CN107325736A - A kind of automobile external-use fluorinated graphene glazing protects wax - Google Patents
A kind of automobile external-use fluorinated graphene glazing protects wax Download PDFInfo
- Publication number
- CN107325736A CN107325736A CN201710658827.5A CN201710658827A CN107325736A CN 107325736 A CN107325736 A CN 107325736A CN 201710658827 A CN201710658827 A CN 201710658827A CN 107325736 A CN107325736 A CN 107325736A
- Authority
- CN
- China
- Prior art keywords
- parts
- fluorinated graphene
- wax
- automobile external
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to automobile external-use wax field, specially a kind of automobile external-use fluorinated graphene glazing protection wax.Formed by the uniform mixed preparing of the raw material of following mass fraction：20~40 parts of Brazil wax；10~20 parts of atoleine；5~10 parts of ethylene glycol；2~6 parts of dimethyl polysiloxane；5~8 parts of glyceryl monostearate；0.5~2 part of fluorinated graphene.A kind of fluorinated graphene glazing protection wax that the present invention is provided includes fluorinated graphene; with excellent performances such as the lubricities that hydrophobicity is strong, high temperature resistant, corrosion-resistant, rub resistance, chemical property are stable and good; used in car surface; with superpower expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as; it can prevent dust dirt from sticking to bodywork surface simultaneously, self-cleaning effect is good.
Description
Technical field
The present invention relates to automobile external-use wax field, specially a kind of automobile external-use fluorinated graphene glazing protection wax.
Background technology
Automobile has higher requirement as the most common vehicles in the modern life, people except the performance to automobile
Outside, the outward appearance also to automobile is increasingly paid attention to, because automobile is often exposed in air, unavoidably can be long by wind and weather
This can bring damage to the lacquer painting of automobile in the past, influence automobile it is attractive in appearance, it is therefore desirable to automobile external-use wax is protected to lacquer painting
Support and protect.General automobile external-use wax is merely capable of to a certain extent maintaining automobile finish, but due to itself property
Matter limits and is unable to reach good expelling water, anti-scratch and self-cleaning and other effects.It is therefore desirable to by improving, there is provided a kind of more preferable
Automobile external-use wax, with superpower expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as, together
When can prevent dust dirt from sticking to bodywork surface, with good self-cleaning effect.
The content of the invention
In order to overcome the deficiencies in the prior art, it is an object of the invention to provide a kind of automobile external-use fluorinated graphene glazing
Protect wax, with good expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as, while energy
Enough prevent dust dirt from sticking to bodywork surface, with good self-cleaning effect.
In order to solve the above problems, the technical scheme is that：
A kind of automobile external-use fluorinated graphene glazing protects wax, by the uniform mixed preparing of the raw material of following mass fraction
Into：
20~40 parts of Brazil wax；10~20 parts of atoleine；5~10 parts of ethylene glycol；Dimethyl polysiloxane 2~6
Part；5~8 parts of glyceryl monostearate；0.5~2 part of fluorinated graphene.
Described automobile external-use fluorinated graphene glazing protection wax, the degree of fluorination of fluorinated graphene is 0.2~0.9.
Described automobile external-use fluorinated graphene glazing protection wax, the size of fluorinated graphene is 5~300 μm.
The design philosophy of vehicle glazing of the present invention protection wax composition is：
Vehicle glazing of the present invention protection wax is by 20~40 parts of Brazil wax；10~20 parts of atoleine；Ethylene glycol 5~10
Part；2~6 parts of dimethyl polysiloxane；5~8 parts of glyceryl monostearate；0.5~2 part of fluorinated graphene etc. is constituted.It is above-mentioned each
The effect of individual composition and synergy each other are as follows：
Brazil wax：It is the complex mixture that the main ester by acid and carboxylic acid is constituted, is that a kind of quality is very rigid
Nontoxic pure natural wax, it has good emulsibility, tack, frictional property, release, slip and viscosity hardness
Scalability, is one of most commonly used native paraffin of applicability in the world.
Atoleine：Semi-transparent clear oily liquids, it is stable to light, heat, acid etc., but contact light and heat can be slowly for a long time
Oxidation.For manufacturing washing powder, synthetic detergent, synthetic petroleum albumen, farm chemical emulgent etc..
Ethylene glycol：Colourless, pleasantly sweet, thick liquid, is mainly used in polyester dacron processed, polyester resin, hygroscopic agent, plasticising
Agent, surfactant, synthetic fibers, cosmetics and explosive, and be used as the solvent of dyestuff, ink etc., prepare the freeze proof of engine
Agent, gas dewatering agent, manufacture resin, the wetting agent that can also be used for glassine paper, fiber, leather, adhesive.
