be present in the toner of system.Specifically, the toner in the present invention preferably by accounting for 34% according to the weight percentage of raw materials
EG is red, 16% 136 Huangs, 25% transparent purplish blue and the green compoundings of 25% 5B form.
As the further improvement of such scheme, the molecular weight of the C5 Petropols is 1500~2500, its softening point
For 110~120 DEG C.
As the further improvement of such scheme, the barium sulfate is through the surface-treated sulfuric acid of zinc stearate and EBS
Barium, it effectively improves the dispersiveness of barium sulfate, so as to optimize the combination property of polypropene composition.Specifically, barium sulfate
It is surface-treated as in closed high-speed mixer, 3min is handled under 100 DEG C of temperature conditionss after addition zinc stearate and EBS,
Wherein the addition of zinc stearate and EBS is respectively the 1% of the gross weight of not surface treated barium sulfate.Further, originally
Particle diameter≤7 μm of barium sulfate used by invention.
As the further improvement of such scheme, the acrylic resin in the composition in the laser carving master batch with adding
Acrylic resin it is identical, the HOPP resin from high-crystallinity, its melt flow rate > 30g/10min.
As the further improvement of such scheme, the nucleator is aryl phosphoric acids salt nucleator.
As the further improvement of such scheme, the antioxidant is selected from Hinered phenols antioxidant, phosphorous acid esters antioxygen
At least one of agent, sulfur type antioxidant and composite antioxidant.Yet further, wherein the Hinered phenols antioxidant be selected from β-
The positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid, four [β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid]
Pentaerythritol ester, 1,3,5- tri- (the 4- tert-butyl group -3- hydroxyl -2,6- dimethyl benzyls) -1,3,5- triazines -2,4,6- (1H, 3H,
5H)-triketone, triethylene-glycol it is double [β-(3- tertiary butyl-4-hydroxy -5- aminomethyl phenyls) propionic ester, it is double (3,5- di-t-butyls -
4- benzylphosphonic acids mono ethyl ester) calcium, N, N '-bis--[3- (3,5- di-tert-butyl-hydroxy phenyls) propionyl] hexamethylene diamine,
One of which in 4,4'- thiobis (the 6- tert-butyl group -3- methylphenols);The phosphite ester kind antioxidant is selected from phosphorous acid three
One of which in (2,4- di-tert-butyl-phenyls) ester, four (2,4- di-tert-butylphenols) -4,4- xenyl diphosphites;It is described
One of which of the sulfur type antioxidant in Anoxsyn442, DLTP, Irganox1035,1192;The composite antioxidant is selected from
One of which in Ultranox815A, 817A, Naugard900, CyanoxXS4.
As the further improvement of such scheme, it is double hard that the lubricant is selected from pentaerythritol stearate, N, N '-supportted
At least one of acyl amine, glycerin monostearate, amide waxe, n-butyl stearate, zinc stearate, calcium stearate.
It is a kind of it is as described above it is a kind of can the high preparation method for flowing high brilliant black polypropene composition of laser marking, its be by
Each component addition mixer is well mixed by raw material weight percentages, is then added in double screw extruder, at 180~230 DEG C
Extruding pelletization after melt blending under processing temperature, the preferable draw ratio of extruder are 40:1.
The beneficial effects of the invention are as follows:
(1) laser carving master batch of the invention is using acrylic resin as carrier, using the laser printing mechanism of high polymer material,
Be used in mixed way by sensitising agent and inorganic oxide, so as to significantly improve by the laser carving master batch be used as can laser marking poly- third
The definition of laser marking and the whiteness of mark word after active ingredient in ene compositions.
(2) C5 Petropols be with the addition of in polypropene composition of the invention, because its molecular weight is relatively low, glossiness compared with
Height, there is good parcel ability to acrylic resin and filler, the glossiness and toner of polypropene composition can be effectively improved
Colorability, while the addition of C5 Petropols can also be effectively improved the melt flow rate of polypropene composition, and then
It is effectively improved its machine-shaping property.
Carbon parent system
Carbon parent system.And the carbon parent system such as carbon black used in tradition can cause very as toner to the mark whiteness of laser marking
Big to influence, the present invention can be effectively improved the definition and whiteness of laser marking using three primary colors toner system, make product more beautiful
See, further ensure that the effect of laser marking.
(4) it is of the invention can the polypropene composition of laser marking there is high fluidity, highlighted blackness, laser mark Gao Bai
Degree and fine definition, ensure that the outward appearance mark of product after final laser marking is not easy to be destroyed, while its preparation method is simple,
It is adapted to large-scale industrial production.Said composition has good application prospect on household appliances shell.
Embodiment
The present invention is specifically described with reference to embodiment, in order to art personnel to the present invention
Understand.It is necessary that herein the present invention will be further described it is emphasized that embodiment is only intended to, it is impossible to be interpreted as to this
The limitation of invention protection domain, art person skilled in the art, the non-intrinsically safe made according to foregoing invention content to the present invention
The modifications and adaptations of property, should still fall within protection scope of the present invention.Simultaneously following mentioned raw materials are unspecified, are
Commercially available prod;The processing step or preparation method not referred in detail be processing step known to a person skilled in the art or
Preparation method.
