CN107338554A - A kind of artificial silk and terylene mixed textile technique - Google Patents
A kind of artificial silk and terylene mixed textile technique Download PDFInfo
- Publication number
- CN107338554A CN107338554A CN201710784829.9A CN201710784829A CN107338554A CN 107338554 A CN107338554 A CN 107338554A CN 201710784829 A CN201710784829 A CN 201710784829A CN 107338554 A CN107338554 A CN 107338554A
- Authority
- CN
- China
- Prior art keywords
- terylene
- artificial silk
- water
- mixed textile
- pressure value
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of artificial silk and terylene mixed textile technique, comprise the following steps：（1）Terylene is positioned in water steam box, water temperature is 90 110 degrees Celsius, and water steamed the time for 80 90 hours；（2）Terylene after water is steamed is put in pre-setting 15 25 hours under nature；（3）Test out the maximum elongation fracture pressure value of artificial silk；（4）Using water-jet loom, under maximum elongation fracture pressure value, mixed textile is carried out to artificial silk and terylene.The advantage of the invention is that：The present invention is by measuring the stretchable maximum pressure value of artificial silk, because the tensile capacity of artificial silk is weaker than terylene, therefore carrying out blending using the maximum pressure value that can apply to artificial silk can ensure that the tension force of artificial silk and terylene all can be not easy to break in tolerance range at it；Meanwhile before mixed textile is carried out, terylene is pre-processed so that artificial silk is more consistent with the characteristic of terylene, so as to be advantageous to the progress of subsequent technique.
Description
Technical field
The present invention relates to technical field of textile production, and in particular to a kind of artificial silk mixes with terylene
Textile technology.
Background technology
When carrying out mixed textile using different material silk, the tension force of various raw material threads and suitable processing temperature etc. are all to influence
The important parameter of end product quality, therefore need when designing textile technology to look after the characteristic of different material silk.Utilize people
Make silk with polyester filament mixed textile into fabric when, due to artificial silk and polyester filament characteristic difference it is larger, need to just use specific
Technique is weaved.Specifically, artificial silk poor water resistance, chance water is easily broken, and tensile capacity is weak, and stress is easily broken；And terylene is grown
The silk twist is high, and tensile capacity is strong.In order to look after different material silk when above-mentioned artificial silk and polyester filament are carried out into mixed textile
Characteristic is to ensure the quality of end product, in the prior art, tractive force and pretreating process processing it is improper so that the production being made into
More blind occurs in product.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to now provide a kind of technology maturation, weaving finished product is excellent
Artificial silk and terylene mixed textile technique.
To achieve the above object, the technical scheme is that：A kind of artificial silk and terylene mixed textile technique, it is innovated
Point is：Comprise the following steps：
（1）Terylene is positioned in water steam box, the water temperature is 90-110 degrees Celsius, and the water steaming time is 80-90 hours；
（2）Terylene after water is steamed is put in pre-setting 15-25 hours under nature；
（3）Test out the maximum elongation fracture pressure value of artificial silk；
（4）Using water-jet loom, under maximum elongation fracture pressure value, mixed textile is carried out to artificial silk and terylene.
Further, when the water-jet loom is drawn to terylene, nozzle of the specification for 30-45 is used, to artificial silk
When being drawn, nozzle of the specification for 10-20 is used.
Further, water temperature of the terylene in water steam box is 100 degrees Celsius.
Beneficial effects of the present invention are as follows：The present invention is by measuring the stretchable maximum pressure value of artificial silk, due to artificial
The tensile capacity of silk is weaker than terylene, therefore can ensure artificial silk using the maximum pressure value progress blending that can apply to artificial silk
All can be not easy to break in tolerance range at it with the tension force of terylene；Meanwhile before mixed textile is carried out, terylene is carried out
Pretreatment so that artificial silk is more consistent with the characteristic of terylene, so as to be advantageous to the progress of subsequent technique.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1
A kind of artificial silk and terylene mixed textile technique, comprise the following steps：
（1）Terylene is positioned in water steam box, water temperature is 90 degrees Celsius, and water steamed the time for 80 hours；
（2）Terylene after water is steamed is put in pre-setting 15 hours under nature；
（3）Test out the maximum elongation fracture pressure value of artificial silk；
（4）Using water-jet loom, under maximum elongation fracture pressure value, mixed textile is carried out to artificial silk and terylene, water spray is knitted
When machine is drawn to terylene, use specification for 30 nozzle, when being drawn to artificial silk, use specification for 10 nozzle.
Embodiment 2
A kind of artificial silk and terylene mixed textile technique, comprise the following steps：
（1）Terylene is positioned in water steam box, water temperature is 110 degrees Celsius, and water steamed the time for 90 hours；
（2）Terylene after water is steamed is put in pre-setting 25 hours under nature；
（3）Test out the maximum elongation fracture pressure value of artificial silk；
（4）Using water-jet loom, under maximum elongation fracture pressure value, mixed textile is carried out to artificial silk and terylene, water spray is knitted
When machine is drawn to terylene, use specification for 45 nozzle, when being drawn to artificial silk, use specification for 20 nozzle.
Embodiment 3
A kind of artificial silk and terylene mixed textile technique, comprise the following steps：
（1）Terylene is positioned in water steam box, water temperature is 100 degrees Celsius, and water steamed the time for 85 hours；
（2）Terylene after water is steamed is put in pre-setting 20 hours under nature；
（3）Test out the maximum elongation fracture pressure value of artificial silk；
（4）Using water-jet loom, under maximum elongation fracture pressure value, mixed textile is carried out to artificial silk and terylene, water spray is knitted
When machine is drawn to terylene, use specification for 45 nozzle, when being drawn to artificial silk, use specification for 15 nozzle.
The present invention is by measuring the stretchable maximum pressure value of artificial silk, because the tensile capacity of artificial silk is weaker than terylene,
Therefore carrying out blending using the maximum pressure value that can apply to artificial silk can ensure that the tension force of artificial silk and terylene all can at it
It is not easy to break in tolerance range；Meanwhile before mixed textile is carried out, terylene is pre-processed so that artificial silk and
The characteristic of terylene is more consistent, so as to be advantageous to the progress of subsequent technique.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
The technical scheme that can be realized on the basis of above-described embodiment without creative work, it is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (3)
1. a kind of artificial silk and terylene mixed textile technique, it is characterised in that：Comprise the following steps：
（1）Terylene is positioned in water steam box, the water temperature is 90-110 degrees Celsius, and the water steaming time is 80-90 hours；
（2）Terylene after water is steamed is put in pre-setting 15-25 hours under nature；
（3）Test out the maximum elongation fracture pressure value of artificial silk；
（4）Using water-jet loom, under maximum elongation fracture pressure value, mixed textile is carried out to artificial silk and terylene.
2. a kind of artificial silk according to claim 1 and terylene mixed textile technique, it is characterised in that：Water-jet loom is to washing
When synthetic fibre is drawn, nozzle of the specification for 30-45 is used, when being drawn to artificial silk, uses nozzle of the specification for 10-20.
3. a kind of artificial silk according to claim 1 and terylene mixed textile technique, it is characterised in that：The terylene is in water
Water temperature in steam box is 100 degrees Celsius.