Dimethyl polysiloxane：Dimethyl polysiloxane, nickname Dimethicone, dimethicone are mainly used in disappearing
Infusion, fruit glaze agent, anticaking agent.
Glyceryl monostearate：Glyceryl monostearate is a kind of chemicals, pure white to pink wax.
Particularly fluorinated graphene is laminated structure, is dispersed in cooperative effect in wax body system obvious.
Advantages of the present invention is with beneficial effect：
1st, the present invention is a kind of new material for the class laminated structure being made up of carbon, fluorine atom using fluorinated graphene, is had
Intensity is high, specific surface area is big, uvioresistant, lubrication, scratch resistant the features such as.
2nd, traditional vehicle wax is combined fluorinated graphene by the present invention, can lift scratch resistance and the performance such as finish paint is anti-aging.
Embodiment
In order to be best understood from the present invention, a part of specific embodiment is set forth below, and the present invention will be described, but related hair
Bright form of implementation is not limited to such example.
Embodiment 1
In the present embodiment, automobile external-use fluorinated graphene glazing protection wax is uniformly mixed by the raw material of following mass fraction
It is formulated：
35 parts of Brazil wax, 19 parts of atoleine, 7 parts of ethylene glycol, 6 parts of dimethyl polysiloxane, glycerol monostearate
4 parts of ester, 1 part of fluorinated graphene.Degree of fluorination (the i.e. fluorocarbons CF of the fluorinated graphene of usexMiddle x value) it is 0.6, piece
Footpath is 100nm.
In the present embodiment, the using effect of automobile external-use fluorinated graphene glazing protection wax is as follows：Used in car surface,
With superpower expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as, while can prevent
Dust dirt sticks to bodywork surface, and self-cleaning effect is good.
Embodiment 2
In the present embodiment, automobile external-use fluorinated graphene glazing protection wax is uniformly mixed by the raw material of following mass fraction
It is formulated：
40 parts of Brazil wax, 20 parts of atoleine, 10 parts of ethylene glycol, 6 parts of dimethyl polysiloxane, glycerol monostearate
5 parts of ester, 1 part of fluorinated graphene.Degree of fluorination (the i.e. fluorocarbons CF of the fluorinated graphene of usexMiddle x value) it is 0.8, piece
Footpath is 300nm.
In the present embodiment, the using effect of automobile external-use fluorinated graphene glazing protection wax is as follows：Used in car surface,
With superpower expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as, while can prevent
Dust dirt sticks to bodywork surface, and self-cleaning effect is good.
Embodiment 3
In the present embodiment, automobile external-use fluorinated graphene glazing protection wax is uniformly mixed by the raw material of following mass fraction
It is formulated：
25 parts of Brazil wax, 12 parts of atoleine, 8 parts of ethylene glycol, 3 parts of dimethyl polysiloxane, glycerol monostearate
6 parts of ester, 2 parts of fluorinated graphene.Degree of fluorination (the i.e. fluorocarbons CF of the fluorinated graphene of usexMiddle x value) it is 0.4, piece
Footpath is 200nm.
In the present embodiment, the using effect of automobile external-use fluorinated graphene glazing protection wax is as follows：Used in car surface,
With superpower expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as, while can prevent
Dust dirt sticks to bodywork surface, and self-cleaning effect is good.
Embodiment result shows that a kind of fluorinated graphene glazing protection wax that the present invention is provided includes fluorinated graphene, has
There are the excellent performances such as the lubricity that hydrophobicity is strong, high temperature resistant, corrosion-resistant, rub resistance, chemical property are stable and good, in vapour
Car surface is used, with superpower expelling water, uvioresistant, Acid Rain, prevent automobile finish scratch and gloss it is lasting the effects such as, together
When can prevent dust dirt from sticking to bodywork surface, self-cleaning effect is good.
Claims (3)
1. a kind of automobile external-use fluorinated graphene glazing protects wax, it is characterised in that uniformly mixed by the raw material of following mass fraction
Conjunction is formulated：
20~40 parts of Brazil wax；10~20 parts of atoleine；5~10 parts of ethylene glycol；2~6 parts of dimethyl polysiloxane；It is sweet
Oily 5~8 parts of monostearate；0.5~2 part of fluorinated graphene.
2. automobile external-use fluorinated graphene glazing according to claim 1 protects wax, it is characterised in that fluorinated graphene
Degree of fluorination is 0.2~0.9.
3. automobile external-use fluorinated graphene glazing according to claim 1 protects wax, it is characterised in that fluorinated graphene
Size is 5~300 μm.