CN107335925A - Stainless steel high frequency splicing method - Google Patents
Stainless steel high frequency splicing method Download PDFInfo
- Publication number
- CN107335925A CN107335925A CN201710426616.9A CN201710426616A CN107335925A CN 107335925 A CN107335925 A CN 107335925A CN 201710426616 A CN201710426616 A CN 201710426616A CN 107335925 A CN107335925 A CN 107335925A
- Authority
- CN
- China
- Prior art keywords
- ingredient
- stainless steel
- level accessory
- level
- forms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses stainless steel high frequency splicing method, comprise the following steps:100:Stainless steel fitting is subjected to first-surface processing and forms one-level accessory;200:Default multicolour pattern is produced on one-level accessory surface by laser and forms two level accessory;300:Secondary surface processing is carried out to the cellulose acetate plate of pre- ingredient and the processing of default groove position forms three-level accessory;400:Two level accessory and three-level accessory are subjected to ingredient and form component 500:The component completed to ingredient finishes.The marking of multicolour pattern is carried out using laser technology by stainless steel material, stainless steel material carries out ingredient with cellulose acetate material simultaneously, high temperature not eclipsed, undistorted, organic solvent-resistant characteristic during reaching stainless steel material colouring, effectively solve multicolour pattern not subtle problems, while safety and environmental protection existing for cellulose acetate ingredient.
Description
Technical field
The present invention relates to stainless steel ingredient technology, particularly stainless steel high frequency splicing method.
Background technology
The ingredient method of existing cellulose acetate, the chemical ingredient method welded mostly using organic solvent such as acetone, no
Rust steel oil spout or the pattern of stainless steel color ink-jet, color part dissolving can be made in organic solvent using the method ingredient,
Cause dim pattern.Even if using the method for high frequency splicing, also because ingredient temperature reaches 270 degree or so, pattern can be caused oily
Paint is destroyed, causes pattern distortion.
By the way that stainless steel surfaces are carried out with the research of ps pulsed laser and ns pulsed laser Treatment Analysis, obtain a result:Ps pulsed laser and ns pulsed laser
Micro-structural is formd in stainless steel surfaces, changes sample surface morphology.Stainless steel is existed using ps pulsed laser and ns pulsed laser in experiment
Irradiated in air, have studied evolution condition of the surface micro-structure under different scanning speed, sweep current and scanning times.
The market prospects of stainless steel are very considerable, and also love green grass or young crops narrows again for the development of nanosecond laser pulses technology, by material and emerging technology phase
With reference to having good Research Significance.By the process that stainless steel surfaces are carried out with nanosecond pulse processing, it has been found that nanosecond swashs
The different sweep speed of light, sweep current with and scanning times can all produce different influence to processing effect.
The content of the invention
It is an object of the invention to provide a kind of processing method to solve cellulose acetate flitch and stainless steel material ingredient
Existing multicolour pattern is not fine, the problem of pattern color distortion.
To realize that object above provides following technical scheme:
Stainless steel high frequency splicing method comprises the following steps:
100:Stainless steel fitting is subjected to first-surface processing and forms one-level accessory;
200:Default multicolour pattern is produced on one-level accessory surface by laser and forms two level accessory;
300:Secondary surface processing is carried out to the cellulose acetate plate of pre- ingredient and the processing of default groove position forms three-level
Accessory;
400:Two level accessory and three-level accessory are subjected to ingredient and form component;
500:The component completed to ingredient finishes.
Preferably, described step 400 includes:
401:Two level accessory is put into the groove position of three-level accessory, and transparent fabric is covered on two level accessory prevents table
Face aoxidizes to form first assembly;
402:First assembly is put into ingredient mould;
403:Adjusting process parameter starts ingredient, forms component.
Preferably, described technological parameter includes:Electric current is 0.9-1.1A, pressure 100-105MPa, warm-up time
60s, fall time 4s, chilling temperature 20-25 degree, cool time 150s.
Preferably, the step 500 through finishing include:The processing in located in connection hole, the planing surface and finishing impression of component reach
To the effect for going flash removed and finishing outward appearance.
Beneficial effects of the present invention are:The marking of multicolour pattern is carried out using laser technology by stainless steel material,
Stainless steel material carries out ingredient with cellulose acetate material simultaneously, and to reach when stainless steel material is painted, high temperature is not eclipsed, does not lose
Very, the characteristic of organic solvent-resistant, the not subtle problems of multicolour pattern existing for cellulose acetate ingredient is effectively solved, are pacified simultaneously
Loopful is protected.
Brief description of the drawings
Fig. 1 is holistic approach flow chart of the present invention;
Fig. 2 is the specific method flow chart of step 400;
Fig. 3 is the holistic approach flow chart of embodiment one;
Fig. 4 is the specific method flow chart of step S4 in embodiment one;
Fig. 5 is the laser emission design sketch of embodiment one;
Fig. 6 is the ingredient design sketch of embodiment one.
Embodiment
The technical program is described in detail in conjunction with the accompanying drawings and embodiments.