Embodiment 1
A kind of laser carving master batch, it is according to the weight percentage of raw materials by 75% polypropylene, 20% inorganic oxide and 5%
Sensitising agent LS8835 composition.Wherein, the inorganic oxide is by 7% diatomite, 5% aluminum oxide and 8% mica powder
Mixing composition;The polypropylene be high-crystallinity HOPP resin, its melt flow rate > 30g/10min.
Preparation method:
Each component is added into mixer according to the weight percentage of raw materials and mixes 3min, is then added to double screw extruder
In, the extruding pelletization after melt blending under 210 DEG C of processing temperatures, obtain the laser carving master batch finished product of embodiment 1.
Embodiment 2
A kind of laser carving master batch, it is according to the weight percentage of raw materials by 70% polypropylene, 25% inorganic oxide and 5%
Sensitising agent LS8835 composition.Wherein, the inorganic oxide is by 10% diatomite, 5% aluminum oxide and 10% mica powder
Mixing composition;The polypropylene be high-crystallinity HOPP resin, its melt flow rate > 30g/10min.
Preparation method:
Each component is added into mixer according to the weight percentage of raw materials and mixes 5min, is then added to double screw extruder
In, the extruding pelletization after melt blending under 200 DEG C of processing temperatures, obtain the laser carving master batch finished product of embodiment 2.
Embodiment 3
A kind of laser carving master batch, it is according to the weight percentage of raw materials by 80% polypropylene, 15% inorganic oxide and 5%
Sensitising agent LS8835 composition.Wherein, the inorganic oxide is by 5% diatomite, 4% aluminum oxide and 6% mica powder
Mixing composition;The polypropylene be high-crystallinity HOPP resin, its melt flow rate > 30g/10min.
Preparation method:
Each component is added into mixer according to the weight percentage of raw materials and mixes 2min, is then added to double screw extruder
In, the extruding pelletization after melt blending under 220 DEG C of processing temperatures, obtain the laser carving master batch finished product of embodiment 3.
Embodiment 4
One kind can laser marking be high flows high brilliant black polypropene composition, and it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The molecular weight of the C5 Petropols is 1500~2500, and its softening point is 110~120 DEG C;The barium sulfate is warp
Zinc stearate and the barium sulfate of surface-treated particle diameter≤7 μm of EBS;The toner is by according to the weight percentage of raw materials 34%
EG is red, 16% 136 Huangs, 25% transparent purplish blue and the green compoundings of 25% 5B form.
Preparation method:
Each component addition mixer is well mixed according to the weight percentage of raw materials, is then added in double screw extruder,
Extruding pelletization after melt blending under 180~230 DEG C of processing temperatures, the preferable draw ratio of extruder are 40:1, obtain embodiment 4
Polypropene composition.
Embodiment 5
One kind can laser marking be high flows high brilliant black polypropene composition, and it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The molecular weight of the C5 Petropols is 1500~2500, and its softening point is 110~120 DEG C;The barium sulfate is warp
Zinc stearate and the barium sulfate of surface-treated particle diameter≤7 μm of EBS;The toner is by according to the weight percentage of raw materials 34%
EG is red, 16% 136 Huangs, 25% transparent purplish blue and the green compoundings of 25% 5B form.
Preparation method is identical with the preparation method of embodiment 4, obtains the polypropene composition of embodiment 5.
Embodiment 6
One kind can laser marking be high flows high brilliant black polypropene composition, and it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The molecular weight of the C5 Petropols is 1500~2500, and its softening point is 110~120 DEG C;The barium sulfate is warp
Zinc stearate and the barium sulfate of surface-treated particle diameter≤7 μm of EBS;The toner is by according to the weight percentage of raw materials 34%
EG is red, 16% 136 Huangs, 25% transparent purplish blue and the green compoundings of 25% 5B form.
Preparation method is identical with the preparation method of embodiment 4, obtains the polypropene composition of embodiment 6.
Embodiment 7
One kind can laser marking be high flows high brilliant black polypropene composition, and it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The molecular weight of the C5 Petropols is 1500~2500, and its softening point is 110~120 DEG C;The barium sulfate is warp
Zinc stearate and the barium sulfate of surface-treated particle diameter≤7 μm of EBS;The toner is by according to the weight percentage of raw materials 34%
EG is red, 16% 136 Huangs, 25% transparent purplish blue and the green compoundings of 25% 5B form.
Preparation method is identical with the preparation method of embodiment 4, obtains the polypropene composition of embodiment 7.
Comparative example 1
A kind of black polypropene composition, it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The molecular weight of the C5 Petropols is 1500~2500, and its softening point is 110~120 DEG C;The barium sulfate is warp
Zinc stearate and the barium sulfate of surface-treated particle diameter≤7 μm of EBS;The toner is by according to the weight percentage of raw materials 34%
EG is red, 16% 136 Huangs, 25% transparent purplish blue and the green compoundings of 25% 5B form.
