CN107326269A - A kind of metallic element carbon steel - Google Patents
A kind of metallic element carbon steel Download PDFInfo
- Publication number
- CN107326269A CN107326269A CN201710382426.1A CN201710382426A CN107326269A CN 107326269 A CN107326269 A CN 107326269A CN 201710382426 A CN201710382426 A CN 201710382426A CN 107326269 A CN107326269 A CN 107326269A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon
- weight
- metallic element
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of metallic element carbon steel, using carbon and iron as raw material, includes the component of following parts by weight：0.12 0.25 parts of gold；0.65 0.7 parts of manganese；0.45 0.6 parts of cobalt；0.1 0.3 parts of magnesium；0.2 0.35 parts of palladium；0.22 0.34 parts of chromium.The beneficial effects of the invention are as follows：Using carbon and iron as primary raw material, proportioning is scientific and reasonable, and the gold element of addition increases the intensity of metal material, increase abrasion resistant effect and corrosion resistance, improves the stability of metal material.
Description
Technical field
The present invention relates to a kind of metal material, more particularly to a kind of metallic element carbon steel.
Background technology
Parts are in most of Mechanical Product's Machinings, engineering structure construction, the maintenance of all products and daily life
Using quite varied.It should have the high surface hardened and the tough and tensile center portion of soft, while also having high-speed cutting, processability
Can, with certain processing red hardness, particularly shear can not jump mouth, chip off-falling, peeling etc..Because steel grade should have these special
Performance, conventional parts mainly add a large amount of alloying element chromium Cr, nickel, molybdenum Mo, vanadium V etc. with steel in medium carbon steel,
Even also increase the valuable rare heavy metals such as tungsten W, titanium Ti and cobalt Co, by controlling alloy smelting, rolling (forging) temperature control cold
But, processing and heat treatment, forms melting tissue admittedly, separating out carbon compound hardening constituent for disperse, you can obtain required by above parts
Mechanical property, processing characteristics etc..It is well known that alloying element chromium Cr, nickel, molybdenum Mo, vanadium V etc., or tungsten W, titanium Ti and cobalt Co
Etc. expensive, the steel grade cost produced using these alloying elements is high, and the inevitable price of parts of manufacture is high, market sale
Amount is few.Meanwhile, the instrument manufactured using these expensive steel, service life is greatly rich, and resource has been wasted.In addition, with
The development of metallurgical technology, ferrous materials degree of purity is improved, and the technological level such as processing and heat treatment is specialized, is added in parts steel
Alloy is gradually reduced.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of metallic element carbon steel.
The technical solution adopted by the present invention is：
A kind of metallic element carbon steel, using carbon and iron as raw material, includes the component of following parts by weight：0.12-0.25 parts
Gold；0.65-0.7 parts of manganese；0.45-0.6 parts of cobalt；0.1-0.3 parts of magnesium；0.2-0.35 parts of palladium；0.22-0.34 parts
Chromium.
Further, the parts by weight of the carbon are 5-8 parts.
Further, the parts by weight of the iron are 85-90 parts.
Further, the golden parts by weight are 0.185 part.
Further, the parts by weight of the manganese are 0.65 part.
The beneficial effects of the invention are as follows：Using carbon and iron as primary raw material, proportioning is scientific and reasonable, and the gold element of addition is increased
The intensity of metal material, increase abrasion resistant effect and corrosion resistance, improve the stability of metal material.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
A kind of metallic element carbon steel, using carbon and iron as raw material, the parts by weight of carbon are 5 parts, and the parts by weight of iron are 85 parts,
Also include the component of following parts by weight：0.12 part of gold；0.65 part of manganese；0.45 part of cobalt；0.1 part of magnesium；0.2 part of palladium；
0.22 part of chromium.
The beneficial effects of the invention are as follows：Using carbon and iron as primary raw material, proportioning is scientific and reasonable, and the gold element of addition is increased
The intensity of metal material, increase abrasion resistant effect and corrosion resistance, improve the stability of metal material.
Embodiment 2
A kind of metallic element carbon steel, using carbon and iron as raw material, the parts by weight of carbon are 6 parts, and the parts by weight of iron are 87 parts,
Also include the component of following parts by weight：0.2 part of gold；0.68 part of manganese；0.5 part of cobalt；0.2 part of magnesium；0.28 part of palladium；
0.3 part of chromium.
The beneficial effects of the invention are as follows：Using carbon and iron as primary raw material, proportioning is scientific and reasonable, and the gold element of addition is increased
The intensity of metal material, increase abrasion resistant effect and corrosion resistance, improve the stability of metal material.
Embodiment 3
A kind of metallic element carbon steel, using carbon and iron as raw material, the parts by weight of carbon are 8 parts, and the parts by weight of iron are 90 parts,
Also include the component of following parts by weight：0.25 part of gold；0.7 part of manganese；0.6 part of cobalt；0.3 part of magnesium；0.35 part of palladium；
0.34 part of chromium.
The beneficial effects of the invention are as follows：Using carbon and iron as primary raw material, proportioning is scientific and reasonable, and the gold element of addition is increased
The intensity of metal material, increase abrasion resistant effect and corrosion resistance, improve the stability of metal material.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within model claimed of the invention
Enclose.
Claims (5)
1. a kind of metallic element carbon steel, it is characterised in that：Using carbon and iron as raw material, include the component of following parts by weight：
0.12-0.25 parts of gold；0.65-0.7 parts of manganese；0.45-0.6 parts of cobalt；0.1-0.3 parts of magnesium；0.2-0.35 parts of palladium；
0.22-0.34 parts of chromium.
2. a kind of metallic element carbon steel according to claim 1, it is characterised in that：The parts by weight of the carbon are 5-
8 parts.
3. a kind of metallic element carbon steel according to claim 1, it is characterised in that：The parts by weight of the iron are
85-90 parts.
4. a kind of metallic element carbon steel according to claim 1, it is characterised in that：The golden parts by weight are
0.185 part.
5. a kind of metallic element carbon steel according to claim 1, it is characterised in that：The parts by weight of the manganese are
0.65 part.