It is as shown in Figure 1 the inventive method flow chart, specifically includes:
100:Stainless steel fitting is subjected to first-surface processing and forms one-level accessory;
200:Default multicolour pattern is produced on one-level accessory surface by laser and forms two level accessory;
300:Secondary surface processing is carried out to the cellulose acetate plate of pre- ingredient and the processing of default groove position forms three-level
Accessory;
400:Two level accessory and three-level accessory are subjected to ingredient and form component;
500:The component completed to ingredient finishes.
Wherein, step 400 as shown in Figure 2 includes:
401:Two level accessory is put into the groove position of three-level accessory, and transparent fabric is covered on two level accessory prevents table
Face aoxidizes to form first assembly;
402:First assembly is put into ingredient mould;
403:Adjusting process parameter starts ingredient, forms component.
Wherein, ingredient technique includes using high frequency splicing machine, technological parameter:Electric current is 0.9-1.1A, and pressure is
100-105MPa, warm-up time 60s, fall time 4s, chilling temperature 20-25 degree, cool time 150s.
Wherein, step 500 through finishing include:The processing in located in connection hole, the planing surface and finishing impression of component reach removal
The effect of burr and finishing outward appearance.
Using cellulose acetate material safety and environmental protection.
Embodiment one
Such as Fig. 3, a kind of decorative pattern engraving process of stainless steel spectacle frame, including:
S1:Stainless steel spectacle frame is subjected to first-surface processing and forms one-level spectacle frame;
S2:Default multicolour pattern is produced on one-level spectacle frame surface by laser and forms two level spectacle frame;
S3:Secondary surface processing is carried out to the cellulose acetate plate of pre- ingredient and the processing of default groove position forms three-level eye
Mirror holder;
S4:Two level spectacle frame and three-level spectacle frame are subjected to ingredient and form spectacle frame;
S5:The spectacle frame completed to ingredient finishes.
Wherein, step S4 as shown in Figure 4 includes:
S41:Two level frame is put into the groove position of three-level spectacle frame, and transparent fabric is covered on two level spectacle frame prevented
Surface oxidation forms the first spectacle frame;
S42:First spectacle frame is put into ingredient mould;
S43:Adjusting process parameter starts ingredient, forms spectacle frame.
Wherein, first-surface processing is to carry out acid corrosion, cleaning, polishing and throwing to the one-level spectacle frame with general frame
The processing such as light;The processing such as secondary surface processing is Dichlorodiphenyl Acetate cellulose plate sawing sheet, plane material, section, oven.
Wherein, step S41 transparent fabric be thickness in 2-3mm transparent cellulose acetate material, be covered in two level eye
Mirror holder surface.
Wherein, ingredient technique includes using high frequency splicing machine, technological parameter:Electric current is 0.9-1.1A, and pressure is
100-105MPa, warm-up time 60s, fall time 4s, chilling temperature 20-25 degree, cool time 150s.
Wherein, step S5 through finishing include:The processing in located in connection hole, the planing surface and finishing impression of component reach defeathering
The effect of thorn and finishing outward appearance.
Wherein, the laser implementation in step S2 is:
It is 254mm in field lens F:
Color | Pulsewidth (ns) | Frequency (khz) | Fill spacing (mm) | Speed (mm/s) | Power |
It is red | 60 | 80 | 0.001 | 1000 | 70% |
Blueness | 6 | 200 | 0.001 | 1000 | 40% |
Green | 9 | 350 | 0.001 | 1000 | 60% |
Yellow | 100 | 120 | 0.01 | 600 | 60% |
It can be seen from data above:Show the difference of color, single pulse energy of main stimulated light itself and it stainless
Laser beam overlap ratio on steel disc influences.
The two level spectacle-frame 101 and two level leg of spectacles 102 of two level spectacle frame after laser emission are illustrated in figure 5, such as Fig. 6 institutes
It is shown as the two level spectacle-frame 101 of two level spectacle frame and the three-level spectacle-frame 103 and three-level of two level leg of spectacles 102 and three-level spectacle frame
Effect diagram after the ingredient of leg of spectacles 104.
Claims (4)
1. stainless steel high frequency splicing method is it is characterised in that it includes following steps:
100:Stainless steel fitting is subjected to first-surface processing and forms one-level accessory;
200:Default multicolour pattern is produced on one-level accessory surface by laser and forms two level accessory;
300:Secondary surface processing is carried out to the cellulose acetate plate of pre- ingredient and the processing of default groove position forms three-level accessory;
400:Two level accessory and three-level accessory are subjected to ingredient and form component;
500:The component completed to ingredient finishes.
2. stainless steel high frequency splicing method according to claim 1, it is characterised in that described step 400 includes:
401:Two level accessory is put into the groove position of three-level accessory, and transparent fabric is covered on two level accessory prevents Surface Oxygen
Change forms first assembly;
402:First assembly is put into ingredient mould;
403:Adjusting process parameter starts ingredient, forms component.
3. stainless steel high frequency splicing method according to claim 2, it is characterised in that described technological parameter includes:Electricity
Flow for 0.9-1.1A, pressure 100-105MPa, warm-up time 60s, fall time 4s, chilling temperature 20-25 degree, cool time
150s。
4. stainless steel high frequency splicing method according to claim 1, it is characterised in that the step 500 through finishing
Including:The processing in located in connection hole, the planing surface and finishing impression of component have the function that flash removed and finishing outward appearance.