CN107326270A - A kind of metal handware plating nickel material - Google Patents
A kind of metal handware plating nickel material Download PDFInfo
- Publication number
- CN107326270A CN107326270A CN201710382492.9A CN201710382492A CN107326270A CN 107326270 A CN107326270 A CN 107326270A CN 201710382492 A CN201710382492 A CN 201710382492A CN 107326270 A CN107326270 A CN 107326270A
- Authority
- CN
- China
- Prior art keywords
- parts
- nickel
- metal
- weight
- plating nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal handware plating nickel material, using nickel as raw material, include the component of following parts by weight：0.1 0.35 parts of carbon；70 80 parts of iron；0.5 0.8 parts of manganese；58 parts of copper；0.44 0.89 parts of cobalt；0.12 0.35 parts of tungsten.The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, using nickel as raw material, and increased tungsten, manganese and cobalt increase the intensity of metal material, increase abrasion resistant effect and corrosion resistance, improve the stability of material.
Description
Technical field
The present invention relates to a kind of metal material, more particularly to a kind of metal handware plating nickel material.
Background technology
Hardware ＆ tools is important basic part, is built in most of Mechanical Product's Machinings, engineering structure, the dimensions of all products
Repair and daily life in using quite varied.Hardware ＆ tools is highly professional steel grade with steel, and it should have what height hardened
Surface and the tough and tensile center portion of soft, while also there is high-speed cutting, processing characteristics, with certain processing red hardness, especially
It is to shear can not jump mouth, chip off-falling, peeling etc..Because steel grade should have these special performances, conventional hardware ＆ tools uses steel master
If a large amount of alloying element chromium Cr, nickel, molybdenum Mo, vanadium V etc. are added in medium carbon steel, or even also increase tungsten W, titanium Ti and cobalt Co etc.
Valuable rare heavy metal, by controlling alloy smelting, the cooling of rolling (forging) temperature control, processing and heat treatment, forms consolidating for disperse
Molten tissue, precipitation carbon compound hardening constituent, you can mechanical property, processing characteristics required by acquisition above hardware ＆ tools etc..It is many
Well known, alloying element chromium Cr, nickel, molybdenum Mo, vanadium V etc., or tungsten W, titanium Ti and cobalt Co etc. are expensive, using these alloys member
The steel grade cost of element production is high, and the inevitable price height of hardware ＆ tools of manufacture, the market sales volume are few.Meanwhile, it is expensive using these
The instrument of steel manufacture, service life is greatly rich, and resource has been wasted.In addition, with the development of metallurgical technology, ferrous materials
Degree of purity is improved, and the technological level such as processing and heat treatment is specialized, and the alloy added in hardware ＆ tools steel is gradually reduced.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of metal handware plating nickel material.
The technical solution adopted by the present invention is：
A kind of metal handware plating nickel material, using nickel as raw material, includes the component of following parts by weight：
0.1-0.35 parts of carbon；
70-80 parts of iron；
0.5-0.8 parts of manganese；
5-8 parts of copper；
0.44-0.89 parts of cobalt；
0.12-0.35 parts of tungsten.
Further, the parts by weight of the carbon are 1.5 parts.
Further, the parts by weight of the copper are 6 parts.
Further, the parts by weight of the tungsten are 0.22 part.
Further, the parts by weight of the manganese are 0.65 part.
Further, the parts by weight of the nickel are 3-8 parts.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, and using nickel as raw material, increased tungsten, manganese and cobalt increase metal
The intensity of material, increase abrasion resistant effect and corrosion resistance, improve the stability of material.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
A kind of metal handware plating nickel material, using nickel as raw material, the parts by weight of nickel are 3-8 parts, in addition to following parts by weight
Component：
0.1 part of carbon；
70 parts of iron；
0.5 part of manganese；
5 parts of copper；
0.44 part of cobalt；
0.12 part of tungsten.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, and using nickel as raw material, increased tungsten, manganese and cobalt increase metal
The intensity of material, increase abrasion resistant effect and corrosion resistance, improve the stability of material.
Embodiment 2
A kind of metal handware plating nickel material, using nickel as raw material, the parts by weight of nickel are 3-8 parts, in addition to following parts by weight
Component：
0.25 part of carbon；
75 parts of iron；
0.65 part of manganese；
6.5 parts of copper；
0.65 part of cobalt；
0.2 part of tungsten.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, and using nickel as raw material, increased tungsten, manganese and cobalt increase metal
The intensity of material, increase abrasion resistant effect and corrosion resistance, improve the stability of material.
Embodiment 3
A kind of metal handware plating nickel material, using nickel as raw material, the parts by weight of nickel are 3-8 parts, in addition to following parts by weight
Component：
0.35 part of carbon；
80 parts of iron；
0.8 part of manganese；
8 parts of copper；
0.89 part of cobalt；
0.35 part of tungsten.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, and using nickel as raw material, increased tungsten, manganese and cobalt increase metal
The intensity of material, increase abrasion resistant effect and corrosion resistance, improve the stability of material.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within model claimed of the invention
Enclose.
Claims (6)
1. a kind of metal handware plating nickel material, it is characterised in that：Using nickel as raw material, include the component of following parts by weight：
0.1-0.35 parts of carbon；
70-80 parts of iron；
0.5-0.8 parts of manganese；
5-8 parts of copper；
0.44-0.89 parts of cobalt；
0.12-0.35 parts of tungsten.
2. a kind of metal handware according to claim 1 plating nickel material, it is characterised in that：The parts by weight of the carbon
For 1.5 parts.
3. a kind of metal handware according to claim 1 plating nickel material, it is characterised in that：The parts by weight of the copper
For 6 parts.
4. a kind of metal handware according to claim 1 plating nickel material, it is characterised in that：The parts by weight of the tungsten
For 0.22 part.
5. a kind of metal handware according to claim 1 plating nickel material, it is characterised in that：The parts by weight of the manganese
For 0.65 part.
6. a kind of metal handware according to claim 1 plating nickel material, it is characterised in that：The parts by weight of the nickel
For 3-8 parts.