Preparation method is identical with the preparation method of embodiment 4, obtains the polypropene composition of comparative example 1.
Comparative example 2
A kind of polypropene composition, it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The barium sulfate is the barium sulfate through surface-treated particle diameter≤7 μm of zinc stearate and EBS;The toner is by by original
The EG of material percentage by weight meter 34% is red, the 136 of 16% yellow, 25% transparent purplish blue and the green compoundings of 25% 5B form.
Preparation method is identical with the preparation method of embodiment 4, obtains the polypropene composition of comparative example 2.
Comparative example 3
A kind of polypropene composition, it is based on parts by weight of raw materials including following component:
Wherein described acrylic resin be high-crystallinity HOPP resin, its melt flow rate > 30g/
10min;The molecular weight of the C5 Petropols is 1500~2500, and its softening point is 110~120 DEG C;The barium sulfate is warp
Zinc stearate and the barium sulfate of surface-treated particle diameter≤7 μm of EBS.
Preparation method is identical with the preparation method of embodiment 4, obtains the polypropene composition of comparative example 3.
Embodiment 8:Performance detection
The polypropene composition elder generation injection molded high gloss colour table that embodiment 4~7 and comparative example 1~3 are prepared into is again through swashing
Light mark is fabricated to detection sample.
First foaming degree, definition and the whiteness of its laser printing mark are assessed respectively using 15 times of magnifying glasses,
It is divided into four grades by white laser labeled effect:It is good it is white, normal it is white, slightly turn to be yellow white and not white, it is right respectively
Answer number of levels 4,3,2,1.Its glossiness is tested respectively using glossiness tester afterwards.Spectrophotometer is reused to dividing
It is other that its blackness is detected.Finally, related mechanics properties testing is carried out to each detection sample respectively.Its performance test results
It is as shown in table 1 below.
The polypropene composition performance test results that the embodiment 4~7 of table 1 and comparative example 1~3 are prepared into
Detecting data according to table 1 can obtain, comparative example 4 and comparative example 1, embodiment 5 and comparative example 2, embodiment 5 with it is right
The contrast of ratio 3 is found out, with the addition of C5 Petropols, can significantly improve glossiness and its flowing of polypropene composition
Property, the surface gloss of polypropene composition brings up to 92% from 85.2%, the addition for the laser carving master batch that the present invention is prepared into,
The definition of laser marking and the whiteness of laser marking word, contrastive colours powder system and the female dye of addition carbon can be obviously improved
Color, obvious relatively white using the definition of the laser marking of the polypropene composition of toner system and the whiteness of mark word, carbon is female
System laser marking effect is undesirable.
Above-described embodiment is the preferred embodiments of the present invention, all with similar technique of the invention and the equivalence changes made,
The protection category of the present invention all should be belonged to.
Claims (10)
- A kind of 1. laser carving master batch, it is characterised in that:Using polypropylene as master batch carrier, including gross weight is accounted for according to the weight percentage of raw materials The inorganic oxide of amount 15~25%.
- A kind of 2. laser carving master batch according to claim 1, it is characterised in that:The inorganic oxide is selected from diatomite, oxygen Change at least one of aluminium, mica powder.
- A kind of 3. laser carving master batch according to claim 1, it is characterised in that:According to the weight percentage of raw materials by 70~80% Polypropylene, 15~25% inorganic oxide and 3~7% sensitising agent LS8835 composition.
- A kind of 4. laser carving master batch according to claim 1 or 3, it is characterised in that:The polypropylene is equal for high-crystallinity Poly- acrylic resin, its melt flow rate > 30g/10min.
- A kind of 5. preparation method of laser carving master batch as described in any one of Claims 1 to 4, it is characterised in that:By raw material weight Each component addition mixer is well mixed by percentages, is then added in double screw extruder, in 200~220 DEG C of processing temperatures Extruding pelletization after lower melt blending.
- 6. one kind can laser marking be high flows high brilliant black polypropene composition, it is characterised in that including such as based on parts by weight of raw materials Lower component:
- 7. one kind according to claim 6 can laser marking be high flows high brilliant black polypropene composition, it is characterised in that:Institute Toner is stated by EG is red, 136 yellow, transparent purplish blue and the green compoundings of 5B form.
- 8. one kind according to claim 6 can laser marking be high flows high brilliant black polypropene composition, it is characterised in that:Institute The molecular weight for stating C5 Petropols is 1500~2500.
- 9. one kind according to claim 6 can laser marking be high flows high brilliant black polypropene composition, it is characterised in that:Institute It is through the surface-treated barium sulfate of zinc stearate and EBS to state barium sulfate.
- 10. it is a kind of as described in any one of claim 6~9 it is a kind of can laser marking is high flow high brilliant black polypropene composition Preparation method, it is characterised in that:Each component addition mixer is well mixed according to the weight percentage of raw materials, is then added to twin-screw In extruder, the extruding pelletization after melt blending under 180~230 DEG C of processing temperatures.